The aim of this chapter is to give an overview of basic and advanced state-of-the-art microstructural and spectroscopic analytics to investigate inorganic material corrosion in the context of biochemically aggressive sewers. The chapter covers optical methods, electron beam, X-ray and neutron techniques (SEM, MLA, XRF, XRD, CT, Neutron radiography and tomography), and spectroscopic methods (MAS-NMR, FT-IR, and Raman). For each technique, a short section on the fundamental scientific background of the method precedes and examples of data output from the latter in respect to the corrosion of cementitious materials including reinforced concrete is presented.
This chapter aims to give a brief introduction into the field of alkali activated materials (AAM) and their physicochemical material behavior when exposed to sulfuric acid and in biochemically aggressive sewer environments. Additionally, the differences in material behavior within chemical (abiotic) and microbially induced acid environments are highlighted. Finally, existing data on overall performance of AAM, compared to conventional concrete-based building materials in sewer systems will be discussed.
Metakaolin-based alkali activated mortars (AAM) - with and without CuSO4·5H2O and ZnO addition (mass ratio Mn+/solid binder 0.08% to 1.7%) - were casted and exposed within an extensive long-term field campaign over the period of 20 months to a sewer basin, strongly affected by biogenic acid corrosion. (Un-)exposed AAM were tested regarding their physicochemical and microstructural properties, bioreceptivity and overall durability. Metal addition led to a retarding effect during alkali-activation reaction, as well as to an increase in open porosity of up to 3.0% and corresponding lower compressive strength of up to 10.9%. Reduced microbial colonization and diversity were observed on AAM with Cu, while Zn addition led to increased biodiversity. We propose that the observed higher durability of Cu-doped AAM is due to antibacterial effects and associated reduction of biogenic acid production, superseding overall negative effects of metal-dosage on physical material properties. Observed lower durability of Zn-doped AAM was related to combined negative physicochemical and microbial effects.