Chemie und Prozesstechnik
Filtern
Dokumenttyp
- Zeitschriftenartikel (1171)
- Vortrag (1069)
- Posterpräsentation (442)
- Beitrag zu einem Tagungsband (175)
- Forschungsdatensatz (55)
- Sonstiges (36)
- Buchkapitel (24)
- Forschungsbericht (23)
- Dissertation (15)
- Beitrag zu einem Sammelband (13)
- Preprint (7)
- Handbuch (5)
- Video (5)
- Zeitschriftenheft (Herausgeberschaft für das komplette Heft) (3)
- Sammelband (Herausgeberschaft für den kompletten Band) (2)
- Tagungsband (Herausgeberschaft für den kompletten Band) (1)
- Newsletter (1)
Sprache
- Englisch (3047) (entfernen)
Schlagworte
- Nanoparticles (114)
- Fluorescence (112)
- Concrete (89)
- LIBS (81)
- Mechanochemistry (72)
- Quantum yield (71)
- Ultrasound (71)
- SAXS (69)
- Non-destructive testing (68)
- XPS (61)
Organisationseinheit der BAM
- 1 Analytische Chemie; Referenzmaterialien (1085)
- 6 Materialchemie (973)
- 8 Zerstörungsfreie Prüfung (774)
- 6.1 Oberflächen- und Dünnschichtanalyse (348)
- 6.3 Strukturanalytik (322)
- 1.1 Anorganische Spurenanalytik (277)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (232)
- 8.0 Abteilungsleitung und andere (224)
- 1.2 Biophotonik (210)
- 4 Material und Umwelt (186)
Paper des Monats
- ja (26)
Many techniques are available for measuring particle size distribution. For ideal materials (spherical particles, well dispersed) it is possible to evaluate the Performance of These methods. The performance of the analytical instrumentation for the purpose of classifying materials according to EC Definition is unknown. In this work the performance of commercially available particle sizing techniques on representative NanoDefine set of real-world testing materials (RTM) and quality control materials (QCM) for the implementation of the Definition is evaluated.
Austenitic stainless steel welds as well as dissimilar metal welds with nickel alloy filler material, used in safety relevant parts of nuclear power plants, still challenge the ultrasonic inspection. The weld material forms large oriented grains which lead on the one hand to high sound scattering and on the other hand – to inhomogeneity and to the acoustic anisotropy of the weld structure. The ultrasonic wave fronts propagate not linearly, as in ferritic weld joints, but along the curves, which depend on the specific grain structure of the weld. Due the influence of these phenomena, it is difficult to analyze the inspection results and to classify the ultrasonic indications, which could be both from the weld geometry and from the material defects. A correct flaw sizing is not possible.
In an ongoing research project, different techniques to improve the reliability of ultrasonic testing at these kinds of welds are investigated. In a first step (in the previous research project) two ultrasonic inspection techniques were developed and validated on plane test specimens with artificial and realistic flaws. In the ongoing project, these techniques are applied to circumferential pipe welds with longitudinal and transverse flaws.
The technique developed at the Federal Institute for Materials Research and Testing (BAM) in Germany uses a combination of ray tracing and synthetic aperture focusing technique (SAFT). To investigate the unknown grain structure, the velocity distribution of weld-transmitting ultrasound waves is measured and used to model the weld by ray tracing.
The second technique, developed at the Fraunhofer Institute for Nondestructive Testing (IZFP) in Germany, uses Sampling Phased Array (Full Matrix Capture) combined with the reverse phase matching (RPM) and the gradient elastic constant descent algorithm (GECDM). This inspection method is able to estimate the elastic constants of the columnar grains in the weld and offers an improvement of the reliability of ultrasonic testing through the correction of the sound field distortion. The unknown inhomogeneity and anisotropy are investigated using a reference indication and the special optimization algorithm.
Both reconstruction techniques give quantitative inspection results and allow the defect sizing. They have been compared to conventional ultrasonic testing with techniques, which are state of the art for components in nuclear power plants. The improvement will be quantified by the comparison of the probability of detection (POD) of each technique.
In this presentation, we report on the Determination of the glass transition temperature of thin layers of Polyvinylmethylether (PVME) depending on the thickness of the polymer layer. The glass Transition of thin polymer layers is currently under much investigation due to the nano-confinement effects proposed to appear in dependence on the layer thicknesses in the nm range. The properties of the polymer, the temperature range, as well as the thicknesses range of the polymer layers pose a serious challenge to the investigation by means of
spectroscopic ellipsometry. By careful choice of experimental parameters, we were able to investigate the thickness change by temperature of PVME layers in the range between 2 and 300 nm and in the temperature range between 200 K and 340 K. By optimizing the analysis process, we were able to determine Tg values within this parameter range with sufficient accuracy to investigate the Tg change due to confinement effects.
Alongside the change of position of the glass transition with thickness, we discuss the details of the ellipsometric analysis and its implications for the resulting thermal properties of the thin polymer layers as well as the accuracy of the Tg value with respect to the method used in the analysis process.
Quenching and partitioning (Q&P) heat Treatment increases the deformability of high-strength martensitic steels. Therefore, it is necessary to have some metastable austenite in the microstructure, which transforms in martensite during plastic deformation (TRIP effect). The austenitic-martensitic microstructure is gained by an increased austenitization temperature, water quenching and additional partitioning. The partitioning enables local carbon diffusion, which stabilizes retained austenite and leads to partial reversion of martensite to austenite. The influence of partitioning time was studied for the martensitic stainless steel AISI 420 (X46Cr13, 1.4034). In line with these efforts, metallographic, XRD and EBSD measurements were performed to characterize the microstructural evolution. The mechanical properties were tested using tension and compression loading. Additional corrosion investigations showed the benefits of Q&P heat treatment compared to conventional tempering. The reversion of austenite by the partitioning treatment was verified with EBSD and XRD. Furthermore, the results of the mechanical and corrosion testing showed improved properties due to the Q&P heat treatment.
For assuring the safety and reliability of components and constructions in energy applications made of fiber-reinforced polymers (e.g., blades of wind turbines and tidal power plants, engine chassis, flexible oil and gas pipelines) innovative non-destructive testing methods are required. Within the European Project VITCEA complementary methods (shearography, microwave, ultrasonics and thermography) have been further developed and validated. Together with partners from the industry, test specimens have been constructed and selected on-site containing different artificial and natural defect artefacts. As base materials, carbon and glass fibers in different orientations and layering embedded in different matrix materials (epoxy, polyamide) have been considered. In this contribution, the validation of flash and lock-in thermography to these testing problems is presented. Data analysis is based on thermal contrasts and phase evaluation techniques. Experimental data are compared to analytical and numerical models. Among others, the influence of two different types of artificial defects (flat bottom holes and delaminations) with varying diameters and depths and of two different materials (CFRP and GFRP) with unidirectional and quasi-isotropic fiber alignment is discussed.
Morphology and structure of TixOy nanoparticles generated by femtosecond laser ablation in water
(2018)
In this work femto-second pulsed laser ablation in liquid (PLAL) procedure for the generation of titanium oxide nanoparticles (NP) is reported with the purpose of understanding morphology and structure of the newly generated NPs. Ablation duration was varied for optimization of NP generation processes between 10 and 90 min. Surface morphology of NPs as well as their size and shape (distribution) were analysed by various complementary electron microscopy techniques, i.e. SEM, TSEM and TEM. The crystalline structure of titanium oxide particles was investigated byXRD(two instruments operated in different geometries) and HR-TEM. Concentration of generated titanium oxide NPs in liquid was analysed by ICP-MS. A mix of crystalline (mainly anatase), partly crystalline and amorphous spherical titanium oxide NPs can be reported having a mean size between 10 and 20 nm, which is rather independent of the laser ablation (LA) duration. A second component consisting of irregularly shaped, but crystalline titanium oxide nanostructures is co-generated in the LA water, with more pronounced occurrence at longer LA times. The provenance of this component is assigned to those spherical particles generated in suspension and passing through the converging laser beam, being hence subject to secondary irradiation effects, e. g. fragmentation.
Copper alloys have found widespread application in various fields. The elemental composition determines the properties of the alloys and consequently their application. Therefore, knowing the composition of a copper alloy is very important.
Metrological institutes like the BAM (German Federal Institute for Materials Research and Testing) offer reference materials that can be used to prove the accuracy of the applied analysis method.
The aim of this application note is to demonstrate how Micro-X-ray fluorescence spectroscopy (Micro-XRF) expediently supplements the analysis of copper alloys by
using Bruker’s micro-focus X-ray source XTrace attached to a scanning electron microscope (SEM) and operating with an energy dispersive spectrometer.
Ellipsometry is well known as a highly sensitive and reproducible surface analysis technique. However, in a context of metrological applications, the most important property of a measurement process is accuracy, relying on statistical precision, (reproducibility) and trueness (in an absolute sense versus a given standard). The latter is much more difficult to achieve. In this presentation, we discuss the possibility of establishing ellipsometry in a diverse metrological landscape by means of defining standard procedures and best practice methodologies for the measurement and for calibration purposes. The most important task of this approach is to determine the model-inherent uncertainty, originating from parameter coupling. We achieve this by means of sensitivity analysis of the parameters resulting from the fit process. We discuss the definition of reference materials by which accuracy can be made available for ellipsometry, passed along between ellipsometry laboratories and for other measurement techniques. The determination of uncertainty is presented in this work for a number of examples involving difficult analysis models employed for samples from different production environments. We present a standardization initiative with the goal to disseminate this work into an international standard alongside an inter-laboratory study comparing the results for complex samples gained by laboratories with different instrumentation. We also present the results gained within EURAMET projects focused on the metrology of materials with strong non-idealities used in photovoltaics and other energy technology.
The common characterization and identification of pollen is a time-consuming task that mainly relies on microscopic determination of the genus-specific pollen morphology. A variety of spectroscopic and spectrometric approaches have been proposed to develop a fast and reliable pollen identification using specific molecular information. Amongst them, matrix-assisted laser desorption/ionization time-of-flight mass spectrometry (MALDI-TOF MS) shows a high potential for the successful investigation of such complex biological samples. Based on optimized MALDI sample preparation using conductive carbon tape, the application of multivariate statistics (e.g. principal components analysis, PCA) yields an enormous improvement concerning taxonomic classification of pollen species compared to common microscopic techniques.
Since multivariate evaluation of the recorded mass spectra is of vital importance for classification, it’s helpful to implement the applied sequence of standard Matlab functions into a graphical user interface (GUI). In this presentation, a stand-alone application (GUI) is shown, which provides multiple functions to perform fast multivariate analysis on multiple datasets. The use of a GUI enables a first overview on the measured dataset, conducts spectral pretreatment and can give classification information based on HCA and PCA evaluation. Moreover, it can be used to improve fast spectral classification and supports the development of a simple routine method to identify pollen based on mass spectrometry.
We designed micro-hollow cathode discharge prototypes under atmospheric pressure and investi-gated their acoustic characteristics. For the acoustic model of the discharge, we correlated the self-organisation effect of the current density distribution with the ideal model of an acoustic membrane. For validation of the obtained model, sound particle velocity spectroscopy was used to detect and analyse the acoustic emission experimentally. The results have shown a behaviour similar to the ideal acoustic membrane. Therefore, the acoustic excitation is decomposable into its eigenfrequencies and predictable. The model was unified utilising the gas exhaust velocity caused by the electrohydrodynamic force. The results may allow a contactless prediction of the current density distribution by measuring the acoustic emission or using the micro-discharge as a tunable acoustic source for specific applications as well.
Investigation of core-shell nanoparticles using scanning transmission x-ray microscopy (STXM)
(2018)
A scanning transmission x-ray microscopy (STXM) based methodology is introduced for determining the dimensions (shell thickness, core and total diameter) of core-shell nanoparticles which exhibit a strong x-ray absorption contrast and a well-defined interface between core and shell material. A low radiation dosage during data acquisition and, therefore, less x-ray beam induced damage of the sample is achieved by recording STXM images only at two predetermined energies of maximum absorption contrast, instead of recording a stack of images across the whole absorption edge. A model core-shell nanoparticle, polytetrafluoroethylene (PTFE) cores with polystyrene (PS) shell, is used for demonstration. Near edge x-ray absorption fine structure (NEXAFS) spectroscopy confirms the significant difference in x-ray absorption behavior between PTFE and PS. Additionally, due to the insolubility of styrene in PTFE a well-defined interface between particle core and shell is expected. In order to validate the STXM results, both the naked PTFE cores as well as the complete core-shell nanoparticles are examined by scanning electron microscopy (SEM). The introduced STXM based methodology yields particle dimensions in good agreement with the SEM results (deviation equal or less than 10%) and provides additional information such as the position of the particle core which cannot be extracted from a SEM micrograph.
Absolute Isotope Ratios
(2018)
Measurement results and scientific models leading to important decisions in forensics, food fraud or climatology are based on isotope ratio data. Molar masses of multi-isotopic elements are as well based on isotope ratio data. Thus, in the case of Si, isotope ratios directly impact the redefinition of the SI base units kilogram and mole. Therefore, new strategies are required leading to new primary isotope reference materials, whose isotope ratios are traceable to the SI. This in turn will ensure the comparability of isotope ratio data and will render the traceability exception requested by the CCQM superfluous. Such new procedures will be developed for the key elements S, Si, Ca, Sr and Nd at relative uncertainty levels of ≤ 0.01 %.
In chemical elements with three or more stable isotopes, mass-dependent stable isotope fractionation is expressed by co-varying isotope ratios. In the three-isotope space ((δ’m2/δ’m1)/(( δ’m3/δ’m1)) these plot along a line with a slope (β), the so called ‘terrestrial fractionation line’. This partitioning of stable isotopes results from both kinetic and equilibrium reactions that are characterized by specific β-values.
For the natural range of isotope ratios of ‘novel’ stable isotope systems such as Si, Mg, Fe, Zn, Cu this information cannot be accessed because samples fall close to the delta-zero standard where the current measurement precision is too low to resolve small differences in β. We present a new approach to resolve deviations from a reference slope β by standard-sample bracketing against material offset from the natural range. We use this approach to explore the isotope fractionation mechanism in the mammalian food web. We have analyzed Mg stable isotope ratios in bone bioapatite of herbivore, omnivore and carnivore mammals. Positive shifts in δ26/24Mg along the trophic chain (from herbivore to carnivore) together with β= 0.513 suggest the presence of two isotope fractionation mechanisms operating during biomineralization. While positive shifts in δ26/24Mg are in favor of equilibrium isotope fractionation process, the proximity of β to the theoretically calculated β(kinetic) of typically 0.511 suggests the presence of a second component that fractionates stable isotopes kinetically. The herein presented approach is applicable to any element with 3+ stable isotopes analyzed by multi-collector inductively coupled plasma mass spectrometry.
This is the first time that PE frits were used to quantify sulfur in copper and its alloys by isotope dilution combined with LA-ICP-MS: an alternative approach for sample preparation. The following properties of the PE frit meet the requirements for isotope dilution LA-ICPMS:: porous material, thermo plastic (melting point >100oC), chemical resistance (nitric acid >70%) and high adsorption efficiency. The breakthrough, however, as a support material, especially when comparing the PE frit with other materials such gelatin or sodium silicate is the low blank, which is only two times of the gas flow blank (2.3-4.0 x 104 cps). Additionally, the porosity of the frit was considered, as it directly affects the adsorption efficiency for the sample solution, which is present in the cavities of the frit.
Adsorption efficiency was studied by depositing sulfur standards with varying sulfur amounts (0, 2, 5, 10, 20, 40 and 80 µg S) on the frits. The remaining sulfur which was not absorbed by the frit was rinsed off and was measured by ICP-MS. This indirect method shows that more than 99.5 % of the loaded sulfur was absorbed by the frit. Such high absorption efficiency is completely sufficient for a support material to be used in LA-ICP-IDMS. The so prepared frits whith increasing sulfur amount were measured by LA-ICP-MS showing a good linearity between 0 µg S and 40 µg S whit a correlation coefficient r2 of 0.9987 and sensitivy of 3.4x104 cpsµg-1 for 32S.
Three copper reference materials produced by BAM were selected to develop and validate the LA-ICP-IDMS procedure. The IDMS technique was applied to these samples as follows: the samples were spiked, dissolved, digested and then the digest was adsorbed on the frits.
For the first time polyethylene (PE) frits were used to quantify sulphur in copper metal and its alloys by isotope dilution combined with LA-ICP-MS: an alternative approach for sample preparation. The properties of the PE frit meet the requirements for isotope dilution LA-ICPMS which are porous material, thermal and chemical resistance and high absorption efficiency. The breakthrough, however, as a support material, is the low sulphur blank, which is only two times of the gas flow blank (2.3-4.0 x 10⁴ cps). Additionally, the porosity of the frit was considered, as it directly affects the absorption efficiency for the sample solution, which is present in the cavities of the frit.
The absorption efficiency was studied by loading sulphur standards with varying sulphur amounts (0 - 80 µg S) onto the frits. The remaining sulphur which was not absorbed by the frit was rinsed off and was measured by ICP-MS. This indirect method shows that more than 99.5 % of the loaded sulphur was absorbed by the frit. The so prepared frits with increasing sulphur amount were measured by LA-ICP-MS showing a good linearity between 0 µg S and 40 µg S with a coefficient of determination, r2 of 0.9987 and a sensitivity of 3.4x10⁴ cps µgˉ¹ for 32S.
Three copper reference materials produced by BAM (BAM-M376a, BAM-228 and BAM-227) were selected to develop and validate the LA-ICP-IDMS procedure. The IDMS technique was applied to these samples as follows: the samples were spiked, dissolved, digested and then the digested solution was absorbed on the frits. The dried frit samples were then analyzed by LA-ICP-IDMS and it could be demonstrated that the sample solution dispersed on the frits did not influence the 32S/34S ratio significantly even though the sulphur intensities were fluctuating along the scan lines. Relative standard deviations of the isotope ratios were below 5 % in average between 3 lines (except for the pure spike solution and procedure blank). The measurement results were validated by comparing them with the results obtained by conventional ICP-IDMS. Plotting the mass fraction of sulphur in copper obtained by LA-ICP-IDMS versus those obtained by ICP-IDMS yields a linear curve with a correlation coefficient of 0.9999 showing a strong agreement between both techniques.
The metrological traceability to the SI for the mass fraction of sulphur in copper is established by an unbroken chain of comparisons, each accompanied by an uncertainty budget. Thus, the measurement results are considered reliable, acceptable and comparable within the stated measurement uncertainty. The metrological traceability chain from the kg down to the final mass fraction in the samples obtained by LA-ICP-IDMS is illustrated in this presentation.
Sulfur is one of the major impurity elements in copper. Previously applied methods for the quantification of sulfur in copper and other pure metals revealed a lack of traceability and showed inconsistent result. Therefore, in this study a procedure was developed for the quantification of total sulfur in copper at low concentration levels using inductively coupled plasma-isotope dilution mass spectrometry (ICP-IDMS). A major challenge for the quantification of sulfur in copper (alloyed/unalloyed) by ICPMS is the copper matrix itself, causing matrix effects and making an extensive cleaning (cones, extraction lens) necessary after measurements. Matschat et al investigated the analysis of high-purity metals (including copper) by high resolution ICP-MS and found that the copper matrix shows strong matrix effects on the sensitivity resulting from Cu deposition on the cones. Therefore, the major part of the copper matrix has to be separated, which was accomplished by adding ammonia which forms a complex with the copper while releasing the sulfur. This was followed by a chromatographic separation using a weak cation resin. After that the sulfur fraction was further purified by chromatographic means using an anion exchange method followed by a chelating resin.
The anion exchange resin (AG1X8), however, is selective to sulfate and sulfite but less-selective to sulfide. Therefore, when quantifying total sulfur in copper, the different species of sulfur need to be oxidized to sulfate prior to the sulfur-matrix separation on the AG1X8 resin in order to avoid any measurement bias. When applying the HPA oxidation with concentrated HNO3 and H2O2 a complete conversion from sulfide and sulfite to sulfate could be achieved. The recovery of all investigated sulfur species is quantitative within measurement uncertainties. The copper samples investigated in this study contain copper in the range of 0.85-0.99 kg·kg-1 and zinc from <10 to 300 g·kg-1. Approximately 0.10-0.25 g of these samples were used to perform the sulfur-copper separation. After applying the complete three stage separation procedure the mass fractions of both elements were significantly reduced to below 400 ng·g-1 for copper and below 50 ng·g-1 for zinc, respectively. The developed procedure shows high performance, especially concerning high efficiency in matrix removal (> 99.999%) while keeping the recovery of sulfur above 80%.
The procedure blank was determined by IDMS as well and yielded values for the individual IDMS measurement sequences ranging from 3 ng to 53 ng. The average of these individual procedure blanks (n=22) was calculated and yielded a total procedure blank of 14 ng sulphur with standard deviation of 12 ng. The limit of detection (LOD, blank+3SD) calculated on this basis was 0.20 µg·g-1 while the limit of quantification (LOQ, blank+10SD) was 0.54 µg·g-1, when considering a sample weight of 0.25 g.
The quantification of low sulfur contents (< 15 µg/g) by conventional IDMS is hindered by the very high Cu/S ratio, which clearly affects the separation in a negative way: The recovery of sulfur dropped to about 30 % for four replicates, while two further replicates even showed recoveries below 10%. To enable measurement without completely changing the separation procedure, an exact amount of sulfur was added prior to spiking, such that the sulfur mass fraction was shifted to the optimum working range of the separation procedure. Thus exact amounts of sulfur were added to enhance the mass fraction of sulfur from 15 µg·g-1 to 40 µg·g-1, then the IDMS analysis was performed as usual and finally the added sulfur amount was subtracted. The so obtained measurement result agreed well with the certified value within the uncertainties. The relative expanded measurement uncertainties for conventional IDMS are below 1%. When applying the modified IDMS procedure, where back-spike is added to the sample before spiking, the relative expanded measurement uncertainties are larger and up to 5%. With the presented sulfur-matrix procedure a working range from approximately 15 µg·g-1 to 1500 µg·g-1 can be achieved.
The developed procedure for the quantification of low sulfur amounts in copper has been validated here via three different routes: first an inter-laboratory comparison at highest metrological level, second a step-by-step validation by checking each single step of the procedure and third the setup of a complete uncertainty budget.
The procedure is sufficient to facilitate value assignment of total sulfur mass fraction in reference materials. Additionally, relative measurement uncertainties were calculated below 1 % and the measurement results are traceable to the SI, which is clearly demonstrated in this work. The procedure reported in this study is a new reference procedure for sulfur measurement in copper, well meeting the requirements of the two major purposes: the certification of reference materials and the assignment of reference values for inter-laboratory comparison.
An immunohistochemical method is described to visualize the distribution of metallothioneins 1/2 (MT 1/2) and metallothionein 3 (MT 3) in human ocular tissue. It is making use of (a) antibodies conjugated to gold nanoclusters (AuNCs) acting as labels, and (b) laser ablation (LA) coupled to inductively coupled plasma – mass spectrometry (ICP-MS). Water-soluble fluorescent AuNCs (with an average size of 2.7 nm) were synthesized and then conjugated to antibody by carbodiimide coupling. The surface of the modified AuNCs was then blocked with hydroxylamine to avoid nonspecific interactions with biological tissue. Immunoassays for MT 1/2 and MT 3 in ocular tissue sections (5 μm thick) from two post mortem human donors were performed. Imaging studies were then performed by fluorescence using confocal microscopy, and LA-ICP-MS was performed in the retina to measure the signal for gold. Signal amplification by the >500 gold atoms in each nanocluster allowed the antigens (MT 1/2 and MT 3) to be imaged by LA-ICP-MS using a laser spot size as small as 4 μm. The image patterns found in retina are in good agreement with those obtained by conventional fluorescence immunohistochemistry which was used as an established reference method.
The spectroscopic characterization by surface-enhanced Raman scattering (SERS) has shown great potential in studies of heterogeneous catalysis. We describe a plug-in multifunctional optofluidic platform that can be tailored to serve both as a variable catalyst material and for sensitive optical characterization of the respective reactions using SERS in microfluidic systems. The platform enables the characterization of reactions under a controlled gas atmosphere and does not present with limitations due to nanoparticle adsorption or memory effects. Spectra of the gold-catalyzed reduction of p-nitrothiophenol by sodium borohydride using the plug-in probe provide evidence that the borohydride is the direct source of hydrogen on the gold surface, and that a radical anion is formed as an intermediate. The in situ monitoring of the photoinduced dimerization of p-aminothiophenol indicates that the activation of oxygen is essential for the plasmon-catalyzed oxidation on gold nanoparticles and strongly supports the central role of metal oxide species.
The accurate EDS microanalysis of light elements such as boron and carbon by spectrum imaging will be demonstrated using a sintered hard ceramic material composed of the three major phases titanium boride (TiB2), titanium carbide (TiC), silicon carbide (SiC) and minor phases, sub-μm in size.
The combination of these three materials leads to improved mechanical and tribological properties. Silicon carbide is a material used for mechanical seals. It has the disadvantage of reduced failsafe running functions, causing increased wear when running dry. The added titanium components (TiC and TiB2) improve the failsafe running functions. This technology has already been transferred to industrial applications.
In order to provide further evidence of damage mechanisms predicted by the recent solid-state transformation creep (SSTC) model, direct observation of damage accumulation during creep of Al–3.85Mg was made using synchrotron X-ray refraction. X-ray refraction techniques detect the internal specific surface (i.e. surface per unit volume) on a length scale comparable to the specimen size, but with microscopic sensitivity. A significant rise in the internal specific surface with increasing creep time was observed, providing evidence for the creation of a fine grain substructure, as predicted by the SSTC model. This substructure was also observed by scanning electron microscopy