7.6 Korrosion und Korrosionsschutz
Filtern
Erscheinungsjahr
- 2024 (4) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (2)
- Vortrag (1)
- Posterpräsentation (1)
Referierte Publikation
- nein (4)
Schlagworte
- Offshore (2)
- Corrosion (1)
- Drawing layers (1)
- Emission (1)
- Environment (1)
- Environmental Chemistry (1)
- Hydrogen‐induced stress corrosion cracking (1)
- Korrosion (1)
- Materials Chemistry (1)
- Mechanical Engineering (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (1)
The corrosion behavior of galvanized steels and zinc components under atmospheric exposure depends mostly on the corrosion product‐based cover layer formation under the prevailing conditions. The use of agar‐based gel electrolytes makes it possible to use electrochemical methods to obtain a characteristic value from these cover layers that describe their current and future protective capacity. It is shown here that different states of galvanized steel can be distinguished very well under laboratory conditions and that this method is also suitable for use under practical conditions. Based on the characteristic values and assuming future time of wetness, it is very easy to draw up a forecast for the future corrosion rate, which provides plausible values.
To combat climate change the share of renewable energy production must increase drastically. Offshore energy production – offshore wind and power-to-X – are crucial to achieving climate targets. However, the impact of these offshore constructions – wind turbines and production platforms – on the marine environment remains unclear in many aspects. Potential sources of chemical emissions are corrosion protection systems, remobilization of contaminants from old sediments during construction, the brine of desalination plants and increased shipping for maintenance and transportation. In order to minimize the environmental impact of renewable energies, close monitoring is essential. The goal of this project is the development of a monitoring concept for an offshore power-to-X production platform.
Tests for assessing prestressing steels' susceptibility to hydrogen‐induced stress corrosion cracking are essential for approvals, in‐house monitoring, and third‐party material testing. According to ISO 15630‐3, the time to brittle fracture by constant load under corrosive conditions in thiocyanate test solutions (A or B) at 50°C is measured. In the literature, a high scattering in stress corrosion tests is reported, which questions the integrity of the test procedure. This paper shows the results of studies about the influence of solution composition on hydrogen charging in electrochemical and permeation measurements. Electrochemical experiments show that polished steel surfaces without common drawing layers have more consistent free corrosion currents, polarization resistances, and B‐values in solution A with low scattering compared to the solution B experiments. The influence of temperature at 50°C and an ambient temperature of 22°C was also tested.
Mit dem Klimawandel verändert sich nicht nur das Wetter, also Regenmengen, Temperaturen oder Starkwind- bzw. Sturmzeiten. Mit diesen Veränderungen gehen auch Veränderungen der örtlichen Korro-siviät der Atmosphäre einher. Sind die Datengrundlagen der aktuellen nationalen und internationalen Normen mit Datenerhebungen aus den 1970igern und 80iger Jahren noch repräsentativ? Hierzu werden an realen Offshorestrukturen valide Daten erfasst, die als Grundlage für KI-basierte Modellbildung verwendet werden sollen.