Chemische Charakterisierung und Spurenanalytik
Filtern
Dokumenttyp
Sprache
- Englisch (2)
Referierte Publikation
- ja (2)
Schlagworte
- Li-ion battery (2) (entfernen)
Organisationseinheit der BAM
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.6 Anorganische Referenzmaterialien (1)
- 3 Gefahrgutumschließungen; Energiespeicher (1)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (1)
- 5 Werkstofftechnik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- 6 Materialchemie (1)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (1)
- S Qualitätsinfrastruktur (1)
- S.1 Qualität im Prüfwesen (1)
In this work, we employed glow discharge optical emission spectrometry (GD-OES) depth profiling as a fast and semi-quantitative method to investigate the aluminum (Al) current collector degradation in commercial lithium cobalt oxide (LCO) pouch cells with no Al2O3 pretreatment. After battery aging, a heterogeneous deposit was found on the surface of the cathode. Gray hotspot areas within an extensive pale white region were formed. Consistent with energy dispersive X-ray (EDX) analysis of micro-cross sections milled via targeted focused ion beam (FIB), an Al-containing layer of approximately 3 µm can be observed using GD-OES. We attribute one main cause of this layer is the degradation of the Al current collector. The nonuniform growth of this layer was investigated by performing GD-OES depth profiling at different in-plane positions. We found that the gray area has a higher mass concentration of Al, probably in metallic form, whereas the white area was probably covered more homogeneously with Al2O3, resulting from the inhomogeneous distribution of the pitting positions on the current collector. Compared to FIB-EDX, GD-OES enables a faster and more convenient depth profile analysis, which allows the more productive characterization of lithium-ion batteries (LIBs), and consequently benefits the development of preferable battery materials.
Li-rich nanoparticles of Li1+xMn2–xO4 doped with Al, Co, or Ni are successfully synthesized using a facile, fast, and efficient microwave-assisted hydrothermal route. Synchrotron X-ray diffraction confirms the formation of the crystalline cubic spinel phase type. X-ray absorption spectroscopy analysis at the Co and Ni K- and L-edges verifies that the dopants are within the Li1+xMn2–xO4 spinel structure and are inactive during cycling in the bulk and at the surface. Moreover, we demonstrate that nanocrystallinity and cationic doping play an important role in improving the electrochemical performance with respect to LiMn2O4 microparticles. They significantly reduce the charge-transfer resistance, lower the first cycle irreversible capacity loss to 6%, and achieve a capacity retention between 85 and 90% after 380 cycles, with excellent Coulombic efficiency close to 99% without compromising the specific charge at a 5C cycling rate. Furthermore, the Mn K- and L-edges attest that after long cycling, the Mn oxidation state in the bulk differs from that at the surface caused by the Mn disproportion reaction; however, the cationic doping helps mitigate the Mn dissolution with respect to the undoped Li1+xMn2–xO4 nanoparticles, as indicated by inductively coupled plasma atomic emission spectrometry.