Degradation von Werkstoffen
Filtern
Dokumenttyp
- Vortrag (837)
- Zeitschriftenartikel (431)
- Beitrag zu einem Tagungsband (184)
- Posterpräsentation (131)
- Sonstiges (23)
- Zeitschriftenheft (Herausgeberschaft für das komplette Heft) (20)
- Forschungsbericht (19)
- Buchkapitel (14)
- Dissertation (13)
- Beitrag zu einem Sammelband (7)
Sprache
- Englisch (1114)
- Deutsch (563)
- Mehrsprachig (4)
- Russisch (2)
- Chinesisch (2)
- Französisch (1)
- Spanisch (1)
Schlagworte
- Corrosion (125)
- Korrosion (98)
- Welding (61)
- Nichtrostender Stahl (56)
- Hydrogen (55)
- Additive Fertigung (47)
- Additive manufacturing (46)
- KorroPad (44)
- Wasserstoff (41)
- Degradation (39)
Organisationseinheit der BAM
- 9 Komponentensicherheit (576)
- 7 Bauwerkssicherheit (417)
- 9.4 Integrität von Schweißverbindungen (362)
- 5 Werkstofftechnik (360)
- 7.6 Korrosion und Korrosionsschutz (267)
- 8 Zerstörungsfreie Prüfung (248)
- 6 Materialchemie (174)
- 9.2 Versuchsanlagen und Prüftechnik (170)
- 8.5 Röntgenbildgebung (146)
- 9.0 Abteilungsleitung und andere (140)
- 5.1 Mikrostruktur Design und Degradation (119)
- 5.2 Metallische Hochtemperaturwerkstoffe (116)
- 3 Gefahrgutumschließungen; Energiespeicher (114)
- 4 Material und Umwelt (90)
- 9.3 Schweißtechnische Fertigungsverfahren (86)
- 6.6 Physik und chemische Analytik der Polymere (80)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (71)
- 7.1 Baustoffe (63)
- 5.3 Polymere Verbundwerkstoffe (60)
- 5.6 Glas (56)
- 5.5 Materialmodellierung (55)
- 4.1 Biologische Materialschädigung und Referenzorganismen (50)
- 8.0 Abteilungsleitung und andere (49)
- 6.2 Material- und Oberflächentechnologien (39)
- 8.4 Akustische und elektromagnetische Verfahren (38)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (35)
- 3.4 Sicherheit von Lagerbehältern (32)
- 6.3 Strukturanalytik (32)
- 9.5 Tribologie und Verschleißschutz (32)
- 9.6 Additive Fertigung metallischer Komponenten (27)
- 1 Analytische Chemie; Referenzmaterialien (25)
- 6.1 Oberflächen- und Dünnschichtanalyse (24)
- 3.0 Abteilungsleitung und andere (21)
- 4.3 Schadstofftransfer und Umwelttechnologien (21)
- 5.0 Abteilungsleitung und andere (21)
- 3.2 Gefahrguttanks und Unfallmechanik (19)
- 8.6 Faseroptische Sensorik (14)
- 7.2 Ingenieurbau (13)
- 7.4 Baustofftechnologie (13)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (12)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (11)
- 4.2 Material-Mikrobiom Wechselwirkungen (10)
- 1.2 Biophotonik (9)
- 2 Prozess- und Anlagensicherheit (9)
- 3.3 Sicherheit von Transportbehältern (9)
- 7.0 Abteilungsleitung und andere (9)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (7)
- 1.6 Anorganische Referenzmaterialien (6)
- 4.0 Abteilungsleitung und andere (6)
- 4.5 Kunst- und Kulturgutanalyse (6)
- 5.4 Multimateriale Fertigungsprozesse (6)
- 2.1 Sicherheit von Energieträgern (5)
- 6.4 Materialinformatik (5)
- 1.4 Prozessanalytik (4)
- 2.2 Prozesssimulation (4)
- 3.5 Sicherheit von Gasspeichern (4)
- 6.7 Materialsynthese und Design (4)
- Z Zentrale Dienstleistungen (4)
- Z.1 Organisation, Controlling (4)
- 1.7 Organische Spuren- und Lebensmittelanalytik (3)
- S Qualitätsinfrastruktur (3)
- 1.1 Anorganische Spurenanalytik (2)
- 6.0 Abteilungsleitung und andere (2)
- S.3 Ökodesign und Energieverbrauchskennzeichnung (2)
- VP Vizepräsident (2)
- VP.1 eScience (2)
- 1.0 Abteilungsleitung und andere (1)
- 1.9 Chemische und optische Sensorik (1)
- 3.6 Elektrochemische Energiematerialien (1)
- 8.3 Thermografische Verfahren (1)
- P Präsident (1)
- P.0 Präsident und andere (1)
- S.0 Abteilungsleitung und andere (1)
Paper des Monats
- ja (13)
The manufacture of sintered glasses and glass-ceramics, glass matrix composites, and glass-bounded ceramics or pastes is often affected by un-expected gas bubble formation also named foaming. Against this background, in this presentation the main aspects and possible reasons of foaming are shown for completely different glass powders: a barium silicate glass powders used as SOFC sealants, and bioactive glass powders using different powder milling procedures.
Sintering and foaming were measured by means of heating microscopy backed up by XRD, differential thermal analysis (DTA), vacuum hot extraction (VHE), optical and electron microscopy, and infrared spectroscopy, and time-of-flight secondary ion mass spectrometry (ToF-SIMS).
Different densification was reached followed by significant foaming starting partly immediately, partly at higher temperature. Foaming increased significantly as milling progressed. For moderately milled glass powders, subsequent storage in air could also promote foaming. Although the milling atmosphere significantly affects the foaming of uniaxially pressed powder compacts sintered in air.
VHE studies show that foaming is driven by carbon gases and carbonates were detected by Infrared spectroscopy to provide the major foaming source. Carbonates could be detected even after heating to 750 °C, which hints on a thermally very stable species or mechanical trapping or encapsulating of CO2. Otherwise, dark gray compact colors for milling in isopropanol indicate the presence of residual carbon as well. Its significant contribution to foaming, however, could not be proved and might be limited by the diffusivity of oxygen needed for carbon oxidation to carbon gas.
Up to now, oriented surface crystallization phenomena are discussed controversially, and related studies are restricted to few glasses. For silicate glasses we found a good correlation between the calculated surface energy of crystal faces and oriented surface nucleation. Surface energies were estimated assuming that crystal surfaces resemble minimum energy crack paths along the given crystal plane. This concept was successfully applied at the Institute of Physics of Rennes in calculating fracture surface energies of glasses. Several oriented nucleation phenomena can be herby explained assuming that high energy crystal surfaces tend to be wetted by the melt. This would minimize the total interfacial energy of the nucleus. Furthermore, we will discuss the evolution of the microstructure and its effect on the preferred crystal orientation.
Bislang wird das Phänomen der orientierten Oberflächenkristallisation kontrovers diskutiert und entsprechende Studien beschränken sich auf nur wenige Gläser. Für Silikatgläser haben wir eine gute Korrelation zwischen der berechneten Oberflächenenergie von Kristallflächen und der orientierten Oberflächenkeimbildung gefunden. Die Oberflächenenergien wurden unter der Annahme abgeschätzt, dass die Kristalloberflächen bei der Keimbildung den Kristallebenen mit minimaler Energie entsprechen, denen ein Riss beim Bruch folgt. Dieses Konzept wurde am Institut für Physik in Rennes erfolgreich bei der Berechnung der Bruchflächenenergien von Gläsern angewandt. Mehrere orientierte Keimbildungsphänomene lassen sich dadurch erklären, dass man annimmt, dass Kristalloberflächen mit hoher Energie dazu neigen, von der Schmelze benetzt zu werden. Dies minimiert die gesamte Grenzflächenenergie des Keims. Darüber hinaus werden wir die Entwicklung der Mikrostruktur beim weiteren Kristallwachstum und ihre Auswirkungen auf die bevorzugte Kristallorientierung diskutieren.
Das Ausbreitungsverhalten geführter Ultraschallwellen ermöglicht die großflächige Prüfung von Platten und schalenförmigen Bauteilen wie Rohren und Laminaten auf Fehlstellen von wenigen Prüfpunkten aus. Während die beschränkte Divergenz der geführten Wellen die Ultraschallprüfung begünstigt, erschwert das dispersive und multimodale Verhalten der Lamb-Wellen die Auswertung der Ultraschallsignale. Die dispersive und multimodale Wellenausbreitung verkompliziert die Bestimmung der Fehlerposition bei der Auswertung der Geschwindigkeiten einzelner Wellenpakete. Zudem ist es herausfordernd, einen einfachen Zusammenhang zwischen den Reflexionen der Fehlstelle und deren Größe und Form herzustellen. Eine Möglichkeit zur genauen Bestimmung der Fehlerposition und -geometrie bietet der direkte Vergleich der Messsignale mit den Signalen aus einem Simulationsmodell. Die Nachbildung des Schadens im Simulationsmodell stellt ein inverses Problem dar, das iterativ gelöst werden kann, indem ein Vorwärtsmodell immer weiter optimiert wird. Klassische Ansätze wie die Finite Elemente Methode (FEM) sind für die Simulation von Ultraschallwellen aufgrund der kleinen Wellenlängen im Vergleich zur Bauteilgröße meist ineffizient. Aus diesem Grund basiert das vorgestellte Vorwärtsmodell auf der semi-analytischen Scaled Boundary Finite Element Method (SBFEM), die große Teile der Wellenausbreitung analytisch berechnet. In diesem Beitrag wird die Validierung des zweidimensionalen Modells an Platten mit einer rechteckigen Nut als Ersatzfehler präsentiert und es werden erste Schritte zur Validierung von 3D-Modellen vorgestellt.
Das Ausbreitungsverhalten geführter Ultraschallwellen ermöglicht die großflächige Prüfung von Platten und schalenförmigen Bauteilen wie Rohren und Laminaten auf Fehlstellen von wenigen Prüfpunkten aus. Während die beschränkte Divergenz der geführten Wellen die Ultraschallprüfung begünstigt, erschwert das dispersive und multimodale Verhalten der Lamb-Wellen die Auswertung der Ultraschallsignale. Die dispersive und multimodale Wellenausbreitung verkompliziert die Bestimmung der Fehlerposition bei der Auswertung der Geschwindigkeiten einzelner Wellenpakete. Zudem ist es herausfordernd, einen einfachen Zusammenhang zwischen den Reflexionen der Fehlstelle und deren Größe und Form herzustellen. Eine Möglichkeit zur genauen Bestimmung der Fehlerposition und -geometrie bietet der direkte Vergleich der Messsignale mit den Signalen aus einem Simulationsmodell. Die Nachbildung des Schadens im Simulationsmodell stellt ein inverses Problem dar, das iterativ gelöst werden kann, indem ein Vorwärtsmodell immer weiter optimiert wird. Klassische Ansätze wie die Finite Elemente Methode (FEM) sind für die Simulation von Ultraschallwellen aufgrund der kleinen Wellenlängen im Vergleich zur Bauteilgröße meist ineffizient. Aus diesem Grund basiert das vorgestellte Vorwärtsmodell auf der semi-analytischen Scaled Boundary Finite Element Method (SBFEM), die große Teile der Wellenausbreitung analytisch berechnet. In diesem Beitrag wird die Validierung des zweidimensionalen Modells an Platten mit einer rechteckigen Nut als Ersatzfehler präsentiert und es werden erste Schritte zur Validierung von 3D-Modellen vorgestellt.
Various software products for the simulation of industrial X-ray radiography have been developed in recent years (e.g., aRTist 2, CIVA CT, Scorpius XLab, SimCT, Wilcore) and their application potential has been shown in numerous works. However, full systematic approaches to characterise a specific CT system for these simulation software products to obtain a truthful digital twin are still missing. In this contribution, we want to present two approaches to obtain realistic grey values in X-ray projections in aRTist 2 simulations based on measured projections. In aRTist 2, the displayed grey value of a pixel is based on the energy density incident on that pixel.
The energy density is calculated based on the X-ray tube spectrum, the attenuation between source and detector as well as an energy-dependent sensitivity curve of the detector. The first approach presented in this contribution uses the sensitivity curve as a free modelling parameter. We measured the signal response at different thicknesses of Al EN-AW6082 at different tube voltages (i.e., different tube spectra). We then regarded the grey values displayed by these projections as a data regression respectively an optimisation problem and obtained the sensitivity curve that is best able to reproduce the measured behaviour in aRTist 2. The resulting sensitivity curve does not necessarily hold physical meaning but is able to simulate the real system behaviour in the simulation software.
The second approach presented in this contribution is to estimate the sensitivity curve based on assumptions about the characteristics of the scintillation detector (e.g., scintillator material, scintillator thickness and signal processing characteristics). For this approach, a linear response function (linear relationship between the deposited energy per pixel and the resulting grey value) is assumed. If the detector characteristics, which affect the simulated deposited energy, are properly modelled, the slope and offset of the response function to match the measured grey values should be the same for different tube spectra. As the offset is constant and given by the grey values measured at no incident radiation, the slope is the remaining parameter to evaluate the success of the detector modelling. We therefore adapted the detector characteristics by changing the detector setup until the slope was nearly the same for all measured tube spectra. We are aware that the resulting parameters of the scintillator material and thickness might not be the real ones, but with those modelling parameters we are able to simulate realistic grey values in aRTist 2. Both of those approaches could potentially be a step forward to a full systematic approach for a digital twin of a real CT system in aRTist 2.
Lithium-ion batteries are a key technology for tackling challenges in energy and climate crisis, but up to 30 % are discarded right after production. Quality is closely related to the homogeneity of the used materials and coatings. Fluorine compounds, both in the polymer and from degradation of the electrolyte, are of special interest for the formation and aging of LIBs. Glow-discharge optical emission spectroscopy (GD-OES) emerged as a fast and convenient method for depth-profiling of battery materials. However, fluorine remains a spectroscopic challenge due to a high excitation energy and only few strong emission lines in the UV/Vis spectral range.
We investigated the partial substitution of argon with neon in the plasma gas. The main emission line at 685.603 nm was monitored by both photo multiplier tube (PMT) with Czerny-Turner monochromator at 20 µm slit-size, and charge-coupled device (CCD) with 1200 lines/mm grating. For calibration, we used a set of hot-pressed copper cylinders with varying calcium fluoride amount fraction, ranging from 1.6 % to 4.4 %. Plasma gas mixtures with a mole fraction of 5 %, 10 % and 20 % neon in argon were used. Sensitivity in comparison to pure argon was increased by factor 4, 7 and 14, respectively. In general, PMT detection was more sensitive than CCD. As expected, sputter rates decreased with higher neon content in the plasma gas. Depth-profiling of the cathodes was performed in pulsed mode at constant voltage and pressure, which resulted in stable plasma conditions. We achieve matrix-independent quantitative information on fluorine distribution by correction based on sputter rates.
This advancement in GD-OES provides a more accurate analytical approach for evaluating the homogeneity of lithium-ion battery materials, potentially leading to more sustainable and cost-effective manufacturing processes.
To address the challenges of the climate crisis, multiple solutions for sustainable energy sources and storage systems are needed. One such solution is lithium-ion batteries (LIBs). Currently, 5 to 30 % of LIBs are discarded immediately after manufacturing. The homogeneous distribution of all materials used in the coating of cathodes and anodes is critical for the quality of LIBs. Furthermore, during formation i.e., the first steps of the charge/discharge cycling, the solid-electrolyte interphase forms on the anode particles, which has a huge impact on the performance. The same happens to some extent on the cathode, forming the cathode-electrolyte interphase. Fluorinated polymers and electrolytes are used in the manufacturing of LIBs. The electrolyte in particular is prone to degradation during formation and aging of the batteries. The interface of the cathode material with the aluminum current collector is also a critical point where degraded fluorine components cause pitting corrosion and at the same time promote passivation of the metal foil. Monitoring the spatial distribution of fluorine on these surfaces and interfaces is essential for sustainable LIB production.
Relation of craze to crack length during slow crack growth phenomena in high‐density polyethylene
(2024)
The craze‐crack mechanism occurring in high‐density polyethylene (HDPE) causing slow crack growth and environmental stress cracking is investigated in detail with respect to the relation of crack length and the related craze zone. This is essential for the understanding of the resulting features of the formed fracture surface and their interpretation in the context of the transition from crack propagation to ductile shear deformation. It turns out that an already formed craze zone does not inevitably result in formation of a propagating crack, but could also undergo ductile failure. For the examination, the full notch creep test (FNCT) was employed with a subsequent advanced fracture surface analysis that was performed using various imaging techniques: light microscopy, laser scanning microscopy, scanning electron microscopy, and X‐ray micro computed tomography scan. FNCT specimens were progressively damaged for increasing durations under standard test conditions applying Arkopal, the standard surfactant solution, and biodiesel as test media were used to analyze the stepwise growth of cracks and crazes. From considerations based on well‐established fracture mechanics approaches, a theoretical correlation between the length of the actual crack and the length of the preceding craze zone was established that could be evidenced and affirmed by FNCT fracture surface analysis. Moreover, the yield strength of a HDPE material exposed to a certain medium as detected by a classic tensile test was found to be the crucial value of true stress to induce the transition from crack propagation due to the craze‐crack mechanism to shear deformation during FNCT measurements.
Highlights
- Progress of crack formation in high‐density polyethylene is analyzed by different imaging techniques
- Determined growth rates depend on distinction between craze zone and crack
- The ratio of the present crack to the anteceding craze zone is validated theoretically
- The transition from crack propagation to ductile shear deformation is identified
- An already formed craze zone may still fail by ductile mechanisms
Advancements in bulk metallic glass thermoplastic forming unleash the potential to fabricate microscale metallic features with unparalleled precision and durability, i.e. microspine gripping structures for mobility platforms on planetary or in-space robots. Four designs of grippers were fabricated and rigorously tested. Coefficient of friction on four test surfaces were measured and compared to SiC paper and Velcro. The hardness and elasticity of the bulk metallic glasses make them a game-changer in the field, offering a superior alternative to conventional nonmetallic grippers.
An interlaboratory study, involving eigth international laboratories and coordinated by COMTES FHT (Czech Republic), was conducted to validate tensile measurements obtained using miniature specimens on additively manufactured (AM) components and artifacts. In addition to AM 316L stainless steel (316L SS), a wrought highstrength steel (34CrNiMo6V, equivalent to AISI 4340) was also used. Based on the results, a precision statement in accordance with ASTM E691 standard practice was developed, intended for inclusion in a proposed annex to the ASTM E8/E8M tension testing method. The primary outcomes of the study highlighted the agreement between yield and tensile strength measured from miniature and standard-sized tensile specimens. Furthermore, most tensile properties exhibited similar standard deviations, offering users insight into the efficacy of miniature specimen applications.
In this study, we investigated the diverse range of materials used for sizing in Iranian paper manuscripts during the Timurid (fifteenth century) to Safavid (sixteenth century) and Qajar (nineteenth century) periods. Our approach combined historical analysis with scientific examination of reconstructed sizings. We reconstructed 15 sizing materials based on identified Persian historical recipes and analysed their physical, optical, and spectral characteristics. Additionally, we assessed their behaviour against the mould fungus Aspergillus flavus. The results revealed distinctive properties for each sizing material, shedding light on their potential applications in paper preservation. Furthermore, our investigation demonstrated variations in hygroscopicity, thickness, grammage, and ash content post-sizing. The sizing materials also exhibited different effects on paper reflectance properties. Additionally, our study revealed insights into the impact of sizing on burnished papers, indicating that the mechanical process of burnishing did not significantly alter the chemical composition or spectral properties of the paper, with only minor changes in brightness observed in specific cases. All tested sizing materials supported varying levels of mould growth, indicating potential implications for paper conservation. Our findings provide valuable insights into the historical practices of Iranian paper sizing and offer practical considerations for the preservation of paper manuscripts.
Mikroplastik Detektion mit Thermoanalytischen Methoden: Analytik, Referenzmaterial, Ringversuche
(2024)
Ich dem Vortrag geht es um die Vorstellung von thermoanalytischen Methoden für die Mikroplastik-Detektion. Verschiedene Kopplungsmöglichkeiten werden gezeigt und die Funktionsweise der TED-GC/MS wird erklärt. Im zweiten Teil werden Referenzmaterialien für die Mikroplastik-Analytik diskutiert. PET -Tabletten des PlasticTrace Projektes werden vorgestellt. Am Ende wird der VAMAS Ringversuch zur Mikroplastik-Detektion gezeigt.
In der Wissenschaft und Technik gibt es verschiedene Gründe, um auf Basis geeigneter Modelle in die Zukunft schauen zu wollen, beispielsweise um zu bewerten, ob ein Bauteil auch noch deutlich länger verwendet werden kann als eigentlich einmal vorgesehen. Eine Methode dieses zu tun, basiert auf dem Zeit-Temperatur-Äquivalenz-Prinzip, welches besagt, dass ein Zustand oder eine Materialeigenschaft gleichwertig bei verschiedenen Zeit-Temperatur-Kombinationen auftritt oder erreicht werden kann. Höhere Temperaturen verkürzen in der Regel die Dauer und umgekehrt. In den letzten Jahrzehnten hat sich ein umfangreiches Methodenspektrum für unterschiedliche Werkstoffe und Anwendungsgebiete entwickelt, sodass die Identifikation einer geeigneten Methode für einen konkreten Anwendungsfall oder neue Materialien eine Herausforderung darstellt. These: „Fortschrittlich wäre, existierende Methoden zusammenzuführen, methodenspezifische Vorteile zu kombinieren, um mit geringerem Aufwand ein geeignetes Prognosemodell zu entwickeln.“
Für metallische Werkstoffe und Polymere verläuft die Entwicklung von Prognosemodellen mit Zeit-Temperatur-Korrelation seit ca. 1940 parallel und unabhängig voneinander. In diesem Zusammenhang bekannte Methoden sind das Zeit-Temperatur-Superpositionsprinzip und Zeit-Temperatur-Parameter, wie der LARSON-MILLER-Parameter. Die jeweiligen methodischen Ansätze sind in der Regel anwendungs- und materialspezifisch und nur einzelnen Fachartikeln zu entnehmen. Eine zusammenführende thematische Übersicht und Untersuchung existierender Methoden wurden bislang nicht publiziert. Diese Forschungsarbeit verfolgt dahingehend einen neuartigen methodischen Ansatz und zeigt untersuchte Gemeinsamkeiten und Unterschiede als auch Analogien für das Zeit-Temperatur-Superpositionsprinzip und Zeit-Temperatur-Parameter anhand bestimmter Merkmale auf. Dafür wurden verschiedene analytische und grafische Ansätze verwendet. Ferner wird eine zusammenführende Untersuchung anhand eines rheologischen Materialmodells sowie anhand eines praktischen Anwendungsbeispiels gezeigt. Hergeleitet wurde u. a., dass das Prinzip der Zeit-Temperatur-Superposition für sogenanntes thermorheologisch einfaches und komplexes Verhalten konkreten Zeit-Temperatur-Parametern zugeordnet werden können. Und dadurch Verschiebefunktionen nicht nur in Abhängigkeit der Temperatur, sondern auch abhängig vom Zustand untersucht und definiert werden können. Ferner ermöglicht eine Skalierung der Zeit-Temperatur-Parameter auf eine Referenztemperatur physikalisch anschaulichere Auswertungen analog zum Zeit-Temperatur-Superpositionsprinzip. Untersuchungen zeigen, dass sich für einen konkreten Anwendungsfall die geeignetste Zeit-Temperatur-Äquivalenz-Methode aus einer gegenseitigen Abhängigkeit bzw. Kompatibilität einzelner Elemente, wie zugrunde gelegte Daten, Koordinatenachsenskalierung, ermittelte Zeit-Temperatur-Äquivalenz, Masterfunktionsansatz und der geforderten Interpolationsgüte herleitet.
Der gewählte Forschungsansatz und die erzielten Ergebnisse bieten eine Plattform für die weitere Entwicklung von Prognosemodellen auf Basis des Zeit-Temperatur-Äquivalenz-Prinzips, insbesondere im Hinblick auf eine Zusammenführung und Kombination existierender Methoden.
In this contribution, we present a physically motivated heat source model for the numerical modeling of laser beam welding processes. Since the calibration of existing heat source models, such as the conic or Goldak model, is difficult, the representation of the heat source using so-called Lamé curves has been established, relying on prior Computational Fluid Dynamics (CFD) simulations.
Lamé curves, which describe the melting isotherm, are used in a subsequent finite-element (FE) simulation to define a moving Dirichlet boundary condition, which prescribes a constant temperature in the melt pool. As an alternative to this approach, we developed a physically motivated heat source model, which prescribes the heat input as a body load directly. The new model also relies on prior CFD simulations to identify the melting isotherm. We demonstrate numerical results of the new heat source model on boundary-value problems from the field of laser beam welding and compare it with the prior CFD simulation and the results of the Lamé curve model and experimental data.
High‐temperature KCl‐induced corrosion of high Cr and Ni alloys investigated by in‐situ diffraction
(2024)
High‐temperature KCl‐induced corrosion in laboratory air was observed in situ utilizing X‐ray diffraction. High Cr‐containing model alloys (Fe‐13Cr, Fe‐18Cr‐12Ni, and Fe‐25Cr‐20Ni) were coated with KCl and exposed to dry air at 560°C. KCl‐free alloys were studied in the equivalent atmosphere as a reference. After exposure to KCl‐free environments, all alloys showed the formation of very thin oxide layers, indicating good corrosion resistance. In contrast, KCl‐bearing alloys showed distinct damage after exposure.
The talk summarizes challenges in microplastic analysis. It shows the preparation of microplastic reference materials as well as the testing on homogeneity and stability. The reference material is used in an international laboratory comparison to compare different detection methods used for microplastic analysis. The methods used were µ-IR (FTIR+LDIR) for number-based methods and TED-GC/MS and Py-GC/MS for mass-based methods. The ILC was done under the umbrella of VAMAS TWA 45. Results of the participants are presented.
Preliminary results of an interlaboratory comparison on microplastics organised by plasticsfate
(2023)
Microplastics are everywhere in the environment, but analytics is challenging. Since harmonisation is missing as well es suitable reference materials, BAM did under th umbrella of VAMAS funded by the EU Horizon 2020 project PlasticsFate a ILC for microplastic detection methods. Methods adressed were IR, Raman, Py-GC/MS and TED-GC/MS. The talk gives a first presentation and evaluation on the results.
Monitoring of microplastics in food matrices is crucial to determinate the human exposure. By direct ingestion microplastics could be released in the food during the production, through packaging and by consumer’s use. The absence of standard methods to quantify and detect different size range and type of microplastics has led to difficult and time consuming procedural steps, poor accuracy and lack of comparability. In this work, matrix characterization and laboratory experiments were used to investigate the efficiency of sample preparation in milk powder. This information is crucial to compile a standard procedure for sample preparation and digestion of common milk powder to detect different particle sizes and types of polymers. Charaterisation is done by TGA and TOC measurements.
For the hydrogen-based energy economy of tomorrow, the construction of the necessary infrastructure will play a central role. Most materials used to date, such as welded steels, can be prone to hydrogen embrittlement under certain conditions. This includes the classic delayed cold cracking during welding as well as degradation phenomena during service of components in hydrogen-containing environment. For the evaluation of any hydrogen effect, for example, on the mechanical properties of a welded metallic material, the hydrogen content must be precisely determined. In the case of weld seams, the carrier gas hot extraction (CGHE) according to ISO 3690 is meanwhile state-of-the-art. CGHE is based on accelerated hydrogen degassing due to the thermal activation of hydrogen at elevated temperatures. In addition to the quantification of hydrogen, thermal desorption analysis (TDA) with varying heating rates can be used to determine and evaluate the hydrogen trapping at microstructural defects in the material. For both techniques, experimental and metrological influences must be considered, which have a major effect on the result. For example, ISO 3690 suggests different sample geometries and minimum extraction times for CGHE. This study summarizes the results and experiences of numerous investigations at the Federal Institute for Materials Research and Testing (BAM) with different sample temperatures and geometries (ISO 3690 type B and cylindrical TDA samples) regarding the influence of the sample surface (polished/welded), measurement accuracy depending on the sample volume and the insufficient monitoring of the effect of PI control on the extraction temperature. A deviating extraction temperature from the target temperature can significantly falsify the measurement results. Based on the results, methods are shown which allow the desired extraction temperature to be reached quickly without physically interfering with the measuring equipment. This serves to significantly improve the reliability of the hydrogen measurement through increased signal stability and accelerated hydrogen desorption. In general, an independent temperature measurement with dummy samples is recommended for the heating procedure of choice to exclude possible undesired temperature influences before the measurement. The methods described can be transferred directly to industrial applications
Stresses in repair welding of high-strength steels—part 2: heat control and stress optimization
(2024)
In welding of high-strength steels, e.g. for foundations and erection structures of wind energy plants, unacceptable defects can occasionally be found in the weld area, which should be removed by thermal gouging and subsequent re-welding. High shrinkage restraint of repair welds may lead to crack formation and component failure, predominantly in interaction with degraded microstructures and mechanical properties due to repair cycles. This study aims for elaboration of recommendations for repair concepts appropriate to the stresses and materials involved to avoid cold cracking, damage and expensive reworking. In part 1 [1] of this study, systematic investigations of influences of shrinkage restraint on residual stresses and cold cracking risk during repair welding of two high-strength steels S500MLO for offshore application and S960QL for mobile crane structures were focussed. In this part 2, the microstructure, particularly hardness, and residual stresses due to gouging and influences of heat control parameters in repair welding are analysed. A clear reduction in residual stress after gouging can be observed, especially for the specimens with restrained transverse shrinkage. Gouging to a depth of approx. 2/3 of the seam height does not lead to a complete relaxation of the observed reaction forces. Particularly for the higher strength steel S960QL, there are pronounced areas influenced by the gouging process in which a degradation of the microstructure and properties should be assumed. Overall, the repair welds show a significant increase in the width of the weld and HAZ compared to the original weld, especially in the case of S960QL/G89. The repair welds show higher welding-induced stresses than the original welds, especially in the areas of the HAZ and the base metal close to the weld seam. This behaviour can be attributed overall to increased restraint conditions due to the remaining root weld or shorter gouge grooves. In good agreement with earlier investigations, the residual stresses transverse to the weld can be significantly reduced by upwardly limited working or interpass temperatures, and the reaction stresses resulting from high restraint conditions can be effectively counteracted. The influence of the heat input on the stress formation is low compared to the interpass temperature for both test materials.
In this work we instigated the fragmentation of Au microparticles supported on a thin amorphous carbon film by irradiating them with a gradually convergent electron beam inside the Transmission Electron Microscope. This phenomenon has been generically labeled as “electron beam-induced fragmentation” or EBIF and its physical origin remains contested. On the one hand, EBIF has been primarily characterized as a consequence of beam-induced heating. On the other, EBIF has been attributed to beam-induced charging eventually leading to Coulomb explosion. To test the feasibility of the charging framework for EBIF, we instigated the fragmentation of Au particles under two different experimental conditions. First, with the magnetic objective lens of the microscope operating at full capacity, i.e. background magnetic field B = 2 T, and with the magnetic objective lens switched off (Lorenz mode), i.e. B = 0 T. We observe that the presence or absence of the magnetic field noticeably affects the critical current density at which EBIF occurs. This strongly suggests that magnetic field effects play a crucial role in instigating EBIF on the microparticles. The dependence of the value of the critical current density on the absence or presence of an ambient magnetic field cannot be accounted for by the beam-induced heating model. Consequently, this work presents robust experimental evidence suggesting that Coulomb explosion driven by electrostatic charging is the root cause of EBIF.
Early detection of fatigue cracks and accurate measurements of the crack growth play an important role in the maintenance and repair strategies of steel structures exposed to cyclic loads during their service life. Observation of welded connections is especially of high relevance due to their higher susceptibility to fatigue damage. The aim of this contribution was to monitor fatigue crack growth in thick welded specimens during fatigue tests as holistically as possible, by implementing multiple NDT methods simultaneously in order to record the crack initiation and propagation until the final fracture. In addition to well-known methods such as strain gauges, thermography, and ultrasound, the crack luminescence method developed at the Bundesanstalt für Materialforschung und -prüfung (BAM), which makes cracks on the surface particularly visible, was also used. For data acquisition, a first data fusion concept was developed and applied in order to synchronize the data of the different methods and to evaluate them to a large extent automatically. The resulting database can ultimately also be used to access, view, and analyze the experimental data for various NDT methods. During the conducted fatigue tests, the simultaneous measurements of the same cracking process enabled a comprehensive comparison of the methods, highlighting their individual strengths and limitations. More importantly, they showed how a synergetic combination of different NDT methods can be beneficial for implementation in large-scale fatigue testing but also in monitoring and inspection programs of in-service structures - such as the support structures of offshore wind turbines.
In this work we instigated the fragmentation of Au microparticles supported on a thin amorphous carbon film by irradiating them with a gradually convergent electron beam inside the Transmission Electron Microscope. This phenomenon has been generically labeled as ‘‘electron beam-induced fragmentation’’ or EBIF and its physical origin remains contested. On the one hand, EBIF has been primarily characterized as a consequence of beam-induced heating. On the other, EBIF has been attributed to beam-induced charging eventually leading to Coulomb explosion. To test the feasibility of the charging framework for EBIF, we instigated the fragmentation of Au particles under two different experimental conditions. First, with the magnetic objective lens of the microscope operating at full capacity, i.e. background magnetic field 𝐵 = 2 T, and with the magnetic objective lens switched off (Lorenz mode), i.e. 𝐵 = 0 T. We observe that the presence or absence of the magnetic field noticeably affects the critical current density at which EBIF occurs. This strongly suggests that magnetic field effects play a crucial role in instigating EBIF on the microparticles. The dependence of the value of the critical current density on the absence or presence of an ambient magnetic field cannot be accounted for by the beam-induced heating model. Consequently, this work presents robust experimental evidence suggesting that Coulomb explosion driven by electrostatic charging is the root cause of EBIF.
Ring-opening polymerizations (ROPs) of l-lactide (LA) were performed with ethyl l-lactate or 11-bromoundecanol as initiators (In) and tin(II) ethyl hexanoate (SnOct2) as catalyst (Cat) using four different LA/In ratios (20/1, 40/1, 60/1, and 100/1). One series of ROPs was conducted in bulk at 120 °C, yielding PLAs with low dispersities (Ð ~ 1.2–1.4), and a second series was conducted in bulk at 160 °C, yielding higher dispersities (Ð ~ 1.3–1.9). Samples from both series were annealed for 1 or 14 days at 140 °C in the presence of SnOct2. Both polycondensation and disproportionation reactions occurred, so that all four samples tended to form the same type of molar mass distribution below 10,000 Da, regardless of their initially different number average molar masses (Mn). Both initiators gave nearly identical results. The thermodynamic control of all reversible transesterification processes favored the formation of crystallites composed of chains with a Mn around 3500–3700, corresponding to a crystal thickness of 10–13 nm.
Durch Auslagerungs- und elektrochemische Tests im Labor kann das Korrosionsverhalten verschiedener metallener Werkstoffe beurteilt werden. Aus den Versuchsergebnissen, die in verschiedenen synthetischen Geothermalwässern im Labor erzielt wurden, lassen sich die folgenden Schlussfolgerungen ziehen:
• Die Anfälligkeit für Spaltkorrosion wurde als wichtigster Aspekt für die Werkstoffqualifizierung ermittelt.
• Der niedriglegierte Stahl 25CrMo4 zeigte bei niedrigem Salzgehalt in MB-Geothermalwasser eine gleichmäßige Korrosion unterhalb der akzeptierten Schwelle von 0,3 mm/Jahr. Daher kann er als geeignet für geothermische Bedingungen mit niedrigem Salzgehalt angesehen werden, wie sie für MB getestet wurden. Es besteht keine Notwendigkeit, auf höherlegierte (teurere) Werkstoffe auszuweichen. Ein niedrigerer pH-Wert (wie bei LHD) führt zu Korrosionsraten oberhalb der akzeptablen Grenzwerte, so dass die niedriglegierten Werkstoffe nicht für Flüssigkeiten mit niedrigem pH-Wert geeignet sind.
• Stark salzhaltige Geothermalwässer erfordern höherlegierte Werkstoffe, da die Korrosionsrate von niedriglegiertem Stahl zu hoch ist.
• Der Duplexstahl X2CrNiMo22-5-3 und der Superduplexstahl X2CrNiMoCuWN25-7-4 wurden aufgrund ihrer kritischen Anfälligkeit für örtliche Korrosion in Form von Loch- und Spaltkorrosion unter Betriebsbedingungen nicht als geeignet für geothermische Anwendungen in Geothermalwässern mit einer mit NDB und ORG vergleichbaren Zusammensetzung angesehen.
• Der superaustenitische Stahl X1CrNiMoCu32-28-7 eignet sich für ORG und salzarme Wässer. In NDB-Geothermalwasser wurde er bei 100 °C als geeignet angesehen. Jedoch schränkt seine Anfälligkeit für Spaltkorrosion seine Anwendbarkeit ein. Neben seiner guten Korrosionsbeständigkeit ist sein Repassivierungsverhalten für seine begrenzte Anwendbarkeit in Geothermalwässern mit niedrigem pH-Wert verantwortlich.
• Die Nickelbasislegierung NiCr23Mo16Al wurde als geeignet erachtet und stellt eine sichere Option für den Einsatz in geothermischen Anlagen dar, selbst wenn mit stark salzhaltigem Geothermalwasser gearbeitet wird.
Durch Auslagerungs- und elektrochemische Tests im Labor kann das Korrosionsverhalten verschiedener metallener Werkstoffe beurteilt werden. Aus den Versuchsergebnissen, die in verschiedenen synthetischen Geothermalwässern im Labor erzielt wurden, lassen sich die folgenden Schlussfolgerungen ziehen:
• Die Anfälligkeit für Spaltkorrosion wurde als wichtigster Aspekt für die Werkstoffqualifizierung ermittelt.
• Der niedriglegierte Stahl 25CrMo4 zeigte bei niedrigem Salzgehalt in MB-Geothermalwasser eine gleichmäßige Korrosion unterhalb der akzeptierten Schwelle von 0,3 mm/Jahr. Daher kann er als geeignet für geothermische Bedingungen mit niedrigem Salzgehalt angesehen werden, wie sie für MB getestet wurden. Es besteht keine Notwendigkeit, auf höherlegierte (teurere) Werkstoffe auszuweichen. Ein niedrigerer pH-Wert (wie bei LHD) führt zu Korrosionsraten oberhalb der akzeptablen Grenzwerte, so dass die niedriglegierten Werkstoffe nicht für Flüssigkeiten mit niedrigem pH-Wert geeignet sind.
• Stark salzhaltige Geothermalwässer erfordern höherlegierte Werkstoffe, da die Korrosionsrate von niedriglegiertem Stahl zu hoch ist.
• Der Duplexstahl X2CrNiMo22-5-3 und der Superduplexstahl X2CrNiMoCuWN25-7-4 wurden aufgrund ihrer kritischen Anfälligkeit für örtliche Korrosion in Form von Loch- und Spaltkorrosion unter Betriebsbedingungen nicht als geeignet für geothermische Anwendungen in Geothermalwässern mit einer mit NDB und ORG vergleichbaren Zusammensetzung angesehen.
• Der superaustenitische Stahl X1CrNiMoCu32-28-7 eignet sich für ORG und salzarme Wässer. In NDB-Geothermalwasser wurde er bei 100 °C als geeignet angesehen. Jedoch schränkt seine Anfälligkeit für Spaltkorrosion seine Anwendbarkeit ein. Neben seiner guten Korrosionsbeständigkeit ist sein Repassivierungsverhalten für seine begrenzte Anwendbarkeit in Geothermalwässern mit niedrigem pH-Wert verantwortlich.
• Die Nickelbasislegierung NiCr23Mo16Al wurde als geeignet erachtet und stellt eine sichere Option für den Einsatz in geothermischen Anlagen dar, selbst wenn mit stark salzhaltigem Geothermalwasser gearbeitet wird.
AbstractThis study applies Semantic Web technologies to advance Materials Science and Engineering (MSE) through the integration of diverse datasets. Focusing on a 2000 series age-hardenable aluminum alloy, we correlate mechanical and microstructural properties derived from tensile tests and dark-field transmission electron microscopy across varied aging times. An expandable knowledge graph, constructed using the Tensile Test and Precipitate Geometry Ontologies aligned with the PMD Core Ontology, facilitates this integration. This approach adheres to FAIR principles and enables sophisticated analysis via SPARQL queries, revealing correlations consistent with the Orowan mechanism. The study highlights the potential of semantic data integration in MSE, offering a new approach for data-centric research and enhanced analytical capabilities.
The stress-induced tetragonal to monoclinic (t-m) zirconia phase transformation can provide a certain degree of plasticity to Ceria-stabilized (Ce-TZP) zirconia-based composites. Characterizing and monitoring this phase transition on a millimeter-size range, within the bulk and in-situ remains a challenge. In this work, the mechanical behavior of Ce-TZP based composite was studied in tension, combining microscopy and synchrotron Xray refraction techniques. In contrast with microscopy methods, which only provide surface information, X-ray refraction radiography (SXRR) allowed the visualization of all the transformation bands, over the entire length and thickness of tested specimens, opening up new avenues for in-situ stress-induced t-m transformation studies.
Investigation on the Durability of a Polypropylene Geotextile under Artificial Aging Scenarios
(2024)
Geosynthetics are widely used in various civil engineering applications, such as geotextiles in coastal protection, and display a sustainable alternative to natural mineral materials. However, the full benefits of using geosynthetics can only be gained with a long service lifetime of the products. With the use of added stabilizers to the polymers, service lifetimes can be achieved in the range of 100 years. Therefore, accelerated aging methods are needed for the assessment of the long-term performance of geotextiles. In the present study, the behavior of geosynthetic materials made of polypropylene was investigated under artificial aging conditions involving elevated temperatures ranging from 30 to 80 °C, increased oxygen pressures ranging from 10 to 50 bar in water-filled autoclaves, and UV irradiation under atmospheric conditions. ATR-IR spectroscopy was employed to detect the increase in the carbonyl index over various aging durations, indicating the oxidative degradation of the geotextile. The most pronounced increase was observed in the case of aging through UV irradiation, followed by thermal aging. Elevated pressure, on the other hand, had a lower impact on oxidation. High-temperature size exclusion chromatography was utilized to follow the reduction in molar mass under different degradation conditions, and the results were consistent with those obtained from ATR-IR spectroscopy. In polyolefins such as polypropylene, Hindered Amine Stabilizers (HAS) are used to suppress oxidation caused by UV radiation. The quantitative analysis of HAS was carried out using a UV/Vis method and HPLC. The degradation of UV stabilizers during the aging of geotextiles is responsible for the oxidation and the reduction in the molar mass of polypropylene. From the results, it can be concluded that applications of PP geotextile without soil or sand cover might cause the risk of the formation of microplastic particles. Material selection, design, and maintenance of the construction must follow best practices, including the system’s removal or replacement at end-of-life. Otherwise, a sustainable use of geotextiles in civil engineering is not possible.
The presentation gives an overview of BAM's activities on processing influences and application properties of MPEAs in the form of joined and machined high and medium entropy alloys (CoCrFeMnNi and CoCrNi). In the case of welding, the focus is on defect-free welded joints with sufficient mechanical properties. In the case of machining, the focus is on the possible influence on the surface quality of the materials through adequate milling parameters. In addition, the hydrogen absorption and diffusion properties as well as the electrochemical corrosion behavior are fundamentally examined.
Adhesively bonded composite joints can develop voids and porosity during fabrication, leading to stress concentration and a reduced load-carrying capacity. Hence, adhesive porosity analysis during the fabrication is crucial to ensure the required quality and reliability. Ultrasonic-guided wave (UGW)-based techniques without advanced signal processing often provide low-resolution imaging and can be ineffective for detecting small-size defects. This article proposes a damage imaging process for adhesive porosity analysis of bonded composite plates using UGWs measured by scanning laser Doppler vibrometer (LDV). To implement this approach, a piezoelectric transducer is mounted on the composite joint specimen to generate UGWs, which are measured over a densely sampled area. The signals obtained from the scan are processed using the proposed signal processing in different domains. Through the utilization of filter banks in frequency and wavenumber domains, along with the root-mean-square calculation of filtered signals, damage images of the adhesive region are obtained. It has been observed that different filters provide information related to different void sizes. Combining all the images reconstructed by filters, a final image is obtained which contains damages of various sizes. The images obtained by the proposed method are verified by radiography results and the porosity analysis is presented. The results indicate that the proposed methodology can detect the pores with the smallest detectable pore area of 2.41 mm^2, corresponding to a radius of 0.88 mm, with an overall tendency to overestimate the pore size by an average of 11%.
The heat-resistant cast iron EN-GJSA-XNiSiCr35-5-2 (Ni-Resist D-5S) was investigated for its fatigue crack growth behavior at room and high temperatures. Force-controlled tests were carried out at constant temperatures (20 °C, 500 °C, 700 °C) without and with hold time and different load ratios. The crack growth behavior was also characterized under TMF loading (Tmin = 400 °C, Tmax = 700 °C) by applying IP and OP conditions and different load ratios. Three different techniques were combined to monitor crack growth: potential drop, thermography, and compliance method. The effect of the different loading conditions on the fatigue crack growth behavior will be presented and discussed.
Ground Granulated Blast-Furnace Slag (GGBFS), a by-product of the iron-making process, has gained significant attention as a supplementary cementitious material and has become increasingly popular in recent years due to its remarkable properties. GGBFS can significantly reduce the environmental impact of cement production when it comes to building concrete structures. GGBFS can either be blended with ordinary Portland cement (OPC) (up to a 90% replacement), or it can be used in the production of alkali-activated materials (AAMs). However, a comprehensive understanding of the pore solution composition is necessary for understanding various aspects of cementitious materials and their durability, including corrosion behavior, passivation of steel, and resistance to deteriorative processes. In the present work, the pore solutions of seven different GGBFS-containing cements (alkali-activated slag, alkali-activated slag/fly ash blends, a hybrid alkaline cement, CEM III/C, and CEM III/B) were extracted and analysed by inductively coupled plasma-optical emission spectroscopy, ion chromatography, pH, redox potential, and conductivity measurements. For comparison, a Portland cement pore solution was analysed similarly. The Concentrations of reduced sulfur were noteworthy in all GGBFS-containing cements, particularly in alkali-activated cements, where concentrations were notably higher compared to standard cements. The redox potentials of the pore solutions were primarily dictated by the concentrations of reduced sulfur, although other factors may contribute. Additionally, sulfur species in the pore solutions had an impact on pH, electrical conductivity, and other properties pertinent to the corrosion of reinforcements.
Die additive Fertigung mittels Schweißverfahren bietet große ökonomische Vorteile für eine ressourceneffiziente Bauteilherstellung. Offene Fragen bezüglich Homogenität, Anisotropie der Schweißgefüge und den damit verbundenen Bauteileigenschaften stehen einer wirtschaftlichen Verarbeitung oftmals im Wege. Finale Bauteilgeometrie und Oberflächengüte erfordern meist komplementäre subtraktive Fertigungsschritte. Werkstoffe für hochbelastbare Komponenten sind oftmals schwer spanbar. In einem Vorhaben der BAM und des ISAF wurde untersucht, wie die Modifikation der AM-Schweißzusätze und das ultraschallunterstützte Fräsen (US) die Zerspanungssituation verbessern. Der vorliegende Artikel stellt wesentliche Zusammenhänge zwischen Legierung, Gefüge und Zerspanung zweier schwer spanbarer Hochleistungslegierungen (FeNi und CoCr) dar. Großes Potenzial zeigte neben dem US die Modifikation mit Zr und Hf bei Zulegierung in das Schweißgut mittels Beschichtung von Massivdrähten bzw. Herstellung von Fülldrähten.
Es werden die Ergebnisse eines mehrjährigen Forschungsvorhabens der BAM in Zusammenarbeit mit Straßenbauverwaltungen der Länder und Industriebeteiligten zur betriebstechnischen Ausrüstung von Straßentunneln präsentiert. Schwerpunkte waren die Bestimmung der Korrosivität der Atmosphäre von 3 ausgewählten Straßentunneln, die Analyse korrosionsrelevanter Ablagerungen und von Klimadaten. Die Auswirkungen dieser Einflussgrößen auf die Dauerhaftigkeit von Konstruktionen aus nichtrostenden Stählen wurde ermittelt und in Abhängigkeit verschiedener Einflussparameter dargestellt. Die Ergebnisse der systematischen Untersuchungen an Prüfköpern decken sich mit Beobachtungen an realen Bauteilen. Spaltbehaftete Konstruktionen aus Werkstoffen der CRC III führen demnach in Zeiträumen zwischen 10 und 15 Jahren zu Korrosionserscheinungen, welche die technische Sicherheit beeinträchtigen können und die erwartete Dauerhaftigkeit nicht erfüllen. Die Folge sind zusätzliche Sperrungen und ein vorzeitig notwendiger Unterhaltsaufwand, die erhebliche Kosten verursachen. Im Ergebnis ist eine Überarbeitung des aktuellen Regelwerkes erforderlich, um die angestrebte Dauerhaftigkeit von 30 Jahren zu gewährleisten.
The corrosion behavior of galvanized steels and zinc components under atmospheric exposure depends mostly on the corrosion product‐based cover layer formation under the prevailing conditions. The use of agar‐based gel electrolytes makes it possible to use electrochemical methods to obtain a characteristic value from these cover layers that describe their current and future protective capacity. It is shown here that different states of galvanized steel can be distinguished very well under laboratory conditions and that this method is also suitable for use under practical conditions. Based on the characteristic values and assuming future time of wetness, it is very easy to draw up a forecast for the future corrosion rate, which provides plausible values.
While alkali-activated binders offer certain advantages over traditional Portland cement binders, particu¬larly in terms of resistance against chemical attacks and potentially environmental footprint, their degra¬dation mechanisms remain incompletely understood at present, specifically carbonation. Thus, this study investigates the impact of natural and accelerated carbonation (1% and 4% CO2) on three different compositions of alkali-activated concretes: 100% calcined clay (C100) binder, 100% ground blast furnace slag (S100) binder, and a 40% calcined clay and 60% blast furnace slag blend (C40S60). C100 concretes exhibit faster carbonation kinetics, with five times greater natural carbonation depths than S100. This difference diminishes under accelerated carbonation, showing a 1.5 times difference for 1% CO2 and complete carbonation for 4% CO2 at 90 days. The results thus confirm that accelerated carbonation testing of low-Ca alkali-activated concretes yields results that are not representative of natural carbonation. The C40S60 sample demonstrates a carbonation profile similar to a CEM I concrete, i.e., a high carbonation resistance. Microstructure analysis indicates the formation of three polymorphs of calcium carbonate for S100 (calcite, vaterite, and aragonite), with a higher CO2 concentration favouring aragonite over vaterite. C100 exhibits no calcium carbonates; instead, sodium carbonates form, including trona for 4% CO2 and natrite for both accelerated tests. C40S60 shows calcium and sodium carbonates, although to a lesser extent, containing predominantly calcite and minor signals of natrite. Suitable compositions, like C40S60, prove as effective during natural or accelerated carbonation tests as conventional Portland cement concrete.
The present Ph.D. thesis provides a comprehensive experimental and theoretical study of the bulging-cracking relationship in laser beam welding of thick unalloyed steel sheets. It focuses on experimentally proving the existence of the bulging region and on developing a coupled multiphysics mathematical framework to analyze its influence on the three critical factors controlling the susceptibility to solidification cracking, namely the thermal, metallurgical, and mechanical factors.
The research employs a novel experimental setup, utilizing a combination of transparent quartz glass and thick unalloyed steel sheet, enabling real-time visualization of the weld pool geometry and confirming the existence of a distinctive bulging region. To deepen the understanding of these experimental insights, an extensive multiphysics mathematical framework was developed and rigorously verified and validated. This framework introduces an innovative approach using Lamé curves for accurately describing complex three-dimensional weld pool geometries, including the bulging region's characteristics. Through analytical solutions and numerical procedures, it facilitates the computation of solidification parameters, which are crucial for understanding the metallurgical aspects of crack formation. The framework also incorporates a mechanical model to assess and evaluate the local stress distribution within the bulging region.
The findings indicate that an elongated, sharply shaped bulging region significantly increases the susceptibility to solidification cracking. This is attributed to its adverse impact on the distribution and local dwell time of liquid metal residing at grain boundaries during solidification, combined with the localized tensile stresses identified in the bulging region.
In essence, this research contributes to the broader understanding of solidification cracking in laser beam welding of thick unalloyed steel sheets, with a particular focus on the bulging region. The insights and methodologies developed in this thesis are valuable for future research and advancements in the application of the laser beam welding technology for joining high-thickness unalloyed steel components.
Bruchmechanik-basierende Methoden können für die Ermüdungsbewertung von mechanischen Bauteilen angewendet werden, die Defekte oder Risse enthalten und zyklischen Belastungen ausgesetzt sind. Die Kenntnis des Risswachstumsverhaltens für kurze und lange Risse ermöglicht die Bestimmung sowohl endlicher als auch unendlicher Lebensdauer. Ein erstes Problem ergibt sich jedoch aus der empirischen Bestimmung von Ermüdungswerkstoffkennwerten, die je nach Prüfbedingungen, z. B. Prüfmethode, Frequenz und Spannungsverhältnis R, variieren. Dies ist auf die Rissschließeffekte und weitere Umgebungsphänomene zurückzuführen, die das Rissfortschrittsverhalten beeinflussen. Ein zweites Problem ist das Fehlen von Standardversuchsverfahren zur Bestimmung des Schwellenwerts gegen Ermüdungsrissausbreitung ΔKth in Abhängigkeit von der Rissausbreitung. Dies ist problematisch, da ΔKth mit der Zunahme der Rissschließeffekte im Kurzrissbereich zunimmt und seine ungenaue experimentelle Bestimmung zu großen Abweichungen bei der Bewertung und, was noch kritischer ist, zu nicht konservativen Vorhersagen führt. Mit dem Ziel, zuverlässigere und sicherere Bewertungsverfahren bereitzustellen, wird in dieser Arbeit eine Methode vorgeschlagen, die auf effektiven Risswachstumsdaten basiert, die bei hohen Spannungsverhältnissen (R ≈ 0,8) ermittelt wurden. Zur Beschreibung der Entwicklung der Rissschließeffekte wird ein Kurzrissmodell auf der Grundlage von zyklischen R-Kurven und CPLR-Daten verwendet. Die analytischen Vorhersagen werden mit experimentellen Daten verglichen, die zur Validierung des Verfahrens durchgeführt wurden, und die daraus entstandenen Unterschiede werden diskutiert.
Übersetzt mit DeepL.com (kostenlose Version)
Unlike conventional alloys, which typically consist of one main element, high-entropy alloys (HEAs) contain five or more principal elements, which broaden chemical complexity and with it a realm of synergistic mechanisms. The AlMo0.5NbTa0.5TiZr HEA initiated a subclass of Al-containing refractory (r)HEAs that has recently drawn attention [2]. The alloy has a superalloy-resembling B2/bcc nanostructure, which inspired its name refractory high entropy superalloy (RSA). With high-temperature (HT) compressive strengths beyond conventional Ni-based superalloys, this nanostructure could be used for improved HT structural applications. However, in the application-relevant HT regime the Al-Zr-rich B2 phase decomposes to form a hexagonal Al-Zr-based intermetallic (Al4-xZr5; x: 0..1) [3,4]. This work explores the fascinating yet fatal micromechanisms associated to this phase transformation, in the context of creep, annealing and oxidation experiments performed between 800 and 1200 °C.
The material was produced by arc-melting and heat treatment in argon, which lead to grain boundaries decorated with up to 7%. Interrupted constant-load creep tests were performed under vacuum (at 10-4 Pa), at 900–1100 °C with external tensile stresses of 30–120 MPa. Oxidation experiments were separately conducted for 24 hours at 800 and 1000 °C in both dry (21% O2 + 79% N2) and humid (8% O2 + 74% N2 + 18% H2O) air. After the experiments, the samples were characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy to reveal degradation mechanisms. Crystallographic texture, orientation relationships and stabilization of an oxygen-containing iso structure (Al4-xZr5(Ox-y); y: 0..x) of the Al-Zr-rich intermetallic are found and discussed.
Die Umweltwirkungen auf ein Material werden als Überlapp der Funktionskurven von Materialempfindlichkeit und einwirkenden Umweltparametern betrachtet. Wenn entweder die Empfindlichkeit oder die Beanspruchungen Null sind, ergibt sich auch keine Umweltwirkung und bei beidseitig Werten größer Null das jeweilige Produkt der beiden. Die Akkumulation der nicht-reversiblen Effekte über die Zeit und allen Eigenschaftsänderungen entspricht der Alterung des Materials für den jeweiligen Expositionszeitraum.
Die digitale Umweltsimulation gliedert sich hier in drei Teilaspekte. Ein erster, rein materialwissenschaftlicher Teil hat die Aufgabe, alle relevanten Materialempfindlichkeiten experimentell zu quantifizieren. Ein zweiter – unter Umständen numerischer Teil – hat die Aufgabe, das Bauteil und seine Einbaulage zu digitalisieren und aus den makroskopischen Umgebungsbedingungen die relevanten mikroklimatischen Umweltparameter für alle Oberflächen- oder Volumenelemente zu bestimmen. In einem dritten Teil werden die Einwirkungen über den betrachteten Zeitraum berechnet und kumuliert. Dieses Konzept, das auf den so genannten Expositions-Reaktions-Funktionen (ERF) basiert, wird an Beispielen der Photoxidation erläutert. Dieses Vorgehen wurde schon beim ViPQuali-Projekt als Numerische Umweltsimulation umgesetzt.
Überprüft werden muss das Modell unbedingt an einer realitätsnahen Validierungsbeanspruchung. Hier werden die ermittelten ERFs mit über den kompletten Beanspruchungszeitraum geloggten Umweltparametern gekoppelt, um die berechnete mit der experimentell erfahrenen Alterungswirkung zu vergleichen. Nur so kann sichergestellt sein, dass alle für die Anwendungsumgebung relevanten Materialempfindlichkeiten einbezogen wurden.
Die Umweltwirkungen auf ein Material werden als Überlapp der Funktionskurven von Materialempfindlichkeit und einwirkenden Umweltparametern betrachtet. Wenn entweder die Empfindlichkeit oder die Beanspruchungen Null sind, ergibt sich auch keine Umweltwirkung und bei beidseitig Werten größer Null das jeweilige Produkt der beiden. Die Akkumulation der nicht-reversiblen Effekte über die Zeit und allen Eigenschaftsänderungen entspricht der Alterung des Materials für den jeweiligen Expositionszeitraum.
Die digitale Umweltsimulation gliedert sich hier in drei Teilaspekte. Ein erster, rein materialwissenschaftlicher Teil hat die Aufgabe, alle relevanten Materialempfindlichkeiten experimentell zu quantifizieren. Ein zweiter – unter Umständen numerischer Teil – hat die Aufgabe, das Bauteil und seine Einbaulage zu digitalisieren und aus den makroskopischen Umgebungsbedingungen die relevanten mikroklimatischen Umweltparameter für alle Oberflächen- oder Volumenelemente zu bestimmen. In einem dritten Teil werden die Einwirkungen über den betrachteten Zeitraum berechnet und kumuliert. Dieses Konzept, das auf den so genannten Expositions-Reaktions-Funktionen (ERF) basiert, wird an Beispielen der Photoxidation erläutert. Dieses Vorgehen wurde schon beim ViPQuali-Projekt als Numerische Umweltsimulation umgesetzt.
Überprüft werden muss das Modell unbedingt an einer realitätsnahen Validierungsbeanspruchung. Hier werden die ermittelten ERFs mit über den kompletten Beanspruchungszeitraum geloggten Umweltparametern gekoppelt, um die berechnete mit der experimentell erfahrenen Alterungswirkung zu vergleichen. Nur so kann sichergestellt sein, dass alle für die Anwendungsumgebung relevanten Materialempfindlichkeiten einbezogen wurden.
Processing and cytocompatibility of Cu-doped and undoped fluoride-containing bioactive glasses
(2024)
Sintered or additive-manufactured bioactive glass (BG) scaffolds are highly interesting for bone replacement applications. However, crystallization often limits the high-temperature processability of bioactive glasses (BGs). Thus, the BG composition must combine high bioactivity and processability. In this study, three BGs with nominal molar (%) compositions 54.6SiO2-1.7P2O3-22.1CaO-6.0Na2O-7.9K2O-7.7MgO (13–93), 44.8SiO2-2.5P2O3-36.5CaO-6.6Na2O-6.6K2O-3.0CaF2 (F3) and 44.8SiO2-2.5P2O3-35.5CaO-6.6Na2O-6.6K2O-3.0CaF2-1.0CuO (F3–Cu) were investigated. The dissolution and ion release kinetics were investigated on milled glass powder and crystallized particles (500–600 μm). All glasses showed the precipitation of hydroxyapatite (HAp) crystals after 7 days of immersion in simulated body fluid. No significant differences in ion release from glass and crystalline samples were detected. The influence of surface roughness on cytocompatibility and growth of preosteoblast cells (MC3T3-E1) was investigated on sintered and polished BG pellets. Results showed that sintered BG pellets were cytocompatible, and cells were seen to be well attached and spread on the surface after 5 days of incubation. The results showed an inverse relation of cell viability with the surface roughness of pellets, and cells were seen to attach and spread along the direction of scratches.
Derzeit ist die Instandhaltung von großen Betontragwerken wie Brücken oder Windenergieanlagen problemorientiert und von einem reaktiven Vorgehen geprägt. Das bedeutet, erst wenn sichtbare Schäden vorliegen, werden diese meist unter Beeinträchtigung des Betriebs instand gesetzt. Im Hinblick auf die Entwicklung von prädiktiven Instandhaltungsstrategien, deren Fokus in der langfristigen Bauwerksüberwachung und der Vorhersage von Schädigungsentwicklungen liegt, wurde die Anwendung von Ultraschallverfahren für die Identifizierung der Degradationsprozesse von Betontragwerken unter Ermüdungsbeanspruchung untersucht. Hierzu fanden Arbeiten im vom Bundesministerium für Wirtschaft und Klimaschutz (BMWK) geförderten Verbundprojekt WinConFat zum "Einfluss der Probengeometrie und -größe auf die Ermüdung von Beton" an der Bundesanstalt für Materialforschung und -prüfung (BAM) und zu den "Methoden zur Zustandsanalyse von Windenergieanlagen" am Institut für Massivbau (IfMa) der Leibniz Universität Hannover (LUH) statt, welches zudem vom Deutschen Beton- und Bautechnik Verein e.V. (Forschungsvorhaben DBV-311) gefördert wurde. Dabei wurden verschiedene Einflussfaktoren auf die Schädigungsentwicklung unter Ermüdungsbeanspruchung wie die Probekörpergröße, das Belastungsniveau und die Betonfestigkeit untersucht. Als Schädigungsindikator und Vergleichsparameter wurden die Ultraschallgeschwindigkeit und der dynamische E-Modul des Betons verwendet. Um das Potential der Schädigungserfassung im Beton mittels Ultraschallprüfung umfassender zu bewerten, wurden zusätzlich Versuche an Betonproben unter monoton steigender Belastung, Kriechversuche, Temperaturversuche und Untersuchungen an großformatigen Balken durchgeführt.
The output of C&D waste is increasing year by year, among which low-quality recycled brick aggregates (RBAs) have not been well utilized and brought environmental burden. The durability of steam-cured concrete (HCC) is often compromised due to the detrimental effects of this curing regime on the long-term performance and microstructure development of the concrete material. To address this issue, this study investigates the potential of incorporating RBAs to improve the long-term durability of HCC. The results demonstrate that the incorporation of a small amount of RBA (10–20%) not only enhances the 28-d strength of HCC by 2.5–11.3%, but also improves its impermeability by mitigating heat damage effects. The combined application of fine and coarse RBA was found to effectively balance the negative effects of coarse RBA on the performance of HCC. Furthermore, the utilization of RBA in HCC was shown to have economic and environmental benefits. The results of this study demonstrate a simple and effective approach to improve the long-term durability of HCC while promoting the high-value utilization of solid waste.
Im Rahmen eines Kooperationsprojekts mit der Schottel GmbH wurde eine bauteilnahe Probengeometrie entwickelt, mit der sich unter Verwendung einer einachsigen Prüfmaschine das Spannungstiefenprofil in dem unter überlagerter Biege- und Zugspannung beanspruchtem Querschnitt im Schweißnahtübergang des Bauteils reproduzieren ließ.
Proben dieser Geometrie wurden vom Kooperationspartner im geschweißten bzw. geschweißten und spannungsarmgeglühten Zustand bereitgestellt. An der BAM wurden je Wärmebehandlungszustand mittels Senkerodieren zwei verschiedene künstliche Defektgeometrien im Schweißnahtübergang eingebracht.
Anhand der Proben wurden experimentell für alle vier Probenzustände Wöhlerlinien für ein Spannungsverhältnis von R = 0,1 ermittelt.
Zusätzlich wurde das u.a. an der BAM entwickelte IBESS-Verfahren angewandt, um die Wöhlerlinien analytisch zu bestimmen. Hierbei wurde eine sehr gute Übereinstimmung von Berechnung und Experiment erreicht, wobei die Berechnung zu einer leicht konservativen Lebensdauervorhersage führte.
Ultrasonic guided waves interacting with complex geometrical features are of high interest in the SHM field. For example, investigations into the extent to which a small change in defect geometry affects wave propagation have applications in Probability of Detection and defect reconstruction. These fields have to be supported by numerical tools aiming to retrieve accurate and reliable results and, thus, more realistic modeling.
Due to the short wavelengths of ultrasonic waves and the relatively large domains in which the waves propagate, fine grid resolution for the entire domain is usually not possible due to limited computational resources. One solution is to partition the domain into different subdomains and use a specific, efficient approach for each subdomain.
This contribution shows a combination of methods that aims to study these wave defect interactions in an elastic media. Firstly we introduce high-order 3D meshes that can resolve very fine geometrical details and are based on an Octree discretisation technique that employs special transition shape functions to resolve the hanging nodes that may appear due to the nature of the method. Afterward, the Octree mesh is embedded in a prismatic wave-guide based on the semi-analytical formulation of the SBFEM in 3D. To couple the different domains, we employ the mortar method, which enforces the continuity of the wave field across the internal boundaries of the domains. Examples show the power of the approach especially when it comes to parametric analysis.