Umwelt-Material-Interaktionen
Filtern
Erscheinungsjahr
- 2021 (12) (entfernen)
Dokumenttyp
- Vortrag (10)
- Zeitschriftenartikel (1)
- Beitrag zu einem Tagungsband (1)
Schlagworte
- Deckschichtbildung (5)
- Gelartige Elektrolyte (5)
- Zink (5)
- Atmosphärische Korrosion (3)
- Korrosion (3)
- Biodiesel (2)
- Corrosion (2)
- FAME (2)
- Korrosionsuntersuchungen (2)
- Normung (2)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (12) (entfernen)
Eingeladener Vortrag
- nein (10)
Geothermal brines often contain high amounts of lead and copper ions that can precipitate as native Cu and Pb as consequence of galvanic corrosion when brines react with carbon steel materials. This contribution evaluates which materials could overcome the problem of galvanic corrosion at geothermal environment.
The behavior of these materials in water containing high chloride concentration (> 100 g/L NaCl) as well as various amounts of dissolved bCl2 and/or CuCl2 was characterized by electrochemical and exposure measurements.
Both methods reveal carbon steel suffers corrosion susceptibility, accompanied by Cu◦ and/or Pb◦ precipitation on the surface. Electrochemical measurements on stainless steels result in significant difference in corrosion and repassivation potentials (Ecorr = -189 mV, Erep = 70 mV), indicating a good corrosion resistance.
For centuries, churches, secular buildings and museums have been furnished with valuable works of art. Many works of art are UV- and light-sensitive. It is well known that especially UV radiation causes damage and discoloration in paintings, textiles, plastics, wood and other materials. In particular, the wavelengths between 280 and 410 nm cause color changes, embrittlement or destruction of e.g. plastics over time. Therefore, strongly UV-absorbing glasses are advantageous for architecture and are necessary for the protection of cultural assets. As restorers in all disciplines become more and more aware, the demands placed on buildings and their furnishings in terms of climate are becoming increasingly detailed and precise. The aim in each case is to preserve the valuable artwork.
For some years now, the industry has been offering the protection of cultural objects by installing special UV-protective glasses. Currently, UV protection for church buildings is realized by laminated safety glass equipped with appropriate UV-protective plastic films. Technically, this always means a second pane of glass in front of the windows, which is installed outside the building. This creates climatic gaps that are difficult to control and deterioration due to ageing effects can be expected. At the same time, this protective glazing is not invisible and has a considerable aesthetic influence on the interior and exterior appearance of the building. Meanwhile, the preservation of historical monuments accepts such aesthetic cuts on buildings in order to protect the artwork in the interior from UV light. To this day, however, the long-term durability of UV protection provided by inserted plastic films is still controversial.
To date the only available alternative on the market is a mouth-blown UV protection glass which uses a so-called overlay to provide UV protection. This shows that UV protection can also be achieved by glasses without plastic films thus realizing an exclusive inorganic protection which normally is more stable than a polymeric one. So far there are not enough studies to prove long-term durability.
The aim of this project is to provide existing glazing or new glazing to be created with a highly transparent layer that ensures this UV-protective filter function below 400 nm. The glass coating is to be applied to the glass over a large area and fired into the surface like a classic ceramic enamel paint with the same technics. In addition, it should be long-term durable in its function. It means, that the glass has to be fused at temperatures below 630 °C during the firing process, its chemical durability has to be high, its coefficient of thermal expansion has to be as close as the one of the substrate (usually float glass) and the glass has to absorb the UV-radiation within a thin thickness (thinner as 100 µm).
In this project, the long-term durability of commercial UV-protective glasses is examined. New low melting glasses containing UV-absorbing ions are being developed. Their UV-absorption as a thin layer is analyzed as well as their chemical durability and their thermal properties.
We are grateful to BMWI for the financial support in the frame of the Central Innovation Programme for SMEs (ZIM).
Biodiesel (FAME) from rapeseed is an environmentally friendly alternative to common fossil fuels. It is also suitable to serve as blending component to fuels like heating oil. If the fuel composition is changed, materials compatibility must be guaranteed. Adding polar biodiesel to nonpolar heating oil, changes the blend’s solvency and might cause swelling, extraction and solvation of polymers. The objective of this research was to investigate the compatibility of polymeric materials, which are commonly used for components in middle distillate facilities, along with blends of heating oil and 20 % biodiesel (B20). For this propose, ACM, HNBR, FKM, PE, PA 6, POM, PUR and PVC were exposed to heating oil and B20 for 42 and 84 days at 40 °C. In addition, the polymers HNBR, FKM, PA, POM and PVC were also exposed at 70 °C. Furthermore, the resistance of polymers in eight-year aged B10 at 40 °C was evaluated. Ageing of biodiesel increases acidity which might propagate polymer corrosion. The materials were evaluated as resistant, if the loss in tensile properties (tensile strength and elongation at break) and Shore hardness remained under 15 % compared to the initial unexposed material values. For investigations under compressed conditions, the compression set was determined for specimens of ACM, FKM and HNBR after exposure in heating oil B0 and B20 for 3,7,14, 28, 56 and 90 days at 40 °C according to ISO 815-1. It was found that the resistance in B20 at 40 °C was given for all tested polymers except PUR. In the 8 years aged B10, PUR and POM were not compatible and ACM just conditionally compatible. At 70 °C, FKM and PVC were resistant in B20, whereas HNBR and PA 6 were not compatible. Swelling occurred for the elastomers ACM, HNBR and PUR.
Der Fachbereich 7.6 untersucht seit einiger Zeit an Auslagerungsständen auf dem Testgelände in Horstwalde Korrosion im maritimen Bereich. Im Moment läuft das System mit künstlichem Meerwasser und simuliert die Bewitterung von Metallproben unter angenäherten klimatischen Bedingungen ähnlich zum natürlichem Habitat. Im Laufe der Zeit konnte nicht intendierter mikrobieller bewuchs beobachtet werden. Es stellte sich die Frage, welche Mikroorganismen vorlagen und ob diese einen Einfluss auf die Korrosionsuntersuchungen haben könnte. Aus diesem Grund wurden 16S-rRNA Untersuchungen durchgeführt welche alle drei Domänen des Lebens widerspiegeln Bakterien, Archaea und Eukaryoten. Es konnte gezeigt werden, dass über 95% der vorliegenden Biomasse Grünalgen waren, die durch Licht Eintrag in den Container Photosynthese betrieben und dadurch an Biomasse zunahmen. Des weiteren konnten Bakterien detektiert werden, welche in der Regel halophilen und aeroben Habitaten zu finden sind. Allerdings wurden auch Sulfat reduzierende Bakterien (MIC) detektiert, wenn auch in einem geringen prozentualen Anteil. Es muss allerdings Berücksichtigt werden, dass die mikrobielle Zusammensetzung sich im Laufe der Zeit weiter ändern kann. Als Ursprung der Biomasse wird, das künstliche Sediment vermutet. Außerdem wäre es für zukünftige Experiment denkbar, das System mit echtem Sediment aus dem marinen Habitat anzuimpfen.
Biodiesel (FAME) from rapeseed is an environmentally friendly alternative to common fossil fuels. It is also suitable to serve as blending component to fuels like heating oil. If the fuel composition is changed, materials compatibility must be guaranteed. Adding polar biodiesel to nonpolar heating oil, changes the blend’s solvency and might cause swelling, extraction and solvation of polymers.
The objective of this research was to investigate the compatibility of polymeric materials, which are commonly used for components in middle distillate facilities, along with blends of heating oil and 20 % biodiesel (B20). For this propose, ACM, HNBR, FKM, PE, PA 6, POM, PUR and PVC were exposed to heating oil and B20 for 42 and 84 days at 40 °C. In addition, the polymers HNBR, FKM, PA, POM and PVC were also exposed at 70 °C. Furthermore, the resistance of polymers in eight-year aged B10 at 40 °C was evaluated. Ageing of biodiesel increases acidity which might propagate polymer corrosion.
The materials were evaluated as resistant, if the loss in tensile properties (tensile strength and elongation at break) and Shore hardness remained under 15 % compared to the initial unexposed material values. For investigations under compressed conditions, the compression set was determined for specimens of ACM, FKM and HNBR after exposure in heating oil B0 and B20 for 3,7,14, 28, 56 and 90 days at 40 °C according to ISO 815-1.
It was found that the resistance in B20 at 40 °C was given for all tested polymers except PUR. In the 8 years aged B10, PUR and POM were not compatible and ACM just conditionally compatible. At 70 °C, FKM and PVC were resistant in B20, whereas HNBR and PA 6 were not compatible. Swelling occurred for the elastomers ACM, HNBR and PUR.
Die Untersuchungen und Ausführungen im Vortrag belegen, dass verfügbare Modellvorstellungen zur Beschreibung der Deckschichtbildung und Korrosion von Zink unter aktuellen atmosphärischen Bedingungen in Europa nicht mehr gültig sind und neu bewertet werden müssen. So können beispielsweise bisher verfügbare Prognosemodelle den Korrosionsfortschritt nicht mehr ausreichend beschreiben, da durch die Verringerung des Schwefeldioxidgehaltes der Luft veränderte Mechanismen vorliegen.