9 Komponentensicherheit
Filtern
Dokumenttyp
- Vortrag (90)
- Zeitschriftenartikel (46)
- Posterpräsentation (23)
- Beitrag zu einem Tagungsband (17)
- Sonstiges (2)
Schlagworte
- Additive Manufacturing (54)
- Additive manufacturing (42)
- Thermography (31)
- Residual stress (24)
- Additive Fertigung (21)
- Residual Stress (16)
- AGIL (15)
- Neutron diffraction (15)
- Process monitoring (13)
- Laser Powder Bed Fusion (12)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (178) (entfernen)
Eingeladener Vortrag
- nein (90)
The monitoring of oil and gas pipelines by means of distributed fibre optic sensors is becoming common. The most recent development in the field of fibre optic sensing is the distributed acoustic sensing (DAS), which allows to detect and to localize third party threats to pipelines. For this purpose, fibre optic telecommunication cables located close to the pipelines are usually used. However, DAS carries a far greater potential for continuous condition monitoring of pipelines.
The interdisciplinary research project AGIFAMOR (Ageing Infrastructures – Fibre Optic Monitoring of Pipes) at BAM investigates a new technical approach to extend the application field of DAS towards the detection and localization of acoustic signals that indicate critical alterations and certain damage scenarios originated from within the pipeline or the pipe wall. Therefore, the optical fibre sensors are applied onto the pipe itself and the application procedure towards an optimal acoustic signal transduction is optimized.
A number of laboratory scale experiments were performed focusing on the signal transmission of acoustic signals as well as the detection of damage in the pipe wall by means of DAS. Furthermore, real-scale tests on a pipeline DN100 of 38 m length have been carried out at the BAM test site for technical safety (BAM-TTS) to study the detection and localization of leaks and of changing flow profiles due to corrosion or sedimentation processes.
The monitoring of oil and gas pipelines by means of distributed fibre optic sensors is becoming common. The most recent development in the field of fibre optic sensing is the distributed acoustic sensing (DAS), which allows to detect and to localize third party threats to pipelines. For this purpose, fibre optic telecommunication cables located close to the pipelines are usually used. However, DAS carries a far greater potential for continuous condition monitoring of pipelines.
The interdisciplinary research project AGIFAMOR (Ageing Infrastructures – Fibre Optic Monitoring of Pipes) at BAM investigates a new technical approach to extend the application field of DAS towards the detection and localization of acoustic signals that indicate critical alterations and certain damage scenarios originated from within the pipeline or the pipe wall. Therefore, the optical fibre sensors are applied onto the pipe itself and the application procedure towards an optimal acoustic signal transduction is optimized.
A number of laboratory scale experiments were performed focusing on the signal transmission of acoustic signals as well as the detection of damages in the pipe wall by means of DAS. Furthermore, real-scale tests on a pipeline DN100 of 38m length have been carried out at the BAM test site for technical safety (BAM-TTS) to study the detection and localization of leaks and of changing flow profiles due to corrosion or sedimentation processes.
Schäden an Rohrleitungen können zu hohen Umweltbelastungen und wirtschaftlichen Schäden führen. Um die dauerhafte Verfügbarkeit der Infrastruktur zu gewährleisten, wird im Rahmen des Projekts AGIFAMOR an der Bundesanstalt für Materialforschung und -prüfung (BAM) erprobt, inwiefern das Verfahren der verteilten akustischen faseroptischen Sensorik (Distributed acoustic sensing – DAS) zur kontinuierlichen Überwachung von Rohrleitungen eingesetzt werden kann. Neben der DAS werden erprobte Verfahren der zerstörungsfreien Prüfung wie Schallemissionsanalyse (SEA) und Beschleunigungssensoren eingesetzt. An dieser Stelle soll detailliert auf die Hauptschadensursachen an Rohrleitungen, den Versuchsstand zur mechanischen Belastung von Rohren sowie die Möglichkeiten zu Untersuchungen im Realmaßstab eingegangen werden.
Additive manufacturing (AM) offers a range of novel applications. However, the manufacturing process is complex and the production of defect-free parts with a high reliability is still a challenge. Thermography is a valuable tool for process surveillance, especially in metal AM processes. The high process temperatures allow one to use cameras usually operating in the visible spectral range. Here, we compare the results of first measurements during the manufacturing process of a commercial laser metal deposition (LMD) setup using a MWIR camera with those from a VIS high-speed camera with band pass filter in the NIR range.
Additive manufacturing (AM) opens the route to a range of novel applications.However, the complexity of the manufacturing process poses a challenge for the production of defect-free parts with a high reliability. Since process dynamics and resulting microstructures of AM parts are strongly influenced by the involved temperature fields, thermography is a valuable tool for process surveillance. The high process temperatures in metal AM processes allow one to use cameras usually operating in the visible spectral range to detect the thermally emitted radiation from the process. In our work, we compare the results of first measurements during the manufacturing processes of a commercial laser metal deposition (LMD) setup and a laser beam melting (LBM) setup using a MWIR camera with those from a VIS high-speed camera with band pass filter in the NIR range.
Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing.
The residual stress distribution in the bulk of IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-build condition (on a build plate) and after removal from the build plate.
The absolute values of all stress components decreased after removal from the build plate. Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component depending on the thermal gradient in the respective direction.
Influence of deposition hatch length on residual stress in selective laser melted Inconel 718
(2018)
The present study aims to evaluate the bulk residual stresses in SLM parts by using neutron diffraction measurements performed at E3 line -BER II neutron reactor- of Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. Together with microstructure characterization and distortion measurements, it is possible to describe the stress state throughout the whole sample. The sample was measured in as-build condition (on a build plate) and after releasing from the build plate. The used material is the nickel based superalloy 718. This alloy is widely used in aerospace and chemical industries due to its superior corrosion and heat resistant properties.
Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component. The normal and transversal component exhibits a rather compressive behavior while the longitudinal was tensile in the center part of the sample and became compressive towards the tip. As expected, the absolute values of all stress components decreased after releasing the sample from the building plate. A surface scan utilizing a coordinate-measuring machine (CMM) allowed us to present top surface distortion before and after releasing. The top surface showed a distortion around ±80µm after releasing. Microstructure evolution in the scanning-building cross-section is largely dominated by columnar grains. In addition, many small random orientated grains are prominent in the regions of a laser overlap during SLM.
In summary, for the sample of superalloy 718 manufactured by SLM, a small distortion occurred when removing the sample from the build plate whereby the residual stress state decreases. Moreover, the observed columnar grains in the building direction could give a reason for the lowest stress values in that normal direction. However, the most important parameter controlling the residual stresses is the temperature gradient. Hence, future investigations are planned for a different scan strategy to distribute the laser impact in a more homogenous manner.
Acoustic emission testing
(2018)
The influence of the support structure on residual stress and distortion in SLM Inconel 718 parts
(2018)
The effect of support structure and of removal from the base plate on the residual stress state in selective laser melted IN718 parts was studied by means of synchrotron X-ray diffraction. The residual stresses in subsurface region of two elongated prisms in as-built condition and after removal from the base plate were determined. One sample was directly built on a base plate and another one on a support structure. Also, the distortion on the top surface due to stress release was measured by contact profilometry. High tensile residual stress values were found, with pronounced stress gradient along the hatching direction. In the sample on support, stress redistribution took place after removal from the base plate, as opposed to simple stress relaxation for the sample without support. The sample on support structure showed larger distortion compared to sample without support. We conclude that the use of a support decreases stress values but stress-relieving heat treatments are still needed.
Having been introduced almost two decades ago, Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing.
The residual stress distribution in IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron (bulk) and laboratory X-ray (surface) diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-build condition (on a build plate) and after removal from the build plate.
The absolute values of all stress components decreased after removal from the build plate. Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component depending on the thermal gradient in the respective direction.