The publication is an extended abstract on the modelling of the manufacturing process related residual stresses in type 4 pressure vessels for hydrogen storage. A 2D analytical model based on the classical laminate theory and a 3D finite element model are introduced. The calculated residual stress state after the filament winding process as well as the stress state in service are presented and discussed.
In this lecture, the safety assessment of hydrogen gas storage systems is presented using the example of composite pressure vessels. The main element is a probabilistic approval approach based on five steps. Firstly, the testing and evaluation of properties at the beginning of life are shown. Secondly, methods for artificial aging and the effect on the residual strength are presented. Thirdly, testing against dedicated accidents is introduced. Fourthly, effects on the surveillance of production quality are discussed. Finally, degradation and the end of life are estimated. Background information and examples are given for each step. The assessment presented is a method applicable for many safety-related systems.
Im Vortrag wird zunächst erläutert, dass auch im Fall der Wasserstoffversorgung die Schadensanalyse, -vermeidung und die wiederkehrende Prüfung von Speichern in engem Zusammenhang stehen.
Der Wasserstofftransport in Deutschland hat bereits deutlich zugenommen und wird in den nächsten Jahren weiter erheblich zunehmen. Dies führt zu einem stärkeren Fokus auf die wirtschaftlichen Aspekte im Transport und der wiederkehrenden Prüfung. Letztere droht, ohne neue technische Ansätze zum Flaschenhals in der Verfügbarkeit vorhandener Transportkapazitäten zu werden.
Das gegenwärtige System der Wasserdruckprüfung bis zum sog. Prüfdruck mit Innen- und Außenbesichtigung etc., die im Normalfall alle 5 Jahre durchzuführen ist, führt zu jeweils etwa 8 Wochen Stillstand. Das Aufwendige dabei sind die Trocknungs- und Spülprozesse, die notwendig sind, um wieder entsprechend reinen Wasserstoff abfüllen zu können. Auf Basis der BAM GGR‘n 021 und 022 lässt sich beim Nachweis entsprechender, probabilistischer Restzuverlässigkeiten diese Frist in Deutschland auf 10 Jahre ausdehnen. Diesen Weg sind in den letzten Jahren viele Betreiber gegangen.
Mit Blick auf die derzeit fast exponentielle Zunahme von Transporteinheiten kann auch diese Verlängerung der Prüffristen das Problem nicht lösen. Auch das Umschwenken von hydraulischer, auf die heute bereits genehmigungsfähige Gasdruckprüfung bis zum Prüfdruck bringt zwar eine Verkürzung der Stillstandzeiten, erfordert aber erhebliches Investment in Schutzmaßnahmen.
Als hinreichend zielführendes Konzept für Transporteinheiten mit vielen Elementen wird im Vortrag eine Mischung aus probabilistischem Ansatz und zerstörungsfreien Prüfungen erläutert und bzgl. Aufwand und Nutzen im Vergleich zu den üblichen Verfahren visualisiert. Voraussetzung für diesen vorgestellten Ansatz sind die Weiterentwicklung und Qualifizierung der Schallemissionsanalyse als Ersatz für die derzeitig zerstörenden Prüfungen und auch eine durchgängig digitale Lebenslaufakte, die eine lückenlose Zuordnung von Baumusterprüfung, Herstellungslos, Betreiber und Betriebsdaten erlaubt.
Für Transporteinheiten mit wenigen, sehr großen Elementen wird dagegen das sog. Online-Monitoring mit fest installierter und permanent messender Technik gesehen.
Für die Anwendung beider Lösungsansätze sind umfangreiche Änderungen im Recht erforderlich.
The presentation starts with the first agreement of making a national attempt for the introduction of a pV-limit for hydrogen transport. It explains aspects of the technical development, provides an impression of catastrophic incidents, and explains the difference between risk control and consequence limitation. Then the process of determining consequences and the result from the discussion at the UN-WG are explained. The next part summarises the approach for counting the number of impacted persons as a function of the model of pressure wave, the pressure peak, the limits of injured persons and the population density. Finally, the latest state of the discussion and the subsequent recommendations for a pV-value and the adequate phrases for explanation are introduced.
In this presentation safety aspects of hydrogen transportation are discussed. At first, the regulatory background and level of safety are presented. In the second part, the modelling of consequence due to sudden rupture of pressure receptacles is explained. Finally, the results are used to define a limit for consequence to enable an acceptable and safe transport of hydrogen.
Monte-Carlo-Analysis of Minimum Burst Requirements for Composite Cylinders for Hydrogen Service
(2021)
For achieving Net Zero-aims hydrogen is an indispensable component, probably the main component. For the usage of hydrogen, a wide acceptance is necessary, which requires trust in hydrogen based on absence of major incidents resulting from a high safety level. Burst tests stand for a type of testing that is used in every test standard and regulation as one of the key issues for ensuring safety in use. The central role of burst and proof test is grown to historical reasons for steam engines and steel vessels but - with respect for composite pressure vessels (CPVs) - not due an extraordinary depth of outcomes. Its importance results from the relatively simple test process with relatively low costs and gets its importance by running of the different test variations in parallel. In relevant test und production standards (as e. g. ECE R134) the burst test is used in at least 4 different meanings. There is the burst test on a) new CPVs and some others b) for determining the residual strength subsequent to various simulations of ageing effects. Both are performed during the approval process on a pre-series. Then there is c) the batch testing during the CPVs production and finally d) the 100% proof testing, which means to stop the burst test at a certain pressure level. These different aspects of burst tests are analysed and compared with respect to its importance for the resulting safety of the populations of CPVs in service based on experienced test results and Monte-Carlo simulations. As main criterial for this the expected failure rate in a probabilistic meaning is used. This finally ends up with recommendations for relevant RC&S especially with respect to GTR 13.
The damage process of short glass fibre (30% weight) reinforced polyamide caused by mechanical loading was investigated from the beginning on micro cracking level to the incipient crack of mm-dimension. Based on high resolution computer tomography and the X-ray-refraction technique the inner surface due to micro-cracking at the short fibre ends and the fibre matrix debonding of the skin surface of the filament was determined quantitatively. With the knowledge of the fatigue crack propagation rate and fracture toughness of the material from former research projects, it was derived that the total inner surface due to micro cracks measured by X-ray refraction is much higher than the specimen could have withstand the load, supposed the surface is in a localized crack. Hence, the damage process could be described from micro to macro level. Accompanying fractographic investigations endorse the modelling based on the NDT-techniques.