A series of field exposure tests according to ISO 9223 up to 9226 was carried out at different locations to determine the corrosivity and the corrosion progress of different test sites throughout northern and eastern Germany. Standard test specimens of steel, zinc, copper and aluminium were exposed to rural, city and marine atmosphere at test sites of the Bundesanstalt für Materialforschung und -prüfung (BAM). Test sites at city atmosphere comprised exposure on a rooftop, next to a highly frequented road and directly at a motorway. Exposure under marine conditions was carried out at Heligoland in the North Sea. The specimens were stored under sheltered and unsheltered conditions on each test site, respectively. Corrosion rates after the first year of field exposure were determined and used for the classification of the atmospheres and the test sites regarding the corrosivity category.
Results after the first year of exposure were presented at the EUROCORR 2018 in Cracow. The current presentation will present an update of results of the systematic study after five years of exposure. The corrosion progress and the mass loss of the standard metals steel, zinc, copper and aluminium will be presented and discussed with respect to the atmospheric conditions and the time of wetness at the test sites. In addition, the difference between sheltered and unsheltered conditions will be discussed.
Der Vortrag stellt ein neuartiges Korrosionsprüfverfahren für Zinküberzüge auf Basis gelartiger Elektrolyte vor und führt die Vorteile gegenüber konventionellen Prüfverfahren auf. Basierend auf den Ergebnissen wird die Idee für einen IGF-Projektantrag in Kooperation mit dem Fraunhofer IKTS vorgestellt.
Zum Schutz vor Korrosionsprozessen werden metallene Werkstoffe in der Automobilindustrie üblicherweise mit komplexen Beschichtungssystemen versehen. Durch eine Beschädigung des Beschichtungssystems kann bei Zutritt von Feuchtigkeit und korrosionsstimulierenden Ionen das Metallsubstrat korrodieren und unter Umständen die Beschichtung im Bereich neben der Verletzung enthaften. Dabei gibt es verschiedene Mechanismen, die zu einer Unterwanderung und Enthaftung der Beschichtung führen können. In jedem Fall wird aber die Dauerhaftigkeit des Korrosionsschutzes negativ beeinflusst und die Lebensdauer des Bauteils herabgesetzt.
Die Industrie versucht deshalb, Beschichtungssysteme zu entwickeln, die dem Vorgang der kathodischen Enthaftung bestmöglich widerstehen können. Einen kritischen Entwicklungs- und Qualifizierungsschritt stellt dabei die geeignete Prüfung auf kathodische Unterwanderung und Enthaftung dar, da eine Prüfung der Beschichtung möglichst schnell und kosteneffizient zu belastbaren Ergebnissen führen soll. Neben den industriell üblichen Salzsprühnebeltests kommen häufig elektrochemische Polarisationstests zur Anwendung. Verschiedene Automobilherstellerhaben verwenden jeweils angepasste Tests, die sich bezüglich der Prüfparameter unterscheiden. Bei allen Testvarianten wird aber versucht, durch Verschärfung der Prüfparameter kurze Prüfzeiträume zu erreichen. Dabei kann es aber dazu kommen, dass die real ablaufenden Mechanismen der Unterwanderung beeinflusst und verändert werden und das Prüfergebnis von Ergebnissen im Feld zum Teil stark abweicht.
Im Vortrag werden mit Blick auf die geltenden Regelwerke und Normen die Unterschiede verschiedener Prüfmethoden zur kathodischen Enthaftung bei organischen Beschichtungen vorgestellt und deren Aussagekraft kritisch betrachtet. Am Beispiel von systematischen Versuchsreihen an einem ausgewählten Kurzzeittest werden die Grenzen einiger Methoden herausgearbeitet und die Anwendbarkeit für Qualitätsprüfungen betrachtet. Durch den Ansatz der statistischen Versuchsplanung wird der Einfluss einzelner Prüfparameter auf die Enthaftung und das Ergebnis des Kurzzeittests gezeigt.
The present work describes the combination of electrochemical investigations by using a gel‐type electrolyte with Fourier‐transformed infrared spectroscopy to investigate partially extremely thin corrosion product films on titanium‐zinc. The gel pad method enables the determination of corrosion relevant parameters such as the potential and the linear polarization resistance without altering the corrosion product layers, which are extremely prone to re‐dissolution when freshly formed. Complementary infrared spectroscopy enables the determination of main compounds of even very thin surface layers of few tenth of nanometers with a certain lateral resolution. It was found that zinc forms mostly zinc carboxy‐hydroxides such as hydrozincite, under various exposure conditions. The protective properties of these hydrozincite layers depend on the structure of the corrosion product film rather than on its thickness. In mid‐term exposure tests, shallow corrosion pits were found even in the absence of corrosive agents such as chloride.
Der Vortrag stellt ein neuartiges Korrosionsprüfverfahren für Zinküberzüge auf Basis gelartiger Elektrolyte vor und führt die Vorteile gegenüber konventionellen Prüfverfahren auf. Basierend auf den Ergebnissen wird die Idee für einen IGF-Projektantrag in Kooperation mit dem Fraunhofer IKTS vorgestellt.
A new approach to the assessment of the corrosion behaviour of zinc coatings under atmospheric conditions can be achieved using gel-type electrolytes as an alternative to standard aqueous test electrolytes. Gel-type electrolytes allow minimally invasive corrosion investigations on zinc coatings. They also provide the possibility to carry out corrosion investigations onsite. By using gel-type electrolytes corrosion-relevant characteristic values such as corrosion currents and polarization resistanc-es can be determined. These allow to describe the formation and the stability of the formed corrosion product layers under various climatic conditions. With this knowledge, a prediction of the zinc coating life cycle is possible. In this contribution, the value of gel-type electrolytes for corrosion research on zinc coatings is presented.
A new approach to the assessment of the corrosion behaviour of zinc coatings under atmospheric conditions can be achieved using gel-type electrolytes as an alternative to standard aqueous test electrolytes. Gel-type electrolytes allow minimally invasive corrosion investigations on zinc coatings. They also provide the possibility to carry out corrosion investigations onsite. By using gel-type electrolytes corrosion-relevant characteristic values such as corrosion currents and polarization resistances can be determined. These allow to describe the formation and the stability of the formed corrosion product layers under various climatic conditions. With this knowledge, a prediction of the zinc coating life cycle is possible. In this contribution, the value of gel-type electrolytes for corrosion research on zinc coatings is presented.
Im Vortrag werden mit Blick auf die geltenden Regelwerke und Normen die Unterschiede verschiedener Prüfmethoden zur kathodischen Enthaftung bei organischen Beschichtungen vorgestellt und deren Aussagekraft kritisch betrachtet. Am Beispiel von systematischen Versuchsreihen an einem Kurzzeittest werden die Grenzen einiger Methoden herausgearbeitet und die Anwendbarkeit für Reparaturbeschichtungen in Offshore-Bereich ausgelotet.
Im Vortrag werden mit Blick auf die geltenden Regelwerke und Normen die Unterschiede verschiedener Prüfmethoden zur kathodischen Enthaftung bei organischen Beschichtungen vorgestellt und deren Aussagekraft kritisch betrachtet. Am Beispiel von systematischen Versuchsreihen an einem Kurzzeittest werden die Grenzen einiger Methoden herausgearbeitet und die Anwendbarkeit für Reparaturbeschichtungen in Offshore-Bereich ausgelotet.
Ein neuer Ansatz bei elektrochemischen Korrosionsuntersuchungen kann durch den Einsatz von gelartigen Elektrolyten als Alternative zu wässrigen Prüfelektrolyten beschritten werden. Gelartige Elektrolyte ermöglichen minimalinvasive Untersuchungen an natürlich gebildeten Zinkdeckschichten. Dadurch können korrosionsrelevante Kennwerte ermittelt werden, die Aussagen zur Deckschichtbildung und zur Stabilität der gebildeten Deckschichten unter verschiedenen klimatischen Bedingungen erlauben. In diesem Beitrag wird anhand verschiedener Deckschichtzustände an Zink der Mehrwert von Untersuchungen mit gelartigen Elektrolyten für die Korrosionsforschung verdeutlicht.