9 Komponentensicherheit
Filtern
Erscheinungsjahr
- 2018 (183) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (76)
- Vortrag (61)
- Beitrag zu einem Tagungsband (31)
- Posterpräsentation (12)
- Buchkapitel (1)
- Dissertation (1)
- Sonstiges (1)
Sprache
- Englisch (183) (entfernen)
Schlagworte
- Hydrogen (19)
- Friction (18)
- Niobium carbide (18)
- Wear (18)
- Welding (17)
- Additive manufacturing (15)
- Residual stress (13)
- High-strength steels (9)
- Laser metal deposition (9)
- Microstructure (9)
Organisationseinheit der BAM
- 9 Komponentensicherheit (183)
- 9.5 Tribologie und Verschleißschutz (57)
- 9.4 Integrität von Schweißverbindungen (52)
- 9.3 Schweißtechnische Fertigungsverfahren (51)
- 5 Werkstofftechnik (21)
- 9.0 Abteilungsleitung und andere (20)
- 8 Zerstörungsfreie Prüfung (19)
- 6 Materialchemie (16)
- 9.2 Versuchsanlagen und Prüftechnik (12)
- 5.0 Abteilungsleitung und andere (10)
Eingeladener Vortrag
- nein (61)
The wear rates of self-mated alumina couples show that friction as well as wear is largely determined by the above-mentioned hydro-thermal conditions. The presence of water and its amount available in the surrounding system either in liquid or in gaseous form plays a key role for friction and wear behavior and can be beneficial for the tribological profile of steam degradation resistant materials. Hot steam enhances the tribo-chemical formations of oxides and hydroxides on MgO-ZrO2 alumina and antimony impregnated carbon.
The steam technology has attracted attention for recovering energy from waste heat in transportation systems. 40% of the calorific value of the fuel is wasted through the tailpipe. The use of waste heat recovery systems (WHRS) in cars and especially in trucks corresponds to possible energy savings in terms of less fuel consumption in the range of 7 – 18 %. This relates not only to the savings of fuel but also to the non-production of green house gas CO2. Steam expander form tribosystems, which can´t be lubricated with oils, as hot steam hydro-cracks these fluids. Suited tribomaterials as well as their tribo-oxidatively reaction layers must be first steam degradation resistant and for the tribotesting of such candidate material, tribological testing devices for a hot steam environment are needed. Not much is known so far about the tribological properties of any material system running under pressurized hot steam conditions. For these reasons and for being able to evaluate tribological properties in hot steam, BAM has developed and built a new and sealed tribometer for hot steam allowing evaluating tribological properties up to 700°C and 10 bars in gaseous atmospheres like hot steam or ethanol.
Experimental results on the wear of self-mated aluminum oxide and MgO-ZrO2 couples show that friction as well as wear is largely determined by the above mentioned hydro-thermal conditions. In this system the presence of water and its amount available in the system either in liquid or in gaseous form plays a key role for wear behavior and can beneficial. Ethanol and/or water-ethanol mixtures can form beneficial tribofilms, also on specific diamond-like carbon films.
In a first test series, the friction and wear properties of 6 polymeric candidate materials for application in LNG tribosystems were tested. The most favorable properties showed PTFE composite, filled with carbon fibers and PEEK, which showed low and stable friction and a wear coefficient in the order of 10-7 mm3N-1m-1. PTFE containing PEEK composites seem to be also appropriate for LNG applications. Admixtures of graphite as solid lubricant result in lower wear. Contrary, a lubricating mechanism of MoS2 was not observed. The PI-materials showed comparatively high friction and medium wear.
In a first test series, the friction and wear properties of 6 polymeric candidate materials for application in LNG tribosystems were tested. The most favorable properties showed PTFE composite, filled with carbon fibers and PEEK, which showed low and stable friction and a wear coefficient in the order of 10-7 mm3N-1m-1. PTFE containing PEEK composites seem to be also appropriate for LNG applications. Admixtures of graphite as solid lubricant result in lower wear. Contrary, a lubricating mechanism of MoS2 was not observed. The PI-materials showed comparatively high friction and medium wear.
Commercial grade-1 titanium samples (Ti, 99.6%) were treated using three alternative methods, (i) femtosecond laser processing, (ii) thermal heat treatment, and (iii) electrochemical anodization, respectively, resulting in the formation of differently conditioned superficial titanium oxide layers. The laser processing (i) was carried out by a Ti:sapphire laser (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz) in a regime of generating laser-induced periodic surface structures (LIPSS). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning setup for the processing of several square-millimeters large surface areas covered homogeneously by these nanostructures. The differently oxidized titanium surfaces were characterized by optical microscopy, micro Raman spectroscopy, variable angle spectroscopic ellipsometry, and instrumented indentation testing. The tribological performance was characterized in the regime of mixed friction by reciprocating sliding tests against a sphere of hardened steel in fully formulated engine oil as lubricant. The specific tribological performance of the differently treated surfaces is discussed with respect to possible physical and chemical mechanisms.
Additive manufacturing (AM) opens the route to a range of novel applications.However, the complexity of the manufacturing process poses a challenge for the production of defect-free parts with a high reliability. Since process dynamics and resulting microstructures of AM parts are strongly influenced by the involved temperature fields, thermography is a valuable tool for process surveillance. The high process temperatures in metal AM processes allow one to use cameras usually operating in the visible spectral range to detect the thermally emitted radiation from the process. In our work, we compare the results of first measurements during the manufacturing processes of a commercial laser metal deposition (LMD) setup and a laser beam melting (LBM) setup using a MWIR camera with those from a VIS high-speed camera with band pass filter in the NIR range.
The influence of the support structure on residual stress and distortion in SLM Inconel 718 parts
(2018)
The effect of support structure and of removal from the base plate on the residual stress state in selective laser melted IN718 parts was studied by means of synchrotron X-ray diffraction. The residual stresses in subsurface region of two elongated prisms in as-built condition and after removal from the base plate were determined. One sample was directly built on a base plate and another one on a support structure. Also, the distortion on the top surface due to stress release was measured by contact profilometry. High tensile residual stress values were found, with pronounced stress gradient along the hatching direction. In the sample on support, stress redistribution took place after removal from the base plate, as opposed to simple stress relaxation for the sample without support. The sample on support structure showed larger distortion compared to sample without support. We conclude that the use of a support decreases stress values but stress-relieving heat treatments are still needed.
The work presents the procedure developed within the German research project IBESS, which allows for the fracture mechanics-based prediction of the fatigue strength of welded joints under constant amplitude loading. Based on the experimental observations of the crucial failure mechanisms, the approach focuses on the short crack propagation, where elastic-plastic fracture mechanics and the build-up of closure effects must be considered as well as the variability of the local geometry at the weld toe and the modelling of multiple crack interaction. Analytical solutions are provided for the approximation of the through-thickness stress profiles at the weld toe and for the determination of the crack driving force in the form of a plasticity-corrected stress intensity factor range ∆K_p. Proposals for the determination of the initial crack size and the crack closure factor are also included.
The approach is validated against a large number of experimental data, which comprises fatigue tests on individual cracks monitored by heat tinting and beach-marking techniques, as well as stress life curves. Three kinds of welded joints, two steels of significant different strengths and three stress ratios are considered. The results show that the procedure provides good estimations of the statistical distribution of the fatigue strength of welded joints both for the finite and infinite life regime. Furthermore, the predictions are compared with available benchmark data for structural steels.