For intumescent coatings durability is an important aspect. Due to ageing, which is caused by climatic conditions, the thermal protection performance of intumescent coatings can be reduced during the working life. The national German and the European procedures to assess the durability of intumescent coatings presume a working life of 10 years. For a longer period, additional investigations are required. However, the European assessment procedure does not provide specific information how to prove a durability of more than 10 years. In addition to this formal reason, also from a scientifical position, it is necessary to investigate the degradation of intumescent coatings in detail to propose a corresponding test concept for a durability of more than 10 years.
The presentation summarises the existing knowledge about the degradation behaviour and ageing of intumescent coatings. Furthermore, the results of different approaches from a recently conducted research project are presented. Starting from a water-based and an epoxy-based guide formulation, in a first approach a degradation of the intumescent coating was carried out directly during the production process, i.e. by reducing the concentration of functionally relevant chemical components. In another approach, the duration of the short-term weathering tests was significantly extended, i.e. by multiple repetition of the artificial weathering. The thermal protection performance of the intumescent coating was assessed by fire tests and tests with electrical heating source. In addition, small-scale tests were carried out to determine the thermal material properties of the intumescent coating and thermo-analytical methods were applied to characterise the degradation. Derived from this knowledge, possibilities to test and assess a working life for a period of more than 10 years are proposed.
From halogenated flame retardants to non-halogenated to nanocomposites, each milestone in flame retardancy research led to an increase in performance and safety. With the rise of ceramic precursors in flame retardants, a new field of applications in extreme fire scenarios has become accessible. Intumescent coatings combined with precursors for ceramics show a high temperature transition to a ceramic foam, which provides much better fire resistance than conventional coatings at temperatures beyond 1200°C. Even a protection at 2000 °C for several minutes can be achieved. Combining the expansion property of traditional intumescent coatings with a ceramification at high temperatures leads to high-performance coatings, whose unique properties may prove useful for emergency insulation systems for re-entry bodies in the aerospace industry or special fire protection applications.
In this study, the protection performance in extreme fire conditions, the development of the expansion and the following ceramic transition of a high-performance coating are investigated. To this end, a small scale high-performance burner setup was created. The coated (2.5/4 mm) steel plates (75 x 75 x 2 mm) were exposed to direct flame treatment of a propane-oxygen-burner controlled by two flow controllers. During the test, temperatures above of 1800 °C were reached and steel and flame temperature were recorded. Fire tests of different durations (1, 2.5, 5, 10 and 20 min) were performed. The residues of the different development stages were analysed with non-destructive µ-computed tomography and scanning electron microscopy. The 3D images of the computed tomography provide an insight into the developing cell structure and state of ceramification of the residues.