9.2 Versuchsanlagen und Prüftechnik
Filtern
Dokumenttyp
Schlagworte
- Residual stress (3)
- Abdichtbauwerk (2)
- Additive manufacturing (2)
- Bohrlochsonde (2)
- IN718 (2)
- Neutron diffraction (2)
- Selective laser melting (2)
- Ultraschall-Echoverfahren (2)
- Verschlussbauwerk (2)
- Zerstörungsfreie Prüfung (2)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (7) (entfernen)
Influence of Surface Preparation on Cracking Phenomena in TIG-Welded High and Medium Entropy Alloys
(2022)
Multi-element systems with defined entropy (HEA—high entropy alloy or MEA—medium entropy alloy) are rather new material concepts that are becoming increasingly important in materials research and development. Some HEA systems show significantly improved properties or combinations of properties, e.g., the overcoming of the trade-off between high strength and ductility. Thus, the synthesis, the resulting microstructures, and properties of HEA have been primarily investigated so far. In addition, processing is crucial to achieve a transfer of potential HEA/MEA materials to real applications, e.g., highly stressed components. Since fusion welding is the most important joining process for metals, it is of vital importance to investigate the weldability of these materials. However, this has rarely been the subject of research to date. For that reason, in this work, the weldability depending on the surface preparation of a CoCrFeMnNi HEA and a CoCrNi MEA for TIG welding is investigated. The fusion welding of longer plates is described here for the first time for the CoCrNi alloy. The welds of both materials showed distinct formation of cracks in the heat affected Zone (HAZ). Optical and scanning electron microscopy analysis clearly confirmed an intergranular fracture topography. However, based on the results, the crack mechanism cannot be conclusively identified as either a liquid metal embrittlement (LME) or hot cracking-like liquid film separation.
Entwicklung einer Bohrlochsonde für Ultraschalluntersuchungen an Abschlussbauwerken in Endlagern
(2021)
Für die Qualitätssicherung von Abschlusswerken für Endlager wird eine Ultraschall-Bohrlochsonde entwickelt. Mithilfe dieser Sonde, die aus einer Vielzahl von einzelnen koppelmittelfreien Ultraschall-Punktkontaktprüfköpfen besteht, soll die Rissfreiheit der Versuchsbauwerke überprüft werden.
Ein erster Prototyp der Sonde wurde mit einem kommerziellen Ultraschallgerät betrieben und bestand aus 12 Transversalwellen-Punktkontaktprüfköpfen von denen jeweils sechs als Sender und sechs als Empfänger parallelgeschaltet waren. Um den erzeugten Schalldruck der Bohrlochsonde zu steigern, wurde bei der Neuentwicklung die Prüfkopfanzahl erhöht und zusätzlich die laufzeitgesteuerte Anregung der einzelnen Prüfköpfe vorgesehen. Für die Anregung der Prüfköpfe mit programmierten Zeitverzögerungen wurde ein neuartiger mehrkanaliger Sender für bipolare Rechtecksignale entwickelt.
Durch die Entwicklung der Bohrlochsonde soll eine dynamische Anpassung der Prüfkopf-Apertur sowie eine Fokussierung des Schallfeldes in Abhängigkeit der zu untersuchenden Tiefe erfolgen. Mithilfe entsprechender Anregungsfunktionen kann das Schallfeld der Bohrlochsonde unterschiedlich geformt werden, z. B. ist auch ein Schwenken des fokussierten Schallbündels möglich. Dadurch wird das erfasste Prüfvolumen begrenzt und auf diese Weise das Signal-Störverhältnis der Empfangssignale verbessert. In Kombination mit SAFT-Rekonstruktionsrechnungen wird durch eine optimierte Abstrahlcharakteristik der Sonde mit einem hohen Schalldruck unter verschiedenen Winkeln eine verbesserte Signalqualität und damit eine erhöhte Aussagesicherheit der Ergebnisse in der Objektabbildung erwartet.
Entwicklung einer Bohrlochsonde für Ultraschalluntersuchungen an Abschlussbauwerken in Endlagern
(2021)
Für die Qualitätssicherung von Abschlusswerken für Endlager wird eine Ultraschall-Bohrlochsonde entwickelt. Mithilfe dieser Sonde, die aus einer Vielzahl von einzelnen koppelmittelfreien Ultraschall-Punktkontaktprüfköpfen besteht, soll die Rissfreiheit der Versuchsbauwerke überprüft werden.
Ein erster Prototyp der Sonde wurde mit einem kommerziellen Ultraschallgerät betrieben und bestand aus 12 Transversalwellen-Punktkontaktprüfköpfen von denen jeweils sechs als Sender und sechs als Empfänger parallelgeschaltet waren. Um den erzeugten Schalldruck der Bohrlochsonde zu steigern, wurde bei der Neuentwicklung die Prüfkopfanzahl erhöht und zusätzlich die laufzeitgesteuerte Anregung der einzelnen Prüfköpfe vorgesehen. Für die Anregung der Prüfköpfe mit programmierten Zeitverzögerungen wurde ein neuartiger mehrkanaliger Sender für bipolare Rechtecksignale entwickelt.
Durch die Entwicklung der Bohrlochsonde soll eine dynamische Anpassung der Prüfkopf-Apertur sowie eine Fokussierung des Schallfeldes in Abhängigkeit der zu untersuchenden Tiefe erfolgen. Mithilfe entsprechender Anregungsfunktionen kann das Schallfeld der Bohrlochsonde unterschiedlich geformt werden, z. B. ist auch ein Schwenken des fokussierten Schallbündels möglich. Dadurch wird das erfasste Prüfvolumen begrenzt und auf diese Weise das Signal-Störverhältnis der Empfangssignale verbessert. In Kombination mit SAFT-Rekonstruktionsrechnungen wird durch eine optimierte Abstrahlcharakteristik der Sonde mit einem hohen Schalldruck unter verschiedenen Winkeln eine verbesserte Signalqualität und damit eine erhöhte Aussagesicherheit der Ergebnisse in der Objektabbildung erwartet.
The residual stress distribution in IN718 elongated prisms produced by Selective Laser Melting was studied by means of neutron (bulk) and laboratory X-ray (surface) diffraction.
Two deposition hatch lengths were considered. A horizontal plane near the top surface (perpendicular to the building direction) and a vertical plane near the lateral surface (parallel to the building direction) were investigated. Samples both in as-built (AB) condition and removed (RE) from the base plate were characterized.
While surface stress fields seem constant for AB condition, X-ray diffraction shows stress gradients along the hatch direction in the RE condition. The stress profiles correlate with the distortion maps obtained by tactile probe measurements.
Neutron diffraction shows bulk stress gradients for all principal components along the main sample directions. We correlate the observed stress patterns with the hatch length, i.e. with its effect on temperature gradients and heat flow. The bulk stress gradients partially disappear after removal from the baseplate.
Giant magneto-resistive (GMR) sensor based metal magnetic memory (MMM) technique is proposed for mapping of deformation-induced self-magnetic leakage fields (SMLFs) in carbon steel. The specimens were subjected to different amounts of tensile deformation and the deformation-induced SMLFs were measured using a GMR sensor after unloading the specimens. 3D-nonlinear finite element modeling was performed to predict stress–strain state in a steel specimen under tensile load. The experimentally obtained SMLF images were correlated with the finite element model predicted stress–strain states. Studies reveal that the MMM technique can detect the plastic deformation with signal-to-noise ratio better than 20 dB. The technique enables the mapping of plastic deformation in carbon steels for the evaluation of the severity of deformation. The study also reveals that deformation-induced SMLF is influenced by the presence of initial surface residual stress, introduced by shot peening. The intensity of SMLF signal is found to increase with increase in tensile load and decrease with shot peening.
Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing.
The residual stress distribution in the bulk of IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-build condition (on a build plate) and after removal from the build plate.
The absolute values of all stress components decreased after removal from the build plate. Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component depending on the thermal gradient in the respective direction.
Influence of deposition hatch length on residual stress in selective laser melted Inconel 718
(2018)
The present study aims to evaluate the bulk residual stresses in SLM parts by using neutron diffraction measurements performed at E3 line -BER II neutron reactor- of Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. Together with microstructure characterization and distortion measurements, it is possible to describe the stress state throughout the whole sample. The sample was measured in as-build condition (on a build plate) and after releasing from the build plate. The used material is the nickel based superalloy 718. This alloy is widely used in aerospace and chemical industries due to its superior corrosion and heat resistant properties.
Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component. The normal and transversal component exhibits a rather compressive behavior while the longitudinal was tensile in the center part of the sample and became compressive towards the tip. As expected, the absolute values of all stress components decreased after releasing the sample from the building plate. A surface scan utilizing a coordinate-measuring machine (CMM) allowed us to present top surface distortion before and after releasing. The top surface showed a distortion around ±80µm after releasing. Microstructure evolution in the scanning-building cross-section is largely dominated by columnar grains. In addition, many small random orientated grains are prominent in the regions of a laser overlap during SLM.
In summary, for the sample of superalloy 718 manufactured by SLM, a small distortion occurred when removing the sample from the build plate whereby the residual stress state decreases. Moreover, the observed columnar grains in the building direction could give a reason for the lowest stress values in that normal direction. However, the most important parameter controlling the residual stresses is the temperature gradient. Hence, future investigations are planned for a different scan strategy to distribute the laser impact in a more homogenous manner.