Degradation von Werkstoffen
Filtern
Dokumenttyp
- Vortrag (462)
- Posterpräsentation (106)
- Beitrag zu einem Tagungsband (95)
- Zeitschriftenartikel (42)
- Buchkapitel (13)
- Sonstiges (11)
- Forschungsdatensatz (6)
- Beitrag zu einem Sammelband (5)
- Dissertation (3)
Sprache
- Englisch (743) (entfernen)
Referierte Publikation
- nein (743) (entfernen)
Schlagworte
- Corrosion (96)
- Welding (44)
- Hydrogen (41)
- Additive Manufacturing (32)
- Additive manufacturing (28)
- Residual stress (23)
- Degradation (22)
- Microplastics (20)
- Microstructure (19)
- MIC (17)
Organisationseinheit der BAM
- 9 Komponentensicherheit (254)
- 5 Werkstofftechnik (196)
- 7 Bauwerkssicherheit (154)
- 9.4 Integrität von Schweißverbindungen (147)
- 8 Zerstörungsfreie Prüfung (105)
- 7.6 Korrosion und Korrosionsschutz (100)
- 6 Materialchemie (87)
- 5.1 Mikrostruktur Design und Degradation (73)
- 8.5 Röntgenbildgebung (66)
- 5.2 Metallische Hochtemperaturwerkstoffe (62)
The corrosion behavior of galvanized steels and zinc components under atmospheric exposure depends mostly on the corrosion product‐based cover layer formation under the prevailing conditions. The use of agar‐based gel electrolytes makes it possible to use electrochemical methods to obtain a characteristic value from these cover layers that describe their current and future protective capacity. It is shown here that different states of galvanized steel can be distinguished very well under laboratory conditions and that this method is also suitable for use under practical conditions. Based on the characteristic values and assuming future time of wetness, it is very easy to draw up a forecast for the future corrosion rate, which provides plausible values.
While alkali-activated binders offer certain advantages over traditional Portland cement binders, particu¬larly in terms of resistance against chemical attacks and potentially environmental footprint, their degra¬dation mechanisms remain incompletely understood at present, specifically carbonation. Thus, this study investigates the impact of natural and accelerated carbonation (1% and 4% CO2) on three different compositions of alkali-activated concretes: 100% calcined clay (C100) binder, 100% ground blast furnace slag (S100) binder, and a 40% calcined clay and 60% blast furnace slag blend (C40S60). C100 concretes exhibit faster carbonation kinetics, with five times greater natural carbonation depths than S100. This difference diminishes under accelerated carbonation, showing a 1.5 times difference for 1% CO2 and complete carbonation for 4% CO2 at 90 days. The results thus confirm that accelerated carbonation testing of low-Ca alkali-activated concretes yields results that are not representative of natural carbonation. The C40S60 sample demonstrates a carbonation profile similar to a CEM I concrete, i.e., a high carbonation resistance. Microstructure analysis indicates the formation of three polymorphs of calcium carbonate for S100 (calcite, vaterite, and aragonite), with a higher CO2 concentration favouring aragonite over vaterite. C100 exhibits no calcium carbonates; instead, sodium carbonates form, including trona for 4% CO2 and natrite for both accelerated tests. C40S60 shows calcium and sodium carbonates, although to a lesser extent, containing predominantly calcite and minor signals of natrite. Suitable compositions, like C40S60, prove as effective during natural or accelerated carbonation tests as conventional Portland cement concrete.
The present Ph.D. thesis provides a comprehensive experimental and theoretical study of the bulging-cracking relationship in laser beam welding of thick unalloyed steel sheets. It focuses on experimentally proving the existence of the bulging region and on developing a coupled multiphysics mathematical framework to analyze its influence on the three critical factors controlling the susceptibility to solidification cracking, namely the thermal, metallurgical, and mechanical factors.
The research employs a novel experimental setup, utilizing a combination of transparent quartz glass and thick unalloyed steel sheet, enabling real-time visualization of the weld pool geometry and confirming the existence of a distinctive bulging region. To deepen the understanding of these experimental insights, an extensive multiphysics mathematical framework was developed and rigorously verified and validated. This framework introduces an innovative approach using Lamé curves for accurately describing complex three-dimensional weld pool geometries, including the bulging region's characteristics. Through analytical solutions and numerical procedures, it facilitates the computation of solidification parameters, which are crucial for understanding the metallurgical aspects of crack formation. The framework also incorporates a mechanical model to assess and evaluate the local stress distribution within the bulging region.
The findings indicate that an elongated, sharply shaped bulging region significantly increases the susceptibility to solidification cracking. This is attributed to its adverse impact on the distribution and local dwell time of liquid metal residing at grain boundaries during solidification, combined with the localized tensile stresses identified in the bulging region.
In essence, this research contributes to the broader understanding of solidification cracking in laser beam welding of thick unalloyed steel sheets, with a particular focus on the bulging region. The insights and methodologies developed in this thesis are valuable for future research and advancements in the application of the laser beam welding technology for joining high-thickness unalloyed steel components.
Unlike conventional alloys, which typically consist of one main element, high-entropy alloys (HEAs) contain five or more principal elements, which broaden chemical complexity and with it a realm of synergistic mechanisms. The AlMo0.5NbTa0.5TiZr HEA initiated a subclass of Al-containing refractory (r)HEAs that has recently drawn attention [2]. The alloy has a superalloy-resembling B2/bcc nanostructure, which inspired its name refractory high entropy superalloy (RSA). With high-temperature (HT) compressive strengths beyond conventional Ni-based superalloys, this nanostructure could be used for improved HT structural applications. However, in the application-relevant HT regime the Al-Zr-rich B2 phase decomposes to form a hexagonal Al-Zr-based intermetallic (Al4-xZr5; x: 0..1) [3,4]. This work explores the fascinating yet fatal micromechanisms associated to this phase transformation, in the context of creep, annealing and oxidation experiments performed between 800 and 1200 °C.
The material was produced by arc-melting and heat treatment in argon, which lead to grain boundaries decorated with up to 7%. Interrupted constant-load creep tests were performed under vacuum (at 10-4 Pa), at 900–1100 °C with external tensile stresses of 30–120 MPa. Oxidation experiments were separately conducted for 24 hours at 800 and 1000 °C in both dry (21% O2 + 79% N2) and humid (8% O2 + 74% N2 + 18% H2O) air. After the experiments, the samples were characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy to reveal degradation mechanisms. Crystallographic texture, orientation relationships and stabilization of an oxygen-containing iso structure (Al4-xZr5(Ox-y); y: 0..x) of the Al-Zr-rich intermetallic are found and discussed.
Processing and cytocompatibility of Cu-doped and undoped fluoride-containing bioactive glasses
(2024)
Sintered or additive-manufactured bioactive glass (BG) scaffolds are highly interesting for bone replacement applications. However, crystallization often limits the high-temperature processability of bioactive glasses (BGs). Thus, the BG composition must combine high bioactivity and processability. In this study, three BGs with nominal molar (%) compositions 54.6SiO2-1.7P2O3-22.1CaO-6.0Na2O-7.9K2O-7.7MgO (13–93), 44.8SiO2-2.5P2O3-36.5CaO-6.6Na2O-6.6K2O-3.0CaF2 (F3) and 44.8SiO2-2.5P2O3-35.5CaO-6.6Na2O-6.6K2O-3.0CaF2-1.0CuO (F3–Cu) were investigated. The dissolution and ion release kinetics were investigated on milled glass powder and crystallized particles (500–600 μm). All glasses showed the precipitation of hydroxyapatite (HAp) crystals after 7 days of immersion in simulated body fluid. No significant differences in ion release from glass and crystalline samples were detected. The influence of surface roughness on cytocompatibility and growth of preosteoblast cells (MC3T3-E1) was investigated on sintered and polished BG pellets. Results showed that sintered BG pellets were cytocompatible, and cells were seen to be well attached and spread on the surface after 5 days of incubation. The results showed an inverse relation of cell viability with the surface roughness of pellets, and cells were seen to attach and spread along the direction of scratches.
The output of C&D waste is increasing year by year, among which low-quality recycled brick aggregates (RBAs) have not been well utilized and brought environmental burden. The durability of steam-cured concrete (HCC) is often compromised due to the detrimental effects of this curing regime on the long-term performance and microstructure development of the concrete material. To address this issue, this study investigates the potential of incorporating RBAs to improve the long-term durability of HCC. The results demonstrate that the incorporation of a small amount of RBA (10–20%) not only enhances the 28-d strength of HCC by 2.5–11.3%, but also improves its impermeability by mitigating heat damage effects. The combined application of fine and coarse RBA was found to effectively balance the negative effects of coarse RBA on the performance of HCC. Furthermore, the utilization of RBA in HCC was shown to have economic and environmental benefits. The results of this study demonstrate a simple and effective approach to improve the long-term durability of HCC while promoting the high-value utilization of solid waste.
In situ chemical analysis of duplex stainless steel weld by laser induced breakdown spectroscopy
(2024)
The high corrosion resistance and good mechanical properties of duplex stainless steel (DSS) are due to its special chemical composition, which is a balanced phase ratio of ferrite (α) and austenite (γ). Many industrial applications require the integration of DSS components. For this, Gas tungsten arc welding (GTAW) is an excellent choice, as it allows an automated operation with high reproducibility. However, when the weld pool solidifies, critical ratios of α- and γ- phases can occur, which lead to solidification cracking, increased susceptibility to corrosion, and a decrease in ductility and critical strength. Previous studies have shown that these defects can be caused by the accumulation of manganese and chromium in the heat affected zone (HAZ), requiring ongoing monitoring of this accumulation. A suitable method for such monitoring is laser-induced breakdown spectroscopy (LIBS), which can be used in two operating modes: calibration using standard reference samples and calibration-free. Unlike conventional quantitative LIBS measurements, which require reference samples to generate a calibration curve, calibration-free LIBS (CF-LIBS) allows chemical compositions to be determined solely from the emission spectrum of the plasma. Numerous publications show that CF-LIBS is a fast and efficient analytical method for the quantitative analysis of metal samples. In this work, CF-LIBS is applied to spectra obtained during GTAW DSS welding and the result is compared with those obtained by PLS analysis. A good correlation was found between both types of analysis, demonstrating the suitability of the CF-LIBS method for this application. The CF-LIBS method has a significant advantage over conventional LIBS due to the rapid in situ measurement of concentrations of major alloying elements without calibration procedure. This, combined with fast feedback and appropriate adjustment of welding parameters, helps prevent welding defects.
Ultrasonic guided waves interacting with complex geometrical features are of high interest in the SHM field. For example, investigations into the extent to which a small change in defect geometry affects wave propagation have applications in Probability of Detection and defect reconstruction. These fields have to be supported by numerical tools aiming to retrieve accurate and reliable results and, thus, more realistic modeling.
Due to the short wavelengths of ultrasonic waves and the relatively large domains in which the waves propagate, fine grid resolution for the entire domain is usually not possible due to limited computational resources. One solution is to partition the domain into different subdomains and use a specific, efficient approach for each subdomain.
This contribution shows a combination of methods that aims to study these wave defect interactions in an elastic media. Firstly we introduce high-order 3D meshes that can resolve very fine geometrical details and are based on an Octree discretisation technique that employs special transition shape functions to resolve the hanging nodes that may appear due to the nature of the method. Afterward, the Octree mesh is embedded in a prismatic wave-guide based on the semi-analytical formulation of the SBFEM in 3D. To couple the different domains, we employ the mortar method, which enforces the continuity of the wave field across the internal boundaries of the domains. Examples show the power of the approach especially when it comes to parametric analysis.
For structural health monitoring systems or non-destructive testing, it is crucial to study the interactions of ultrasonic-guided waves with inhomogeneities or damage in structural components. Simulation of these interactions poses a challenge.
After the wave-damage interaction, the numerical model must reproduce features like mode conversion or wave scattering. Mathematically, damages are discontinuities in a computational domain, and each interacts diversely depending on its geometrical features. We propose a quadtree-based meshing in the current contribution to capture these geometrical
characteristics.
This kind of discretisation approach requires special techniques to couple cells of different sizes since, after a quadtree decomposition, the problem of so-called hanging nodes may arise. Transition elements based on high-order transfinite shape functions are used to solve this issue. The advantage is that these elements allow the correct coupling of the cells while retaining a high-order interpolation. Moreover, the reuse of the dynamic stiffness matrices can be exploited based on the similarity of the cells. This procedure renders the approach very efficient.
Examples show the scattering characteristics of different guided wave modes after interacting with inhomogeneities and discontinuities in a plate.
The weldability of stainless steels is largely controlled by the chemical composition, and alloys with ferritic or ferritic-austenitic solidification show the highest resistance to hot cracking. As the resulting phase balance also
affects the final properties, it may be beneficial to both foresee and measure the weld metal ferrite content. The WRC ’92 constitution diagram is currently the most accurate prediction tool available, but it does not take the cooling rate into consideration and the precision may be less accurate for stainless steels with high ferrite numbers (FN). This study aims to validate the reliability of the WRC ’92 diagram for weld metals with FN > 50. The chemical composition was altered through gas tungsten arc welding (GTAW) of UNS S32205 with ER347 filler wire that had been PVD-coated with either niobium (Nb), copper (Cu), nickel (Ni), manganese (Mn), carbon (C), or silicon (Si). The actual ferrite content was assessed using image analysis, FERITSCOPE® and X-ray diffraction (XRD). While the WRC ’92 diagram predictions were deemed accurate to acceptable for Ni, Si, and Mn, notable deviations were observed for Nb, Cu, and C. The FeriteScope exhibited a consistent trend with image analysis, though the values were higher, and scatter was wider, and the conversion factor is open for discussion. The lowest accuracy and largest spread were obtained using non-contact XRD, rendering it unsuitable for ferrite measurements of welds.