Fluorides are well-known as wood preservatives. One of the limitations of fluoride-based wood preservatives is their high leachability. Alternative to current fluoride salts such as NaF used in wood protection are low water-soluble fluorides. However, impregnation of low water-soluble fluorides into wood poses a challenge. To address this challenge, low water-soluble fluorides like calcium fluoride (CaF2) and magnesium fluoride (MgF2) were synthesized as nanoparticles via the fluorolytic sol−gel synthesis and then impregnated into wood specimens. In this study, the toxicity of nano metal fluorides was assessed by termite mortality, mass loss and visual analysis of treated specimens after eight weeks of exposure to termites, Coptotermes formosanus. Nano metal fluorides with sol concentrations of 0.5 M and higher were found to be effective against termites resulting in 100% termite mortality and significantly inhibited termite feeding. Among the formulations tested, the least damage was found for specimens treated with combinations of CaF2 and MgF2 with an average mass loss less than 1% and visual rating of “1”. These results demonstrate the efficacy of low water-soluble nano metal fluorides to protect wood from termite attack.
This work reported the investigation on the effect of relaxation to the permittivity (epsilon' r ) characteristic of Mg1-x Zn x TiO3 ceramics for x = 0 – 0.5 (MZT0 – MZT0.5) measured from 1 Hz to 330 MHz. Within that frequency range, the relaxation effect that consists of the space charge (SC) and the dipolar (D) polarization mechanisms were identified. The contribution of the D relaxation in MZT0 – MZT0.2 systems extents overall from about 100 Hz to 330 MHz, while that in MZT0.3 – MZT0.5 systems is from 50 kHz to 330 MHz. The remaining frequencies, i.e. from 1 to 90 Hz for MZT0 – MZT0.2 and from 1 Hz to 50 kHz for MZT0.3 – MZT0.5, are attributed to the SC relaxation. The D polarization mechanism provides constant epsilon' r values which vary from (15.4 – 17.0) ± 0.3 throughout the samples. Contribution of the SC polarization mechanism to the characteristic is supported by the simultaneous presence of different content and level of resistivity of the secondary phase of (Mg1-αZnα)2TiO4 in MZT0 – MZT0.2 systems and of (Zn1-αMgα)2TiO4 in MZT0.3 – MZT0.5, along with the presence of the main Mg1-x Zn x TiO3 phase, as a result of the variation of zinc content in the systems.
Trace humidity was measured by using miniaturized planar coulometric sensors in technical gases such as hydrogen, nitrogen, helium, nitrous oxide, and synthetic air. Frost point temperatures tf in the gases ranged from −60 °C to −30 °C, which is equivalent to a vapour mole fraction xv from 10 μmol mol−1 to 376 μmol mol−1. In addition, the generated humidity was determined by using a precision dew point hygrometer as reference. Nonlinear calibration functions were calculated that correlated electric current (sensor signal) and reference humidity. Parameters of functions were tested with one-way analysis of variances (ANOVA) to prove if all used sensors had a similar behavior in the same gas during experiments. Results of ANOVA confirmed that averaged functions can be applied for trace humidity measurement in nitrogen, helium, nitrous oxide, and synthetic air. The calculated functions were negligibly different for nitrogen, helium, and synthetic air. In humidified nitrous oxide, a minor change of parameters was observed due to lower electrical currents. In total contrast to that, the measured sensor signals were significantly higher in humidified hydrogen and each sensor required its own calibration function. The reason was a recombination effect that favoured multiple measurements of water molecules. Nevertheless, it was possible to measure continuously trace humidity in all tested gases by using coulometric sensors with an expanded uncertainty below 2 K (k = 2).