Chemie und Prozesstechnik
Filtern
Erscheinungsjahr
- 2018 (4) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (3)
- Sonstiges (1)
Sprache
- Englisch (4)
Schlagworte
- Concrete and screed (2)
- Embedded humidity sensors (2)
- Material moisture (2)
- Pore volume distribution (2)
- Calibration (1)
- Cement (1)
- Chlorine (1)
- Data in brief (1)
- Embedded sensors (1)
- LIBS (1)
Organisationseinheit der BAM
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (4) (entfernen)
The determination of chloride is still one of the main tasks for the evaluation of reinforced concrete structures.
The corrosion of the reinforcement induced by the penetrating chlorides is the dominant damage process affecting the lifetime of concrete structures. In the recent years different research groups demonstrated that LIBS can be a fast and reliable method to quantify chlorine in cement-bound materials. Because chlorine in concrete can only occur as solved ions in the pore solution or bound in salts or hydrated cement phases, the detected emission of chlorine can be correlated with the chloride concentration determined e.g. with potentiometric titration. This work inter alia describes the production of reference samples and possible side effects during the production process. Due to transport processes in the porous matrix of the cement a misinterpretation of the concentrations is possible. It is shown how to overcome these effects and higher precisions of the single measurements can be realised. Using the calibration method, blank sample method and noise method, three different ways of calculating the limit of detection (LOD) and limit of quantification (LOQ) are compared. Due to the preparation of the reference samples a precision of the whole calibration model of sx0 = 0.023 wt% is determined.
The validation of the model is based on different test sets, which are varying in their composition
(different Cl-salts, water-to-cement ratios and additives). The determined mean error of the validation is
0.595 ± 0.063 wt%, which is comparable to standardised methods like potentiometric titration, direct potentiometry
or photometry (0.40 ± 0.06 wt%) [1].
Four cement-based and four calcium-sulphate-based screed types are investigated. The samples have a diameter of 300 mm and a height of 35 or 70 mm. Up to ten humidity sensors are embedded directly during the concreting of the screed samples. Thus, the humidity over the sample height is monitored during hardening, hydration, evaporation, and oven drying. Furthermore, the screed samples are weighed during every measurement to determine the total mass and the corresponding moisture loss.
To define the pore system precisely, mercury intrusion porosimetry as well as gas adsorption is performed. According to the data, the entire pore volume distribution is known. The measured pore diameters range from 0.8 nm to 100 µm and the total porosity of the examined screeds ranges between 11% and 22%.
Based on these measurement data, moisture transport, pore saturation as well as sorption isotherms and their hysteresis may be calculated quantitatively as described in “Monitoring of the absolute water content in porous materials based on embedded humidity sensors” (Strangfeld and Kruschwitz, 1921).
Monitoring of the absolute water content in porous materials based on embedded humidity sensors
(2018)
Moisture transport monitoring may indicate the onset of deterioration in porous building materials Prior to damage occurring. Most moisture measurement systems provide only qualitative values, require extensive calibration, or are destructive. Thus, non-destructive and calibration-free monitoring Systems are required. Our approach of moisture monitoring is to embed sensors that measure the relative humidity.
In our experiment, screed samples are monitored during the Hydration and evaporation process. Every test sample is equipped with 10 embedded sensors which measure the relative humidity across the sample thickness. Based on Hillerborg’s approach, the relative humidity is converted into the corresponding pore saturation. In our study, the free water is computed without knowledge of the Sorption isotherm. The free water in the pore system is predicted and validated. The predicted weight decrease corresponds conclusively to gravimetrically measured weights. The embedded sensors yield the absolute liquid water content and enable an experimental, non-destructive monitoring of liquid water in porous materials.
Four cement-based and four calcium-sulphate-based screed types are investigated. The samples have a diameter of 300 mm and a height of 35 or 70 mm. Up to ten humidity sensors are embedded directly during the concreting of the screed samples. Thus, the humidity over the sample height is monitored during hardening, hydration, evaporation, and oven drying. Furthermore, the screed samples are weighted during every measurement to determine the total mass and the corresponding moisture loss.
To define the pore system precisely, mercury intrusion porosimetry as well as gas adsorption is performed. According to the data, the entire pore volume distribution is known. The measured pore diameters range from 0.8 nm to 100 μm and the total porosity of the examined screeds ranges between 11 % and 22 %.
Based on these measurement data, moisture transport, pore saturation as well as sorption isotherms and their hysteresis may be calculated quantitatively as described by Strangfeld et al.