- Hydration (4)
- Portland cement (3)
- Calcium sulfoaluminate cement (2)
- Durability (2)
- Alkali-activated concrete (1)
- Alternative materials (1)
- Açaí fiber (1)
- C&D waste (1)
- Calcined clay (1)
- Calcium sulfoaluminate (CSA) cement (1)
Organisationseinheit der BAM
The output of C&D waste is increasing year by year, among which low-quality recycled brick aggregates (RBAs) have not been well utilized and brought environmental burden. The durability of steam-cured concrete (HCC) is often compromised due to the detrimental effects of this curing regime on the long-term performance and microstructure development of the concrete material. To address this issue, this study investigates the potential of incorporating RBAs to improve the long-term durability of HCC. The results demonstrate that the incorporation of a small amount of RBA (10–20%) not only enhances the 28-d strength of HCC by 2.5–11.3%, but also improves its impermeability by mitigating heat damage effects. The combined application of fine and coarse RBA was found to effectively balance the negative effects of coarse RBA on the performance of HCC. Furthermore, the utilization of RBA in HCC was shown to have economic and environmental benefits. The results of this study demonstrate a simple and effective approach to improve the long-term durability of HCC while promoting the high-value utilization of solid waste.
While alkali-activated binders offer certain advantages over traditional Portland cement binders, particu¬larly in terms of resistance against chemical attacks and potentially environmental footprint, their degra¬dation mechanisms remain incompletely understood at present, specifically carbonation. Thus, this study investigates the impact of natural and accelerated carbonation (1% and 4% CO2) on three different compositions of alkali-activated concretes: 100% calcined clay (C100) binder, 100% ground blast furnace slag (S100) binder, and a 40% calcined clay and 60% blast furnace slag blend (C40S60). C100 concretes exhibit faster carbonation kinetics, with five times greater natural carbonation depths than S100. This difference diminishes under accelerated carbonation, showing a 1.5 times difference for 1% CO2 and complete carbonation for 4% CO2 at 90 days. The results thus confirm that accelerated carbonation testing of low-Ca alkali-activated concretes yields results that are not representative of natural carbonation. The C40S60 sample demonstrates a carbonation profile similar to a CEM I concrete, i.e., a high carbonation resistance. Microstructure analysis indicates the formation of three polymorphs of calcium carbonate for S100 (calcite, vaterite, and aragonite), with a higher CO2 concentration favouring aragonite over vaterite. C100 exhibits no calcium carbonates; instead, sodium carbonates form, including trona for 4% CO2 and natrite for both accelerated tests. C40S60 shows calcium and sodium carbonates, although to a lesser extent, containing predominantly calcite and minor signals of natrite. Suitable compositions, like C40S60, prove as effective during natural or accelerated carbonation tests as conventional Portland cement concrete.
Binary systems composed of Portland cement (PC) and calcium sulfoaluminate (CSA) cement have stood out for applications requiring high early strengths. Nevertheless, the application of these systems may be limited due to their properties in the fresh state, which requires a better understanding of the rheological behavior of these materials. Thus, this study evaluated the incorporation of different polycarboxylate-based superplasticizer (SP) contents (0.15, 0.20, and 0.25 wt%) on PC and PC-CSA binary cement pastes. Rotational rheometry, isothermal calorimetry, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and nitrogen adsorption and desorption tests to assess the pore size distribution of cement pastes were conducted. While the SP incorporation reduced the dynamic yield stress of PC pastes, it progressively increased the yield stress of PC-CSA systems. The increase in SP content increased the main heat flow peak of PC-CSA pastes, although it did not significantly affect the cumulative heat after 160 h of hydration. FTIR and XRD confirm higher ettringite contents in the binary systems and indicate the presence of carboaluminates phases after 7 d of hydration in both PC and PC-CSA and hemicarboaluminate in PC-CSA pastes. The CSA incorporation reduced the cumulative pore volume by up to 32% compared to PC pastes, while the SP content evaluated did not significantly affect the porosity of PC-CSA pastes.
This paper aimed to perform an exploratory literature review, focusing on the aspects of hydration and rheological properties of cementitious composites with açaí fibers. The use of natural fibers as a reinforcement in cementitious matrices has been widely studied, and açaí fiber is a promising option due to its unique characteristics. However, there is still a lack of knowledge regarding the correlation between fiber parameters and the technological properties of composites, which limits the development of new applications, such as 3D printing. The review provided an overview of the main characteristics of açaí fibers and the parameters for their application in cementitious matrices. Alkali treatment with 5% NaOH solution for 1 h shows increased mechanical and physical properties in açaí fibers. Despite the potential advantages of these composites, they pose challenges due to the different fiber surface treatment and interfacial transitions and the processing conditions of the fibers. Although small addition of açaí fibers slightly decreases the cement hydration process, keeping the cross-compatibility index high (>95). To overcome these challenges, it is necessary to evaluate the rheological behavior of cementitious materials with açaí fibers, which has not been reported in the literature. By doing so, it will be possible to optimize the processing conditions and develop new applications, such as additive manufacturing, which has never been explored with açaí fibers.
Volumetric changes follow Portland cement hydration reactions: aluminates' hydration is generally expansive, whereas silicates' reaction leads to shrinkage. Determining the volumetric variation at very early ages (i.e., first minutes/hours) presents operational challenges; most standards prescribe the measurement on specimens that are already hardened, while measurements from the fresh state are not standardized. This article reports the first attempt to use in-situ X-ray diffraction (XRD) to measure the early-age volumetric variation of a cementitious paste. For this purpose, a C3A + gypsum paste was assessed for 36 h, measuring its vertical displacement over time through XRD. The results showed that the expansion increased in the first ∼13 h, in line with the ettringite formed up to ∼11 h. In addition, the volumetric expansion agreed well with the heat release in calorimetry. It is concluded that the volumetric variation measurement of cementitious pastes through in-situ XRD is a promising technique, but further studies are needed to make this technique consolidated.
This study investigated the effect of incorporating three types of nanosilica (NS), two powders, and one colloidal suspension on the hydration, strength, and microstructure of calcium sulfoaluminate (CSA) cement pastes prepared with and without a superplasticizer (SP). X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy (SEM), and compressive strength tests were performed after 2, 5, and 28 days of hydration. The results showed that both NS powders delayed cement hydration at an early age, which was attributed to particle agglomeration (confirmed by dynamic light scattering). Whereas well-dispersed colloidal NS did not significantly affect the hydration of CSA at the investigated ages. SP incorporation improved the dispersion of CSA cement particles, resulting in a 10% increase in the degree of hydration of ye’elimite at 28 days for the system without NS. Conversely, when the SP was incorporated in NS-containing mixtures, it hindered cement hydration of the systems with powdered NS, but did not significantly affect the cement hydration of the system containing colloidal NS. The SEM images suggested that the SP changed the ettringite morphology, thereby negatively affecting the mechanical strength of the CSA pastes.
Dredging sediment refers to materials removed from the bottom of a water body during dredging operations. Mainly the dreading mud contains clay, silt, sand, water, and alkalis. This work incorporated dredging mud into the calcium sulfoaluminate cement at replacement levels of 0%, 10%, 30%, and 50% by weight. Pastes were evaluated after 1d, 28d, and 90d- hydration through mechanical strengths and the reaction rate by isothermal conduction calorimetry. XRD and MIP characterized the reaction products. The findings showed that small replacements (10% and 30%) increased early strength with higher ettringite formation in the system at 1d of curing. However, the evolution of mechanical strength was lower than the reference (0% replacement) over time. The results showed that in low replacement dosages, the dredging mud act as a nucleation site for the hydration of calcium sulfoaluminate phases.