Chemische Charakterisierung und Spurenanalytik
Filtern
Dokumenttyp
- Posterpräsentation (9) (entfernen)
Sprache
- Englisch (9)
Referierte Publikation
- nein (9)
Schlagworte
- ICP-MS (9) (entfernen)
Organisationseinheit der BAM
Contamination of the environment with antibiotics is of great concern as it promotes the evolution of antimicrobial resistances. In case of amoxicillin (AMX) in the aquatic environment, further risk arises from hydrolysis products (HPs) which can cause allergy. To assess these risks, a comprehensive investigation and understanding of the degradation of AMX is necessary. We investigated the hydrolysis rate of AMX in different types of water as well as the influence of temperature and irradiation. The content of the heavy metal ions copper and zinc was found to be crucial for the hydrolysis rate of AMX and stability of HPs. Eventually, a new degradation pathway for AMX could be elaborated and confirmed by tandem mass spectrometry (LC-MS/MS).
Nearly all disease processes are associated with variations of components of the extracellular matrix (ECM) that are typically observed during the development of inflammation. This concerns for example proteoglycans and their associated glycosaminoglycans (GAG), which have been shown to bind to cationic metal imaging probes due to their strong complexing activity. The complexing activity largely depends on the degree of GAG sulfation and/or carboxylation as well as on the GAG isomericity. In this central project, we investigate GAG structures from inflammatory disorders (namely cardiovascular diseases, inflammatory intestinal diseases and neuroinflammation) provided by researchers of the Collaborative Research Center at the molecular disaccharidic level using chromatographic and mass spectrometric methods. In parallel, the spatial localization and quantification of metal-based imaging probes are evaluated by LA-ICP-MS imaging.
Metallic nanoparticles (NPs) are currently applied in a variety of consumer products and are also attractive for medical applications. With their widespread use, the potential for human exposure to NPs — either intended or unintended — is increasing. Therefore, many studies have evaluated the toxicity and transport mechanism of NPs. In comparison with two-dimensional cultured cells, multicellular spheroids (MCS) look promising to be used as a three-dimensional cellular model, having unique advantages in nanoparticle studies due to the fact that interactions with excreted extracellular matrix can be investigated. Fibroblast cells are one of the most important cell systems to express a microenvironment by excreting an abundant extracellular matrix. For bioimaging laser ablation inductively coupled-plasma mass spectrometry (LA-ICP-MS) is used in this investigation to study the interaction of metallic NPs with MCS for multi-element detection offering a wide dynamic range. As a mass spectrometer we have applied a time-of-flight (TOF) instrument for (quasi-) simultaneous detection of all isotopes of elements of interest.
The aim of this study is to investigate the localization of silver (Ag) NPs exposed to fibroblast MCSs by means of LA-ICP-TOF-MS. In addition, for demonstrating elemental microscopy we chose phosphorous (31P) and iron (56Fe) to visualize regions of enriched extracellular matrix and single cells, respectively. In this presentation, we show that exposed Ag NPs are highly accumulated at the same position of single cells in an outer rim of fibroblast MCSs.
Optimization of protein quantification via isotope dilution ICP-MS of a standard reference protein
(2019)
Quantitative proteomics are nowadays one of the key tasks in life sciences. A multitude of methods for protein quantification are established and more techniques are developed each year, but there still is a lack of well characterized and quantified protein standards. We aim to develop an ICP-MS based method to quantify pure proteins reliably and traceable to SI. Here, we employ isotope Dilution analysis for the quantification of proteins of known stoichiometry via their sulfur content.
We have applied laser ablation inductively coupled plasma mass spectrometry (LA-ICP-MS) with subcellular resolution as an elemental mass microscope to investigate the distributions of Ag nanoparticles (NP) in a 3-dimentional multicellular spheroid (MCS) model. The production of MCS has been optimized by changing the seeding cell number (500 to 40,000 cells) and the growth period (1 to 10 days). Incubations of MCS with Ag nanoparticle suspensions were performed with a concentration of 5 µg mL-1 for 24 hours. Thin-sections of the Eosin stained MCS were analysed by elemental mass microscopy using LA-ICP-MS to image distributions of 109Ag, 31P, 63Cu, 66Zn and 79Br. A calibration using NP suspensions was applied to convert the measured Ag intensity into the number of particles being present in each measurement pixel. The numbers of NP determined ranged from 30 up to 4,000 particles in an enrichment zone. The particle distribution was clearly correlated to 31P, 66Zn and 79Br and was localized in an outer rim of proliferating cells (confirmed by DAPI) with a width of about two-single cell diameters. For the highest seeding cell number NPs were only detected in this outer rim, whereas small molecules as for instance 79Br and 109Ag ions were detected in the core of the MCS as well. Aniline blue staining demonstrated that this outer rim was rich in collagen structures in which fibroblast cells were embedded and a thin-membrane was visible which separated the core from the biological active cell layer functioning as biological barriers for NP transport. In this presentation, we will show the possibility using this 3-dimensional model for toxicological and medical applications.
Nanoparticles (NPs) have found a wide range of applications in research and industry. Thereby the interaction of NPs with biological systems like cells has become a major field of interest, ranging from medical applications to nanotoxicology. Size, shape and surface modification of the nanomaterials determine the uptake rate and pathway into the cells, and therefore impact specific cell components and processes.
Laser ablation inductively coupled plasma mass spectrometry (LA-ICP-MS) is an established quantitative multi-elemental analysis and mapping technique. In recent years, it was shown that LA-ICP-MS can provide quantitative as well as distribution information of metal containing nanoparticles (NPs) in cell samples.
Here LA-ICP-MS was applied for the imaging of individual fibroblast cells to study the uptake and intracellular processing of NPs. Our results show that LA-ICP-MS can be used to localize nanoparticle aggregates within cellular compartments. The studied NPs accumulate in the perinuclear region in the course of intracellular processing, but do not enter the cell nucleus. The uptake efficiency depends strongly on the physico-chemical properties of the nanostructures as well as on the incubation conditions like concentration and incubation time.
ICP-MS was used to determine the composition of the nanomaterials as well as the number of NPs in cells after acid digestion of the samples.
Quantification of sulphur in copper metals by isotope dilution LA-ICP-MS using polyethylene frits
(2018)
Sulphur is one of the relevant impurities in copper and its alloys affecting their material properties. To ensure the quality of copper products, fast direct solid sampling techniques are very attractive. However, for the calibration suitable matrix reference materials are required. For the certification of such reference materials appropriate, SI-traceable analytical methods are essential. Therefore, a procedure was developed to quantify total sulphur in copper by combining the classical isotope dilution (ID) technique and laser ablation inductively coupled plasma mass spectrometry (LA-ICP-MS).
Here, for the first time, polyethylene (PE) frits were used to prepare appropriate solid samples for the sulphur quantification in copper metals (alloyed/unalloyed) by isotope dilution LA-ICP-MS. The properties of the PE frit meet the requirements as porous material with high absorption efficiency, thermal and chemical resistance as well as low sulphur blank. Different copper reference materials were used to develop and validate the procedure. The copper samples were spiked with 34S, digested with nitric acid and then the digests were absorbed on PE frits. After drying, the frits were analysed by LA-ICP-IDMS using a Nd:YAG laser at 213 nm coupled to an ICP sector field mass spectrometer. It could be demonstrated, that the sample solution dispersed on the frits did not influence the 32S/34S ratio significantly even though the sulphur intensities were fluctuating along the scanned lines. Relative standard deviations of the isotope ratios were below 5 % in average between three line scans (except for the pure spike solution and procedure blank). The measurement results were validated by comparing them with the results obtained by conventional ICP-IDMS after analyte-matrix separation. Plotting the mass fraction of sulphur in copper obtained by LA-ICP-IDMS versus those obtained by ICP-IDMS yields a linear curve with a correlation coefficient of 0.9999 showing a strong agreement between both techniques.
The metrological traceability to the SI from the kg down to the sulphur mass fraction in copper is established by an unbroken chain of comparisons, each accompanied by an uncertainty budget. Thus, the measurement results are considered reliable, acceptable and comparable within the stated measurement uncertainty.
Nanoparticles (NPs) have found a wide range of applications in research and industry. Thereby the interaction of NPs with biological systems like cells has become a major field of interest, ranging from medical applications to nanotoxicology. Size, shape and surface modification of the nanomaterials determine the uptake rate and pathway into the cells, and therefore impact specific cell components and processes.
Inductively coupled plasma mass spectrometry (ICP-MS) is a well-established analytical method offering high sensitivity and multi-element capability. By coupling a laser ablation (LA) system to an ICP-MS the analysis of different kinds of solid samples is possible. In recent years, it was shown that LA-ICP-MS can provide quantitative as well as distribution information of metal containing nanoparticles (NPs) in cell samples.
Here LA-ICP-MS was applied for the imaging of individual fibroblast cells to study the uptake and intracellular processing of NPs. Our results show that LA-ICP-MS can be used to localize nanoparticle aggregates within cellular compartments. The studied NPs accumulate in the perinuclear region in the course of intracellular processing, but do not enter the cell nucleus. The uptake efficiency depends strongly on the physico-chemical properties of the nanostructures as well as on the incubation conditions like concentration and incubation time.
ICP-MS was used to determine the composition of the nanomaterials as well as the number of NPs in cells after acid digestion of the samples.
Sulfur is one of the major impurity elements in copper. Previously applied methods for the quantification of sulfur in copper and other pure metals revealed a lack of traceability and showed inconsistent result. Therefore, in this study a procedure was developed for the quantification of total sulfur in copper at low concentration levels using inductively coupled plasma-isotope dilution mass spectrometry (ICP-IDMS). A major challenge for the quantification of sulfur in copper (alloyed/unalloyed) by ICPMS is the copper matrix itself, causing matrix effects and making an extensive cleaning (cones, extraction lens) necessary after measurements. Matschat et al investigated the analysis of high-purity metals (including copper) by high resolution ICP-MS and found that the copper matrix shows strong matrix effects on the sensitivity resulting from Cu deposition on the cones. Therefore, the major part of the copper matrix has to be separated, which was accomplished by adding ammonia which forms a complex with the copper while releasing the sulfur. This was followed by a chromatographic separation using a weak cation resin. After that the sulfur fraction was further purified by chromatographic means using an anion exchange method followed by a chelating resin.
The anion exchange resin (AG1X8), however, is selective to sulfate and sulfite but less-selective to sulfide. Therefore, when quantifying total sulfur in copper, the different species of sulfur need to be oxidized to sulfate prior to the sulfur-matrix separation on the AG1X8 resin in order to avoid any measurement bias. When applying the HPA oxidation with concentrated HNO3 and H2O2 a complete conversion from sulfide and sulfite to sulfate could be achieved. The recovery of all investigated sulfur species is quantitative within measurement uncertainties. The copper samples investigated in this study contain copper in the range of 0.85-0.99 kg·kg-1 and zinc from <10 to 300 g·kg-1. Approximately 0.10-0.25 g of these samples were used to perform the sulfur-copper separation. After applying the complete three stage separation procedure the mass fractions of both elements were significantly reduced to below 400 ng·g-1 for copper and below 50 ng·g-1 for zinc, respectively. The developed procedure shows high performance, especially concerning high efficiency in matrix removal (> 99.999%) while keeping the recovery of sulfur above 80%.
The procedure blank was determined by IDMS as well and yielded values for the individual IDMS measurement sequences ranging from 3 ng to 53 ng. The average of these individual procedure blanks (n=22) was calculated and yielded a total procedure blank of 14 ng sulphur with standard deviation of 12 ng. The limit of detection (LOD, blank+3SD) calculated on this basis was 0.20 µg·g-1 while the limit of quantification (LOQ, blank+10SD) was 0.54 µg·g-1, when considering a sample weight of 0.25 g.
The quantification of low sulfur contents (< 15 µg/g) by conventional IDMS is hindered by the very high Cu/S ratio, which clearly affects the separation in a negative way: The recovery of sulfur dropped to about 30 % for four replicates, while two further replicates even showed recoveries below 10%. To enable measurement without completely changing the separation procedure, an exact amount of sulfur was added prior to spiking, such that the sulfur mass fraction was shifted to the optimum working range of the separation procedure. Thus exact amounts of sulfur were added to enhance the mass fraction of sulfur from 15 µg·g-1 to 40 µg·g-1, then the IDMS analysis was performed as usual and finally the added sulfur amount was subtracted. The so obtained measurement result agreed well with the certified value within the uncertainties. The relative expanded measurement uncertainties for conventional IDMS are below 1%. When applying the modified IDMS procedure, where back-spike is added to the sample before spiking, the relative expanded measurement uncertainties are larger and up to 5%. With the presented sulfur-matrix procedure a working range from approximately 15 µg·g-1 to 1500 µg·g-1 can be achieved.
The developed procedure for the quantification of low sulfur amounts in copper has been validated here via three different routes: first an inter-laboratory comparison at highest metrological level, second a step-by-step validation by checking each single step of the procedure and third the setup of a complete uncertainty budget.
The procedure is sufficient to facilitate value assignment of total sulfur mass fraction in reference materials. Additionally, relative measurement uncertainties were calculated below 1 % and the measurement results are traceable to the SI, which is clearly demonstrated in this work. The procedure reported in this study is a new reference procedure for sulfur measurement in copper, well meeting the requirements of the two major purposes: the certification of reference materials and the assignment of reference values for inter-laboratory comparison.