8.3 Thermografische Verfahren
Filtern
Dokumenttyp
- Zeitschriftenartikel (69) (entfernen)
Schlagworte
- Thermography (25)
- Additive manufacturing (10)
- NDT (9)
- Additive Manufacturing (8)
- Laser thermography (8)
- Infrared thermography (7)
- GFRP (5)
- Super resolution (5)
- In situ monitoring (4)
- Internal defects (4)
Organisationseinheit der BAM
- 8.3 Thermografische Verfahren (69)
- 8 Zerstörungsfreie Prüfung (68)
- 9 Komponentensicherheit (15)
- 8.5 Röntgenbildgebung (10)
- 9.3 Schweißtechnische Fertigungsverfahren (8)
- 9.6 Additive Fertigung metallischer Komponenten (8)
- 9.4 Integrität von Schweißverbindungen (4)
- 1 Analytische Chemie; Referenzmaterialien (3)
- 5 Werkstofftechnik (3)
- 5.1 Mikrostruktur Design und Degradation (3)
Paper des Monats
- ja (3)
Since laser powder bed fusion (PBF-LB/M) is prone to the formation of defects during the building process, a fundamental requirement for widespread application is to find ways to assure safety and reliability of the additively manufactured parts. A possible solution for this problem lies in the usage of in-situ thermographic monitoring for defect detection. In this contribution we investigate possibilities and limitations of the VIS/NIR wavelength range for defect detection. A VIS/NIR camera can be based on conventional silicon-based sensors which typically have much higher spatial and temporal resolution in the same price range but are more limited in the detectable temperature range than infrared sensors designed for longer wavelengths. To investigate the influence, we compared the thermographic signatures during the creation of artificially provoked defects by local parameter variations in test specimens made of a nickel alloy (UNS N07208) for two different wavelength ranges (~980 nm and ~1600 nm).
Infrared thermography (IRT) using a focused laser is effective for surface defect detection. Nevertheless, testing complex‐shaped components remains a challenging task. The state‐of‐the‐art focuses on testing a limited region of interest rather than the full sample. Thus, detection and location of surface defects has been less researched. Most attempts require a manual scan of the full sample, which makes it hard to reconstruct the full scanned surface. Here, we introduce a reliable workflow for crack detection and semi‐automated inspection of complex‐shaped components using IRT excited with a laser line. A 6‐axis robot arm is used for moving the sample in front of the setup. This approach has been tested on a section of a rail and a gear, both containing defects due to heavy use. Crack detection is based on the segmentation of thermograms obtained by Fourier transform of sorted temperatures. Moreover, texture mapping is used to visualize a reconstructed thermogram on the 3D model of the sample. Our approach illustrates a reliable process towards the digitalization of thermographic testing.
A hybrid deterministic-probabilistic framework is presented that combines in-situ measurements and numerical analysis to predict the characteristic size of corrosion pits over extended periods of exposure to seawater. A probabilistic model, informed by corrosion current density and temperature data, applies a sampling method to a range of overpotential values to reflect the surface deterioration in terms of pitting. The model is calibrated and validated with pit size data obtained from corroded coupons. Results reveal a positively skewed truncated lognormal distribution of pit depths which implies a higher prevalence of smaller pit depths, corroborated both experimentally and numerically.
Welded steel structures used in the offshore wind industry are exposed to harsh marine environments, which can result in corrosion-induced fatigue damage. Of particular concern is the heat affected zone (HAZ) of welded joints, a region known for its altered microstructure and mechanical properties, which can significantly influence the initiation and propagation of fatigue cracks. This study investigates the short and long fatigue crack growth rates, and the effect of seawater exposure, for the HAZ in S355 steel weldments. Single-edge notch bend (SENB) specimens are used, with a shallow notch in the HAZ. A series of specimens is immersed in synthetic seawater that is continuously circulated at a controlled temperature to assess the synergistic effects of corrosion and fatigue. The experimental method integrates a novel application of front face strain compliance for monitoring short cracks, alongside an extended back-face strain compliance approach for monitoring long crack propagation. It is concluded that the short fatigue crack growth rate of the HAZ is 2.7 to 3.5 times higher in seawater as compared to air. As the crack propagates and enters into the long crack regime, the ratio decreases to 2.2 times at the transition point of the two-stage crack growth curve and further decreases to 1.5 times when the notch advances towards fracture. The findings indicate that the fatigue crack growth rates documented in standards tend to be on the conservative side. This study significantly enriches the fatigue crack growth data available in literature, which will contribute to a more accurate lifetime assessment offshore wind turbine structures.
Additively manufactured components are characterized by heterogeneous mechanical properties due to variations of the microstructure, flaws and residual stresses resulting from the inhomogeneous fabrication process. The large number of influencing factors poses a further challenge in understanding the correlation between material properties, process parameters and component geometry. Therefore, the qualification of components based on witness specimens produced within the same job is questionable. This work aims to present a new strategy for the characterization of PBF-LB/M components based on representative specimens. The key assumption is the feasibility of a transfer of the thermal history from a component to a specimen. It is assumed that similar material properties are determined for components and specimens produced adopting a similar thermal history. After the definition of a region of interest in the component, a combination of thermal analyses by means of finite elements and in-situ experimental determination of the thermal history through infrared thermography is used to produce test coupons with a similar thermal history. The effectiveness of the procedure is demonstrated on a pressure vessel for applications in the chemical industry.
For a deep process understanding of the laser powder bed fusion process (PBF-LB/M), recording of the occurring surface temperatures is of utmost interest and would help to pave the way for reliable process monitoring and quality assurance. A notable number of approaches for in-process monitoring of the PBF-LB/M process focus on the monitoring of thermal process signatures. However, due to the elaborate calibration effort and the lack of knowledge about the occurring spectral directional emissivity, only a few approaches attempt to measure real temperatures. In this study, to gain initial insights into occurring in the PBF-LB/M process, measurements on PBF-LB/M specimens and metal powder specimens were performed for higher temperatures up to T = 1290 °C by means of the emissivity measurement apparatus (EMMA) of the Center for Applied Energy Research (CAE, Wuerzburg, Germany). Also, measurements at ambient temperatures were performed with a suitable measurement setup. Two different materials—stainless steel 316L and aluminum AlSi10Mg—were examined. The investigated wavelength λ ranges from the visible range (λ-VIS= 0.40–0.75 µm) up to the infrared, λ = 20 µm. The influence of the following factors were investigated: azimuth angle φ, specimen temperature TS, surface texture as for PBF-LB/M surfaces with different scan angles α, and powder surfaces with different layer thicknesses t.
In this work, the thermal properties of ternary Li₃ₓCo₇₋₄ₓSb₂₊ₓO₁₂ solid solutions are studied for different concentrations in the range 0 ≤ x ≤ 0.7. Samples are elaborated at four different sintering temperatures: 1100, 1150, 1200 and 1250 °C. The effect of increasing the content of Li⁺ and Sb⁵⁺, accompanied by the reduction of Co²⁺, on the thermal properties is studied. It is shown that a thermal diffusivity gap, which is more pronounced for low values of x, can be triggered at a certain threshold sintering temperature (around 1150 °C in this study). This effect is explained by the increase of contact area between adjacent grains. Nevertheless, this effect is found to be less pronounced in the thermal conductivity. Moreover, a new framework for heat diffusion in solids is presented that establishes that both the heat flux and the thermal energy (or heat) satisfy a diffusion equation and therefore highlights the importance of thermal diffusivity in transient heat conduction phenomena.
Laser powder bed fusion of metallic components (PBF-LB/M) is gaining acceptance in industry. However, the high costs and lengthy qualification processes required for printed components create the need for more effective in-situ monitoring and testing methods. This article proposes multispectral Optical Tomography (OT) as a new approach for monitoring the PBF-LB/M process. Compared to other methods, OT is a low-cost process monitoring method that uses long-time exposure imaging to observe the build process. However, it lacks time resolution compared to expensive thermographic sensor systems. Monochromatic OT (1C-OT) is already commercially available and observes the building process layer-wise using a single wavelength window in the NIR range. Multispectral OT (nC-OT) utilizes a similar setup but can measure multiple wavelength ranges per location simultaneously. By comparing the classical 1C-OT and nC-OT approaches, this article examines the advantages of nC-OT (two channel OT and RGB-OT) in reducing the false positive rate for process deviations and approximating maximum temperatures for a better comparison between different build processes and materials. This could ultimately reduce costs and time for part qualification. The main goal of this contribution is to assess the advantages of nC-OT compared to 1C-OT for in-situ process monitoring of PBF-LB/M.
The capability to produce complexly and individually shaped metallic parts is one of the main advantages of the laser powder bed fusion (PBF LB/M) process. Development of material and machine specific process parameters is commonly based on results acquired from small cubic test coupons of about 10 mm edge length. Such cubes are usually used to conduct an optimization of process parameters to produce dense material. The parameters are then taken as the basis for the manufacturing of real part geometries. However, complex geometries go along with complex thermal histories during the manufacturing process, which can significantly differ from thermal conditions prevalent during the production of simply shaped test coupons. This may lead to unexpected and unpredicted local inhomogeneities of the microstructure and defect distribution in the final part and it is a root cause of reservations against the use of additive manufacturing for the production of safety relevant parts. In this study, the influence of changing thermal conditions on the resulting melt pool depth of 316L stainless steel specimens is demonstrated. A variation of thermo-graphically measured intrinsic preheating temperatures was triggered by an alteration of inter layer times and a variation of cross section areas of specimens for three distinct sets of process parameters. Correlations between the preheating temperature, the melt pool depth, and occurring defects were analyzed. The limited expressiveness of the results of small density cubes is revealed throughout the systematic investigation. Finally, a clear recommendation to consider thermal conditions in future process parameter optimizations is given.
Laser powder bed fusion is one of the most promising additive manufacturing techniques for printing complex-shaped metal components. However, the formation of subsurface porosity poses a significant risk to the service lifetime of the printed parts. In-situ monitoring offers the possibility to detect porosity already during manufacturing. Thereby, process feedback control or a manual process interruption to cut financial losses is enabled.
Short-wave infrared thermography can monitor the thermal history of manufactured parts which is closely connected to the probability of porosity formation. Artificial intelligence methods are increasingly used for porosity prediction from the obtained large amounts of complex monitoring data. In this study, we aim to identify the potential and the challenges of deep-learning-assisted porosity prediction based on thermographic in-situ monitoring.
Therefore, the porosity prediction task is studied in detail using an exemplary dataset from the manufacturing of two Haynes282 cuboid components. Our trained 1D convolutional neural network model shows high performance (R² score of 0.90) for the prediction of local porosity in discrete sub-volumes with dimensions of (700 x 700 x 40) μm³.
It could be demonstrated that the regressor correctly predicts layer-wise porosity changes but presumably has limited capability to predict differences in local porosity. Furthermore, there is a need to study the significance of the used thermogram feature inputs to streamline the model and to adjust the monitoring hardware. Moreover, we identified multiple sources of data uncertainty resulting from the in-situ monitoring setup, the registration with the ground truth X-ray-computed tomography data and the used pre-processing workflow that might influence the model’s performance detrimentally.