Low transformation temperature (LTT) alloys allow to control residual stresses already during the welding process. Especially high-strength structural steel applications may benefit from the LTT effect as they are sensitive to residual stresses due to a limited ductility. Within this study, two modified LTT alloys were tested concerning their weldability under varying conditions. Beside the transformation behavior, basic material properties were determined from all weld metal. Hot cracking as well as cold cracking susceptibility was evaluated using specific tests. The materials' capability for residual stress control was characterized by online measurements of the occurring loads during double-sided multipass fillet welding in a special test facility. Varying heat control parameters were found to affect the stress buildup significantly. In the specific case, the results revealed that higher working temperatures may favor lower stress buildup despite the higher overall heat input. Local residual stress measurements using X-ray diffraction support this finding.
The objective of the FATWELDHSS project was to study post-weld treatment techniques and their effect on the fatigue life of MAG welded attachments in High Strength Steel (HSS). Fatigue cracks in steel structures often occur at welded joints, where stress concentrations due to the joint geometry and tensile residual stresses are relatively high. Fatigue life improvement techniques, which rely on improving the stress field and/or the surface geometry around the welded joints, are generally known to be beneficial. Therefore, within the framework of this project, the following were examined: diode laser weld toe re-melting; High Frequency Mechanical Impact (HFMI) treatment; Low Transformation Temperature (LTT) filler wires Laser diode re-melting was used to improve the surface profile at the weld toe and thus reduce stress concentrations. HFMI treatment involving high frequency hammering of the weld toe is another technique that can produce a smooth weld toe profile but, more significantly, which also can introduce compressive residual stresses. Lastly, two new LTT filler wires were developed within the project as these can decrease or even remove tensile residual stresses resulting from weld zone shrinkage. An extensive fatigue testing programme was set up to establish the levels of improvement in the fatigue lives of the welded attachments achieved by application of the selected improvement techniques. Furthermore, two industrial demonstrators were selected that could show the project achievements in terms of facilitating the introduction of high strength steels by overcoming the limitations posed by the fatigue properties of the welded joints. In addition, modelling tools were developed to predict the residual stresses at the welded joint. Finally, practical guidelines were developed for enhancing the fatigue strength of HSS welded structures
The results reported in this research study are part of a larger EU RFCS (Research Fund for Coal and Steel) project where the aim is to study the fatigue behavior of improved welds in high strength steels by utilizing different improvement techniques. In this particular study LTT (Low Transformation Temperature) weld filler material have been investigated and their possibility to improve the fatigue strength. The characteristic of these filler material is that they undergo phase transformation at temperature close to room temperature which will reduce the tensile residual stress in the weld and in some cases result in compressive residual stresses. Two different LTT alloy compositions have been developed, with different Ms (Martensite Start) temperatures in order to study the amount of tensile/compressive residual stresses produced by these wires. Welding residual stress measurements were carried out by X-ray diffraction technique. Plates with welded longitudinal attachments were fabricated in 700 MPa and 960 MPa steel grades using different LTT filler materials. These specimens were fatigue tested in constant and variable amplitude loading and the fatigue test results were compared with results from specimen welded with conventional weld filler material.