Polymer deposition morphology by electrospray deposition - Modifications through distance variation
(2014)
Electrospray deposition (ESD) of highly diluted polymers was examined with regard to the deposited surface structure. Only the flight distance (flight time) onto the resulting deposited surface was varied from 20 to 200 mm.
An apparatus without any additional heating or gas flows was used. Polyacrylic acid (PAA) and polyallylamine (PAAm) in methanol were deposited on Si wafers. The polymer layers were characterized by scanning electron microscopy, X-ray photoelectron spectroscopy, derivatization reactions and Fourier transform infrared spectroscopy using a grazing incidence unit.
SEM images illustrated the changing structures of PAA and PAAm. For PAA the deposited structure changed from a smooth film (20 mm) to a film with individual droplets on the coated surface (100 mm and 200 mm), while for PAAm individual droplets can be seen at all distances. The ESD process with cascades of splitting droplets slows down for PAA after distances greater than 40 mm. In contrast, the ESD process for PAAm is nearly stopped within the first flight distance of 20 mm. Residual solvent analysis showed that most of the solvent evaporated within the first 20 mm capillary-sample distance.
Substrate-induced self-assembly of donor-acceptor type compounds with terminal thiocarbonyl groups
(2013)
Two types of conjugated thiocarbonyl-terminated compounds have been synthesized and their ability to be adsorbed on surfaces of the different nature, namely, glass, polytetrafluoroethylene (PTFE), and gold has been studied. Different morphology of the films prepared by thermal vacuum evaporation and drop-casting from solutions has been observed depending on the surface used. It has been found that gold surface has a unique property to influence self-assembly of both monolayer and larger aggregates or crystals of the compounds, in contrast to glass and PTFE substrates. It was found that thiocarbonyl group is able to be chemisorbed to the gold surface. However, it was concluded that in spite of the fact that the thiocarbonyl groups are important for the chemical interaction with the gold surface, physical adsorption on the substrate surface, compoundcompound and compound–solvent (when using solution) interactions are of great significance to drive self-assembly of the final film.