7.6 Korrosion und Korrosionsschutz
Filtern
Erscheinungsjahr
- 2019 (123) (entfernen)
Dokumenttyp
- Vortrag (73)
- Zeitschriftenartikel (16)
- Sonstiges (16)
- Beitrag zu einem Tagungsband (15)
- Forschungsbericht (3)
Sprache
- Deutsch (64)
- Englisch (57)
- Mehrsprachig (2)
Schlagworte
- Korrosion (43)
- Corrosion (32)
- Nichtrostender Stahl (11)
- Carbon steel (9)
- Deckschichtbildung (8)
- Gelartige Elektrolyte (7)
- Korrosionsschutz (7)
- KorroPad (6)
- Korrosionsprüfung (6)
- CCS (5)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (123)
- 7.6 Korrosion und Korrosionsschutz (123)
- 5 Werkstofftechnik (15)
- 5.1 Mikrostruktur Design und Degradation (14)
- 3 Gefahrgutumschließungen; Energiespeicher (8)
- 3.2 Gefahrguttanks und Unfallmechanik (8)
- 7.4 Baustofftechnologie (4)
- 8 Zerstörungsfreie Prüfung (3)
- 8.0 Abteilungsleitung und andere (2)
- 5.3 Polymere Verbundwerkstoffe (1)
Eingeladener Vortrag
- nein (73)
Der Vortrag berichtet über die Auslagerung von Standardproben nach DIN EN ISO 9223 bis 9226 aus Zink, Stahl, Kupfer und Aluminium auf den verschiedenen atmosphärischen Bewitterungsständen der Bundesanstalt für Materialforschung und -prüfung (BAM). Im Vortrag werden die Masseverluste, Korrosionsgeschwindigkeiten und Korrosivitätskategorien der Standardproben im freibewitterten und überdachten Bereich nach einem Jahr vorgestellt und Unterschiede hinsichtlich der Atmosphärenbedingungen aufgezeigt. Freibewitterte Proben zeigen dabei deutliche Unterschiede hinsichtlich ihres Korrosionsverhaltens im Vergleich zu überdachten Proben. Die ermittelten Korrosivitätskategorien sind sowohl standort- als auch materialspezifisch.
Ein neuer Ansatz bei elektrochemischen Korrosionsuntersuchungen kann durch den Einsatz von gelartigen Elektrolyten als Alternative zu wässrigen Prüfelektrolyten beschritten werden. Gelartige Elektrolyte ermöglichen minimalinvasive Untersuchungen an natürlich gebildeten Zinkdeckschichten. Dadurch können korrosionsrelevante Kennwerte ermittelt werden, die Aussagen zur Deckschichtbildung und zur Stabilität von atmosphärisch gebildeten Deckschichten erlauben. In diesem Beitrag wird anhand verschiedener Untersuchungen an Reinzink der Mehrwert von gelartigen Elektrolyten für die Korrosionsforschung und -prüfung verdeutlicht. Darüber hinaus werden neue Erkenntnisse zur Deckschichtbildung von Zink unter atmosphärischen Bedingungen vorgestellt.
Der Vortrag berichtet über die Auslagerung von Standardproben nach DIN EN ISO 9223 bis 9226 aus Zink, Stahl, Kupfer und Aluminium auf den verschiedenen atmosphärischen Bewitterungsständen der Bundesanstalt für Materialforschung und -prüfung (BAM). Im Vortrag werden die Masseverluste, Korrosionsgeschwindigkeiten und Korrosivitätskategorien der Standardproben im freibewitterten und überdachten Bereich nach einem Jahr vorgestellt und Unterschiede hinsichtlich der Atmosphärenbedingungen aufgezeigt. Freibewitterte Proben zeigen dabei deutliche Unterschiede hinsichtlich ihres Korrosionsverhaltens im Vergleich zu überdachten Proben. Die ermittelten Korrosivitätskategorien sind sowohl standort- als auch materialspezifisch.
Geothermal energy is one of the most promising energy resources to replace fossil fuel. To extract this energy, hot fluids of various salts and gases are pumped up from a geothermal well having a certain depth and location. Geothermal wells in volcanic regions often contain highly corrosive CO2 and H2S gases that can be corrosive to the geothermal power-plants, which are commonly constructed of different steels, such as carbon steel. This research focuses on the corrosion behaviour of carbon steel exposed to an artificial geothermal fluid containing CO2 gas, using an artificial acidic-saline geothermal brine as found in Sibayak, Indonesia. This medium has a pH of 4 and a chloride content of 1,500 mg/L. Exposure tests were conducted for seven days at 70 °C and 150 °C to simulate the operating temperatures for low and medium enthalpy geothermal sources. Surface morphology and cross-section of the specimens from the above experiments were analysed using scanning electron microscope (SEM) and energy dispersive X-ray (EDX). Electrochemical tests via open circuit potential (OCP) and electrochemical impedance spectroscopy (EIS) were performed to understand the corrosion processes of carbon steel in CO2-containing solution both at 70 °C and 150 °C. Localized corrosion was observed to a greater extent at 70 °C due to the less protectiveness of corrosion product layer compared to that at 150 °C, where FeCO3 has a high corrosion resistance. However, a longer exposure test for 28 days revealed the occurrence of localized corrosion with deeper pits compared to the seven-day exposed carbon steel. In addition, corrosion product transformation was observed after 28 days, indicating that more Ca2+ cations incorporate into the FeCO3 structure.
Electrochemical deposition of polyaniline on carbon steel for corrosion study in geothermal solution
(2019)
Polyaniline has been widely developed for many applications, e.g. sensor, supercapacitor components, electrochromic devices, and anticorrosion pigments. Although the addition of polyaniline pigment in organic coatings has been an alternative for corrosion protection in industrial applications, the protection mechanism is still not fully understood. Herein in this study, as a part of the development of polyaniline/silicon dioxide coating for geothermal application, polyaniline has been deposited electrochemically on carbon steel surface in oxalic acid medium and tested in geothermal solution to understand the contribution of polyaniline to the corrosion protection of a polyaniline-based composite in the geothermal system. To observe the surface/interface reaction between the electrolyte and electrode surface during the electrochemical polymerization, electrochemical impedance spectroscopy (EIS) was applied after each cycle. For corrosion study in the geothermal application, an artificial geothermal solution was used with the composition of 1,500 mg/l Cl⁻, 20 mg/l SO₄²⁻, 15 mg/l HCO₃⁻, 200 mg/l Ca²⁺, 250 mg/l K⁺, and 600 mg/l Na⁺, and pH 4 to simulate a geothermal brine found in Sibayak, Indonesia. An electrochemical measurement was performed by monitoring the open circuit potential over seven days, with the interruption by EIS every 22 hours. The experiments were performed at room temperature and 150 °C (1 MPa) in an oxygen-free environment. Impedance spectra showed a reduction of the total impedance value of approximately 10 times for specimens measured at 150 °C compared to the specimens measured at room temperature, suggesting a less stable layer at high temperature.
This study focuses on the corrosion mechanism of carbon steel exposed to an artificial geothermal brine influenced by carbon dioxide (CO2) gas. The tested brine simulates a geothermal source in Sibayak, Indonesia, containing 1500 mg/L of Cl-, 20 mg/L of SO4 2-, and 15 mg/L of HCO3-with pH 4. To reveal the temperature effect on the corrosion behavior of carbon steel, exposure and electrochemical tests were carried out at 70 °C and 150 °C. Surface analysis of corroded specimens showed localized corrosion at both temperatures, despite the formation of corrosion products on the surface. After 7 days at 150 °C, SEM images showed the formation of an adherent, dense, and crystalline FeCO3 layer. Whereas at 70 °C, the corrosion products consisted of chukanovite (Fe2(OH)2CO3) and siderite (FeCO3), which are less dense and less protective than that at 150 °C.
Control experiments under Ar-environment were used to investigate the corrosive effect of CO2. Free corrosion potential (Ecorr) and electrochemical impedance spectroscopy (EIS) confirm that at both temperatures, the corrosive effect of CO2 was more significant compared to that measured in the Ar-containing solution. In terms of temperature effect, carbon steel remained active at 70 °C, while at 150 °C, it became passive due to the FeCO3 formation. These results suggest that carbon steel is more susceptible to corrosion at the near ground surface of a geothermal well, whereas at a deeper well with a higher temperature, there is a possible risk of scaling (FeCO3 layer). A longer exposure test at 150 °C with a stagnant solution for 28 days, however, showed the unstable FeCO3 layer and therefore a deeper localized corrosion compared to that of seven-day exposed specimens.
Fireside Chat - Sharing PhD
(2019)