Calcined clays as supplementary cementitious materials (SCMs) have been identified and credited to be a viable solution in mitigating the CO2 emissions related to cement production and consumption. Calcined clays range from a variety of different clay types based on an assortment of varying minerals and compositions. While extensive data is available on kaolinitic clays (based on the 1:1 clay type), other clays such as brick clays (based on the 2:1 clay type) are currently understudied, although such clays are largely more available than the kaolinitic clays.
The aim of this thesis is to draw attention to the varying compositions present in two selected brick clays in Germany and elaborate on how such compositions affect their suitability to be used as SCMs in blended cement systems. The novelty of this thesis explains the relationship between the reactivity of the bricks to their varying compositions and their suitability for their employment as SCMs. This was based on their chemical and physical transformations in the calcination temperature range 650–900 or 950 °C, and the performance of the calcined brick clays in blended cement systems measured by their heat evolution, strength development and durability-related properties. The results of their performance were compared to two kaolinitic clays with varying compositions. While the kaolinitic clays generally exhibited the best performance as SCMs, the brick clay with a lower Fe2O3 content showed promising results similar to the kaolinitic clays when an optimum calcination temperature is applied and when substituted at a moderate cement substitution rate. Thus, this finding promoted further efforts made to improve the reactivity of the brick clay by producing a mixed clay composed of 50 % brick clay (with lower Fe2O3 content) and 50 % kaolinitic clay. The mixed clay was compared to the two individual brick clays and one kaolinitic clay, whereby optimum calcination conditions were performed in large-scale simulating an industrial-scale production of SCMs. All calcined clays exhibited pozzolanic reactivity, with the performance of the brick clays inferior to the kaolinitic clay, however, the mixed clay performed very similar to the kaolinitic clay.
At a similar degree of hydration compared to plain Portland cement, the good performance of the mixed clays was especially evident in the strength development and improved chloride penetration resistance, which was caused by a refinement in the pore structure in the cementitious systems. Moreover, it was deduced that not only the high surface area, but also, the solubility of Si and Al ions in the resulting calcinate of the mixed clays plays a significant role when calcined at ~600–700 °C, which points to viable options for optimal employment of brick clays in cementitious systems.
While calcined clays in general have been credited with a great potential to mitigate CO2 emissions related to cement production and consumption, calcined brick clays are currently understudied in this regard. In the present work, two brick clays, a low-grade kaolinitic clay, and a mixed clay composed of 50% brick clay and 50% low-grade kaolinitic clay were studied regarding transformations on calcination, and strength and durability performance as well as pore structure of mortars made with the blended cements. All calcined clays exhibited pozzolanic reactivity, with the performance of the brick clays inferior to the low-grade kaolinitic clay. However, the mixed clay performed very similar to the low-grade kaolinitic clay, which points to a viable option for optimal use of brick clays in cementitious systems. The carbonation resistance of the blended cement mortars was generally worse than that of the plain Portland cement mortar, as expected, but the former exhibited a significantly improved chloride penetration resistance. The latter improvement was due to pore structure refinement in the blended cement mortars, compared to the Portland cement mortar.
Two brick clays (rich in 2:1 clay minerals) and a low-grade kaolinitic clay were studied regarding their transformations during calcination and their performance in blended cement mortars. The mortars with calcined clays exhibited decreased workability (slump flow), but this effect could be mitigated by employment of a conventional superplasticizer; however, compressive strength of the hardened mortar was lowered in some cases. While the kaolinitic clay generally yielded the highest strength, the performance of a brick clay could be increased by grinding to higher fineness and by mixing it with the kaolinitic clay.
The production of Portland cement causes a substantial environmental impact, since the calcination of limestone results in high emissions of carbon dioxide. The use of supplementary cementitious materials such as calcined clays as partial replacement for Portland cement offers a solution to limit this environmental impact. This paper investigates four clays from deposits in central Germany with the aim of obtaining pozzolans for the production of Portland-pozzolana cement. The results obtained show that the calcined clays possess pozzolanic properties, which differ depending on calcination temperature and the relative amounts of Kaolinite and 2:1 clay minerals.