Binary systems composed of Portland cement (PC) and calcium sulfoaluminate (CSA) cement have stood out for applications requiring high early strengths. Nevertheless, the application of these systems may be limited due to their properties in the fresh state, which requires a better understanding of the rheological behavior of these materials. Thus, this study evaluated the incorporation of different polycarboxylate-based superplasticizer (SP) contents (0.15, 0.20, and 0.25 wt%) on PC and PC-CSA binary cement pastes. Rotational rheometry, isothermal calorimetry, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and nitrogen adsorption and desorption tests to assess the pore size distribution of cement pastes were conducted. While the SP incorporation reduced the dynamic yield stress of PC pastes, it progressively increased the yield stress of PC-CSA systems. The increase in SP content increased the main heat flow peak of PC-CSA pastes, although it did not significantly affect the cumulative heat after 160 h of hydration. FTIR and XRD confirm higher ettringite contents in the binary systems and indicate the presence of carboaluminates phases after 7 d of hydration in both PC and PC-CSA and hemicarboaluminate in PC-CSA pastes. The CSA incorporation reduced the cumulative pore volume by up to 32% compared to PC pastes, while the SP content evaluated did not significantly affect the porosity of PC-CSA pastes.
Volumetric changes follow Portland cement hydration reactions: aluminates' hydration is generally expansive, whereas silicates' reaction leads to shrinkage. Determining the volumetric variation at very early ages (i.e., first minutes/hours) presents operational challenges; most standards prescribe the measurement on specimens that are already hardened, while measurements from the fresh state are not standardized. This article reports the first attempt to use in-situ X-ray diffraction (XRD) to measure the early-age volumetric variation of a cementitious paste. For this purpose, a C3A + gypsum paste was assessed for 36 h, measuring its vertical displacement over time through XRD. The results showed that the expansion increased in the first ∼13 h, in line with the ettringite formed up to ∼11 h. In addition, the volumetric expansion agreed well with the heat release in calorimetry. It is concluded that the volumetric variation measurement of cementitious pastes through in-situ XRD is a promising technique, but further studies are needed to make this technique consolidated.
This study investigated the effect of incorporating three types of nanosilica (NS), two powders, and one colloidal suspension on the hydration, strength, and microstructure of calcium sulfoaluminate (CSA) cement pastes prepared with and without a superplasticizer (SP). X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy (SEM), and compressive strength tests were performed after 2, 5, and 28 days of hydration. The results showed that both NS powders delayed cement hydration at an early age, which was attributed to particle agglomeration (confirmed by dynamic light scattering). Whereas well-dispersed colloidal NS did not significantly affect the hydration of CSA at the investigated ages. SP incorporation improved the dispersion of CSA cement particles, resulting in a 10% increase in the degree of hydration of ye’elimite at 28 days for the system without NS. Conversely, when the SP was incorporated in NS-containing mixtures, it hindered cement hydration of the systems with powdered NS, but did not significantly affect the cement hydration of the system containing colloidal NS. The SEM images suggested that the SP changed the ettringite morphology, thereby negatively affecting the mechanical strength of the CSA pastes.
Dredging sediment refers to materials removed from the bottom of a water body during dredging operations. Mainly the dreading mud contains clay, silt, sand, water, and alkalis. This work incorporated dredging mud into the calcium sulfoaluminate cement at replacement levels of 0%, 10%, 30%, and 50% by weight. Pastes were evaluated after 1d, 28d, and 90d- hydration through mechanical strengths and the reaction rate by isothermal conduction calorimetry. XRD and MIP characterized the reaction products. The findings showed that small replacements (10% and 30%) increased early strength with higher ettringite formation in the system at 1d of curing. However, the evolution of mechanical strength was lower than the reference (0% replacement) over time. The results showed that in low replacement dosages, the dredging mud act as a nucleation site for the hydration of calcium sulfoaluminate phases.