Integration of fibre reinforcement in high-performance cementitious materials has become widely applied in many fields of construction. One of the most investigated advantages of steel fibre reinforced concrete (FRC) is the deceleration of crack growth and hence it’s improved sustainability due to e.g. decrease of permeability of concrete by aggressive substances. Additional benefits are associated with the structural properties of FRC, where fibres can significantly increase the ductility and the tensile strength of concrete. In some applications, such as tunnel linings or industrial slabs, it is even possible to entirely replace the conventional reinforcement, leading to significant logistical and environmental benefits. Fibre reinforcement can, however, have critical disadvantages and even hinder the performance of concrete, since it can induce an anisotropic material behaviour of the mixture if the fibres are not appropriately oriented. For a safe use of FRC in the future, reliable non-destructive methods need to be identified to assess the fibres’ orientation in hardened concrete. In this study, ultrasonic material testing, electrical impedance testing, and X-ray computer tomography have been investigated for this purpose using specially produced samples with biased or random fibre orientations. This paper demonstrates the capabilities of each of these NDT techniques for fibre orientation measurements and draws conclusions based on these results about the most promising areas for future research and development using these techniques.
Intensified Alkali-Silica Reaction (ASR) damage has occurred on German roadways in recent years, leading to requirements for compulsory pre-construction investigation of aggregate alkali sensitivity using concrete tests with external alkali supply. However, since these tests are time-consuming and cost-intensive, there is interest in replacing them with a solubility test on pure aggregate in 0.1 M KOH solution at 80°C with a defined NaCl content (1wt.-%). In this context, the influence of aggregate pore structure on SiO2 and Al2O3 solubility was investigated in this project. This paper compares the results of porosity studies with X-ray Computed Tomography (3D-CT) and the Brunauer-Emmett-Teller (BET) method on individual quarried and river gravel granules of both rhyolite and greywacke. For visualization and quantification of both externally accessible and fully enclosed surfaces of granules using X-ray 3D-CT, special software tools were developed. The results demonstrated that the river gravel granules had significantly larger externally accessible surfaces than the quarried granules. BET measurements on individual stones showed, as expected, that measured surfaces were about three orders of magnitude larger than those from the X-ray 3D-CT analyses due to the higher spatial resolution of BET. There was no apparent correlation between the X-ray 3D-CT and BET surface areas. Mercury porosimetry measurements indicate that this may be due to the presence of significant porosity below the spatial resolution of the X-ray 3D-CT. A comparison of SiO2 and Al2O3 solubility measurements with the X-ray 3D-CT and BET surface area data resulted only in weak, inconclusive correlations, indicating the need for further experimental investigation.