Datei im Netzwerk der BAM verfügbar ("Closed Access")
Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (73)
- Vortrag (54)
- Beitrag zu einem Tagungsband (13)
- Posterpräsentation (10)
- Buchkapitel (2)
Schlagworte
- Additive manufacturing (28)
- Computed tomography (23)
- X-ray refraction (22)
- Residual stress (20)
- Neutron Diffraction (16)
- Neutron diffraction (16)
- Additive Manufacturing (12)
- Porosity (11)
- Computed Tomography (10)
- Composites (9)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (101)
- 8.5 Röntgenbildgebung (99)
- 5 Werkstofftechnik (12)
- 9 Komponentensicherheit (10)
- 9.4 Integrität von Schweißverbindungen (8)
- 5.0 Abteilungsleitung und andere (5)
- 5.2 Metallische Hochtemperaturwerkstoffe (4)
- 7 Bauwerkssicherheit (4)
- 8.0 Abteilungsleitung und andere (4)
- 5.1 Mikrostruktur Design und Degradation (3)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (54)
A new titanium alloy improving the operation of implants additively manufactured and including laterally closed lattice structures is proposed. The new alloy possesses an increased affinity to the bone. The measured bone–interface implant (BII) of less than 10 mm and bone–implant contact (BIC) of 95% demonstrated an excellent osseointegration. Furthermore, since additive manufacturing naturally leads to a high-roughness surface finish, the wettability of the implant is increased. The combination of these factors is pushing ossification beyond its natural limits. In addition, the quality and speed of the ossification and osseointegration in/around laterally closed lattice implants open the possibility of bone spline key of prostheses. This enables the stabilization of the implant into the bone while keeping the possibility of punctual hooks allowing the implant to be removed more easily if required.
Large temperature gradients inherent to additive manufacturing (AM) processes induce large residual stress (RS) in the final part. Because RS can influence the tribological properties, this study focuses on the relationship between wear sliding properties and RS in IN718 coatings. Such coatings were deposited with a Laser metal deposition (LMD) machine using two different scanning strategies.
The wear resistance and RS state were investigated after surface milling. RS were measured before and after wear tests on a reciprocating sliding test apparatus.
Two different X-ray diffraction techniques were employed to measure the surface and subsurface state RS: Laboratory Energy Dispersive X-ray Diffraction (LEDXD) and Synchrotron X-ray Energy Dispersive Diffraction (SXEDD). Due to the milling process, the coatings show similar depth distributions of RS from 22 to 92 μm depth, but exhibit different magnitudes depending on the scanning strategy used. Reciprocating sliding wear tests induced high compressive residual stresses that erased the initial RS state, and a similar wear behavior was observed in the two samples. These samples possess similar texture and grain morphology. This demonstrates that the influence of RS on wear resistance is a second-order effect. Nevertheless, it was observed that RS can still impact the wear performance at the early testing stages of the repaired parts.
The overview of the activity of Federal Institute for Material Research and Testing (BAM, Belin, Germany) in the field of additively manufacturing material characterization will be presented. The research of our group is focused on the 3D imaging of AM materials by means of X-ray Computed Tomography at the lab and at synchrotron, and the residual stress characterization by diffraction (nondestructive technique). Also, two successful research project in collaboration with CAM2, Sweden are presented.
Electron backscatter diffraction (EBSD) images of extruded pure aluminum were statistically analyzed to investigate creep-induced subgrain structures after applying two different levels of creep stress, corresponding to the power law (PL) and power-law breakdown (PLB) regimes. Kernel average misorientation analysis of EBSD measurements revealed 2D morphologies, which were subdivided by a multi-step segmentation procedure into subgranular arrangements. Various descriptors were employed to characterize the “subgrains” quantitatively, including their size, shape, spatial arrangement, and crystallographic orientation. In particular, the analysis of the orientations of subgrains was conducted by neglecting rotations around the loading axis. This approach facilitated the individual investigation of the {001} and {111} subgrain families with respect to the loading axis for two investigated stress levels plus a reference specimen. For the PL regime, the statistical analysis of subgrain descriptors computed from segmented image data revealed a similar degree of strain accumulation for {111} and {001} subgrains. In contrast, for the PLB regime, the analyzed descriptors indicate that {111} subgrains tend to accumulate significantly more strain than {001} ones. These observations suggest that the mechanisms leading to PLB may be associated with strain localization dependent on intergranular stress, hindering the recovery process within {111} grains.
X-ray refraction is analogous to visible light deflection by matter; it occurs at boundaries between different media. The main difference between visible light and X-rays is that in the latter case deflection angles are very small, from a few seconds to a few minutes of arc (i.e., the refraction index n is near to 1). Importantly, deflection of X-rays is also sensitive to the orientation of the object boundaries. These features make X-ray refraction techniques extremely suitable to a) detect defects such as pores and microcracks and quantify their densities in bulk (not too heavy) materials, and b) evaluate porosity and particle properties such as orientation, size, and spatial distribution (by mapping). While X-ray refraction techniques cannot in general image single defects, they can detect objects with size above a few wavelengths of the radiation.
Such techniques, especially at the Synchrotron BESSY II, Berlin, Germany, can be used in-situ, i.e. when the specimen is subjected to temperatures or external loads.
The use of X-ray refraction analysis yields quantitative information, which can be directly input in kinetics, mechanical and damage models.
We hereby show the application of non-destructive X-ray refraction radiography (SXRR, 2D mapping also called topography) to problems in additive manufacturing:
1) Porosity analysis in PBF-LM-Ti64. Through the use of SXRR, we could not only map the (very sparse) porosity distribution between the layers and quantify it, but also classify, and thereby separate, the filled porosity (unmolten powder) from the keyhole and gas pores (Figure 1).
2) In-situ heat treatment of laser powder bed fusion PBF-LM-AlSi10Mg to monitor microstructure and porosity evolution as a function of temperature (Figure 2). By means of SXRR we indirectly observed the initial eutectic Si network break down into larger particles as a function of increasing temperature. We also could detect the thermally induced porosity (TIP). Such changes in the Si-phase morphology upon heating is currently only possible using scanning electron microscopy, but with a much smaller field-of-view. SXRR also allows observing the growth of some individual pores, usually studied via X-ray computed tomography, but again on much smaller fields-of-view.
Our results show the great potential of in-situ SXRR as a tool to gain in-depth knowledge of the defect distribution and the susceptibility of any material to thermally induced damage and/or microstructure evolution over statistically relevant volumes.
High energy X-ray synchrotron diffraction is used to investigate the elastic anisotropy of the nickel-based superalloy IN718 produced by laser powder bed fusion (PBF-LB). This material is characterized by a columnar grain morphology with some crystallographic texture. The material is subjected to elastic loading to determine the diffraction elastic constants (DECs). Furthermore, the single-crystal elastic constants (SCEC) are refined from these experiments using different micromechanical models. The results show that each micromechanical model predicts a specific set of SCEC that well describes the elastic anisotropy of PBF-LB/IN718.
We discuss the non-linear stress–strain behavior of microcracked polycrystalline ceramics under uniaxial tension and compression (displacement control).
Micromechanics explanation and modeling of its basic features, such as non-linearity and hysteresis in stress–strain curves, are developed, with stable microcrack propagation and “roughness” of intergranular cracks playing critical roles in tension and crack sliding playing a critical role in compression. Experiments involving complex loading histories are explained, and themodel is shown to reproduce the basic features of the observed stress–strain curves.
Adopting X-ray computed tomography (XCT) for ex-situ characterization of battery materials has gained interest in the past decade. The main goal of this paper is to demonstrate the effectiveness of several X-ray computer tomography techniques to study commercial batteries. General guidelines are provided to select the most suitable imaging equipment and parameters for investigations of lithium-ion batteries, spanning the length scales from cell to electrode, down to particle level. Relevantly, such parameters would also be suitable for operando experiments.
Safety mechanisms and manufacturing inconsistencies at cell level as well as defects and inhomogeneity in cathode and anode is illustrated and quantified. Furthermore, relation of beam energy and sample-detector-distance on contrast retrieved from attenuation and phase shift is inspected using Synchrotron XCT.
We propose a novel iterative segmentation algorithm (i.S.Sy.Da.T.A: Iterative Segmentation Synthetic Data Training Algorithm) employing Deep Convolutional Neural Networks and synthetic training data for X-ray tomographic reconstructions of complex microstructures. In our method, we reinforce the synthetic training data with experimental XCT datasets that were automatically segmented in the previous iteration. This strategy produces better segmentations in successive iterations. We test our algorithm with experimental XCT re constructions of a 6-phase Al-Si Matrix Composite reinforced with ceramic fibers and particles. We perform the analysis in 3D with a special network architecture that demonstrates good generalization with synthetic training data. We show that our iterative algorithm returns better segmentations compared to the standard single training approach. More specifically, phases possessing similar attenuation coefficients can be better segmented: for Al2O3 fibers, SiC particles, and Intermetallics, we see an increase of the Dice score with respect to the classic approach: from 0.49 to 0.54, from 0.66 to 0.72, and from 0.55 to 0.66 respectively. Furthermore, the overall Dice score increases from 0.77 to 0.79. The methods presented in this work are also applicable to other materials and imaging techniques.