Material
Filtern
Erscheinungsjahr
- 2019 (8) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (6)
- Vortrag (2)
Sprache
- Englisch (8)
Schlagworte
- Indium phosphide (6)
- Quantum dots (5)
- Cytotoxicity (2)
- Gallium doping (2)
- Core-shell structures (1)
- EXAFS (1)
- Gold nanoclusters (1)
- Lead-free (1)
- Perovskite (1)
- Photostability (1)
Organisationseinheit der BAM
- 1 Analytische Chemie; Referenzmaterialien (8) (entfernen)
Eingeladener Vortrag
- nein (2)
Eu2+ is used to replace toxic Pb2+ in metal halide perovskite nanocrystals (NCs). The synthesis implies injection of cesium oleate into a solution of europium (II) bromide at an experimentally determined optimum temperature of 130 ○C and a reaction time of 60 s. Structural analysis indicates the formation of spherical CsEuBr3 nanoparticles with a mean size of 43 ± 7 nm. Using EuI2 instead of EuBr2 leads to the formation of 18-nm CsI nanoparticles, while EuCl2 does not show any reaction with cesium oleate forming 80-nm EuCl2 nanoparticles.
The obtained CsEuBr3 NCs exhibit bright blue emission at 413 nm (FWHM 30 nm) with a room temperature photoluminescence quantum yield of 39%. The emission originates from the Laporte-allowed 4f7–4f65d1 transition of Eu2+ and shows a PL decay time of 263 ns.
The long-term stability of the optical properties is observed, making inorganic lead-free CsEuBr3 NCs promising deep blue emitters for optoelectronics.
Semiconductor nanocrystals (quantum dots, QDs) are well known for their superior optoelectronic properties and enabled advancements in several key technologies of the 21st century. II-VI QDs containing the heavy metal element cadmium plaid a central role in this research area. Due to the concerns regarding their toxic potential, the European Union will ban cadmium in 2020 from use in any consumer product.
Due to their comparable optoelectronic properties and a more environmentally friendly character, indium phosphide based QDs (InP-QDs) are a promising alternative. Their large application potential was already shown in their utilization in the newest commercial TV screens. A vital role for highly luminescent QDs for such an application plays the growth of a surface passivating shell around the InP core. The combination of InP/ZnSe/ZnS in so-called core/shell/shell materials exploits the advantages of a small lattice mismatch (3.3%) between InP and ZnSe and the large band gap of ZnS to efficiently confine the excitons in the core and to increase the overall chemical stability. Using a thin ZnSe layer and a thick ZnS shell has shown to improve the optical properties of InP QDs and only recently, the prevention of blinking and mono-exponential decay kinetics could be achieved with a thick ZnSe Shell.
In our contribution, we investigated the influence of the thickness of the intermediate ZnSe layer (1 to 8 monolayers (ML)) on the photophysical properties of InP/ZnSe/ZnS core/shell/shell QDs with a final size of about 10 nm on the ensemble and the single-particle level. By rendering these InP QDs water-soluble, we were able to compare their properties in the organic and aqueous phase and further studied their toxicological potential depending on the chemical composition of their surface shell.
Semiconductor nanocrystals (quantum dots, QDs) are well known for their superior photophysical properties and enabled advancements in several key technologies of the 21st century and numerous technological applications. However, the most studied II-VI semiconductor nanocrystals contain the toxic heavy metal element cadmium, which is limiting their utilization in commercial applications. This has drawn the interest to alternative materials with less toxicity but having similar photophysical features.
The newest generation of TV screens based on QDs have shown that there is a promising environmentally friendly alternative with similar optoelectronic properties, namely indium phosphide (InP) QDs. InP QDs possess a bulk band gap of 1.35 eV with an exciton Bohr radius of ca. 10 nm and thus allow to tune their photoluminescence (PL) from the visible to the near-infrared. Tuning the size and shape of InP QDs and thus tailor their optoelectronic properties can be achieved by different strategies, which range from different types and concentrations of precursors, synthesis temperature or post-synthetic manipulations like etching. The incorporation of other elements like Gallium within the InP core synthesis is another possibility. Using a GaP intermediate layer before growing a ZnS shell has been shown to increase the PL quantum yield, which has been attributed to reduced lattice strain and the removal of phosphor vacancies. Different Ga precursors were investigated but a thorough investigation in terms of their reactivity, localization in the QD and influence on the photophysical properties is lacking to date.
In this contribution we will present the detailed investigation of the presence of two different Ga precursors within the InP core synthesis. Photophysical characterizations (steady-state and PL life-time measurements), transmission electron microscopy, XRD and EDX gave insights into the reactivity of the Ga precursors, the Ga localization in the InP core and influences on the photophysical properties. The variation of the precursor and surfactant concentration and the utilization of different ligands for the Ga precursor allowed tuning the PL emission towards the blue or the red. Depending on the used precursor type we observed the formation of larger-sized InP/GaP core/shell nanocrystals or the formation of InGaP alloy structures enabling to assess the blue range of emission (475 nm).
In Vivo Biotransformations of Indium Phosphide Quantum Dots Revealed by X‑Ray Microspectroscopy
(2019)
Many attempts have been made to synthesize cadmium-free quantum dots
(QDs), using nontoxic materials, while preserving their unique optical properties. Despite impressive advances, gaps in knowledge of their intracellular fate, persistence, and excretion from the targeted cell or organism still exist, precluding clinical applications. In this study, we used a simple model organism (Hydra vulgaris) presenting a tissue grade of organization to determine the biodistribution of indium phosphide (InP)-based QDs by X-ray fluorescence imaging. By complementing elemental imaging with In L-edge X-ray absorption near edge structure, unique information on in situ chemical speciation was obtained. Unexpectedly, spectral profiles indicated the appearance of In−O species within the first hour post-treatment, suggesting a fast degradation of the InP QD core in vivo, induced mainly by carboxylate groups. Moreover, no significant difference in the behavior of bare core QDs and QDs capped with an inorganic Zn(Se,S) gradient shell was observed. The results paralleled those achieved by treating animals with an equivalent dose of indium salts, confirming the preferred bonding type of In3+ ions in Hydra tissues. In conclusion, by focusing on the chemical identity of indium along a 48 h long journey of QDs in Hydra, we describe a fast degradation process, in the absence of evident toxicity. These data pave the way to new paradigms to be considered in the biocompatibility assessment of QD-based biomedical applications, with greater emphasis on the dynamics of in vivo biotransformations, and suggest strategies to drive the design of future applied materials for nanotechnology-based diagnosis and therapeutics.
With the goal to improve their photostability, InP-based QDs are passivated with three types of inorganic shells, namely (i) a gradient ZnSexS1−x shell, (ii) an additional ZnS shell on top of the gradient shell with two different thicknesses (core/shell/shell, CSS), (iii) an alumina coating on top of ZnS. All three systems have photoluminescence Quantum yields (PLQY) > 50%and similar PL decay times (64–67 ns). To assess their photostability they are incorporated into a transparent poly (methyl methacrylate) (PMMA) matrix and exposed to continuous irradiation with simulated sunlight in a climate chamber. The alumina coated core/shell system exhibits the highest stability in terms of PLQY Retention as well as the lowest shift of the PL maximum and lowest increase of the PL linewidth, followed by the CSS QDs and finally the gradient shell system. By means of XPS studies we identify the degradation of the ZnS outer layer and concomitant xidation of the emissive InZnP core as the main origins of degradation in the gradient structure. These modifications do not occur in the case of the alumina-capped sample, which exhibits excellent chemical stability. The gradient shell and CSS systems could be transferred to the aqueous phase using surface ligand exchange with penicillamine. Cytotoxicity studies on human primary keratinocytes revealed that exposure for 24 h to 6.25–100 nM of QDs did not affect cell viability. However, a trend toward reduced cell proliferation is observed for higher concentrations of gradient shell and CSS QDs with a thin ZnS shell, while CSS QDs with a thicker ZnS shell do not exhibit any impact.
Due to their unique optical properties, quantum dots (QDs) are used in a number of optoelectronic devices and are forecasted to be used in the near future for biomedical applications. The most popular QD composition consists of cadmium selenide (CdSe) or cadmium telluride (CdTe), which has been shown to pose health risks due to the release of toxic cadmium (Cd) ions. Due to similar optical properties but lower intrinsic toxicity, indium phosphide (InP) QDs have been proposed as a safer alternative. Nevertheless, investigations regarding their safety and possible toxicological effects are still in their infancy.
The fate and toxicity of seven different water-dispersible indium (In) based QDs, either pristine or after ageing in a climatic chamber, was evaluated. The core of these QDs was composed of indium, zinc and phosphorus (InZnP) or indium, zinc, phosphorus and sulfur (InZnPS). They were assessed either as core-only or as core-shell QDs, for which the core was capped with a shell of zinc, selenium and sulfur (Zn(Se,S)). Their Surface was functionalized using either penicillamine or glutathione.
In their pristine form, these QDs showed essentially no cytotoxicity. The particular case of InZnPS QD showed that core-shell QDs were less cytotoxic than core-only QDs. Moreover, surface functionalization with either penicillamine or glutathione did not appreciably influence cytotoxicity but affected QD stability. These QDs did not lead to over-accumulation of reactive oxygen species in exposed cells, or to any oxidative damage to cellular DNA. However, accelerated weathering in a climatic chamber led to QD precipitation and degradation, together with significant cytotoxic effects. Ageing led to dissociation of IneP and ZneS bonds, and to complexation of In Zn ions with carboxylate and/or phosphate moieties.
These results show that InZnP and InZnPS alloyed QDs are safer alternatives to CdSe QDs. They underline the necessity to preserve as much as possible the structural integrity of QDs, for instance by developing more robust shells, in order to ensure their safety for future applications.
Gallium – a versatile element for tuning the photoluminescence properties of InP quantum dots
(2019)
With the goal to tune the emission properties of colloidal InP quantum dots, the incorporation of Ga was explored. Unexpectedly, depending on the nature of the gallium precursor, the photoluminescence shifted either to the red (gallium oleate) or to the blue (gallium acetylacetonate). In the first case, larger-sized InP/GaP core/shell nanocrystals were formed, while in the second case the formation of an InGaP alloy structure enabled the blue range of emission (475 nm) to be accessed.
High photoluminescence of shortwave infrared-emitting anisotropic surface charged gold nanoclusters
(2019)
Incorporating anisotropic surface charges on atomically precise gold nanoclusters (Au NCs) led to a strong absorption in the nearinfrared region and could enable the formation of self-assembled Au NCs xhibiting an intense absorption band at ∼1000 nm. This surface modification showed a striking enhancement of the photoluminescence in the Shortwave Infrared (SWIR) region with a quantum yield as high as 6.1% in water.