Degradation von Werkstoffen
Filtern
Dokumenttyp
- Vortrag (832)
- Zeitschriftenartikel (428)
- Beitrag zu einem Tagungsband (182)
- Posterpräsentation (129)
- Sonstiges (23)
- Zeitschriftenheft (Herausgeberschaft für das komplette Heft) (20)
- Forschungsbericht (19)
- Buchkapitel (14)
- Dissertation (13)
- Beitrag zu einem Sammelband (7)
Sprache
- Englisch (1105)
- Deutsch (561)
- Mehrsprachig (3)
- Russisch (2)
- Chinesisch (2)
- Französisch (1)
- Spanisch (1)
Schlagworte
- Corrosion (125)
- Korrosion (98)
- Welding (61)
- Nichtrostender Stahl (56)
- Hydrogen (55)
- Additive Fertigung (47)
- Additive manufacturing (45)
- KorroPad (44)
- Wasserstoff (41)
- Degradation (39)
Organisationseinheit der BAM
- 9 Komponentensicherheit (575)
- 7 Bauwerkssicherheit (416)
- 9.4 Integrität von Schweißverbindungen (361)
- 5 Werkstofftechnik (354)
- 7.6 Korrosion und Korrosionsschutz (267)
- 8 Zerstörungsfreie Prüfung (244)
- 6 Materialchemie (174)
- 9.2 Versuchsanlagen und Prüftechnik (169)
- 8.5 Röntgenbildgebung (144)
- 9.0 Abteilungsleitung und andere (140)
Paper des Monats
- ja (13)
Häufig ist es wünschenswert, für neue Materialien oder Anwendungen künstliche Bewitterungsverfahren zu benutzen, die auf die spezifischen Anforderungen besser zugeschnitten sind, als es bei bestehenden standardisierten Verfahren der Fall ist. Nachdem man die spezifischen Parameter der Beanspruchung unter Anwendungsbedingungen und die spezifische Empfindlichkeit des Materials erfasst hat, beginnt ein Prozess, der als „Test Tailoring“ häufig abstrakt verwendet, auf den aber nur selten näher eingegangen wird. Genau dieser Prozess soll hier am Beispiel der Entwicklung eines künstlichen Bewitterungstests unter saurer Beaufschlagung, dem in der BAM entwickelten Acid Dew and Fog Test, beispielhaft erläutert werden.
Häufig ist es wünschenswert, für neue Materialien oder Anwendungen künstliche Bewitterungsverfahren zu benutzen, die auf die spezifischen Anforderungen besser zugeschnitten sind, als es bei bestehenden standardisierten Verfahren der Fall ist. Nachdem man die spezifischen Parameter der Beanspruchung unter Anwendungsbedingungen und die spezifische Empfindlichkeit des Materials erfasst hat, beginnt ein Prozess, der als „Test Tailoring“ häufig abstrakt verwendet, auf den aber nur selten näher eingegangen wird. Genau dieser Prozess soll hier am Beispiel der Entwicklung eines künstlichen Bewitterungstests unter saurer Beaufschlagung, dem in der BAM entwickelten Acid Dew and Fog Test, beispielhaft erläutert werden.
Um den wachsenden Anforderungen an den stofflichen und konstruktiven Leichtbau sowie den Forderungen nach Ressourceneffizienz Rechnung zu tragen, werden in vielen Industriebranchen zunehmend höherfeste Feinkornbaustähle mit Streckgrenzen über 690 MPa eingesetzt. Allerdings werden mit zunehmender Festigkeit deutlich höhere Anforderungen an deren schweißtechnische Verarbeitung gestellt, da die Sensibilität gegenüber einer Herabsetzung der mechanischen Eigenschaften durch den beim Schweißen aufgenommenen diffusiblen Wasserstoff mit steigender Festigkeit zunehmen kann. In den vergleichenden Untersuchungen von konventionellem Übergangslichtbogen und modifiziertem Sprühlichtbogen bei reduziertem Nahtöffnungswinkel konnte gezeigt werden, dass die Schweißprozessparameter die in das Schweißgut eingebrachte Wasserstoffkonzentration beeinflussen. Grundsätzlich ist den erarbeiteten Ergebnissen zu entnehmen, dass im Schweißgut von Stumpfstoßverbindungen mit reduziertem Nahtöffnungswinkel erhöhte mittlere Wasserstoffkonzentrationen vorliegen. Diese können mit geeigneten Wärmeführungen signifikant reduziert werden. Dabei erwies sich eine Nachwärmprozedur aus der Schweißwärme heraus als zielführend. Zudem konnte der Effekt der Nachwärmprozedur anhand fremdbeanspruchter Kaltrissprüfungen nachgewiesen werden.
In the late 1980s, a new type of corrosion appeared in drinking water installations where galvanized steel pipes failed forming a deep groove with no corrosion at the other surfaces. The reason was discussed quite fiercely between failure analysts and material suppliers. In the end the discussion lead to the solution: inductive welded pipes of a certain sulphur content were prone to selective corrosion. The history of the arguments is discussed using old communications between Wilhelm Schwenk and Wolfgang Stichel, who later published the results in a paper unfortunately only I german.
Thus the knowledge got lost and new cases based on the same material problems are observed in application of so-called C-Steel piping systems. Failure cases are shown.
A method of solving the thermo-fluid dynamics problem is presented, enabling the prediction of the shape and dimensions of the weld pool during keyhole laser welding of thick plates. It is shown that the rear weld pool boundary can be satisfactorily approximated by a set of superellipses (Lamé curves). The presence of a convex rear weld pool boundary in the mid-plane has been observed experimentally and reproduced numerically. It was shown that in this zone the concentration of liquating impurities increases and the local solidification temperature decreases, contributing to the susceptibility to hot cracking.
It is proposed to model the experimentally observed weld pool boundary with superellipses (Lamé curves) and to find the unknown parameters of the curves using optimization methods. It has been shown experimentally that during laser welding of austenitic stainless steel with a thickness of 2 mm at a speed of 20 mm/s, the rear weld pool part has a shape close to triangular which can be accurately approximated by a superellipse. Analytical dependences of the trajectory and growth rate of the crystal and its cross-sectional area on the geometry of the rear weld pool part are obtained.
Eine Aufgabe des Fachbereichs 3.4 Sicherheit von Lagerbehältern der Bundesanstalt für Materialforschung und -prüfung (BAM) ist es, die Sicherheit von Behältern zur Lagerung von radioaktivem Abfall mit vernachlässigbarer Wärmeentwicklung zu bewerten. Da solche Behälter vor der Entsorgung transportiert und gelagert werden, ist während dieser Zeit ein sicherer Einschluss des radioaktiven Inhalts von größter Bedeutung. Zur Abdichtung dieser Behälter sind Elastomer-O-Ringe weit verbreitet. Um für solche, wie auch für viele andere Anwendungen, eine Voraussage über die Lebensdauer dieser Komponenten treffen zu können, ist es unerlässlich zu verstehen, welchen Einfluss der durch Alterung hervorgerufene Abbau auf Dauer auf die Elastomerdichtungen hat. In einem Langzeittest wurden drei Kautschukarten (EPDM und FKM, die für die Anwendung relevant sind, und HNBR als Vergleich) über mehrere Jahre untersucht. Dabei wurden die Veränderungen der mechanischen Eigenschaften (z. B. Härte und Bruchdehnung) bei vier verschiedenen Alterungstemperaturen (75 °C, 100 °C, 125 °C und 150 °C) sowie das Dichtungsverhalten betrachtet. Um den Einfluss von Vernetzung und Kettenspaltung auf die beobachteten Alterungseffekte zu bestimmen, wurden Messungen zur kontinuierlichen und intermittierenden Druckspannungsrelaxation durchgeführt. Dadurch konnten Erkenntnisse über Kinetik und Mechanismus der Abbaureaktionen
gewonnen werden. Zur Einschätzung des Dichtungsverhaltens wurden Durckverformungsrest und Leckagerate gemessen. Die Ergebnisse zeigen, dass die O-Ringe unter statischen Bedingungen auch dann dicht halten, wenn die Werte für Druckverformungsrest, Druckspannungsrelaxation und mechanische Eigenschaften schon auf einen fortgeschrittenen Alterungsabbau hindeuten. Aus diesem Grund wurde ein modifizierter Dichtigkeitsversuch mit einer geringen und schnellen teilweisen Entlastung der Dichtung entwickelt, mit dessen Hilfe sich ein Lebensdauerkriterium bestimmen lässt, das eine Sicherheitsspanne für thermische Schrumpfung und Vibrationen beinhaltet.
Ein wesentliches Ziel der deutschen Industriepolitik besteht darin, Rahmenbedingungen zu schaffen, welche die Positionierung nachhaltiger Produkte und Prozesse innerhalb globaler Wertschöpfungsketten ermöglichen und ökoeffiziente Fertigungsprozesse langfristig sichern. In diesem Beitrag werden aktuelle Forschungsarbeiten zur Bewertung der Umweltwirkungen der schweißtechnischen Fertigungskette anhand ausgewählter Schmelzschweißverfahren unter Berücksichtigung vor- sowie nachgelagerter Fertigungsschritte dargestellt. Eine weit verbreitete und standardisierte Methode zur Abschätzung der Umweltwirkungen eines Produkts oder Prozesses ist die Ökobilanzierung. Hierbei stellen die Sachbilanzierung, das heißt die Ermittlung sämtlicher relevanter Energie- und Ressourcenverbräuche während der schweißtechnischen Fertigung, aufgrund des hohen Dokumentationsaufwands, sowie die Ableitung assoziierter Wirkkategorien das größte Hindernis für eine Etablierung und Akzeptanz der Ökobilanzierung in der Praxis dar. Gleichwohl wird seitens Unternehmen, welche als Zulieferer von OEM’s (engl.: original equipment manufacturer) agieren, die Dokumentation des fertigungsspezifischen CO2-Verbrauches gefordert. Ein weiterer Aspekt der Arbeiten beinhaltet Methoden zur automatisierten Erfassung von schweißtechnischen Produktionsdaten sowie deren Nachverfolgbarkeit. Anhand unterschiedlicher Schweißverfahren werden die aus den Produktionsdaten abgeleiteten Energie- und Ressourcenverbräuche automatisiert in die relevanten Umweltwirkungen überführt. Die analysierten Schweißprozesse umfassen dabei ein breites für kleine und mittlere Unternehmen (KMU) relevantes Spektrum. Durch die softwareseitige Bereitstellung der aufgestellten Umweltprofile ist der Anwender in der Lage, Schweißprozesse unter ökologischen Aspekten zu bewerten und die effizienteste Variante zu identifizieren.
In diesem Vortrag werden die aktuellen Forschungsergebnisse im Bereich der ökologischen Bilanzierung von Schweißprozessen dargestellt. Der Fokus liegt hierbei in der automatisierten Berechnung der Umweltwirkungen der Schweißprozesse unter Berücksichtigung vor- und nachgelagerter Prozessschritte. Die Ermittlung der Ökobilanz eines Schweißprozesses erfordert lediglich die Sachbilanzierung relevanter In- und Outputströme. Letztere werden auf Basis entsprechender Sensormessdaten (Leistungsaufnahme Schweißanlagen, Medienverbrauch, etc.) automatisiert nachverfolgbar für jede Schweißung ermittelt.
In diesem Vortrag werden die aktuellen Forschungsergebnisse im Bereich der ökologischen Bilanzierung von Schweißprozessen dargestellt. Der Fokus liegt hierbei in der Ermittlung relevanter Wirkkategorien zur Charakterisierung der Umweltwirkungen von Schweißprozessen. Exemplarisch für verschiedene Verfahrenskombinationen werden die ökologischen Umweltwirkungen auf Basis eines Life Cycle Assessments ermittelt und verfahrensspezifische Einflussgrößen analysiert.
Ein wesentliches Ziel der deutschen Industriepolitik besteht darin, Rahmenbedingungen zu schaffen, welche die Positionierung nachhaltiger Produkte und Prozesse innerhalb globaler Wertschöpfungsketten ermöglichen und ökoeffiziente Fertigungsprozesse langfristig sichern. In diesem Beitrag werden aktuelle Forschungsarbeiten zur Bewertung der Umweltwirkungen der schweißtechnischen Fertigungskette anhand ausgewählter Schmelzschweißverfahren unter Berücksichtigung vor- sowie nachgelagerter Fertigungsschritte dargestellt. Eine weit verbreitete und standardisierte Methode zur Abschätzung der Umweltwirkungen eines Produkts oder Prozesses ist die Ökobilanzierung. Hierbei stellen die Sachbilanzierung, das heißt die Ermittlung sämtlicher relevanter Energie- und Ressourcenverbräuche während der schweißtechnischen Fertigung, aufgrund des hohen Dokumentationsaufwands, sowie die Ableitung assoziierter Wirkkategorien das größte Hindernis für eine Etablierung und Akzeptanz der Ökobilanzierung in der Praxis dar. Gleichwohl wird seitens Unternehmen, welche als Zulieferer von OEM’s (engl.: original equipment manufacturer) agieren, die Dokumentation des fertigungsspezifischen CO2-Verbrauches gefordert. Ein weiterer Aspekt der Arbeiten beinhaltet Methoden zur automatisierten Erfassung von schweißtechnischen Produktionsdaten sowie deren Nachverfolgbarkeit. Anhand unterschiedlicher Schweißverfahren werden die aus den Produktionsdaten abgeleiteten Energie- und Ressourcenverbräuche automatisiert in die relevanten Umweltwirkungen überführt. Die analysierten Schweißprozesse umfassen dabei ein breites für kleine und mittlere Unternehmen (KMU) relevantes Spektrum. Durch die softwareseitige Bereitstellung der aufgestellten Umweltprofile ist der Anwender in der Lage, Schweißprozesse unter ökologischen Aspekten zu bewerten und die effizienteste Variante zu identifizieren.
µCT is used to validate the capability of online monitoring for in-situ detection of defects during the L-PBF build process, which is a focus of the TF project ProMoAM.
Our first experiments show that online monitoring using thermography and optical tomography cameras are able to detect defects in the built part. But further research is needed to understand root cause of the correlation.
Zuverlässigkeitsbetrachtungen bei der Ultraschallprüfung von Radsatzwellen im Ausbildungsbetrieb
(2019)
Im Rahmen der UT1-M1 Ausbildung im Ausbildungszentrum Wittenberge der DGZfP wurden statistische Untersuchungen am Beispiel der Radsatzwellenprüfung mit Testradsatzwellen durchgeführt. Diese Untersuchungen hatten zum Ziel, die wesentlichen Einflussparameter bei der Prüfung auf das Prüfergebnis zu evaluieren. Dabei wurde unter anderem die intrinsische Fähigkeit des Prüfverfahrens zum Auffinden verschiedener Reflektorgeometrien ermittelt. Die Ergebnisse der Handprüfung wurden mit Ergebnissen mechanisierter Prüfungen verglichen. Im Rahmen der Zuverlässigkeitsbetrachtung wurden die Probability of Detection (POD) und die Nachweisgrenzen ermittelt.
Ziel dieser Arbeit war es auch, menschliche und organisatorische Einflussfaktoren auf die Ultraschall-Handprüfung von Radsatzwellen zu identifizieren, um Empfehlungen zur Optimierung der Ausbildung auszuarbeiten. Dazu wurden prüfungsbezogene Risiken in der Praxis mittels Fehlzustandsart- und –auswirkungsanalyse (FMEA) analysiert sowie von den Prüfern empfundene Probleme während der Ausbildung und in der Praxis mittels Fragebogen identifiziert. Die Ergebnisse der FMEA haben gezeigt, dass während des gesamten Prozesses Fehler auftreten können, für die Gegenmaßnahmen getroffen und implementiert werden sollten. Aus den Hinweisen und Erkenntnissen wurden einige Empfehlungen zur Optimierung der Ausbildung erarbeitet.
Zuverlässigkeitsbetrachtungen bei der Ultraschallprüfung von Radsatzwellen im Ausbildungsbetrieb
(2019)
Im Rahmen des UT1 E W im Ausbildungszentrum Wittenberge der DGZfPwurden statistische Untersuchungen am Beispiel der Radsatzwellenprüfung mit Testradsatzwellen durchgeführt. Diese Untersuchungen hatten zum Ziel, die wesentlichen Einflussparameter bei der Handprüfung auf das Prüfergebnis zu evaluieren. Im Rahmen der Zuverlässigkeitsbetrachtung wurden die ProbabilityofDetection(POD) und die Nachweisgrenzen ermittelt.Die durchgeführte Studie zeigt, dass die Bewertung der gesamten Zuverlässigkeit der ZfP komplex ist. Dieses verlangt eine detaillierte Versuchsplanung und die Einbeziehung von unterschiedlichen Faktoren, von den Anwendungsparametern bis hin zu den komplexen menschlichen und organisatorischen Faktoren. Die im Rahmen der Studie ermittelten Ergebnisse lassen aufgrund der geringen Anzahl an Testreflektoren keine allgemeingültige Übertragung auf beliebige Korbbogen-geometrienund Reflektorgeometrienzu.
Im Zuge der wasserstoffbasierten Energiewirtschaft von morgen, kommt der Errichtung der dementsprechenden Infrastruktur die zentrale Rolle zu. Der überwiegende Teil bisher eingesetzter und meist geschweißter Werkstoffe, wie Stähle, kann unter bestimmten Bedingungen zur Wasserstoffversprödung neigen. Dies umfasst die klassische verzögerte Kaltrissbildung während der Schweißverarbeitung als auch Versprödungsphänomene während des Betriebs. Für die Bewertung eines jeden Wasserstoffeffektes auf bspw. die mechanischen Eigenschaften eines geschweißten metallischen Werkstoffes, muss der Wasserstoffgehalt präzise bestimmt werden, Im Fall von Schweißnähten ist die beispielsweise nach der ISO 3690, die klassische isotherme Trägergas-Heißextraktion (TGHE). Die TGHE basiert dabei auf der beschleunigten Wasserstoffentgasung aufgrund der thermischen Aktivierung des Wasserstoffs bei erhöhten Temperaturen. Neben der reinen Quantifizierung des Wasserstoffs, kann über die thermische Desorptionsanalyse (TDA) mit variierten Heizraten, der Bindungszustand an mikrostrukturellen Defekten im Material festgestellt und bewertet werden. Für beide Techniken sind experimentelle und messtechnische Einflüsse zu beachten, die großen Effekt auf das Ergebnis haben. Für die TGHE schlägt die ISO 3690 schlägt beispielswiese verschiedene Probengeometrien sowie Mindestextraktionszeiten vor. Die vorliegende Studie fasst Ergebnisse und Erfahrungen zahlreicher Untersuchungen an der Bundesanstalt für Materialforschung und -prüfung (BAM) mit unterschiedlichen Probentemperaturen und Geometrien (ISO 3690 Typ B und zylindrische TDA-Proben) zusammen hinsichtlich: Einfluss der Probenoberfläche (poliert/geschweißt), Messgenauigkeiten in Abhängigkeit des Probenvolumens sowie die unzureichende Überwachung des Effektes des PI-Reglers auf die Extraktionstemperatur. Insbesondere eine abweichende Extraktionstemperatur zur eingestellten Temperatur, kann die Messergebnisse wesentlich verfälschen. Basierend auf den Ergebnissen werden Methoden aufgezeigt, um schnell die gewünschte Extraktionstemperatur zu erreichen, ohne physisch in das Messequipment eingreifen zu müssen. Dies dient der wesentlichen Verbesserung der Zuverlässigkeit der Wasserstoffmessung durch erhöhte Signalstabilität und beschleunigte Wasserstoffdesorption. Im Allgemeinen ist eine unabhängige Temperaturmessung mit Dummy-Proben für die gewählte Heizprozedur angeraten, um mögliche unerwünschte Temperatureinflüsse bereits vor der Messung auszuschließen. Die beschriebenen Methoden können ohne großen Aufwand direkt in die industrielle Anwendung überführt werden.
Im Zuge der wasserstoffbasierten Energiewirtschaft von morgen, kommt der Errichtung der dementsprechenden Infrastruktur die zentrale Rolle zu. Der überwiegende Teil bisher eingesetzter und meist geschweißter Werkstoffe, wie Stähle, kann unter bestimmten Bedingungen zur Wasserstoffversprödung neigen. Dies umfasst die klassische verzögerte Kaltrissbildung während der Schweißverarbeitung als auch Versprödungsphänomene während des Betriebs. Für die Bewertung eines jeden Wasserstoffeffektes auf bspw. die mechanischen Eigenschaften eines geschweißten metallischen Werkstoffes, muss der Wasserstoffgehalt präzise bestimmt werden, Im Fall von Schweißnähten ist die beispielsweise nach der ISO 3690, die klassische isotherme Trägergas-Heißextraktion (TGHE). Die TGHE basiert dabei auf der beschleunigten Wasserstoffentgasung aufgrund der thermischen Aktivierung des Wasserstoffs bei erhöhten Temperaturen. Neben der reinen Quantifizierung des Wasserstoffs, kann über die thermische Desorptionsanalyse (TDA) mit variierten Heizraten, der Bindungszustand an mikrostrukturellen Defekten im Material festgestellt und bewertet werden. Für beide Techniken sind experimentelle und messtechnische Einflüsse zu beachten, die großen Effekt auf das Ergebnis haben. Für die TGHE schlägt die ISO 3690 schlägt beispielswiese verschiedene Probengeometrien sowie Mindestextraktionszeiten vor. Die vorliegende Studie fasst Ergebnisse und Erfahrungen zahlreicher Untersuchungen an der Bundesanstalt für Materialforschung und -prüfung (BAM) mit unterschiedlichen Probentemperaturen und Geometrien (ISO 3690 Typ B und zylindrische TDA-Proben) zusammen hinsichtlich: Einfluss der Probenoberfläche (poliert/geschweißt), Messgenauigkeiten in Abhängigkeit des Probenvolumens sowie die unzureichende Überwachung des Effektes des PI-Reglers auf die Extraktionstemperatur. Insbesondere eine abweichende Extraktionstemperatur zur eingestellten Temperatur, kann die Messergebnisse wesentlich verfälschen. Basierend auf den Ergebnissen werden Methoden aufgezeigt, um schnell die gewünschte Extraktionstemperatur zu erreichen, ohne physisch in das Messequipment eingreifen zu müssen. Dies dient der wesentlichen Verbesserung der Zuverlässigkeit der Wasserstoffmessung durch erhöhte Signalstabilität und beschleunigte Wasserstoffdesorption. Im Allgemeinen ist eine unabhängige Temperaturmessung mit Dummy-Proben für die gewählte Heizprozedur angeraten, um mögliche unerwünschte Temperatureinflüsse bereits vor der Messung auszuschließen. Die beschriebenen Methoden können ohne großen Aufwand direkt in die industrielle Anwendung überführt werden.
Zur Bewertung der Kaltrissempfindlichkeit moderner hochfester Feinkornbaustähle mit dem Implant-Test
(2020)
Der Implant-Test nach ISO 17642-3 gehört zur Gruppe der fremdbeanspruchten Kaltrisstests, bei dem eine äußere Beanspruchung auf einen zylindrischen Stab (Implant-Probe) definiert aufgebracht wird. Mit dieser Kaltrissprüfung wurden vergleichende Analysen zur Kaltrissempfindlichkeit der modernen hochfesten Feinkornbaustähle S960MC und S960QL durchgeführt. Zudem kamen sowohl Massiv- als auch Metallpulverfülldraht zur Variation der Wasserstoffkonzentration zum Einsatz. Der Einsatz des modernen modifizierten Sprühlichtbogens ermöglichte außerdem die Untersuchung des Einbrandprofils auf die Kaltrissbildung.
Der Stahlbedarf in Deutschland wird maßgeblich neben dem Automobilsektor vom Maschinenbau und allgemeinen Bauwesen geprägt. In diesen Segmenten werden qualitativ hochwertige Stähle mit höchsten Ansprüchen an Festigkeit, Verformungsfähigkeit, schweißtechnische Verarbeitung und sicherheitsrelevante Aspekte gestellt. Wichtige Vertreter, welche diesen Ansprüchen gerecht werden, sind die heutigen modernen höherfesten FKB. Aus der Entwicklung dieser Stähle kristallisierten sich in den letzten Jahrzehnten verschiedene Legierungskonzepte und Herstellungsrouten heraus. Dem liegt neben essentiellen Eigenschaften, z.B. Streck- und Zugfestigkeit, noch weitere Anforderungen, bspw. Kaltumformbarkeit, Kerbschlagzähigkeit und Verschleißfestigkeit, zugrunde. Zunehmend werden im genormten Bereich mit Streckgrenzen bis 700 MPa neben den vergüteten Stählen (Q) auch thermomechanische Stähle (M) eingesetzt. Ein immerwährender paralleler Begleiter während der Stahlherstellung und -verarbeitung ist Wasserstoff.
Wasserstoff wird in den nächsten Jahren als Schlüsselelement für eine nachhaltige Energiewirtschaft angesehen. Aus heutiger Sicht ist Wasserstoff ein Hoffnungsträger für eine klimafreundliche Energiewirtschaft und zukunftsfähige Industrie. Forschung und Industrie arbeiten intensiv an der Erschließung und Weiterentwicklung des enormen Potentials, um eine höhere Nutzbarkeit zu erreichen. Die Gründe liegen zum einen darin, dass Wasserstoff als Brennstoff unproblematisch (Umweltverträglichkeit und Verfügbarkeit) ist und zum anderen ein hervorragender Energieträger ist.
Wasserstoff ist durch seine gebundene Form erst nach dem Lösen aus chemischen Verbindungen zugänglich. Dies geschieht für eine Nutzbarmachung in einer zukunftsfähigen Energiewirtschaft gezielt. Demgegenüber stehen Prozesse, wodurch Wasserstoff aus seiner chemischen Verbindung gelöst wird und aufgrund seiner Größe bzw. geringsten Atommasse von Werkstoffen aufgenommen wird. Damit verbunden interagiert der aufgenommene Wasserstoff mit dem Gefüge und kann zu einer negativen Beeinflussung der Eigenschaften des Werkstoffs führen.
Wasserstoff kann Degradationsprozesse in Stählen verursachen, die sich insbesondere auf die mechanischen Eigenschaften auswirken. Diese Mechanismen können wasserstoffunterstützte Risse in höherfesten Stählen während der Herstellung oder im industriellen Einsatz verursachen.
Elektrochemisch beladene Zugproben zeigen ein unterschiedliches Degradationsverhalten in ihren Eigenschaften. Die vorliegende Arbeit beschreibt die Wechselwirkungen zwischen Wasserstoff und Gitterdefekten in unterschiedlichen mikrolegierten Systemen und wärmebeeinflussten Zonen in den schweißbaren Feinkornbaustählen. Die Ergebnisse zeigen eine klare Abhängigkeit zwischen Mikrolegierung und Herstellungsprozess dieser Stahlsorten, respektive ihrer simulierten wärmebeeinflussten Bereiche.
Höherfeste Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa neigen bei der schweißtechnischen Fertigung zur Bildung von wasserstoffunterstützten Kaltrissen. Diese Mikrorisse entstehen aus der kritischen Interaktion von lokalem risskritischem Gefüge, lokal erhöhter Wasserstoffkonzentration und lokal erhöhter Beanspruchung bzw. Dehnung. Aktuell gültigen Regelwerken zur schweißtechnischen Verarbeitung höherfester Feinkornbaustähle sind Anweisungen zu entnehmen, um das Risiko einer Kaltrissbildung zu minimieren. Die Weiterentwicklung der Werkstoffe (Legierungskonzepte)und neuer Lichtbogenprozesse zur Verringerung der Nahtöffnungswinkel bei gleichzeitiger Erhöhung der Abschmelzleistung (modifizierter Sprühlichtbogen) brachten jedoch auch neue Fragen hinsichtlich der Wasserstoffmenge in der Schweißverbindung nach dem Schweißen und der Kaltrissempfindlichkeit mit sich. Mikrolegierungselemente (V, Nb und Ti) bedingen bspw. eine verlangsamte Wasserstoffdiffusion. Schweißverbindungen unter reduziertem Nahtöffnungswinkel beinhalten höhere Wasserstoffkonzentrationen. Dieser Beitrag zeigt den Einfluss von Einbrandprofil (höhere Abschmelzleistung) auf die Kaltrissempfindlichkeit an einem höherfesten Feinkornbaustahl mit artähnlichem mikrolegierten Schweißzusatzwerkstoff anhand des fremdbeanspruchten Implant-Tests.
In vielen Industriebranchen werden zunehmend hochfeste Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa eingesetzt. Allerdings werden mit zunehmender Festigkeit deutlich höhere Anforderungen an deren schweißtechnische Verarbeitung gestellt, da gerade die Sensibilität gegenüber einer Degradation der mechanischen Eigenschaften, durch den beim Schweißen aufgenommenen Wasserstoff, mit steigender Festigkeit stark zunimmt. In der vorliegenden Präsentation sind Ergebnisse aus vergleichenden Untersuchungen mit konventionellem Übergangslichtbogen und modifiziertem Sprühlichtbogen mit reduziertem Nahtöffnungswinkel hinsichtlich der Wasserstoffaufnahme beim Schweißen unter Variation von Streckenenergie, Arbeitstemperatur und Nachwärmprozedur dargestellt. Grundsätzlich ist den erarbeiteten Ergebnissen zu entnehmen, dass im Schweißgut von Stumpfstoßverbindungen mit reduziertem Nahtöffnungswinkel erhöhte mittlere Wasserstoffkonzentrationen vorliegen. Geeignete Wärmeführungen führten zu einer signifikanten Reduzierung der Wasserstoffkonzentration beim Einsatz der Nahtkonfiguration mit abgesenktem Nahtöffnungswinkel. Dabei erwies sich eine Nachwärmprozedur aus der Schweißwärme heraus als zielführend. Des weiteren sind Gradienten der Wasserstoffkonzentration in Blechdickenrichtung aufgezeigt.
Zirconium chloro fluoride as catalyst for C-F bond activation and HF transfer of fluoroalkanes
(2023)
In this work, we successfully synthesized amorphous zirconium chloro fluoride (ZCF), which exhibits medium lewis acidity. In addition to investigating the local coordination sphere around the Zr atoms and the material properties, we were able to establish a catalytic behavior of ZCF in C-F bond activation reactions. We present a heterogeneous catalyst that performs dehydrofluorination of a fluoroalkane and consecutive hydrofluorination of an alkyne at room temperature.
Agar gel pads have been used for electrochemical measurements for some time. For zinc in particular, a standard method for measuring the stability of the corrosion product layer is being established. The main interpretation factor is the corrosion product layer resistance RL, as it is easy to determine and interpret. A high corrosion product layer resistance indicates a high level of protection. However, it is not yet known how low the corrosion product layer resistance is for freshly produced zinc samples. As zinc is highly active, it reacts immediately with the environment to form a corrosion product layer, which affects the corrosion product layer resistance. The addition of zinc acetate to the agar gel pads prevents the formation of a surface layer and destroys existing ones.
This makes it possible to measure an almost corrosion product-free zinc surface. This is important in defining the range of corrosion product layer resistance for a protective surface.
Metallische Druckgefäße werden aus Gründen der Gewichtseinsparung zunehmend durch Composite-Druckgefäße ersetzt. Während der Alterungsprozess bei metallischen Druckgefäßen durch Wöhlerkurven hinreichend beschrieben wird, ist der Alterungsmechanismus bei Composite-Druckgefäßen noch nicht vollständig geklärt. Im Rahmen des BAM-interne Themenfeldprojekts COD-AGE werden mit diversen Verfahren alterungsbegleitende, zerstörungsfreie Prüfungen an Composite-Druckgefäßen durchgeführt. Nach einem kurzen Überblick über die BAM und den FB 8.4 werden zunächst die allgemeine Funktionsweise der Wirbelstromprüfung und die bildgebende Wirbelstromprüfung erklärt. Anschließend werden Ergebnisse der konventionellen und hochfrequenten Wirbelstromprüfung vorgestellt.
Der letzte Teil des Vortrages beschäftigt sich mit der Prüfbarkeit von Kunststoffen aus Kunstharz und 3D-Druck mit dem Wirbelstromverfahren durch Zugabe ferromagnetischer Nanopartikel bzw. Verwendung von ferromagnetischem Filament.
The detection of delamination, rot, and cracks in wooden construction elements is a key task for nondestructive testing (NDT). Air-coupled ultrasound (ACU) is used to detect defects and damage without altering the structure permanently. Using through transmission it is possible to detect even small holes and missing adhesive. After interpretation of the inspection data, an assessment of the mechanical properties based on an appraisal of internal defects in the material is feasible. Novel ferroelectret transducers with a high signal-to-noise ratio (SNR) enable a high-precision structure recognition. The transducers made of cellular polypropylene (PP) are quite suitable for ACU testing due to their extremely low Young’s modulus and low density which result in a favorable acoustic impedance for the transmission of ultrasonic waves between the transducer and air. Thus, structures with great dimensions, thickness up to 300 mm and material densities under 500 kg/m³ can be inspected. Promising results were obtained under laboratory conditions with frequencies from 90 kHz to 200 kHz. The advantage of ACU transducers is that they do not require contact to the sample, are accurate, and cost effective. Ultrasonic quality assurance for wood is an important attempt to increase the acceptance of wooden structures and towards sustainability in civil engineering in general.
Composite-Druckgefäße für den Gefahrguttransport sowie für Wasserstoff- und Erdgasfahrzeuge bestehen aus einem lasttragenden Composite und einer gasdichten, metallischen oder polymeren Barriereschicht (Liner). Zur Untersuchung des Alterungsverhaltens solcher Composite-Druckgefäße wurde in der BAM das interdisziplinäre Themenfeldprojekt COD-AGE durchgeführt. Ziel des Projektes war die Entwicklung von Methoden und Modellen zur Beschreibung und Bestimmung des Alterungsverhaltens von Carbonfaser-Compositen am Beispiel von Druckgefäßen, um eine bessere Vorhersage der Alterung und der sicheren Gebrauchsdauer zu ermöglichen. Ein Schwerpunkt in diesem Projekt war die Bereitstellung geeigneter ZfP-Methoden. Dabei ging es sowohl um versuchsbegleitende Prüfungen, als auch um die mögliche Entwicklung von Prüfeinrichtungen für den späteren praktischen Gebrauch.
In dem Vortrag werden Prüfergebnisse der alterungsbegleitenden Wirbelstromprüfung an Composite-Druckgefäßen vorgestellt.
In Alterungsversuchen wurden Druckgefäße aus einem ca. 4 mm dicken Aluminiumliner und ca. 8 mm dicker CFK-Ummantelung untersucht. Typisches Einsatzgebiet solcher Druckgefäße sind Atemschutzgeräte der Feuerwehr. Die Druckgefäße wurden sowohl mit konventioneller Wirbelstromtechnik von außen und von innen als auch mit hochfrequenter Wirbelstromtechnik von außen geprüft. Es konnten sowohl Beschädigungen des metallischen Liners, als auch Strukturen des CFK-Geflechts nachgewiesen werden. Eine besondere mechanische Herausforderung bestand in der Prüfung der Innenseite der Liner, da hier eine zylindrische Fläche mit einem Innendurchmesser von 150 mm durch einen Zugang von nur 15 mm Durchmesser geprüft werden muss.
Composite-Druckgefäße für den Gefahrguttransport sowie für Wasserstoff- und Erdgasfahrzeuge bestehen aus einem lasttragenden Composite und einer gasdichten, metallischen oder polymeren Barriereschicht (Liner). Zur Untersuchung des Alterungsverhaltens solcher Composite-Druckgefäße wurde in der BAM das interdisziplinäre Themenfeldprojekt COD-AGE durchgeführt. Ziel des Projektes war die Entwicklung von Methoden und Modellen zur Beschreibung und Bestimmung des Alterungsverhaltens von Carbonfaser-Compositen am Beispiel von Druckgefäßen, um eine bessere Vorhersage der Alterung und der sicheren Gebrauchsdauer zu ermöglichen. Ein Schwerpunkt in diesem Projekt war die Bereitstellung geeigneter ZfP-Methoden. Dabei ging es sowohl um versuchsbegleitende Prüfungen, als auch um die mögliche Entwicklung von Prüfeinrichtungen für den späteren praktischen Gebrauch.
In dem Vortrag werden Prüfergebnisse der alterungsbegleitenden Wirbelstromprüfung an Composite-Druckgefäßen vorgestellt.
In Alterungsversuchen wurden Druckgefäße aus einem ca. 4 mm dicken Aluminiumliner und ca. 8 mm dicker CFK-Ummantelung untersucht. Typisches Einsatzgebiet solcher Druckgefäße sind Atemschutzgeräte der Feuerwehr. Die Druckgefäße wurden sowohl mit konventioneller Wirbelstromtechnik von außen und von innen als auch mit hochfrequenter Wirbelstromtechnik von außen geprüft. Es konnten sowohl Beschädigungen des metallischen Liners, als auch Strukturen des CFK-Geflechts nachgewiesen werden. Eine besondere mechanische Herausforderung bestand in der Prüfung der Innenseite der Liner, da hier eine zylindrische Fläche mit einem Innendurchmesser von 150 mm durch einen Zugang von nur 15 mm Durchmesser geprüft werden muss.
Diese Arbeit beschäftigt sich mit den Eigenschaften der photonenzählenden und spektralauflösenden Detektortechnik und möglichen Anwendungsgebieten in der zerstörungsfreien Prüfung. Dabei wurden konventionelle und photonenzählende Detektortechniken hinsichtlich der Bildqualität und Anwendbarkeit bei unterschiedlichen Prüfaufgaben verglichen und untersucht, inwiefern sich die Energieschwellwertsetzung auf die erreichbare Bildqualität und eine Materialdiskriminierbarkeit bei verschiedenen radiographischen Verfahren auswirkt.
Anhand von Anwendungsbeispielen wurden diese Eigenschaften und deren Auswirkung auf das Messergebnis analysiert. Neben der Radiographie wurden auch dreidimensionale Verfahren wie CT und Laminographie berücksichtigt.
Als eine der wichtigsten Eigenschaften der photonenzählenden Detektortechnik wurden zunächst die Energieauflösung des photonenzählenden Detektors und die Homogenität der Energieantwort über größere Detektorbereiche bestimmt. Dabei stellte sich heraus, dass die Energieauflösung eines abgegrenzten Detektorbereichs ca. 32 % bei 60 keV beträgt und die Streuung in der Energieantwort der einzelnen Detektorbereiche ca. 12 % ausmacht, woraus sich eine Gesamtunsicherheit in der spektralen Detektorantwort von ca. 44 % ergibt. Die geringe Energieauflösung und das stark heterogene Verhalten der Detektorbereiche ergeben sich vor allem aus der Detektorelektronik, welche nur eine globale Energieschwellwertsetzung zulässt.
Trotz dieser Einschränkungen konnte demonstriert werden, dass auch konventionelle radiographische Verfahren, wie Radiographie oder CT, vom Einsatz der photonenzählenden Technik profitieren. So ist es mit dieser Technik möglich, bei sehr geringen Dosisleistungen (z.B. aufgrund der Durchstrahlung großer Wandstärken von dichten Materialien) noch sehr gute Bildqualitäten zu erreichen. Die hohe Dynamik und Kontrastempfindlichkeit dieser Technik begünstigen die Inspektion von Leichtbauwerkstoffen wie Faserverbunde, was anhand von Vergleichen mit herkömmlicher Detektortechnik und anderen ZfP-Verfahren gezeigt werden konnte. Daneben konnte durch den Einsatz der Energieschwellwertsetzung der Einfluss von nicht bildzeichnender Streustrahlung im Röntgenbild um bis zu 20 % reduziert werden. Die Auswirkungen von Aufhärtungseffekten in der CT konnten sogar um bis zu Faktor 1 000 (in der mittleren quadratischen Abweichung), im Vergleich zu herkömmlicher Detektortechnik, reduziert werden.
Der Einsatz von photonenzählender Detektortechnik mit Röntgenblitzröhren ist hingegen nicht sinnvoll, da aufgrund der hohen Photonendichte pro Puls und einer endlichen Totzeit des Detektors in der Größenordnung der Pulsbreite eines Blitzes nur ein geringes Signal detektiert werden kann.
Im Hinblick auf eine Materialdiskriminierbarkeit konnte demonstriert werden, dass im Fall einer Radiographie anhand der Energieschwellwertsetzung im Detektor eine materialstärkenunabhängige Diskriminierung zwischen zwei Materialien (hier: Al und Fe) erzielt werden kann. Unter Einsatz mehrerer Energiefenster und eines Verfahrens der explorativen und multivariaten Datenanalyse konnte eine materialaufgelöste CT eines Multi-Material-Phantoms erreicht werden, wobei die Schwächungskoeffizienten der enthaltenen Materialien im relevanten Energieberiech teilweise sehr dicht beieinander lagen.
Neben Radiographie und CT wurde auch die Möglichkeit einer materialaufgelösten Laminographie am Beispiel eines glasfaserverstärkten Rotorblatts untersucht. Anhand der Energieschwellwertsetzung war nicht nur eine eindeutige Trennung der Glasfasern von der Epoxidharzmatrix möglich, sondern auch eine signifikante Reduzierung der durch die Laminographie entstandenen Artefakte. Der damit verbundene Gewinn an Information führt zu einer verbesserten Aussagefähigkeit des Untersuchungsergebnisses, was letztendlich eine gesteigerte Betriebssicherheit zur Folge hat.
Das vorgestellte Projekt beschäftigt sich mit den optischen, thermophysikalischen und mechanischen Materialeigenschaften von additiv gefertigten Kunststoffteilen und deren Alterung. Dazu wurden mittels Fused Layer Modeling (FLM) Probekörper aus ABS hergestellt, die anschließend für drei Monate einer künstlichen Bewitterung unterzogen wurden. Die dabei erzeugte definierte Alterung wurde nach drei Zeitabschnitten jeweils mit zerstörungsfreien Methoden charakterisiert. Dabei wurde neben den spektroskopischen Standardmethoden auch die aktive Thermografie eingesetzt. Die Ergebnisse zeigen, dass sich mittels der Thermografie sowohl chemische Veränderungen als auch mechanische Schädigungen (Fehlstellen) darstellen lassen. Die Bewitterung beeinflusst die Teiltransparenz der Proben zumindest im sichtbaren Spektralbereich, was bei der Charakterisierung der Fehlstellen, die mittels optisch angeregter aktiver Thermografie detektiert wurden, berücksichtigt werden muss.
Es wurden mittels Fused Layer Modeling (FLM) Probekörper aus ABS und mittels Laser Sintering (LS) Probekörper aus PA 12 hergestellt, die anschließend für drei Monate einer künstlichen Bewitterung unterzogen wurden. Die dabei erzeugte definierte Alterung wurde nach drei Zeitabschnitten jeweils mit zerstörungsfreien Methoden charakterisiert. Dabei wurde neben den spektroskopischen Standardmethoden auch die aktive Thermografie eingesetzt. Die Ergebnisse zeigen, dass sich mittels der Thermografie sowohl chemische Veränderungen als auch mechanische Schädigungen (Fehlstellen) darstellen lassen. Die Bewitterung beeinflusst die Teiltransparenz der Proben zumindest im sichtbaren Spektralbereich, was bei der Charakterisierung der Fehlstellen, die mittels optisch angeregter aktiver Thermografie detektiert wurden, berücksichtigt werden muss.
Die Erkenntnisse dienen für die Entwicklung einer Strategie für eine Qualitätskontrolle von additiv gefertigten Kunststoffteilen.
Es wurden Prüfkörper aus additiver Fertigung mittels Laser Sinter Verfahren (Polyamid 12, PA 12) und Fused Layer Modeling (Acrylnitril-Butadien-Styrol, ABS) sowie Prüfkörper aus dem Kunststoff-Spritzguss Verfahren (PA 12 und ABS) über 2000 Stunden künstlich bewittert. Vor, während und nach der Bewitterung erfolgte eine zerstörungsfreie Prüfung mittels Thermografie, optischer Mikroskopie und spektralen Methoden (UV/VIS-Spektroskopie und spektrale Reflexion), um den Alterungsfortschritt zu untersuchen und Schäden durch die künstliche Bewitterung sowie eingedruckte Defekte zu identifizieren und zu detektieren.
Zusätzlich wurden zerstörende Zugprüfungen vorgenommen, welche mit einer IR-Kamera verfolgt wurden. Auf diese Weise konnten lokale Temperaturänderungen, hervorgerufen durch elastische sowie plastische Verformungen, zeitaufgelöst erfasst und ausgewertet werden.
Microstructural changes in porous cordierite for diesel particulate filter applications caused by machining were characterized using microtensile testing and X-ray computed tomography (XCT). Young’s modulus was determined on ~215-380 m thick machined samples by digital image correlation. Results show a decrease of Young’s modulus due to machining of the thin samples. Explanation of this phenomenon was provided by XCT: the presence of debris due to machining and the variation of porosity due to removal of the outer layers were quantified and correlated with the introduction of further microcracking.
This dataset contains the processed and analysed small-angle X-ray scattering data associated with all samples from the publications "Bio-SAXS of Single-Stranded DNA-Binding Proteins: Radiation Protection by the Compatible Solute Ectoine" (https://doi.org/10.1039/D2CP05053F).
Files associated with McSAS3 analyses are included, alongside the relevant SAXS data, with datasets labelled in accordance to the protein (G5P), its concentration (1, 2 or 4 mg/mL), and if Ectoine is present (Ect) or absent (Pure). PEPSIsaxs simulations of the GVP monomer (PDB structure: 1GV5 ) and dimer are also included.
TOPAS-bioSAXS-dosimetry extension for TOPAS-nBio based particle scattering simulations can be obtained from https://github.com/MarcBHahn/TOPAS-bioSAXS-dosimetry which is further described in https://doi.org/10.26272/opus4-55751.
This work was funded by the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) under grant number 442240902 (HA 8528/2-1 and SE 2999/2-1). We acknowledge Diamond Light Source for time on Beamline B21 under Proposal SM29806. This work has been supported by iNEXT-Discovery, grant number 871037, funded by the Horizon 2020 program of the European Commission.
This study is shown as an example of the potential of synchrotron X-ray refraction technique to determine the evolution of damage in brittle (microcracked) materials. The strength of X-ray refraction resides in its high detectability of features (e.g., cracks, pores) within large volumes, enabling a macroscopic characterization of the microstructure. The case study is a Zirconia-based cast refractory, which is aimed to function at high temperatures (even in excess of 1700°C) in industrial furnaces to enable the production of special glasses. Therefore, this material must withstand severe in-service conditions (both thermomechanical and chemical). X-ray refraction technique is used to monitor the microcracking evolution of the material, which was previously subjected to thermal cycles (crossing the martensitic phase transformation around 1000°C) at two different stress levels.
Functional materials for energy conversion are important technology drivers needed for the implementation of low carbon energy. Therefore, researchers commonly focus on improving the intrinsic properties of a functional material. However, for applications, the extrinsic properties are at least as important as the intrinsic ones. Consequently, it is important to investigate and understand the external and internal structure of semi-finished products and especially defect dependent properties. The extrinsic properties may change during application and the life cycle of the material as well as through processing and molding steps.
Our studies show how X-ray tomographic (XCT) investigations can contribute to structure investigations in composites and massive samples using the example of magnetic materials for energy conversion. The components are tested non-destructively in 3D in order to localize and characterize cracks, pores, inclusions as well as other defects and their influence on the functional properties and also “in-time” during the life cycle of the material. Exsitu and in-situ experiments performed with non-destructive XCT are predestinated to follow damaging mechanisms of materials under certain load conditions, atmospheres or liquids, e.g. went through several working cycles of a functional material. By combining microtomography with other methods of magnetic and classical material characterization, unique statements about the structure and the functional properties can be made.
From the applications point of view, sometimes complex, three-dimensional geometries are needed to fully exploit the functional properties of the materials, e.g. to ensure a high surface area for heat exchange. Since many functional materials are brittle and difficult to form, shaping is often a big challenge. In principle, additive manufacturing processes offer the possibility to produce complex, porous components from poorly formable alloys.
If all stages of additive manufacturing are accompanied by X-ray tomographic imaging, the process of finding the optimal parameters for material processing can be significantly accelerated.
Based on the quality control of the initial powder material used and also investigations of the shape and arrangement of defects within the molten structure and their relationship with the melting path scanning strategy, Xray tomography has proven to be an ideal tool for additive manufacturing, even for functional materials. Overall, tomographic methods are important tools for the development of functional materials to application maturity.
X-Ray computed tomography and traditional analysis of a capillary absorption test in cement pastes
(2020)
Water absorption testing has the attraction of being simple, relatively quick and use water as a fluid which is the key substance in the possible concrete deterioration. However, in spite of the advantages its application has remained empirical, except for the testing of resistance to frost, through the identification of the critical degree of saturation. Rilem TC-116 studied this test, among others, for the characterization of concrete resistance against transport through the concrete pore network. Results indicated a low discriminating ability of the absorbency for qualifying concrete resistance and then, it seemed necessary to try to move forward by making the link between the absorption testing and the concrete pore microstructure. In the present work, thanks to the X-Ray computed tomography, it is described the evolution of the water front in three paste-specimen with different w/c ratios (different pore radius distributions). The observations allowed us to deduce that all the pores start to fill simultaneously, but the bigger ones fill quicker and rise less. The saturation degree is measured along the height of the sample, showing that each pore size has a different rate which becomes constant after the first hour. Washburn’s equation was applied to the progressive advance of the water front, resulting in a pore radius much smaller than the one expected.
The combination of tomographic, microstructural data with other experimental techniques and with modeling is paramount, if we want to extract the maximum amount of information on material and component properties. In particular, quantitative image analysis, statistical approaches, direct discretization of tomographic reconstructions represent concrete possibilities to extend the power of the tomographic 3D representation to insights into the material and component performance. This logic thread equally holds for industrial and academic research and valorizes expensive experiments such as those carried out at synchrotron sources, which cannot be daily repeated.
I will show a few examples of possible use of X-ray tomographic data for quantitative assessment of damage evolution and microstructural properties, as well as for non-destructive testing. Examples of micro-structured inhomogeneous materials will be given, such as Composites, Ceramics, Concrete, and Additively manufactured parts. I will also show how X-ray refraction computed tomography (CT) can be highly complementary to classic absorption CT, being sensitive to internal interfaces.
Additionally, I will show how Neutron Diffraction, which is extremely well suited to the study of internal stresses, both residual and under external load, can well be coupled to the microstructural framework gained by CT, allowing understanding the microstructure-property relationships in materials.
Bestrebungen zum Leichtbau sowie höhere Anforderungen an das ertragbare Lastkollektiv führen in der Auslegung von Schweißkonstruktionen zunehmend zum Einsatz hochfester Feinkornbaustähle. Ohne Anwendung kostenintensiver Nachbehandlungsverfahren ist die Lebensdauer hochfester Schweißverbindungen unter wechselnder zyklischer Beanspruchung jedoch limitiert. Neben der geometrischen Kerbe sind schweißbedingte Gefügeveränderungen und die Höhe und die Verteilung von Schweißeigenspannungen für die Eigenschaften von Schweißverbindungen von erheblicher Bedeutung. Sogenannte LTT-Zusatzwerkstoffe bieten eine äußerst lukrative Möglichkeit, die resultierenden Schweißeigenspannungen bereits während des Schweißens zu adaptieren. Durch die gezielte Ausnutzung der mit der martensitischen Phasenumwandlung verbundenen Volumenausdehnung können bei hinreichend niedriger Umwandlungstemperatur Druck oder niedrige Zugeigenspannungen induziert werden. Bisherige Untersuchungen konzentrieren sich vorrangig auf die Entwicklung von LTT-Legierungskonzepten sowie dem Nachweis von Druckeigenspannungen, bieten jedoch nur wenige Erkenntnisse zum Einfluss der Wärmeführung, vor allem der Zwischenlagentemperatur, oder der Schrumpfbehinderung auf die Beanspruchung von LTT- Mehrlagenschweißverbindungen unter realitätsnahen Fertigungsbedingungen.
Die Interaktion zwischen der martensitischen Phasenumwandlung und den thermischen bzw. den mechanischen Einflussfaktoren auf die Schweißeigenspannungen wurde einleitend durch elementare Schweißversuche analysiert. Mit Hilfe des Temperaturgradienten wurde der Einfluss der behinderten thermischen Schrumpfung auf den Eigenspannungszustand in LTT-Schweißverbindungen erstmalig richtungsabhängig verstanden. Unter der Vorlage eines hohen Einspanngrades wurden Druckspannungen bevorzugt aufgebaut, wenn der Temperaturgradient während der Phasenumwandlung nur schwach ausgeprägt war. Dabei durchgeführte In-situ-Beugungsexperimente haben gezeigt, dass der Einspanngrad nur in Zusammenhang mit der richtungsabhängig vorliegenden behinderten thermischen Schrumpfung zu betrachten ist, um die Beanspruchung einer Schweißverbindung unter konstruktiver Schrumpfbehinderung bauteilübergreifend bewerten zu können.
Anschließend wurden Mehrlagenschweißversuche unter freier Schrumpfung sowie in einer speziellen Prüfanlage unter konstruktiver Schrumpfbehinderung und realistischen Fertigungsbedingungen durchgeführt. Es gelang der Nachweis, dass durch die Verwendung von LTT-Legierungen das Reaktionsmoment Mx gegenüber einer konventionellen Schweißverbindung unabhängig von der Zwischenlagentemperatur reduziert wird. Dennoch nimmt die Reaktionsspannung σ_total mit zunehmender Zwischenlagentemperatur zu. Mit Hilfe des Temperaturgradienten wurde der Einfluss der behinderten thermischen Schrumpfung auf die lokale und die globale Beanspruchung der untersuchten Schweißverbindungen interpretiert. Unabhängig von der genutzten Zwischenlagentemperatur lag für die LTT-Stumpfstoßverbindungen vor allem in Longitudinalrichtung nur eine geringe Schrumpfbehinderung während der martensitischen Phasenumwandlung vor. Dadurch wurden während der Abkühlung vor allem im Volumen Druckspannungen in Longitudinalrichtung aufgebaut. Der Eigenspannungszustand von LTT-Verbindungen wird darüber hinaus durch inhomogene Phasenumwandlung der Schweißnaht infolge von Konzentrationsunterschieden verschiedener Elemente im Schweißgut bestimmt.
Aufgrund guter mechanischer und chemischer Eigenschaften sowie einer hohen Biokompatibilität sind CoCrMo-Legierungen als Implantatwerkstoffe seit Jahrzehnten fester Bestandteil medizintechnischer Anwendungen. Diese Eigenschaften resultieren bekanntermaßen aus chemischer Zusammensetzung, atomarem Aufbau und dem Gefüge. Letzteres wird durch Legierungszusammensetzung, Herstellungsprozess und Wärmebehandlungen bestimmt. In der Vergangenheit wurden bereits Erkenntnisse zum Einfluss der Mikrostruktur auf mechanische bzw. chemische Eigenschaften von CoCrMo gewonnen. Ebenso wurde in der Literatur das Korrosionsverhalten von CoCrMo im Beisein von Körperflüssigkeiten betrachtet. Bisher fehlt es jedoch an vergleichenden Untersuchung, die das Korrosionsverhalten verschiedener Phasen- bzw. Gefügezustände in verschiedenen Körpermedien betrachten. In dieser Arbeit werden bei einer ausgewählten CoCrMo Legierung verschiedene Gefügezustände durch plastische Verformung und Wärmebehandlung erzeugt und vergleichend untersucht. Das Korrosionsverhalten wird anhand elektrochemischer Untersuchungen in verschiedenen körperflüssigkeitsnahen Lösungen im Vergleich zu Titan charakterisiert und der Einfluss von bestimmten Zusätzen (HCL und H2O2) ermittelt.
Modern wind turbine rotor blades consist of sandwich shell segments made from glass fiber reinforced polymers. During manufacturing, defects can arise which could lead to failure of the whole component under dynamic mechanical and thermal loads. Hence during operation defects can arise which, if detected, can be repaired locally and in-situ by applying repair patches instead of taking the whole rotor blade down and repair it remotely. This method is much more time and cost effective, since the shut-down time of the energy converter is limited to a minimum. These repair patches can, however, also lead to new defects if not applied optimally. Therefore, it is necessary to control the quality of the repair patches to ensure the best possible restoration of structural integrity of the component. As a rotor blade is an object with a large aspect ratio, X-ray laminography is predestined to provide 3D information of the objective volume. To enhance the amount of information gained from laminographic reconstruction, we use in this study a photon counting and energy discriminating X-ray detector and apply a material decomposition algorithm to the data. By inherently separating the incident spectra within the detection process into two distinct energy bins, the basis material decomposition can provide material resolved images. Choosing glass and epoxy resin as basis materials and numerically solving the inverse dual-energy equation system, the reconstructed laminographic datasets contain highly valuable information about the distribution of the basis materials within the structure. Furthermore, cross- artifacts arising from the limited angle of the projection data can be reduced by this method which allows to investigate structures that were hidden underneath the artefacts.
Modern wind turbine rotor blades consist of sandwich shell segments made from glass fiber reinforced polymers. During manufacturing, defects can arise which could lead to failure of the whole component under dynamic mechanical and thermal loads. Hence during operation defects can arise which, if detected, can be repaired locally and in-situ by applying repair patches instead of taking the whole rotor blade down and repair it remotely. This method is much more time and cost effective, since the shut-down time of the energy converter is limited to a minimum. These repair patches can, however, also lead to new defects if not applied optimally. Therefore, it is necessary to control the quality of the repair patches to ensure the best possible restoration of structural integrity of the component. As a rotor blade is an object with a large aspect ratio, X-ray laminography is predestined to provide 3D information of the objective volume. To enhance the amount of information gained from laminographic reconstruction, we use in this study a photon counting and energy discriminating X-ray detector and apply a material decomposition algorithm to the data. By inherently separating the incident spectra within the detection process into two distinct energy bins, the basis material decomposition can provide material resolved images. Choosing glass and epoxy resin as basis materials and numerically solving the inverse dual-energy equation system, the reconstructed laminographic datasets contain highly valuable information about the distribution of the basis materials within the structure. Furthermore, cross- artifacts arising from the limited angle of the projection data can be reduced by this method which allows to investigate structures that were hidden underneath the artefacts.
Aging Mechanisms of Lithium Batteries: How can we make batteries more durable and more sustainable in the future?
Lithium batteries are particularly susceptible to ageing processes. During each charging and discharging process in an electric battery, lithium ions are deposited in the electrodes of the cell like in the pores of a sponge. Over time, however, fractures and cracks occur in the filigree structures. The result: more and more lithium ions no longer fit into the hollow spaces of the „sponge“, instead they accumulate in heaps around the electrodes and hinder the movement of other ions. The performance of the battery decreases.
We present our new project, in which we are developing a fast and cost-effective method with which companies that produce lithium batteries can already assess the ageing behaviour of their batteries in the laboratory.
What isotopes can do...
(2019)
This presentation summarizes outcomes of the CUSP projects POLYRISK and PlasticsFatE according to thermoanalytical methods.It highlights the importants of analytical methods to measure physical and chemical properties of the test materials. These informations are neccessary for interpretation of the toxicological test results.
Die Oberflächen nichtrostender Stähle sind durch eine Passivschicht geschützt. Ist diese beschädigt oder unvollständig ausgebildet, sind Anlagenkomponenten in Gefahr, durch Korrosionsangriffe zerstört zu werden.
KorroPads liefern ein valides Prüfergebnis zum Zustand der Passivschicht. Der Schnelltest dauert nur 15 min.