XPS and NEXAFS spectroscopy were used for the chemical characterization of pulsed plasma-deposited ethylene films before and after exposure to ambient air. The influence of external plasma parameters on the spectroscopic results was investigated. Information on the chemical character of the plasma-polymerized films, such as the regularity of the primary structure, the amount of long-living radicals, and branching or cross-linking or both was derived from this data. Irregularity and radical concentration for post-plasma reactions of the plasma-deposited films increased with the duty cycle or power. A decreased level of monomer fragmentation and, consequently, an increase in regularity is partially concluded from the experimental data when the monomer pressure is increased. The concentration of surface radicals available for post-plasma reactions also increased with monomer pressure. The correlation found between the degree of the post-plasma oxygen incorporation and the variation of the various external parameters agreed with earlier ToF-SSIMS findings.
Chemical properties of plasma-polymerized styrene films can be effectively controlled by the appropriate choice of external plasma parameters, such as duty cycle, power and monomer pressure. Chemical properties here are the regularity of the primary structure, the amount of long living radicals and branching or cross-linking or both in plasma polymerized styrene films, which can be indirectly monitored by X-ray photoelectron spectroscopy (XPS) and near edge X-ray absorption fine structure (NEXAFS) spectroscopy. Principally, XPS and NEXAFS spectra of plasma-polymerized styrene show all the spectroscopic fingerprints characteristic of atactic polystyrene indicating an inherent similarity of the respective primary chemical structures. There is an increase in irregularity and radical concentration for the plasma deposited films with increasing duty cycle or power. With an increase in monomer pressure, a decreased level of monomer fragmentation and, consequently, an increase in regularity must be concluded from the experimental data. The applied power regulates the fragmentation of the monomers as monitored by spectroscopic signals correlated to the aromatic rings. A trend in the extent of the post-plasma oxygen incorporation according to the variation of the various external plasma parameters was deduced, which agrees with earlier ToF-SIMS findings
Plasma-deposited polymer films were prepared from organic molecules and investigated using near edge X-ray absorption fine structure (NEXAFS) and X-ray photoelectron spectroscopy (XPS) for aging effects after exposure to air. Results from the investigation of homopolymers are summarized. Primarily the effect of the deposition parameters duty cycle and power are dealt with. The effect of the deposition parameter pressure is briefly discussed. An example to show the effect of feed gas composition on the aging of plasma polymerized ethylene/allyl alcohol and styrene/allyl alcohol copolymer is also given. In general, change in content of unsaturated or aromatic species, change in concentration of monomer functionality, and change in the oxygen content was observed in the plasma polymerized films on aging.
Plasma polymerised films of acrylic acid, allyl alcohol and allyl amine were prepared and studied by XPS (X-ray photoelectron spectroscopy) and XAS (X-ray absorption spectroscopy). The influence of external plasma parameters on certain chemical aspects of the films was investigated. The use of XPS and NEXAFS (near edge X-ray absorption fine structure) as complimentary tools in the surface characterisation of thin films has been highlighted. Certain chemical aspects of the plasma polymerised films such as presence of ROCdouble bond; length as m-dashO in the case of plasma polymerised acrylic acid films, presence of RCdouble bond; length as m-dashO and RCOR bonds in case of plasma polymerised allyl alcohol films and presence of RCdouble bond; length as m-dashN and C?N in case of plasma polymerised allyl amine films were studied. The concentration of ROCdouble bond; length as m-dashO species was found to decrease with increase in r.f. duty cycle in the case of plasma polymerised acrylic acid films. In case of plasma polymerised allyl alcohol films there is a decrease in the concentration of RCdouble bond; length as m-dashO species and increase in the concentration of RCOR species at higher pressures, while in the case of plasma polymerised allyl amine films the concentration of RCdouble bond; length as m-dashN and C?N increases at higher powers, with an increase in C?N more pronounced at higher powers.
Plasma deposited styrene/allyl alcohol and ethylene/allyl alcohol copolymer films were prepared and characterized using XPS, NEXAFS and ToF-SIMS. The relative partial flow rates of the co-monomers are used as deposition process parameters to vary and all other process parameters were constrained to conditions optimized for retention of functional groups. By doing this it is possible to control certain chemical properties of the copolymer films such as unsaturation, oxygen and hydroxyl group relative surface contents. The aging behavior of the plasma copolymer films on air was studied, too. Non-linear variations of relative oxygen contents, contents of C—OR species and contents of carbonyl species are obtained vs. variation of feed gas composition for both monomer combinations. The chemical character of the plasma copolymer films varies between the limits given by the respective plasma homopolymers. The observed non-linear correlations are discussed in terms of approaches developed for classic radical copolymerization. The aging behavior of the different plasma copolymers films depends on the feed gas composition. Principally these aging phenomena known from plasma polymer aging studies of that respective monomer which dominates the character of the plasma copolymer are observed.
Communication: Fire retardant coatings are deposited on polyamide-66 using plasma polymerisation. Chemical composition and thickness of deposits are adjusted varying the plasma treatment based on hexamethydisiloxane mixed with oxygen. The fire retardancy performances are evaluated using a cone calorimeter. The correlation between fire retardancy and thickness as well as chemical composition is discussed.
The effect of the composite plasma parameter P/F, where P is the plasma power and F is the monomer flow rate, on the chemical character of pulsed plasma deposited allyl alcohol films was investigated by ToF-SSIMS. Information on the unsaturated character, the cross-linked and/or branched character of the plasma polymer films was derived in detail. The problem of the retention of OH groups in plasma deposited allyl alcohol films was elucidated in detail using SSIMS data. The lowest conversion rate from the monomer's hydroxyl groups to other oxygen functionalities in the plasma was concluded for the plasma polymer film produced at a P/F ratio of 0.05 W · sccm-1. It was found that the overall oxygen content of the films decreased vs. increasing P/F ratio. Because the freshly prepared films were investigated without air exposure, ageing on ambient air could be studied in detail. It was found that in the case of plasma deposited allyl alcohol films the ageing on air is probably based on two competing processes which are discussed in detail. Additionally, a review of literature data on the characterization of plasma deposited allyl alcohol films is given.
Pulsed-plasma-deposited ethylene films were studied by time-of-flight static secondary ion mass spectrometry (ToF-SSIMS) before and after exposure to ambient air. The influence of the external plasma parameters on the secondary ion mass spectra of plasma-deposited ethylene films was investigated. From these data, information on the chemical character of the plasma-deposited ethylene films was derived. The investigation of the effect of external plasma parameters on the chemical character of the plasma-deposited ethylene films revealed that there were some drastic changes in the secondary ion mass spectra of the films. It was found that fragmentation and re-arrangement of the monomer molecules in the plasma, which affects the chemical character of the deposited films, vary according to the external plasma parameters. When the plasma polymers are exposed to air, extensive oxygen incorporation occurs. The oxygen uptake is high at the beginning and then it levels of. Some indications for the formation and decay of peroxy radicals (COO) and, subsequently, hydroperoxides (COOH) are found. It was observed that the oxygen uptake of the plasma deposited ethylene films increase when the plasma conditions become harder.
Pulsed plasma deposited styrene and ethylene films were studied by Time of Flight Static Secondary Ion Mass Spectrometry (ToF-SSIMS) before and after exposure to ambient air. The influence of the external plasma parameters on the secondary ion mass spectra of plasma deposited films was investigated. Approaches for the interpretation of SSIMS spectra of organic materials were reviewed and applied to the evaluation of SSIMS data of plasma deposited films. From these data, information on the chemical character of the plasma deposited films was derived.
When the plasma polymers are exposed to air oxygen incorporation occurs. The oxygen uptake is high at the beginning and then it levels of.
A relation that higher the regularity of the film lower is the oxygen uptake was found. Harder plasma conditions, which could be obtained by applying higher plasma power or lower monomer flow rate, result in higher oxygen uptake and vice versa.
Mixtures of hexamethyldisiloxane (HMDSO) and oxygen have been used for deposition of SiO2-like layers by plasma polymerization under low-pressure conditions onto polyethylene and polystyrene used as basecoat. Water glass was cast onto these 0.5 µm plasma thick siloxane-like layers with a thickness of 5 to 40 µm. The adhesion of these bilayer systems and their flame resistance were tested.
The effect of different plasma parameters such as monomer/gas ratio, pressure and power input into the discharge on the deposition rate and the composition of the formed layers was studied. Characterization and chemical composition of the formed films were performed using infrared, X-ray photoelectron and solid state nuclear magnetic resonance spectroscopy.
Peel strengths of composites were measured and the locus of peel front propagation was detected. Thermal properties of composites were analyzed by thermo-gravimetric analysis. Finally, the fire-retardant properties of thick coated polymers were determined by exposure to flames and the behavior of coatings on the polymers during flaming was observed visually.