Laser-induced breakdown spectroscopy (LIBS) is a spectroscopic method for detecting the chemical composition of optically accessible surfaces. In principle, the measurement of all elements of the periodic table is possible. System calibrations allow the quantification of element concentrations. In combination with scanner systems, the two-dimensional element distribution can be determined. Even rough surfaces can be measured by online adjustment of the laser focus. To detect element ingress into the concrete, typically cores are taken, cut in half, and LIBS measurements are performed on the cross-section. The high spatial resolution as well as the simultaneous multi-element analysis enables a separate evaluation of the binder-matrix and aggregates. Therefore, the element concentrations can be determined directly related to the cement paste. LIBS measurements are applicable in the laboratory, on-site and also over a distance of several meters.
Common applications include the investigation of material deterioration due to the ingress of harmful ions and their interaction in porous building materials. LIBS is able to provide precise input parameters for simulation and modelling of the remaining lifetime of a structure. Besides the identification of materials, also their composition can be determined on hardened concrete, such as the type of cement or type of aggregate. This also involves the identification of environmentally hazardous elements contained in concrete. Another possible application is the detection of the composition of material flows during dismantling. Non-contact NDT for “difficult to assess” structures as an example application through safety glass or in combination with robotics and automation are also possible.
This work presents the state of the art concerning LIBS investigations on concrete by showing exemplary laboratory and on-site applications.
Laser-induced breakdown spectroscopy (LIBS) is a spectroscopic method for the analysis of the chemical composition of sample materials. Generally, the measurement of all elements of the periodic table is possible. In particular, light elements such as H, Li, Be, S, C, O, N and halogens can be measured. Calibration with matrix-matching standards allows the quantification of element concentrations. In combination with scanner systems, the two-dimensional element distribution can be determined. Even rough surfaces can be measured by online adjustment of the laser focus. LIBS can also be used on-site with mobile systems. Hand-held systems are available for point measurements.
Common applications include the investigation of material deterioration due to the ingress of harmful ions and their interaction in porous building materials. Due to the high spatial resolution of LIBS and the consideration of the heterogeneity of concrete, the determination of precise input parameters for simulation and modelling of the remaining lifetime of a structure is possible. In addition to the identification of materials, it is also possible to assess the composition for example of hardened concrete, which involves the cement or aggregate type used. Other important fields of application are the detection of environmentally hazardous elements or the material classification for sorting heterogeneous material waste streams during dismantling. Non-contact NDT for “difficult to assess” structures as an example application through safety glass or in combination with robotics and automation are also possible.
In this work, an overview of LIBS investigations on concrete is given based on exemplary laboratory and on-site applications.
Due to the ageing of the infrastructure facilities, a reliable assessment of the condition of concrete structures is of great interest to plan timely and appropriate measures. In concrete structures, pittingcorrosion of the reinforcement is the predominant deterioration mechanism affecting serviceability and eventually structural performance. Determination of quantitative chloride ingress is not only necessary to obtain valuable information on the current condition of a structure, but the data obtained can also be used to predict future developments and the associated risks. An overview of the progress and the possibilities of the application of laser-induced breakdown spectroscopy for concrete analysis in daily civil engineering practice is given. High-resolution 2D measurements of drill cores to determine the penetration of harmful species into concrete is presented. Furthermore, the application of a mobile LIBS system in a parking garage is shown. The system consists of a diode-pumped low-energy laser (3 mJ, 1.5 ns, 100 Hz) and a compact NIR spectrometer. A scanner allows two-dimensional element mapping. Progress towards the establishment of LIBS in a leaflet for the analysis of chlorine ingress into concrete in civil engineering is presented.
The main application of LIBS in civil engineering is the detection of harmful ions in concrete, which can penetrate the component through the porous concrete structure. The advantages of LIBS over standard methods are the possibility of multi-element analysis, measurement speed, spatially resolved measurements, and minimal sample preparation. The spatially resolved measurements of LIBS allow the assessment of the heterogeneity of the concrete by measuring separately the chemical composition of the aggregates and the binder matrix. The latter is particularly relevant because the determined elemental distribution can be directly related to the binder matrix. This is not possible with standard methods, since the material is homogenized to powder during sample preparation stage and the determined concentration is thus related to the total mass. In addition to the use of LIBS for the specific analysis of individual harmful ions, LIBS can also be used to estimate the concrete composition and thus determine, for example, the type of cement used. Corresponding information are relevant for the estimation of the remaining service life and for the preparation of a maintenance concept. In recent years, LIBS has been increasingly used in civil engineering. Currently, however, it is primarily used in research institutions and only occasionally in building materials laboratories. Special commercial devices have also been developed, which greatly simplify the application due to the high degree of automation. Mobile LIBS systems allow on-site application. A central point, which limits the use of LIBS in the commercial sector, is the lack of norms and standards. Therefore, within the framework of a project funded by the German government, work has been carried out on the preparation of a leaflet on quantitative chlorine determination in concrete, which will be published this year. In interlaboratory comparisons the robustness and accuracy for the practical application was demonstrated. LIBS also has great potential in the recycling of construction waste in conjunction with hyperspectral sensors. This issue is currently being addressed in a national project. During the presentation, the state of the art of LIBS in civil engineering will be presented, next steps will be discussed, and future challenges will be outlined.
Laser Induced Breakdown Spectroscopy – A Tool for Imaging the Chemical Composition of Concrete
(2022)
One of the most common causes of damage is the ingress of harmful ions into the concrete, which can lead to deterioration processes and affect structural performance. Therefore, the increasingly aging infrastructure is regularly inspected to assess durability. Regular chemical analysis can be useful to determine the extent and evolution of ion ingress and to intervene in a timely manner. This could prove more economical than extensive repairs for major damage, particularly for critical infrastructure. In addition to already established elemental analysis techniques in civil engineering such as potentiometric titration or X-ray fluorescence analysis, laser-induced breakdown spectroscopy (LIBS) can provide further important complementary information and benefits. The possibilities of LIBS are demonstrated using the example of a drill core taken from a parking garage.
New possibilities for concrete analysis 4.0 with the Laser-Induced Breakdown Spectroscopy (LIBS)
(2020)
In civil engineering the damage assessment of concrete infrastructures is an important task to monitor and ensure the estimated life-time. The aging of concrete is caused by different damage processes like the chloride induced pitting corrosion of the reinforcement. The penetration depth and the concentration of harmful species are crucial factors in the damage assessment. As a highly cost and time-consuming standard procedure, the analysis of concrete drill cores or drilling by wet-chemistry is widely used. This method provides element concentration to the total mass as aggregates and binder are homogenized. In order to provide a method that is capable to detect the element concentration regarding the cement content only, the laser-induced breakdown spectroscopy (LIBS) will be presented. The LIBS method uses a focused pulsed laser on the sample surface to ablate material. The high-power density and the laser-material interaction causes a laser-induced plasma that emits elemental and molecular line emission due to energy transition of the excited species in the plasma during the cooling phase.
As each element provides element-specific line emission, it is in principle possible to detect any element on the periodic table (spectroscopic fingerprint) with one laser shot. In combination with a translation stage the sample under investigation can be spatially resolved using a scan raster with a resolution up to 100 µm (element mapping). Due to the high spatial resolution, the element distribution and the heterogeneity of the concrete can be evaluated. By using chemometrics the non-relevant aggregates can be excluded from the data set and the element concentration can be quantified and referred to a specific solid phase like the binding matrix (cement) only. In order to analyze transport processes like diffusion and migration the twodimensional element distributions can provide deep insight into the transport through the pore space and local enrichments of elements. As LIBS is a multi-elemental method it is also possible to compare the ingress and transport process of different elements like Cl, Na, K, S, C, and Li simultaneously and evaluate cross-correlations between the different ions. Furthermore, the element mapping allows to visualize the transport along cracks. This work will show the state of the art in terms of hardware and software for an automated LIBS system as well as different application for a concrete analysis 4.0. Focus will be the application of LIBS for a fast concrete analysis.
This paper will address the relevance of chloride measurements in practice for durability condition assessment and a description of the working principle of LIBS will be given. Examples of chloride profiles obtained by the common wet chemical analysis will be shown and compared with results from LIBS measurements as to demonstrate the accuracy of the LIBS-technique. The latter will be supported by clear graphs. In addition examples on the extra information resulting from measurements performed with LIBS for improvement of condition assessment and prediction will be shown.
A big part of the infrastructure is made of concrete, which is a multiphase system made of cement, aggregates, water and pores. Concrete is often used in combination with steel as reinforced concrete. Environmental influences, especially the ingress of harmful ions in combination with the ingress of water, trigger different damage processes which reduce the designed lifetime of a structure. The ingress of chlorides from de-icing salt or sea water leads to corrosion of the reinforcement. In addition, the carbonation of the concrete may trigger the corrosion of the reinforcement. The ingress of alkalis from deicing salts may cause the expansion of the amorphous silica aggregates (alkali-silica reaction) through
formation of a swelling gel of calcium silicate hydrate if water is present. The ingress of sulphates may cause spalling of the concrete surface due to ettringite formation.
For the standard procedure in civil engineering cores are taken, cut in slices, grinded and the obtained homogenized powder is solved in acid and investigated by standard procedures.
BAM has developed the LIBS technique for the 2D evaluation of the chemical composition of concrete. The technique is established for automated laboratory use with high numbers of samples to investigate transport processes of harmful species (Cl-, CO2 , SO4 2-and alkalis) in concrete. Information about ingress depth and the quantitative values are important to estimate the remaining lifetime of the infrastructure. LIBS is a surface technique. To get information about the ingress depth, a drill core has to be taken and cut in the middle. The measurements are carried out at the cross section. The main advantages of LIBS are the direct measurement on the surface of the concrete, fast analysis (sample rate 100 Hz) with a spatial resolution of up to 100 µm, the consideration of the heterogeneity of the concrete and the possibility of automated measurements which save a lot of manpower and time. As an example the investigation of ingress profiles for standard diffusion and migration tests in civil engineering takes hours in comparison to just a few minutes using LIBS. At the same time a 2D-evaluation provides information about hot spots of elemental concentration which may not be found by standard methods.
The state of the art of LIBS technique for applications in civil engineering will be presented, including typical results of 2D investigation of concrete in laboratory. The performance is also demonstrated by examples for onsite applications using a mobile LIBS system. The road map to standardization is presented as well.
Concrete is often used in combination with steel as reinforced concrete. Environmental influences, especially the ingress of harmful ions in combination with the ingress of water, trigger different damage processes which reduce the designed lifetime of a structure. The ingress of chlorides from de-icing salt or sea water leads to corrosion of the reinforcement. Also the carbonation of the concrete may trigger the corrosion of the reinforcement. The ingress of alkalis from de-icing salts may cause the expansion of the amorphous silica aggregates (alkali-silica reaction) through formation of a swelling gel of calcium silicate hydrate if water is present. The ingress of sulfates may cause spalling of the concrete surface due to ettringite formation.
BAM has developed the LIBS technique for automated laboratory use with high numbers of samples to investigate transport processes of harmful species (Cl-, CO2, SO42- and alkalis) in concrete. Information about ingress depth and the quantitative values are important to estimate the remaining lifetime of the infrastructure. To get information about the ingress depth, a core has to be taken and cut in the middle. The measurements are carried out at the cross section. The main advantages of LIBS are the direct measurement on the surface of the concrete, fast analysis (sample rate 100 Hz) with a spatial resolution of up to 100 µm, the consideration of the heterogeneity of the concrete. The possibility of automated measurements saves a lot of manpower and time. At the same time a 2D-evaluation provides information about hot spots of elemental concentration which may not be found by standard methods.
Typical results of 2D investigation of concrete in laboratory will be presented. The performance is also demonstrated by examples for onsite applications using a mobile LIBS system. The road map to standardization is presented as well.
The majority of the built infrastructure is made of concrete, which is a multiphase system made of cement, aggregates, water and pores. Concrete is often used in combination with steel as reinforced concrete. Environmental influences, especially the ingress of harmful ions in combination with the ingress of water, trigger different damage processes which reduce the designed lifetime of a structure. The ingress of chlorides from de-icing salt or sea water leads to corrosion of the reinforcement. Also the carbonation of the concrete may trigger the corrosion of the reinforcement. The ingress of alkalis from de-icing salts may cause the expansion of the amorphous silica aggregates (alkali-silica reaction) through formation of a swelling gel of calcium silicate hydrate if water is present. The ingress of sulfates may cause spalling of the concrete surface due to ettringite formation.
For the standard procedure in civil engineering cores are taken, cut in slices, grinded and the obtained homogenized powder is solved in acid and investigated by standard procedures.
BAM has developed the LIBS technique for the 2D evaluation of the chemical composition of concrete [1-11]. The technique is established for automated laboratory use with high numbers of samples to investigate transport processes of harmful species (Cl-, CO2, SO42- and alkalis) in concrete. Information about ingress depth and the quantitative values are important to estimate the remaining lifetime of the infrastructure. LIBS is a surface technique. To get information about the ingress depth, a core has to be taken and cut in the middle. The measurements are carried out at the cross section. The main advantages of LIBS are the direct measurement on the surface of the concrete, fast analysis (sample rate 100 Hz) with a spatial resolution of up to 100 µm, the consideration of the heterogeneity of the concrete and the possibility of automated measurements which save a lot of manpower and time. As an example the investigation of ingress profiles for standard diffusion and migration tests in civil engineering takes hours in comparison to just a few minutes using LIBS. At the same time a 2D-evaluation provides information about hot spots of elemental concentration which may not be found by standard methods.
Ingress of chlorides due to a crack in a repair mortar. Left: Photo of the cross section of a concrete core and the surface investigated by LIBS (area 70 mm x 70 mm). Right: Color coded chlorine intensity on the cross section of a concrete core, dark red represents high chlorine content.
The state of the art of LIBS technique for applications in civil engineering will be presented, including typical results of 2D investigation of concrete in laboratory. The performance is also demonstrated by examples for onsite applications using a mobile LIBS system. The road map to standardization is presented as well.
Detection of ion ingress by LIBS for Evaluation of the remaining lifetime of a concrete structure
(2018)
The majority of the built infrastructure is made of concrete, which is a multiphase system made of cement, aggregates, water and pores. Concrete is often used in combination with steel as reinforced concrete. Environmental influences, especially the ingress of harmful ions in combination with the ingress of water, trigger different damage processes which reduce the designed lifetime of a structure. The ingress of chlorides from de-icing salt or sea water leads to corrosion of the reinforcement. Also the carbonation of the concrete may trigger the corrosion of the reinforcement. The ingress of alkalis from de-icing salts may cause the expansion of the amorphous silica aggregates (alkali-silica reaction) through formation of a swelling gel of calcium silicate hydrate if water is present. The ingress of sulfates may cause spalling of the concrete surface due to ettringite formation.
For the standard procedure in civil engineering cores are taken, cut in slices, grinded and the obtained homogenized powder is solved in acid and investigated by standard procedures.
BAM has developed the LIBS technique for the 2D evaluation of the chemical composition of concrete [1-11]. The technique is established for automated laboratory use with high numbers of samples to investigate transport processes of harmful species (Cl-, CO2, SO42- and alkalis) in concrete. Information about ingress depth and the quantitative values are important to estimate the remaining lifetime of the infrastructure. LIBS is a surface technique. To get information about the ingress depth, a core has to be taken and cut in the middle. The measurements are carried out at the cross section. The main advantages of LIBS are the direct measurement on the surface of the concrete, fast analysis (sample rate 100 Hz) with a spatial resolution of up to 100 µm, the consideration of the heterogeneity of the concrete and the possibility of automated measurements which save a lot of manpower and time. As an example the investigation of ingress profiles for standard diffusion and migration tests in civil engineering takes hours in comparison to just a few minutes using LIBS. At the same time a 2D-evaluation provides information about hot spots of elemental concentration which may not be found by standard methods.
Ingress of chlorides due to a crack in a repair mortar. Left: Photo of the cross section of a concrete core and the surface investigated by LIBS (area 70 mm x 70 mm). Right: Color coded chlorine intensity on the cross section of a concrete core, dark red represents high chlorine content.
The state of the art of LIBS technique for applications in civil engineering will be presented, including typical results of 2D investigation of concrete in laboratory. The performance is also demonstrated by examples for onsite applications using a mobile LIBS system. The road map to standardization is presented as well.
In civil engineering concrete is the most used building material for making infrastructures like bridges and parking decks worldwide. It is as a porous and multiphase material made of aggregates with a defined grain size distribution, cement and water as well as different additives and admixtures depending on the application. Different grain sizes are important to ensure the needed density and compressive strength.
The resulting porous cement matrix contains a mixture of flour grains (aggregates with a grain size below 125 lm) and cement particles (particle size≈50lm). Harmful species like chlorides may penetrate together with water through the capillary pore space and may trigger different damage processes. The damage assessment of concrete structures in Germany is estimated due to the quantification of harmful elements regarding to the cement content only. In the evaluation of concrete using LIBS a two-dimensional scanning is necessary to consider the heterogeneity caused by the aggregates. Therefore, a LIBS system operating with a low energy NdCr:YAG laser, a pulse energy of 3 mJ, a wavelength of 1064 nm, a pulse width of 1.5 ns and a Repetition rate of 100 Hz has been used. Different Czerny-Turner spectrometers with CCD detectors in the UV and NIR range have been used for the detection. Large aggregates (macro-heterogeneity) can be excluded from the evaluation, whereas small aggregates in the range of the laser spot size (flour grains) cannot be spatially resolved. In this work the micro heterogeneity caused by flour grains and their impact on the quantification with LIBS will be discussed. To analyze the effect of changing grain sizes and ratios, the ablation behavior has been determined and compared. Samples with defined grain sizes were made and analyzed using LIBS.
The grain size distributions were analyzed with laser diffraction (LDA).