- Additive manufacturing (17)
- Laser powder bed fusion (12)
- Additive Manufacturing (11)
- Computed tomography (10)
- AGIL (9)
- Residual Stress (9)
- Neutron diffraction (7)
- X-ray refraction (6)
- Residual stress (5)
- Synchrotron radiation (5)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (95)
- 8.5 Röntgenbildgebung (95)
- 9 Komponentensicherheit (23)
- 9.4 Integrität von Schweißverbindungen (16)
- 9.6 Additive Fertigung metallischer Komponenten (11)
- 5 Werkstofftechnik (8)
- 8.0 Abteilungsleitung und andere (8)
- 5.1 Mikrostruktur Design und Degradation (7)
- 5.2 Metallische Hochtemperaturwerkstoffe (6)
- 7 Bauwerkssicherheit (2)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (28)
Vertebrate bones are made of a nanocomposite consisting of water, mineral and organics. Water helps bone material withstand mechanical stress and participates in sensation of external loads. Water diffusion across vertebrae of medaka (bone material lacking osteocytes) and zebrafish (bone material containing osteocytes) was compared using neutron tomography. Samples were measured both wet and following immersion in deuterated-water (D2O). By quantifying H+ exchange and mutual alignment with X-ray lCT scans, the amount of water expelled from complete vertebra was determined. The findings revealed that anosteocytic bone material is almost twice as amenable to D2O diffusion and H2O exchange, and that unexpectedly, far more water is retained in osteocytic zebrafish bone. Diffusion in osteocytic bones (only 33 % – 39 % water expelled) is therefore restricted as compared to anosteocytic bone (~ 60 % of water expelled), presumably because water flow is confined to the lacunar-canalicular network (LCN) open-pore system. Histology and Raman spectroscopy showed that anosteocytic bone contains less proteoglycans than osteocytic bone. These findings identify a previously unknown functional difference between the two bone materials. Therefore, this study proposes that osteocytic bone retains water, aided by non-collagenous proteins, which contribute to its poroelastic mechano-transduction of water flow confined inside the LCN porosity.
Validation of a fast and traceable radiographic scale calibration of dimensional computed tomography
(2022)
A fast and highly precise method of determining the geometrical scale factor of computed tomography (CT) measurements has been validated successfully by Bundesanstalt für Materialforschung und -prüfung (BAM), the Federal Institute of Metrology (METAS) and Physikalisch-Technische Bundesanstalt (PTB) within the scope of AdvanCT (Advanced Computed Tomography for dimensional and surface measurements in industry), a project funded in the European Metrology Programme for Innovation and Research (EMPIR). The method has been developed by PTB and requires only two radiographic images of a calibrated thin 2D standard (hole grid standard) from two opposite directions. The mean grid distance is determined from both radiographs. From this and with the help of the calibration result, the radiographic scale and therefore the voxel size is determined. The procedure takes only a few minutes and avoids a time-consuming CT scan. To validate the method, the voxel sizes determined via this method were compared with voxel sizes determined from CT scans of calibrated objects. Relative deviations between the voxel sizes in the range of 10−5 were
achieved with minimal effort using cone-beam CT systems at moderate magnifications.
The BAMline at the BESSY II synchrotron X-ray source has enabled research for more than 20 years in widely spread research fields such as materials science, biology, cultural heritage and medicine. As a nondestructive characterization method, synchrotron X-ray imaging, especially tomography, plays a particularly important role in structural characterization. A recent upgrade of key equipment of the BAMline widens its imaging capabilities: shorter scan acquisition times are now possible, in situ and operando studies can now be routinely performed, and different energy spectra can easily be set up. In fact, the upgraded double-multilayer monochromator brings full flexibility by yielding different energy spectra to optimize flux and energy resolution as desired. The upgraded detector (based on an sCMOS camera) also allows exploiting the higher flux with reduced readout times. Furthermore, an installed slip ring allows the sample stage to continuously rotate. The latter feature enables tomographic observation of processes occurring in the time scale of a few seconds.
Die Integrität der Verstärkungsfasern in Komposit-Zahnstiften ist entscheidend für die Biegefestigkeit und die langfristige Haftung am Zement in den Wurzelkanälen. Es wurde vermutet, dass die Integrität von glasfaserverstärkten Zahnstiften durch das Beschleifen während der zahnmedizinischen Behandlung beeinträchtigt wird. Eine Beschädigung der Fasern führt zu einer erheblichen strukturellen Schwächung über den gesamten Stiftdurchmesser. Glasfragmente, die durch den Kontakt mit dem Zahnbohrer entstehen, können sich vom Stift lösen und die Haftfähigkeit erheblich verringern. Mit Hilfe hochauflösender Synchrotron-Röntgen-Refraktions-Radiographie (SXRR) konnte das Ausmaß der Schäden zuverlässig identifiziert und charakterisiert werden.
Dazu wurden die Glasfaserstifte sowohl im Herstellungszustand als auch nach der Bearbeitung mit einem Diamantbohrer untersucht. Die Datensätze wurden zur Visualisierung und Quantifizierung der morphologischen Charakteristika intakter und durch das Beschleifen beschädigter Regionen analysiert. Sie zeigen Schäden im bearbeiteten Bereich (z. B. Brüche, Splitter und Risse) sowie herstellungsbedingte Inhomogenitäten der Fasern mit einer signifikanten Zunahme der inneren Oberflächen in Probenregionen, die durch das Beschleifen beschädigt wurden.
Die Integrität der Verstärkungsfasern in Komposit-Zahnstiften ist entscheidend für die Biegefestigkeit und die langfristige Haftung am Zement in den Wurzelkanälen. Es wurde vermutet, dass die Integrität von glasfaserverstärkten Zahnstiften durch das Beschleifen während der zahnmedizinischen Behandlung beeinträchtigt wird. Eine Beschädigung der Fasern führt zu einer erheblichen strukturellen Schwächung über den gesamten Stiftdurchmesser. Glasfragmente, die durch den Kontakt mit dem Zahnbohrer entstehen, können sich vom Stift lösen und die Haftfähigkeit erheblich verringern. Mit Hilfe hochauflösender Synchrotron-Röntgen-Refraktions-Radiographie (SXRR) konnte das Ausmaß der Schäden zuverlässig identifiziert und charakterisiert werden.
Dazu wurden die Glasfaserstifte sowohl im Herstellungszustand als auch nach der Bearbeitung mit einem Diamantbohrer untersucht. Die Datensätze wurden zur Visualisierung und Quantifizierung der morphologischen Charakteristika intakter und durch das Beschleifen beschädigter Regionen analysiert. Sie zeigen Schäden im bearbeiteten Bereich (z. B. Brüche, Splitter und Risse) sowie herstellungsbedingte Inhomogenitäten der Fasern mit einer signifikanten Zunahme der inneren Oberflächen in Probenregionen, die durch das Beschleifen beschädigt wurden.
The manufacturability of metallic alloys using laser-based additive manufacturing methods such as laser powder bed fusion has substantially improved within the last decade. However, local melting and solidification cause hierarchically structured and crystallographically textured microstructures possessing large residual stress. Such microstructures are not only the origin of mechanical anisotropy but also pose metrological challenges for the diffraction-based residual stress determination. Here we demonstrate the influence of the build orientation and the texture on the microstructure and consequently the mechanical anisotropy of as-built Inconel 718. For this purpose, we manufactured specimens with [001]/[011]-, [001]- and [011]/[111]-type textures along their loading direction. In addition to changes in the Young’s moduli, the differences in the crystallographic textures result in variations of the yield and ultimate tensile strengths. With this in mind, we studied the anisotropy on the micromechanical scale by subjecting the specimens to tensile loads along the different texture directions during in situ neutron diffraction experiments. In this context, the response of multiple lattice planes up to a tensile strain of 10% displayed differences in the load partitioning and the residual strain accumulation for the specimen with [011]/[111]-type texture. However, the relative behavior of the specimens possessing an [001]/[011]- and [001]-type texture remained qualitatively similar. The consequences on the metrology of residual stress determination methods are discussed.
The triaxial distribution of the residual stress in laser powder bed fused austenitic steel 316L was determined by X-ray and neutron diffraction. The residual stress analysis results were linked to the thermal history of the specimens, which were manufactured with varying inter-layer-times and scanning velocities. A clear link between the in-process temperature of the specimens and the residual stress was found, based on in-situ monitoring data.
Traceable determination of non-static XCT machine geometry: New developments and case studies
(2022)
It is fundamental to determine the machine geometry accurately for dimensional X-ray computed tomography (XCT) measurements. When performing high-accuracy scans, compensation of a non-static geometry, e.g. due to rotary axis errors or drift, might become necessary. Here we provide an overview of methods to determine and account for such deviations on a per projection basis. They include characterisation of stage error motions, in situ geometry measurements, numerical simulations, and reconstruction-based optimization relying on image quality metrics and will be discussed in terms of their metrological performance. Since a radiographic calibration is always required to provide an initial absolute geometry, this method will be presented as well. The improvements of the XCT geometry correction methods are presented by means of case studies. The methods can be applied individually or in combination and are intended to provide a toolbox for XCT geometry compensation.
Toughening mechanisms and enhanced damage tolerant fatigue behaviour in laminated metal composites
(2022)
In the present study, fatigue crack growth (FCG) in a laminated metal composite (LMC) consisting of Al-based constituents with dissimilar strength was studied. Additionally, the FCG in both monolithic constituent materials was determined and a linear elastic rule of mixture (ROM) concept was calculated as a reference for the FCG of the laminated composite. Crack networks in the laminates were analyzed post-mortem by means of light microscopy and synchrotron X-Ray tomography (SXCT). Significantly reduced FCG rates for the LMC were found at elevated stress intensity ranges compared to both the monolithic constituents as well as the ROM concept. This is the result of the formation of a complex 3D crack network in the laminated architecture caused by the appearance of the two different toughening mechanisms a) crack deflection and b) crack bifurcation at the vicinity of the interfaces.
Metastable austenitic stainless steel (304L) samples with a rectangular cross-section were plastically deformed in torsion during which they experienced multiaxial stresses that led to a complex martensitic phase distribution owing to the transformation induced plasticity effect. A three-dimensional characterization of the phase distributions in these cm-sized samples was carried out by wavelength-selective neutron tomography. It was found that quantitatively correct results are obtained as long as the samples do not exhibit any considerable preferential grain orientation. Optical microscopy, electron backscatter diffraction, and finite element modeling were used to verify and explain the results obtained by neutron tomography. Altogether, neutron tomography was shown to extend the range of microstructure characterization methods towards the meso- and macroscale.
Metastable austenitic stainless steel (304L) samples with a rectangular cross-section were plastically deformed in torsion during which they experienced multiaxial stresses that led to a complex martensitic phase distribution owing to the transformation induced plasticity effect. A three-dimensional characterization of the phase distributions in these cm-sized samples was carried out by wavelength-selective neutron tomography. It was found that quantitatively correct results are obtained as long as the samples do not exhibit any considerable preferential grain orientation. Optical microscopy, electron backscatter diffraction, and finite element modeling were used to verify and explain the results obtained by neutron tomography. Altogether, neutron tomography was shown to extend the range of microstructure characterization methods towards the meso- and macroscale.
The BAMline at the synchrotron X-ray source BESSY II (Berlin, Germany) is supporting researchers in a wide range of research areas since more than 20 years. These fields include biology, cultural heritage, medicine, and also materials science. As a non-destructive characterization method, synchrotron X-ray imaging, especially tomography with hard X-Rays, plays an important role in structural 3D characterization. A recent upgrade of key equipment at the BAMline expands the imaging capabilities towards shorter acquisition times. Therefore, in-situ and operando experiments can now be routinely conducted. Also, different energy resolutions can be set up to optimize flux and energy resolution as desired. This requires an adaptation of the used reconstruction methods in order to perform necessary analyses also during the experiment. In this presentation the equipment, data handling pipeline as well as various examples from material science are presented.
The interest to additively manufacture Nickel-based superalloys has substantially grown within the past decade both academically and industrially. More specifically, additive manufacturing processes such as laser powder bed fusion (LPBF) offer the ability to produce dense parts within a single manufacturing step. In fact, the exceptional freedom in design associated with the layer-based nature of the processes is of particular interest for the complex shapes typically required in turbine applications. In certain cases, the overall part performance can be achieved by tailoring the microstructure and the crystallographic texture to the specific application. However, these advantages must be paid at a price: the large local temperature gradients associated with the rapid melting and solidification produce parts that inherently contain large residual stress in the as-manufactured state. In addition, the presence of pores in the final part may further affect the in-service part failure. As among Nickel-based alloys Inconel 718 exhibits excellent weldability, this alloy has been widely studied in open research in the domain of LPBF. However, significant microsegregation of the heavier alloying elements such as Niobium and Molybdenum accompanied by dislocation entanglements may preclude the application of conventional heat treatment schedules. Therefore, different post processing heat treatments are required for laser powder bed fused Inconel 718 as compared to conventional variants of the same alloy.
In this study, we investigated two different heat treatment routes for LPBF Inconel 718. In a first routine, the samples were stress relieved and subsequently subjected to hot isostatic pressing (HIP) followed by a solution heat treatment and a two-step age (referred to as FHT). In a second routine, the samples were subjected to a single-step direct age post stress relieving heat treatment (referred to DA). We investigated the consequences of such heat treatment schedules on the microstructure, texture, and mechanical behavior. We show that by applying a DA heat treatment the typical columnar microstructure possessing a crystallographic texture is retained, while an equiaxed untextured microstructure prevails in case of an FHT heat treatment. We further evaluate how these heat treatments affect the mechanical behaviour on the macroscopic and microscopic scale.
A software toolbox is introduced that addresses several needs common to computed tomography (CT). Built for the WIPANO CTSimU project to serve as the reference implementation for its image processing and evaluation tasks, it provides a Python 3 interface that is adaptable to many conceivable applications. Foremost, the toolbox features a pipeline architecture for sequential 2D image processing tasks, such as flat field corrections and image binning, and enables the user to create their own processing modules. Beyond that, it provides means to measure line profiles and image quality assessment algorithms to calculate modulation transfer functions (MTF) or to determine the interpolated basic spatial resolution (iSRb) using a duplex wire image. It can also be used to calculate projection matrices for the reconstruction of scans with arbitrary industrial CT geometries and trajectories. The CTSimU project defined a framework of projection- and volume-based test scenarios for the qualification of radiographic simulation software towards its use in dimensional metrology. The toolbox implements the necessary evaluation routines and generates reports for all projection-based tests.
Alternative to conventional transmission-based radiography and computed tomography, X-ray refraction techniques are being increasingly used to detect damage in light materials. In fact, their range of application has been recently extended even to metals. The big advantage of X-ray refraction techniques is that they are able to detect nanometric defects, whose size would lie below the resolution of even state-of-the-art synchrotron-based X-ray computed tomography (SXCT). The superiority of synchrotron X-ray refraction radiography and tomography (SXRR and SXRCT) has been shown in the case of light materials, in particular composites. X-ray refraction techniques also yield a quantitifaction of the amount of damage (the so-called relative internal specific surface) and can well be compared with damage models. At the same time, it is impossible for SXRR and SXRCT to image single defects. We show that the combination of refraction- and transmission-based imaging techniques yields an impressive amount of additional information about the type and amount of defects in microstructured materials such as additively manufactured metals or metal matrix composites. We also show that the use of data fusion techniques allows the classification of defects in statistically significant representative volume elements.
Alternative to conventional transmission-based radiography and computed tomography, X-ray refraction techniques are being increasingly used to detect damage in light materials. In fact, their range of application has been recently extended even to metals. The big advantage of X-ray refraction techniques is that they are able to detect nanometric defects, whose size would lie below the resolution of even state-of-the-art synchrotron-based X-ray computed tomography (SXCT). The superiority of synchrotron X-ray refraction radiography and tomography (SXRR and SXRCT) has been shown in the case of light materials, in particular composites. X-ray refraction techniques also yield a quantitifaction of the amount of damage (the so-called relative internal specific surface) and can well be compared with damage models. At the same time, it is impossible for SXRR and SXRCT to image single defects. We show that the combination of refraction- and transmission-based imaging techniques yields an impressive amount of additional information about the type and amount of defects in microstructured materials such as additively manufactured metals or metal matrix composites. We also show that the use of data fusion techniques allows the classification of defects in statistically significant representative volume elements.
Additive manufacturing methods such as laser powder bed fusion (LPBF) allow geometrically complex parts to be manufactured within a single step. However, as an aftereffect of the localized heat input, the rapid cooling rates are the origin of the large residual stress (RS) retained in as-manufactured parts. With a view on the microstructure, the rapid directional cooling leads to a cellular solidification mode which is accompanied by columnar grown grains possessing crystallographic texture. The solidification conditions can be controlled by the processing parameters and the scanning strategy. Thus, the process allows one to tailor the microstructure and the texture to the specific needs. Yet, such microstructures are not only the origin of the mechanical anisotropy but also pose metrological challenges for the diffraction-based RS determination. In that context the micromechanical elastic anisotropy plays an important role: it translates the measured microscopic strain to macroscopic stress. Therefore, it is of uttermost importance to understand the influence of the hierarchical microstructures and the texture on the elastic anisotropy of LPBF manufactured materials.
This study reveals the influence of the build orientation and the texture on the micro-mechanical anisotropy of as-built Inconel 718. Through variations of the build orientation and the scanning strategy, we manufactured specimens possessing [001]/[011]-, [001]-, and [011]/[111]-type textures. The resulting microstructures lead to differences in the macroscopic mechanical properties. Even further, tensile in-situ loading experiments during neutron diffraction measurements along the different texture components revealed differences in the microstrain response of multiple crystal lattice planes. In particular, the load partitioning and the residual strain accumulation among the [011]/[111] textured specimen displayed distinct differences measured up to a macroscopic strain of 10 %. However, the behavior of the specimens possessing [001]/[011]-and [001]-type texture was only minorly affected. The consequences on the metrology of RS analysis by diffraction-based methods are discussed.
A systematic study has been carried out to investigate the neutron transmission signal as a function of sample temperature. In particular, the experimentally determined wavelength-dependent neutron attenuation spectra for a martensitic steel at temperatures ranging from 21 to 700°C are compared with simulated data. A theoretical description that includes the Debye–Waller factor in order to describe the temperature influence on the neutron cross sections was implemented in the nxsPlotter software and used for the simulations. The analysis of the attenuation coefficients at varying temperatures shows that the missing contributions due to elastic and inelastic scattering can be clearly distinguished: while the elastically scattered intensities decrease with higher temperatures, the inelastically scattered intensities increase, and the two can be separated from each other by analysing unique sharp features in the form of Bragg edges. This study presents the first systematic approach to quantify this effect and can serve as a basis , for example, to correct measurements taken during in situ heat treatments, in many cases being a prerequisite for obtaining quantifiable results.
A recent upgrade of key equipment of the BAMline widens its imaging capabilities: shorter scan acquisition times are now possible, in situ and operando studies can now be routinely performed, and different energy spectra can easily be set up. In fact, the upgraded double-multilayer monochromator brings full flexibility by yielding different energy spectra to optimize flux and energy resolution as desired.
In this work, synchrotron X-ray refraction radiography (SXRR) was combined with in-situ heat treatment to monitor microstructure and porosity evolution as a function of temperature. The investigated material was a laser powder bed fusion (LPBF) manufactured AlSi10Mg, where the initial eutectic Si network is known to break down into larger particles with increasing temperature. Such alloy is also prone to thermally induced porosity (TIP). We show that SXRR allows detecting the changes in the Si-phase morphology upon heating, while this is currently possible only using scanning electron microscopy. SXRR also allows observing the growth of pores, usually studied via X-ray computed tomography, but on much smaller fields-of-view. Our results show the great potential of in-situ SXRR as a tool to gain in-depth knowledge of the susceptibility of any material to thermally induced damage and/or microstructure evolution over statistically relevant volumes.
For the first time, synchrotron X-ray refraction radiography (SXRR) has been paired with in-situ heat treatment to monitor microstructure and porosity evolution as a function of temperature. The investigated material was a laser powder bed fusion (LPBF) manufactured AlSi10Mg, where the initial eutectic Si network is known to disintegrate and spherodize into larger particles with increasing temperature. Such alloy is also prone to thermally induced porosity (TIP). We show that SXRR allows detecting the changes in the Si-phase morphology upon heating, while this is currently possible only using scanning electron microscopy. SXRR also allows observing the growth of pores, usually studied via X-ray computed tomography, but on much smaller fields-of-view. Our results show the great potential of in-situ SXRR as a tool to gain in-depth knowledge of the susceptibility of any material to thermally induced damage and/or microstructure evolution over statistically relevant volumes.
The complexity of any microstructural characterization significantly increases when there is a need to evaluate the microstructural evolution as a function of temperature. To date, this characterization is primarily performed by undertaking elaborative ex-situ experiments where the material’s heating procedure is interrupted at different temperatures or times. Moreover, these studies are often limited to a region smaller than the representative elementary volume, which can lead to partial or even biased interpretations of the collected data. This limitation can be greatly overcome by using in-situ synchrotron X-ray refraction (SXRR). In this study, SXRR has been combined with in-situ heat treatment to monitor the porosity evolution as a function of temperature. It is shown that SXRR is a robust and straightforward method for time-resolved (3-5 min required per scan) evaluation of thermally induced microstructural changes over macroscopically relevant volumes.
The complexity of any microstructural characterization significantly increases when there is a need to evaluate the microstructural evolution as a function of temperature. To date, this characterization is primarily performed by undertaking elaborative ex-situ experiments where the material’s heating procedure is interrupted at different temperatures or times. Moreover, these studies are often limited to a region smaller than the representative elementary volume, which can lead to partial or even biased interpretations of the collected data. This limitation can be greatly overcome by using in-situ synchrotron X-ray refraction (SXRR). In this study, SXRR has been combined with in-situ heat treatment to monitor the porosity evolution as a function of temperature. This technique is a robust and straightforward method for time-resolved (3-5 min required per scan) evaluation of thermally induced microstructural changes over macroscopically relevant volumes.
The complexity of any microstructural characterization significantly increases when there is a need to evaluate the icrostructural evolution as a function of temperature. To date, this characterization is primarily performed by undertaking elaborative ex-situ experiments where the material’s heating procedure is interrupted at different temperatures or times. Moreover, these studies are often limited to a region smaller than the representative elementary volume, which can lead to partial or even biased interpretations of the collected data. This limitation can be greatly overcome by using in-situ synchrotron X-ray refraction (SXRR).
The influence of the inter-layer-time and the scanning velocity on the surface and bulk residual stress in laser powder bed fused 316L specimens was investigated. This study combines X-ray and neutron diffraction results with the thermal history of the specimens acquired through in-situ process monitoring. The process parameter variations were observed to directly influence the thermal history, which gave new insights in the assessment of the residual stress results.
Background Due to physical coupling between mechanical stress and magnetization in ferromagnetic materials, it is assumed in the literature that the distribution of the magnetic stray field corresponds to the internal (residual) stress of the specimen.
The correlation is, however, not trivial, since the magnetic stray field is also influenced by the microstructure and the geometry of component. The understanding of the correlation between residual stress and magnetic stray field could help to evaluate the integrity of welded components.
Objective This study aims at understanding the possible correlation of subsurface and bulk residual stress with magnetic stray field in a low carbon steel weld. Methods The residual stress was determined by synchrotron X-ray diffraction (SXRD, subsurface region) and by neutron diffraction (ND, bulk region). SXRD possesses a higher spatial resolution than ND. Magnetic stray fields were mapped by utilizing high-spatial-resolution giant magneto resistance (GMR) sensors.
Results The subsurface residual stress overall correlates better with the magnetic stray field distribution than the bulk stress.
This correlation is especially visible in the regions outside the heat affected zone, where the influence of the microstructural features is less pronounced but steep residual stress gradients are present.
Conclusions It was demonstrated that the localized stray field sources without any obvious microstructural variations are associated with steep stress gradients. The good correlation between subsurface residual stress and magnetic signal indicates that the source of the magnetic stray fields is to be found in the range of the penetration depth of the SXRD measurements.
Flexible, niedrigdichte Schäume aus Biokunststoffen im Extrusionsverfahren herzustellen war bisher industriell noch nicht möglich. Im Verarbeitungstechnikum Biopolymere des Fraunhofer IAP wurde in einem Projekt die Eignung von PBS-basierten Biokunststofftypen für Schaumanwendungen erforscht und weiterentwickelt.
Additiv gefertigte (AM) dreifach periodische metallische minimale Oberflächenstrukturen (TPMSS, aus dem Englischen Triply Periodic Minimum Surface Structures) erfüllen mehrere Anforderungen sowohl im biomedizinischen als auch im technischen Bereich: Abstimmbare mechanische Eigenschaften, geringe Empfindlichkeit gegenüber Herstellungsfehlern, mechanische Stabilität und hohe Energieabsorption. Allerdings stellen sie auch einige Herausforderungen in Bezug auf die Qualitätskontrolle dar, die ihre erfolgreiche Anwendung verhindern können. Tatsächlich ist die Optimierung des AM-Prozesses ohne die Berücksichtigung struktureller Merkmale wie Fertigungsgenauigkeit, interne Defekte sowie Oberflächentopographie und -rauheit unmöglich. In dieser Studie wurde die quantitative zerstörungsfreie Analyse von Ti-6Al-4V-Legierung TPMSS mit Hilfe der Röntgen-Computertomographie (XCT) durchgeführt. Es werden mehrere neue Bildanalyse-Workflows vorgestellt, um die Auswirkungen der Aufbaurichtung auf die Wanddickenverteilung, die Wanddegradation und die Verringerung der Oberflächenrauheit aufgrund des chemischen Ätzens von TPMSS zu bewerten. Es wird gezeigt, dass die Herstellungsgenauigkeit für die Strukturelemente, die parallel und orthogonal zu den hergestellten Schichten gedruckt werden, unterschiedlich ist. Verschiedene Strategien für das chemische Ätzen zeigten unterschiedliche Pulverabtragsfähigkeiten und damit ein Gradient der Wanddicke. Dies wirkte sich auf die mechanische Leistung unter Druck durch die Verringerung der Streckspannung aus. Eine positive Auswirkung des chemischen Ätzens ist die Verringerung der Oberflächenrauhigkeit, die möglicherweise die Ermüdungseigenschaften der Bauteile verbessern kann. Schließlich wurde XCT eingesetzt, um die Menge des zurückgehaltenen Pulvers mit der Porengröße des TPMSS zu korrelieren, wodurch der Herstellungsprozess weiter verbessert werden kann.
Als bildgebendes und zerstörungsfreies Verfahren eignet sich die Röntgen-Computertomographie (CT) insbesondere bei der Untersuchung von Kunst- und Kulturgütern. Die für Werkstoffprüfung und Materialanalyse konzipierten CT-Anlagen bieten dank hoher Röntgenleistung die Möglichkeit zusätzlich zu Holz, Keramiken und Kunststoffen auch stark schwächende Materialien, wie bspw. Metalle, zu durchdringen. Für eine hohe räumliche Auflösung im unteren Mikrometerbereich (2-200µm) sorgen entsprechend ausgelegte CT-Anlagen. In der Bundesanstalt für Materialforschung und -prüfung (BAM) stehen mehrere solcher CT-Anlagen für unterschiedliche Fragestellungen sowie Probengrößen und - materialien zur Verfügung. Einige Beispiele aus den vergangenen Arbeiten der BAM veranschaulichen das große Potential dieser Untersuchungsmethode.
Da bei einer CT-Messung in der Regel das gesamte Untersuchungsobjekt erfasst und in ein digitales Volumenmodell überführt wird, eröffnet sich für Archäologen und Restoratoren die Möglichkeit Untersuchungen hinsichtlich Materialzusammensetzung, Erhaltungszustand und Herstellungstechnik am virtuellen Objekt vorzunehmen, ohne die Originalsubstanz zu beeinträchtigen. Gegenüber der klassischen Radiografie, bei der nur eine zweidimensionale Abbildung erreicht wird, bietet die CT-Untersuchung die Möglichkeit innenliegende Strukturen dreidimensional zu erfassen. Die notwendige Bestimmung der Objektoberfläche erlaubt zudem die Erstellung eines Oberflächenmodells des untersuchten Gegenstandes. Damit lassen sich unter anderem mechanische Simulationen (Belastung, Durchbiegung, Durchströmung) durchführen. Der erzeugte Datensatz kann somit auch zur Herstellung eines Replikats im 3D-Druckverfahren genutzt werden. Anhand der Untersuchung der Mandoline von Smorsone wird gezeigt, wie eine CT-Messung durchgeführt wird und wie in dem anschließend rekonstruierten 3D-Datensatz mittels Koordinatenmesstechnik Maße (Abstände, Wandstärken, Winkel) exakt ermittelt werden können.
Design of freedom, performance improvement, cost reduction and lead time reduction are key targets when manufacturing parts in a layer-by-layer fashion using the laser powder bed fusion process (LPBF). Many research groups are focussed on improving the LPBF process to achieve the manufacturing of sound parts from a structural integrity perspective. In particular, the formation and distribution of residual stress (RS) remains a critical aspect of LPBF. The determination of the RS in LPBF benefits from the use of neutron diffraction (ND), as it allows the non-destructive mapping of the triaxial RS with a good spatial resolution. Two case studies are presented based on experiments carried out on the angular-dispersive neutron diffractometers Strain Analyser for Large Scale Engineering Applications (SALSA) (Institut Laue Langevin, Grenoble) and STRESS-Spec (FRM II, Garching). The RS in LPBF parts having a rectangular and more complex geometry (lattice structure) is analysed. The former example discusses the mapping of the RS in a rectangular body manufactured from stainless steel 316L. The manufacturing of these parts was monitored using an in-situ thermography set-up to link the RS to the thermal history. The latter discusses the RS in a lattice structure manufactured from the nickel base superalloy IN625. This geometry is challenging to characterise, and the use of a X-ray computed tomography twin is presented as tool to support the alignment of the ND experiment. The results from these case studies show a clear link between the thermal history and the RS magnitudes, as well as giving insights on the RS formation.
Additively manufactured (and in particular laser powder bed fused) materials represent a manyfold challenge for the materials scientist and engineer because of their distinctive microstructure. If laser powder bed fusion is used to produce components, the complexity level increases because meso-structures (e.g., overhanging features, surface and internal defects) gain importance. Furthermore, if the main advantage of additive manufacturing, i.e., the freedom of design, is to be fully exploited, and geometrically complex structures, such as lattices, are manufactured, then such structures become meta-materials. This means that the geometry and the materials properties become equally important.
This matryoshka-like (more literary than the dry “multi-scale”) complexity makes the characterization of the residual stress fields by means of diffraction methods so difficult with the current means, that new paradigms are necessary to tackle the challenge.
Indeed, classic open problems acquire an extra layer of difficulty, such that new solutions need to be found and the sometimes-dormant debate needs to be re-opened. Examples include the determination of: a- the unstrained reference: this reference can become location-dependent and needs to be carefully determined; b- the so-called diffraction elastic constants, which becomes immensely challenging since even the single-crystal elastic constants are not known for additively manufactured materials.
On top of this, other problems arise. The determination of the principal axes of stress becomes non-trivial because the hatching strategy sometimes dominates over the sample geometry. Even further, in complex structures, such as lattices, the textbook statement that the strain measurement in six independent directions uniquely identifies the strain tensor becomes simply invalid. The peculiar surface features of additively manufactured materials transform trivial tasks into formidable challenges: the precise alignment of a specimen in a beam or the determination of surface stresses with laboratory X-rays need to be thoroughly re-discussed and lay far from being routine tasks.
In this paper, we will show a few examples of the cases mentioned above. We will demonstrate that sometimes the classic approach works very well, but other times surprising conclusions can be drawn from in-depth studies of the residual stress in additively manufactured materials. In short, we predicate that classic methods cannot be used on additively manufactured materials and structures without a critical evaluation of their validity and application range.
While the problem of the identification of mechanisms of hydrogen assisted damage has and is being thoroughly studied, the quantitative analysis of such damage still lacks suitable tools. In fact, while, for instance, electron microscopy yields excellent characterization, the quantitative analysis of damage requires at the same time large field-of-views and high spatial resolution. Synchrotron X-ray refraction techniques do possess both features. In this work, we show how synchrotron X-ray refraction computed tomography (SXRCT) can quantify damage induced by hydrogen embrittlement in a lean duplex steel, yielding results that overperform even those achievable by synchrotron X-ray absorption computed tomography. As already reported in literature, but this time using a non-destructive technique, we show that the hydrogen charge does not penetrate to the center of tensile specimens. By the comparison between virgin and hydrogen-charged specimens, we deduce that cracks in the specimen bulk are due to the rolling process rather than hydrogen-assisted. We show that (micro)cracks propagate from the surface of tensile specimens to the interior with increasing applied strain, and we deduce that a significant crack propagation can only be observed short before rupture.
The European Metrology Network (EMN) for Advanced Manufacturing has been established in June 2021. Currently nine EMNs focussing on different important topics of strategic importance for Europe exist and form an integral part of EURAMET, the European Association of National Metrology Institutes (NMI). EMNs are tasked to ▪ develop a high-level coordination of the metrology community in Europe in a close dialogue with the respective stakeholders (SH)
▪ develop a strategic research agenda (SRA) within their thematic areas
▪ provide contributions to the European Partnership on Metrology research programme Based on the analysis of existing metrology infrastructures and capabilities of NMIs, the metrology research needs for advanced manufacturing are identified in close cooperation with academic, governmental and industrial stakeholders.
Here, we report on the progress of the EMN for Advanced Manufacturing.
Additively manufactured (AM) metallic sheet-based Triply Periodic Minimal Surface Structures (TPMSS) meet several requirements in both bio-medical and engineering fields: Tunable mechanical properties, low sensitivity to manufacturing defects, mechanical stability, and high energy absorption. However, they also present some challenges related to quality control. In fact, the optimization of both the AM process and the properties of TPMSS is impossible without considering structural characteristics as manufacturing accuracy, internal defects, and as well as surface topography and roughness. In this study, the quantitative non-destructive analysis of TPMSS manufactured from Ti-6Al-4V alloy by electron beam melting was performed by means of laboratory X-ray computed tomography (XCT).
The residual stresses and load transfer in multiphase metal alloys and their composites (with both random planar-oriented short fibers and particles) will be shown, as studied by neutron diffraction, by X-ray computed tomography, and by a model based on the reformulation of classic Maxwell’s homogenization method.
Contrary to common understanding and state-of-the-art models, we experimentally observe that randomly oriented phases possess non-hydrostatic residual stress. Moreover, we disclose that the unreinforced matrix alloy stays under hydrostatic compression even under external uniaxial compression.
The recently developed modeling approach allows calculating the residual stress in all phases of the composites. It rationalizes the presence of deviatoric stresses accounting for the interaction of random oriented phases with fibers having preferential orientation. It also allows the explanation of the unconventional in-situ behavior of the unreinforced alloy and the prediction of the micromechanical behavior of other similar alloys.
Additively manufactured (AM) triply periodic metallic minimum surface structures (TPMSS, from the English Triply Periodic Minimum Surface Structures) fulfill several requirements in both biomedical and engineering fields: tunable mechanical properties, low sensitivity to manufacturing defects, mechanical stability, and high energy absorption. However, they also present some quality control challenges that may prevent their successful application. In fact, optimization of the AM process is impossible without considering structural features such as manufacturing accuracy, internal defects, and surface topography and roughness. In this study, quantitative nondestructive analysis of Ti-6Al-4V alloy TPMSS was performed using X-ray computed tomography (XCT). Several new image analysis workflows are presented to evaluate the effects of buildup direction on wall thickness distribution, wall degradation, and surface roughness reduction due to chemical etching of TPMSS. It is shown that the fabrication accuracy is different for the structural elements printed parallel and orthogonal to the fabricated layers. Different strategies for chemical etching showed different powder removal capabilities and thus a gradient in wall thickness. This affected the mechanical performance under compression by reducing the yield stress. A positive effect of chemical etching is the reduction of surface roughness, which can potentially improve the fatigue properties of the components. Finally, XCT was used to correlate the amount of powder retained with the pore size of the TPMSS, which can further improve the manufacturing process.
Copper sulfide shows some unique physico-chemical properties that make it appealing as a cathode active material (CAM) for solid-state batteries (SSBs). The most peculiar feature of the electrode reaction is the reversible formation of μm-sized Cu crystals during cycling, despite its large theoretical volume change (75%). Here, the dynamic microstructural evolution of CuS cathodes in SSBs is studied using in situ synchrotron X-ray tomography. The formation of μm-sized Cu within the CAM particles can be clearly followed. This process is accompanied by crack formation that can be prevented by increasing the stack pressure from 26 to 40 MPa. Both the Cu inclusions and cracks show a preferential orientation perpendicular to the cell stack pressure, which can be a result of a z-oriented expansion of the CAM particles during lithiation. In addition, cycling leads to a z-oriented reversible displacement of the cathode
pellet, which is linked to the plating/stripping of the Li counter electrode. The pronounced structural changes cause pressure changes of up to 6 MPa within the cell, as determined by operando stack pressure measurements. Reasons for the reversibility of the electrode reaction are discussed and are attributed to the favorable combination of soft materials.
While laser powder-bed fusion has overcome some of the design constraints of conventional manufacturing methods, it requires careful selection of process parameters and scan strategies to obtain favorable properties. Here we show that even simple scan strategies, complex ones being inevitable when printing intricate designs, can inadvertently produce local alterations of the microstructure and preferential grain orientation over small areas – which easily remain unnoticed across the macroscale. We describe how a combined usage of neutron imaging and electron backscatter diffraction can reveal these localized variations and explain their origin within cm-sized parts. We explain the observed contrast variations by linking the neutron images to simulated data, pole figures and EBSD, providing an invaluable reference for future studies and showing that presumably minor changes of the scan strategy can have detrimental effects on the mechanical properties. In-situ tensile tests reveal that fracture occurs in a region that was re-melted during the building process.
The detection of internal irregularities is crucial for quality assessment in metal-based additive manufacturing (AM) technologies such as laser powder bed fusion (L-PBF). The utilization of in-process thermography as an in situ monitoring tool in combination with post-process X-ray micro computed tomography (XCT) as a reference technique has shown great potential for this aim. Due to the small irregularity dimensions, a precise registration of the datasets is necessary as a
requirement for correlation. In this study, the registration of thermography and XCT reference datasets of a cylindric specimen containing keyhole pores is carried out for the development of a porosity prediction model. The considered datasets show variations in shape, data type and dimensionality, especially due to shrinkage and material elevation effects present in the manufactured part. Since the resulting deformations are challenging for registration, a novel preprocessing methodology is introduced that involves an adaptive volume adjustment algorithm which is based on the porosity distribution in the specimen. Thus, the implementation of a simple three-dimensional image-to-image registration is enabled. The results demonstrate the influence of the part deformation on the resulting porosity location and the importance of registration in terms of irregularity prediction.
The interplay between free charge carriers, charge transfer (CT) states and singlet excitons (S1) determines the recombination pathway and the resulting open circuit voltage (VOC) of organic solar cells. By combining a well-aggregated low bandgap polymer with different blend ratios of the fullerenes PCBM and ICBA, the energy of the CT state (ECT) is varied by 130 meV while leaving the S1 energy of the polymer (ES1) unaffected. It is found that the polymer exciton dominates the radiative properties of the blend when ECT approaches ES1, while the VOC remains limited by the non-radiative decay of the CT state. It is concluded that an increasing strength of the exciton in the optical spectra of organic solar cells will generally decrease the non-radiative voltage loss because it lowers the radiative VOC limit (VOC,rad), but not because it is more emissive. The analysis further suggests that electronic coupling between the CT state and the S1 will not improve the VOC, but rather reduce the VOC,rad. It is anticipated that only at very low CT state absorption combined with a fairly high CT radiative efficiency the solar cell benefit from the radiative properties of the singlet excitons.
The ability of industrial X-ray computed tomography (CT) to scan an object with several internal and external features at once causes increasing adoption in dimensional metrology. In order to evaluate the quality of a measurement value, the task-specific measurement uncertainty has to be determined. Currently, VDI/VDE 2630 part 2.1 gives a guideline to determine the uncertainty of CT measurements experimentally by conducting repeated measurements. This is costly and time-consuming. Thus, the aim is to determine the task-specific measurement uncertainty numerically by simulations (e. g. according to the guide to expression of uncertainty in measurement (GUM) Supplement 1). To achieve that, a digital twin is necessary. This contribution presents a simple first approach how a digital twin can be built. In order to evaluate this approach, a study comparing measurements and simulations of different real CT systems was carried out by determining the differences between the measurement results of the digital twin and of the measurement results of the real-world CT systems. The results have shown a moderate agreement between real and simulated data. To improve on this aspect, a standardized method to characterize CT systems and methods to implement CT parameters into the simulation with sufficient accuracy will be developed.
This contribution presents a set of largely novel reference standards specially designed for testing different important physical effects and functionalities of radiography-based computed tomography (CT) simulation software. These standards were developed within the scope of the German cooperation project “CTSimU – Radiographic Computed Tomography Simulation for Measurement Uncertainty Evaluation” [1] and serve as tools for the basic qualification of the sufficient physical correctness and required features of simulation software of CT-based coordinate measurement systems (CMSs) via the analyses either of 2D projection images only or of full CT scans. The results serve as input to the German standardisation committee for the development of a new national VDI/VDE guideline in the series VDI/VDE 2630 dealing with the basic qualification aspect of CT simulation software and shall lay ground for the measurement uncertainty determination of dimensional measurements using CT.
Integration of fiber reinforcement in high-performance cementitious materials has become widely applied in many fields of construction. One of the most investigated advantages of steel Fiber reinforced concrete (SFRC) is the deceleration of crack growth and hence its improved sustainability.
Additional benefits are associated with its structural properties, as fibers can significantly increase the ductility and the tensile strength of concrete. In some applications it is even possible to entirely replace the conventional reinforcement, leading to significant logistical and environmental benefits.
Fiber reinforcement can, however, have critical disadvantages and even hinder the Performance of concrete, since it can induce an anisotropic material behavior of the mixture if the fibers are not appropriately oriented. For a safe use of SFRC in the future, reliable non-destructive testing (NDT) methods need to be identified to assess the fibers’ orientation in hardened concrete. In this study,
ultrasonic material testing, electrical impedance testing, and X-ray computed tomography have been investigated for this purpose using specially produced samples with biased or random Fiber orientations. We demonstrate the capabilities of each of these NDT techniques for fiber orientation measurements and draw conclusions based on these results about the most promising areas for future research and development.
The overview of the activity of group 8.5 Micro-NDT (BAM, Belin, Germany) in the field of additively manufacturing material characterization will be presented. The challenges in the residual stress analysis of AM components are discussed on the basis on the show studies performed in BAM. Also, the synchrotron X-ray refraction technique, available in BAM, is presented, showing example of in-situ heating test of Al10SiMg AM material.
X-ray refraction is an excellent tool for the characterization of the microstructure of materials. However, there are only a few (synchrotron) laboratories in the world that use this technique for material characterisation. Therefore, the seminar will first explain the basic principles of X-ray refraction and the measurement techniques installed at the hard X-ray beamline BAMline at BESSY II (Berlin, Germany). This is followed by examples of investigations on fibre-reinforced plastic composites (CFRP) as well as ceramic (Cordierite, ZrO2-SiO2) and metallic materials (Ti-6Al-4V, Inconel). Some of the investigations were carried out both ex-situ and in-situ under mechanical and thermal load. The results are correlated with the mechanical properties of the materials.
The micromechanical behavior of an annealed Ti-6Al-4V material produced by Laser Powder Bed Fusion was characterized by means of in-situ synchrotron X-ray diffraction during a tensile test. The lattice strain evolution was obtained parallel and transversal to the loading direction. The elastic constants were determined and compared with the conventionally manufactured alloy. In the plastic regime, a lower plastic anisotropy exhibited by the lattice planes was observed along the load axis (parallel to the building direction) than in the transverse direction.
Also, the load transfer from α to β phase was observed, increasing global ductility of the material. The material seems to accumulate a significant amount of intergranular strain in the transverse direction.
What is meant by ‘Micro Non-Destructive Testing and Evaluation’? This was the central subject of debate in this Special Issue.
At present, sub-millimeter-size components or even assemblies are pervading the industrial and scientific world. Classic examples are electronic devices and watches (as well as parts thereof), but recent examples encompass additively manufactured lattice structures, stents, or other microparts. Moreover, most assemblies contain micro-components. Testing such components or their miniaturized parts would fit well within the topic of micro non-destructive testing and evaluation.
In all cases, performance and integrity testing, quality control, and dimensional tolerances need to be measured at the sub-millimeter level (ideally with a spatial resolution of about a micron); most of the time, such features and components are embedded in much larger assemblies, which also need to be taken into account. The solution to this dilemma (i.e. measuring large parts with high resolution) depends on the part and on the problem under consideration.
Another possible definition of micro non-destructive testing and evaluation can relate to the characterization of micro-features (e.g., the microstructure) in much larger specimens, such as damage in concrete cores or porosity in additively manufactured components. A further aspect is the use of microscopic probes to evaluate macroscopic properties. This is the case, for instance but not at all exclusively, in the use of diffraction techniques to determine macroscopic stress.
The splits between testing and characterization at the micro-level (or of micro parts) from one side and handling of macroscopic assemblies on the other represent a great challenge for many fields of materials characterization. On top of that, including the use of microscopic methods to test integrity would add a further level of complexity.
Imaging, mechanical testing, non-destructive testing, measurement of properties, structural health monitoring, and dimensional metrology all need to be re-defined if we want to cope with the multi-faceted topic of micro non-destructive testing and evaluation.
The challenge has already been accepted by the scientific and engineering communities for a while but is still far from being universally tackled. This Special Issue yields an interesting answer to the questions posed above. It presents the progress made and the different aspects of the challenge as well as at indicates the paths for the future of NDT&E.
What is meant by ‘Micro Non-Destructive Testing and Evaluation’? This was the central subject of debate in this Special Issue.
At present, sub-millimeter-size components or even assemblies are pervading the industrial and scientific world. Classic examples are electronic devices and watches (as well as parts thereof), but recent examples encompass additively manufactured lattice structures, stents, or other microparts. Moreover, most assemblies contain micro-components. Testing such components or their miniaturized parts would fit well within the topic of micro non-destructive testing and evaluation.
In all cases, performance and integrity testing, quality control, and dimensional tolerances need to be measured at the sub-millimeter level (ideally with a spatial resolution of about a micron); most of the time, such features and components are embedded in much larger assemblies, which also need to be taken into account. The solution to this dilemma (i.e. measuring large parts with high resolution) depends on the part and on the problem under consideration.
Another possible definition of micro non-destructive testing and evaluation can relate to the characterization of micro-features (e.g., the microstructure) in much larger specimens, such as damage in concrete cores or porosity in additively manufactured components. A further aspect is the use of microscopic probes to evaluate macroscopic properties. This is the case, for instance but not at all exclusively, in the use of diffraction techniques to determine macroscopic stress.
The splits between testing and characterization at the micro-level (or of micro parts) from one side and handling of macroscopic assemblies on the other represent a great challenge for many fields of materials characterization. On top of that, including the use of microscopic methods to test integrity would add a further level of complexity.
Imaging, mechanical testing, non-destructive testing, measurement of properties, structural health monitoring, and dimensional metrology all need to be re-defined if we want to cope with the multi-faceted topic of micro non-destructive testing and evaluation.
The challenge has already been accepted by the scientific and engineering communities for a while but is still far from being universally tackled. This Special Issue yields an interesting answer to the questions posed above. It presents the progress made and the different aspects of the challenge as well as at indicates the paths for the future of NDT&E.
Methodologies for model parameterization of virtual CTs for measurement uncertainty estimation
(2022)
X-ray computed tomography (XCT) is a fast-growing technology for dimensional measurements in industrial applications. However, traceable and efficient methods to determine measurement uncertainties are not available. Guidelines like the VDI/VDE 2630 Part 2.1 suggest at least 20 repetitions of a specific measurement task, which is not feasible for industrial standards. Simulation-based approaches to determine task specific measurement uncertainties are promising, but require closely adjusted model parameters and an integration of error sources like geometrical deviations during a measurement. Unfortunately, the development of an automated process to parameterize and integrate geometrical deviations into XCT models is still an open issue. In this work, the whole processing chain of dimensional XCT measurements is taken into account with focus on the issues and requirements to determine suitable parameters of geometrical deviations. Starting off with baseline simulations of different XCT systems, two approaches are investigated to determine and integrate geometrical deviations of reference measurements. The first approach tries to iteratively estimate geometric deviation parameter values to match the characteristics of the missing error sources. The second approach estimates those values based on radiographs of a known calibrated reference object. In contrast to prior work both approaches only use a condensed set of parameters to map geometric deviations. In case of the iterative approach, some major issues regarding unhandled directional dependencies have been identified and discussed. Whereas the radiographic method resulted in task specific expanded measurements uncertainties below one micrometre even for bi-directional features, which is a step closer towards a true digital twin for uncertainty estimations in dimensional XCT.
Seit der Antike gehört die Medea-Sage zu den bekanntesten Geschichten der Weltliteratur. Der berühmte französische Künstler Carle Van Loo hat sich dieses Epos um 1759 angenommen und ein beeindruckendes Ölgemälde mit Abmessungen von 2,30x3,28m² erschaffen. Mit Mademoiselle Clairon als Medea und Henri Louis Le Kain als Jason ist ein Kunstwerk entstanden, das seitdem einige Veränderungen und Restaurierungen erfahren hat.
Die Bundesanstalt für Materialforschung und -prüfung (BAM) hatte 2020 die Möglichkeit, dieses und ein zweites Kunstwerk, im Neuen Palais in Potsdam, für die Stiftung Preußische Schlösser und Gärten Berlin-Brandenburg, radiografisch zu untersuchen. Hierbei wurden sowohl technologisch als auch kunsthistorisch einige interessante Entdeckungen gemacht, die im vorliegenden Beitrag vorgestellt werden.
Manufacturing austenitic stainless steels (ASSs) using additive manufacturing is of great interest for cryogenic applications. Here, the mechanical and microstructural responses of a 316L ASS built by laser powder bed fusion were revealed by performing in situ neutron diffraction tensile tests at the low-temperature range (from 373 to 10 K). The stacking fault energy almost linearly decreased from 29.2 ± 3.1 mJm⁻² at 373 K to 7.5 ± 1.7 mJm⁻² at 10 K, with a slope of 0.06 mJm⁻²K⁻¹, leading to the transition of the dominant deformation mechanism from strain-induced twinning to martensite formation. As a result, excellent combinations of strength and ductility were achieved at the low-temperature range.
Metal Additive Manufacturing (AM) technologies such as Laser Powder Bed Fusion (LPBF) are characterized by layer wise construction, which enable advancements of component design, with associated potential gains in performance and efficiency. However, high magnitude residual stresses (RS) are often a product of the rapid thermal cycles typical of the layerwise process. Therefore, a deep understanding of the formation of RS, the influence of process parameters on their magnitude and the impact on mechanical performance is crucial for widespread application. The experimental characterisation of these RS is essential for safety related engineering application and supports the development of reliable numerical models. Diffraction-based methods for RS analysis using neutrons and high energy X-rays enable non-destructive spatially resolved characterisation of both surface and bulk residual stresses in complex components. This presentation will provide an overview of recent research by the BAM at large scale facilities for the characterization of residual stresses in LPBF metallic alloys as a function of process parameters. In addition, the challenges posed by the textured and hierarchical microstructures of LPBF materials on diffraction-based RS analysis in AM materials will be discussed. This will include the question of the d0 reference lattice spacing and the appropriate choice of the diffraction elastic constants (DECs) to calculate the level of RS in LPBF manufactured alloys.
Laser powder-based directed energy deposition (DED-L) is a technology that offers the possibility for 3D material deposition over hundreds of layers and has thus the potential for application in additive manufacturing (AM). However, to achieve broad industrial application as AM technology, more data and knowledge about the fabricated materials regarding the achieved properties and their relationship to the manufacturing process and the resulting microstructure is still needed. In this work, we present data regarding the low-cycle fatigue (LCF) behavior of Ti-6Al-4V. The material was fabricated using an optimized DED-L process. It features a low defect population and excellent tensile properties. To assess its LCF behavior two conventionally manufactured variants of the same alloy featuring different microstructures were additionally tested. The strain-controlled LCF tests were carried out in fully reversed mode with 0.3 % to 1.0 % axial strain amplitude from room temperature up to 400°C. The LCF behavior and failure mechanisms are described. For characterization, optical microscopy (OM), scanning electron microscopy (SEM), and micro-computed tomography (µCT) were used. The low defect population allows for a better understanding of the intrinsic material’s properties and enables a fairer comparison against the conventional variants. The fatigue lifetimes of the DED-L material are nearly independent of the test temperature. At elevated test temperatures, they are similar or higher than the lifetimes of the conventional counterparts. At room temperature, they are only surpassed by the lifetimes of one of them. The principal failure mechanism involves multiple crack initiation sites.
In X-ray computed tomography (XCT), an X-ray beam of intensity I0 is transmitted through an object and its attenuated intensity I is measured when it exits the object. The attenuation of the beam depends on the attenuation coefficients along its path. The attenuation coefficients provide information about the structure and composition of the object and can be determined through mathematical operations that are referred to as reconstruction. The standard reconstruction algorithms are based on the filtered backprojection (FBP) of the measured data. While these algorithms are fast and relatively simple, they do not always succeed in computing a precise reconstruction, especially from under-sampled data. Alternatively, an image or volume can be reconstructed by solving a system of linear equations. Typically, the system of equations is too large to be solved but its solution can be approximated by iterative methods, such as the Simultaneous Iterative Reconstruction Technique (SIRT) and the Conjugate Gradient Least Squares (CGLS). This dissertation focuses on the development of a novel iterative algorithm, the Direct Iterative Reconstruction of Computed Tomography Trajectories (DIRECTT). After its reconstruction principle is explained, its performance is assessed for real parallel- and cone-beam CT (including under-sampled) data and compared to that of other established algorithms. Finally, it is demonstrated how the shape of the measured object can be modelled into DIRECTT to achieve even better reconstruction results.
Laser Powder Bed Fusion (L-PBF) allow the fabrication of lightweight near net shape AlSi10Mg components attractive to the aerospace, automotive, biomedical and military industries. During the build-up process, high cooling rates occur. Thus, L-PBF AlSi10Mg alloys exhibit a Si-nanostructure in the as-built condition, which leads to superior mechanical properties compared to conventional cast materials. At the same time, such high thermal gradients generally involve a deleterious residual stress (RS) state that needs to be assessed during the design process, before placing a component in service. To this purpose post-process heat treatments are commonly performed to relieve detrimental RS. In this contribution two low-temperature stress-relief heat treatments (SRHT) are studied and compared with the as-built state: a SRHT at 265°C for 1 hour and a SRHT at 300°C for 2 hours. At these temperatures microstructural changes occur. In the as-built state, Si atoms are supersaturated in the α-aluminium matrix, which is enveloped by a eutectic Si-network. At 265°C the Si precipitation from the matrix to the pre-existing network is triggered. Thereafter, above 295°C the fragmentation and spheroidization of the Si branches takes place, presumably by Al–Si interdiffusion. After 2 hours the original eutectic network is completely replaced by uniformly distributed blocky particles. The effect of the heat and the microstructure modification on the RS state and the fatigue properties is investigated. Energy dispersive x-ray and neutron diffraction are combined to investigate the near-surface and bulk RS state of a L-PBF AlSi10Mg material. Differences in the endurance limit are evaluated experimentally by high cycle fatigue (HCF) tests and cyclic R-curve determination.
Al-Si alloys produced by Laser Powder Bed Fusion (L-PBF) techniques allow the fabrication of lightweight free-shape components that find space in aerospace, automotive, biomedical and military applications. Due to the high cooling rates occurring during the building process, L-PBF AlSi10Mg alloys exhibit an ultra-fine microstructure that leads to superior mechanical properties in the as-built condition compared to conventional cast Al-Si materials. Nevertheless, L-PBF processing induces high thermal gradients, leading to deleterious residual stress levels that must be considered to avoid part distortion and unpredicted failures. In order to relax detrimental residual stress and to increase the ductility, post-processing stress relief treatments are generally performed. In as-built condition the hypoeutectic AlSi10Mg microstructure consist of fine α-Al cells containing uniformly dispersed silicon nanoparticles, which are, in addition, surrounded by a eutectic Si network. Above 260°C the silicon interconnectivity starts to breakdown into spheroidized particles and to coarsen. At the same time, the heating residual stresses are relieved.
The objective of the contribution is to investigate, under different heat treatment conditions, the evolution of microstructure and residual stresses in view of optimizing the fatigue performance of the alloy. To this purpose various heat treatments in a range of temperatures between 265°C and 300°C for a duration between 15 minutes and 2 hours are performed. The microstructure modifications are analysed using a scanning electron microscope and the residual stress state is measured by laboratory X-ray diffraction.
Influence of the Composition on the Compressive Behaviour of a Semi-Metallic Brake-Pad Material
(2022)
The contact interface between the rotation and static part of a friction brake is central to the optimal functioning of the brake system due to the occurrence of heat dissipation, mechanical interaction and thermal exchanges. Generally, braking performances are evaluated by the energetic efficiency and wear rates of the contact surface. However, the compressive behaviour of the contact materials has also a significant contribution to the overall performances. In this work, the meso- and microscopic compressive behaviour of a sintered semi-metallic brake-pad material is investigated mainly via compression testing coupled with Digital Image Correlation (DIC) technique, as well as optical and scanning electron microscopy (SEM) analysis. The composition of a reference material (RM) is simplified to a selection of nine components, as opposed to up to thirty components typically used in commercial brake-pad materials. The retained components are considered as the most crucial for safe-operating performances. At the studied stress levels, the RM material is flexible (E = 5330 MPa), deformable (Ezz−plastic = −0.21%), and exhibits hysteresis loops. Subsequently, the contribution to the mechanical response of each individual component is investigated by producing the so-called dissociated materials, where the number of components is, at a time, further reduced. It is observed that the macroscopic behaviour is mainly controlled by the content (i.e., size distribution, shape and nature) of graphite particles, and that the hysteresis is only related to one of the two types of graphite used (G2 particles). Moreover, RM containing 13 wt% of G2 particles embedded in a relatively soft matrix (10.86 GPa) is able to increase the hysteresis (by 35%) when compared to the dissociated material containing 20 wt% of G2 particles which is embedded in a stiffer matrix (E = 106 GPa).
Influence of Surface Preparation on Cracking Phenomena in TIG-Welded High and Medium Entropy Alloys
(2022)
Multi-element systems with defined entropy (HEA—high entropy alloy or MEA—medium entropy alloy) are rather new material concepts that are becoming increasingly important in materials research and development. Some HEA systems show significantly improved properties or combinations of properties, e.g., the overcoming of the trade-off between high strength and ductility. Thus, the synthesis, the resulting microstructures, and properties of HEA have been primarily investigated so far. In addition, processing is crucial to achieve a transfer of potential HEA/MEA materials to real applications, e.g., highly stressed components. Since fusion welding is the most important joining process for metals, it is of vital importance to investigate the weldability of these materials. However, this has rarely been the subject of research to date. For that reason, in this work, the weldability depending on the surface preparation of a CoCrFeMnNi HEA and a CoCrNi MEA for TIG welding is investigated. The fusion welding of longer plates is described here for the first time for the CoCrNi alloy. The welds of both materials showed distinct formation of cracks in the heat affected Zone (HAZ). Optical and scanning electron microscopy analysis clearly confirmed an intergranular fracture topography. However, based on the results, the crack mechanism cannot be conclusively identified as either a liquid metal embrittlement (LME) or hot cracking-like liquid film separation.
An important focus of research in Industrial X-ray Computed Tomography (CT) is to determine the task-specific measurement uncertainty of CT measurements numerically by using simulations. For this, all relevant influence factors need to be identified and quantified. It is known, for example, that geometrical misalignments of the detector lead to measurement deviations if the reconstruction does not consider these misalignments. This contribution uses computer simulation of CT data to investigate the influence of geometrical misalignments of the detector on several measurands found in typical measurements tasks in the industry. A newly developed test specimen with a broad variety of features is used for this study. Angular and positional detector deviations are systematically introduced into the simulations and deliberately left uncompensated during the CT reconstruction. The resulting measurement deviations are shown and discussed.
Influence of a 265 °C heat treatment on the residual stress state of a PBF-LB/M AlSi10Mg alloy
(2022)
Laser Powder Bed Fusion (PBF-LB/M) additive manufacturing (AM) induces
high magnitude residual stress (RS) in structures due to the extremely heterogeneous cooling and heating rates. As the RS can be deleterious to the fatigue resistance of engineering components, great efforts are focused on understanding their generation and evolution after post-process heat treatments. In this study, one of the few of its kind, the RS relaxation induced in an as-built PBF-LB/M AlSi10Mg material by a low-temperature heat treatment (265 °C for 1 h) is studied by means of X-ray and neutron diffraction. Since the specimens are manufactured using a baseplate heated up to 200 °C, low RS are found in the as-built condition. After heat treatment a redistribution of the RS is observed, while their magnitude remains constant. It is proposed that the redistribution is induced by a repartition of stresses between the a-aluminium matrix and the silicon phase, as the morphology of the silicon phase is affected by the heat treatment. A considerable scatter is observed in the neutron diffraction RS profiles, which is principally correlated to the presence (or absence) of pockets of porosity developed at the borders of the chessboard pattern.
In this work, we present the recent in-situ imaging developments at the BAMline (of synchrotron BESSY II, HZB), focused on the in-situ characterization and understanding of microstructural evolution of additively manufactured materials subjected to different environments. Two show cases are presented. In the first, X-ray refraction radiography (SXRR) was combined with in-situ heat treatment to monitor the microstructural evolution as a function of temperature in a laser powder bed fusion (LPBF) manufactured AlSi10Mg alloy. We show that SXRR allows detecting the changes in the Si-phase morphology upon heating using statistically relevant volumes. SXRR also allows observing the growth of pores (i.e., thermally induced porosity), usually studied via X-ray computed tomography (XCT), but using much smaller fields-of-view. In the second case study, XCT was combined with in-situ tensile test to investigate the damage mechanism in a LPBF Aluminum Metal Matrix Composite (MMC). In-situ SXCT test disclosed the critical role of the defects in the failure mechanism along with pre-cracks in the reinforcement phase of MMC. We found that cracks were initiated from lack-of-fusion defects and propagated through coalescence with other defects.
Contour scanning and process gas type are process parameters typically considered achieving second order effects compared to first order factors such as laser power and scanning speed. The present work highlights that contour scanning is crucial to ensure geometrical accuracy and thereby the high performance under uniaxial compression of complex Alloy 718 lattice structures. Studies of X-ray computed tomography visualizations of as-built and compression-strained structures reveal the continuous and smooth bending and compression of the walls, and the earlier onset of internal contact appearance in the denser lattices printed with contour. In contrast, the effect of addition of He to the Ar process gas appears to have limited influence on the mechanical response of the lattices and their microstructure as characterized by electron backscattered diffraction. However, the addition of He proved to significantly enhance the cooling rate and to reduce the amount of the generated spatters as evidenced by in situ monitoring of the process emissions, which is very promising for the process stability and powder reusability during laser powder bed fusion.
This sequence of X-Ray images shows how one of the most common Italian moka pots actually work! The sequence starts with a completely prepared moka pot (water in the bottom part, coffee in the middle and hot plate on). During the process the water starts to boil and the steam pressure pushes the hot water through the coffee into the bassin at the top of the pot.
This video sequence and additional explanations can also be found on Wikipedia.
In recent years, low-temperature polymer electrolyte fuel cells have become an increasingly important pillar in a zero-carbon strategy for curbing climate change, with their potential to power multiscale stationary and mobile applications. The performance improvement is a particular focus of research and engineering roadmaps, with water management being one of the major areas of interest for development. Appropriate characterisation tools for mapping the evolution, motion and removal of water are of high importance to tackle shortcomings.
This article demonstrates the development of a 4D high-speed neutron imaging technique, which enables a quantitative analysis of the local water evolution. 4D visualisation allows the time-resolved studies of droplet formation in the flow fields and water quantification in various cell parts. Performance parameters for water management are identified that offer a method of cell classification, which will, in turn, support computer modelling and the engineering of next-generation flow field designs.
The BAMline at the 3rd generation synchrotron X-ray source BESSY II has been supporting researchers in a wide range of research areas for over 20 years. In addition to materials science, these fields also include biology, cultural heritage, and medicine. Being a non-destructive characterization method, synchrotron X-ray imaging, in particular tomography (SXCT), plays a particularly important role in structural characterization. A recent upgrade of key BAMline equipment expands the imaging capabilities: The upgraded dual multilayer monochromator offers flexibility by providing different energy spectra to optimize flux and energy resolution as desired. Different spectra (8 – 60 keV with ΔE/E 0.01%, 1.5%, 4% and pink beam) can be selected. The upgraded detector (in white beam configuration, equipped with an sCMOS camera) allows the higher flux to be exploited with reduced readout times. Shorter tomographic acquisition times in the range of seconds are now possible. Hence, in-situ and operando examinations are routinely available. An integrated slip ring allows continuous rotation of the sample stage for ease of wiring. The pink beam option allows tomographic observation of processes occurring in the time domain of a few seconds with a resolution down to ~ 1 µm. Different scan methods, optimized for quality and speed are available and discussed. Examples of energy related materials from fuel cell and battery research are shown.
An optional end station allows refraction enhanced imaging (synchrotron X-Ray refraction radiography (SXRR) and tomography (SXRCT)). That includes an analyzer Si-crystal in Bragg alignment between sample and detector. This technique obtains sensitivity to smaller structures (cracks, pores) down to a few wavelengths, while obtaining field of view sizes in the range of several mm. Besides medicine (e.g., teeth explants), several applications are found in material science, like studies on diesel particulate filters, ceramics, additively manufactured (AM) alloys and metal matrix composites (MMC). The in-situ capabilities include mechanical load (tension and compression) and heating up to 1100°C. A case study, the microstructural evolution during heat treatment of an AM AlSi10Mg, will be shown.
Laser powder bed fusion (PBF-LB/M) of metallic alloys is a layer wise additive manufacturing process which provides significant scope for more efficient designs of components, benefiting performance and weight, leading to efficiency improvements for various sectors of industry. However, to benefit from these design freedoms, knowledge of the high produced induced residual stress and mechanical property anisotropy associated with the unique microstructures is critical. X-ray and neutron diffraction are considered the benchmark for non-destructive characterization of surface and bulk internal residual stress. The latter, characterized by the high penetration power in most engineering alloys, allows for the use of diffraction angle close to 90° enabling a near cubic sampling volume to be specified. However, the complex microstructures of columnar growth with inherent crystallographic texture typically produced during PBF-LB/M of metallics present significant challenges to the assumptions typically required for time efficient determination of residual stress. These challenges include the selection of an appropriate set of diffraction elastic constants and a representative strain-free reference for the material of interest. In this presentation advancements in the field of diffraction-based residual stress analysis of L-PBF Inconel 718 will be presented. The choice of an appropriate set of diffraction-elastic constants depending on the underlying microstructure will be described.
Fluid inclusion microthermometry is one of the analytical approaches that has been proposed for speleothem-based temperature reconstructions. The proxy of this paleothermometer is the density of drip water relicts that have been enclosed in microscopic fluid inclusions during speleothem growth. Prior to microthermometric analyses, the monophase liquid inclusions need to be transferred from a metastable liquid into a stable liquid-vapour two-phase state by stimulating vapour bubble nucleation by means of single ultra-short laser pulses. Subsequent microthermometric analyses determine the temperature at which the vapour bubble disappears again, the so-called liquid-vapour homogenisation temperature (Th(obs) ). The observed homogenisation temperature depends not only on the water density but also on the inclusion volume. In order to determine the water density, a thermodynamic model is used that takes account of the effect of surface tension on Th(obs) to calculate Th∞. This is the corresponding homogenisation temperature at saturation pressure that determines the water density and defines the formation temperature of the fluid inclusion. The analytical precision of the method ranges between 0.1 and 0.3 °C depending on the size of the inclusions.
The benefits of including fibers in ultra-high performance concrete (UHPC) are attributed to their good bond with the matrix and, hence, an optimal utilization of their properties. At the same time, though, fiber reinforcement may contribute to anisotropy in the composite material and induce weak areas. The influence of the fibers’ orientation on the material properties is a matter of current scientific discourse and it is known to play a vital role in structural design. In the case studies presented herein, mechanical laboratory tests using pulsating load regimes on UHPC with a strength of more than 200 MPa were simulated by use of finite element models. The orientations of the fibers were measured for each test sample prior to failure using an X-ray computed tomography (CT) scanner, and these orientations are explicitly implemented into the model. The paper discusses the methodology of merging data retrieved by CT image processing and state-of-the-art FE simulation techniques Moreover, the CT scanning was carried out throughout the testing procedure, which further enables the comparison of the mechanical tests and the FE models in terms of damage propagation and failure patterns. The results indicate that the overall fiber configuration and behavior of the samples can be realistically modelled and validated by the proposed CT-FE coupling, which can enhance the structural analysis and design process of elements produced with steel fiber reinforced and UHPC materials.
Most of the Al alloys used in additive manufacturing (AM), in particular Laser Powder Bed Fusion (LPBF), do not exceed a strength of 200 MPa, whereas conventionally high-performance alloys exhibit strengths exceeding 400 MPa. The availability of such Al alloys in AM is limited due to difficulties in printability, requiring synergetic material and AM process development to satisfy harsh processing conditions during LPBF [1]. One approach is the addition of reinforcement to the based powder, allowing tailoring composition and properties of a Metal Matrix Composite (MMC) by AM. Still, the effect of the reinforcement on the resulting mechanical properties must be studied to understand the performance and limits of the newly developed material. The goal of this work was to investigate the failure mechanism of LPBF Al-based MMC material using in-situ Synchrotron X-ray Computed Tomography (SXCT) during mechanical testing.
The availability of high-performance Al alloys in AM is limited due to difficulties in printability, requiring both the development of synergetic material and AM process to mitigate problems such as solidification cracking during laser powder bed fusion (LPBF). The goal of this work was to investigate the failure mechanism in a LPBF 7017 Aluminium alloy + 3 wt% Zr + 0.5 wt% TiC. The processing leads to different categories of Zr-rich inclusions, precipitates and defects.
In this work, two X-ray refraction based imaging methods, namely, synchrotron X-ray refraction radiography (SXRR) and synchrotron X-ray refraction computed tomography (SXRCT), are applied to analyze quantitatively cracks and porosity in metallic materials.
SXRR and SXRCT make use of the refraction of X-rays at inner surfaces of the material, e.g., the surfaces of cracks and pores, for image contrast. Both methods are, therefore, sensitive to smaller defects than their absorption based counterparts X-ray radiography and computed tomography. They can detect defects of nanometric size.
So far the methods have been applied to the analysis of ceramic materials and fiber reinforced plastics. The analysis of metallic materials requires higher photon energies to achieve sufficient X-ray transmission due to their higher density. This causes smaller refraction angles and, thus, lower image contrast because the refraction index depends on the photon energy. Here, for the first time, a conclusive study is presented exploring the possibility to apply SXRR and SXRCT to metallic materials. It is shown that both methods can be optimized to overcome the reduced contrast due to smaller refraction angles. Hence, the only remaining limitation is the achievable X-ray Transmission which is common to all X-ray imaging methods. Further, a model for the quantitative analysis of the inner surfaces is presented and verified.
For this purpose four case studies are conducted each posing a specific challenge to the imaging task. Case study A investigates cracks in a coupon taken from an aluminum weld seam. This case study primarily serves to verify the model for quantitative analysis and prove the sensitivity to sub-resolution features. In case study B, the
damage evolution in an aluminum-based particle reinforced metal-matrix composite is analyzed. Here, the accuracy and repeatability of subsequent SXRR measurements is investigated showing that measurement errors of less than 3% can be achieved. Further, case study B marks the fist application of SXRR in combination with in-situ tensile loading. Case study C is out of the highly topical field of additive manufacturing. Here, porosity in additively manufactured Ti-Al6-V4 is analyzed with a special interest in the pore morphology. A classification scheme based on SXRR measurements is devised which allows to distinguish binding defects from keyhole pores even if the defects cannot be spatially resolved. In case study D, SXRCT is applied to the analysis of hydrogen assisted cracking in steel. Due to the high X-ray attenuation of steel a comparatively high photonenergy of 50 keV is required here. This causes increased noise and lower contrast in the data compared to the other case studies. However, despite the lower data quality a quantitative analysis of the occurance of cracks in dependence of hydrogen content and applied mechanical load is possible.
The residual stresses and load transfer in multiphase metal alloys and their composites (with both random planar-oriented short fibers and particles) will be shown, as studied by neutron diffraction, by X-ray computed tomography, and by a model based on the reformulation of classic Maxwell’s homogenization method.
Contrary to common understanding and state-of-the-art models, we experimentally observe that randomly oriented phases possess non-hydrostatic residual stress. Moreover, we disclose that the unreinforced matrix alloy stays under hydrostatic compression even under external uniaxial compression.
The recently developed modeling approach allows calculating the residual stress in all phases of the composites. It rationalizes the presence of deviatoric stresses accounting for the interaction of random oriented phases with fibers having preferential orientation. It also allows the explanation of the unconventional in-situ behavior of the unreinforced alloy and the prediction of the micromechanical behavior of other similar alloys.
The residual stresses and load transfer in multiphase metal alloys and their composites (with both random planar-oriented short fibers and particles) will be shown, as studied by neutron diffraction, by X-ray computed tomography, and by a model based on the reformulation of classic Maxwell’s homogenization method.
Contrary to common understanding and state-of-the-art models, we experimentally observe that randomly oriented phases possess non-hydrostatic residual stress. Moreover, we disclose that the unreinforced matrix alloy stays under hydrostatic compression even under external uniaxial compression.
The recently developed modeling approach allows calculating the residual stress in all phases of the composites. It rationalizes the presence of deviatoric stresses accounting for the interaction of random oriented phases with fibers having preferential orientation. It also allows the explanation of the unconventional in-situ behavior of the unreinforced alloy and the prediction of the micromechanical behavior of other similar alloys.
Entwicklung der Mikrostruktur der mechanischen Eigenschaften und der Eigenspannungen in L-PBF 316L
(2022)
Die additive Fertigung (AM) metallischer Werkstoffe mittels Laser Powder Bed Fusion (L-PBF) ermöglicht einzigartige hierarchische Mikrostrukturen, die zu Verbesserungen bestimmter mechanischer Eigenschaften gegenüber konventionell hergestellten Varianten derselben Legierung führen können. Allerdings ist das L-PBF-Verfahren häufig durch das Vorhandensein hoher Eigenspannungen gekennzeichnet, die es zu verstehen und zu mindern gilt. Daher ist das Verständnis der Mikrostrukturen, der Eigenspannungen und der daraus resultierenden mechanischen Eigenschaften entscheidend für eine breite Akzeptanz bei sicherheitskritischen Anwendungen. Die BAM hat ein multidisziplinäres Forschungsprogramm gestartet, um diese Aspekte bei LPBF 316L zu untersuchen. Der vorliegende Beitrag stellt einige der wichtigsten Ergebnisse vor: der Einfluss von Prozessparametern auf die Mikrostruktur, der Einfluss von Mikrostruktur und Textur auf die Festigkeit, Kriechverhalten und Schädigung und die Stabilität von Eigenspannungen und Mikrostruktur unter Wärmebehandlungsbedingungen.
In Hinblick auf den austenitischen Stahl AISI 316L erzeugt das pulverbettbasierte selektive Laserstrahlschmelzen, als ein additives Fertigungsverfahren, kristallographisch texturierte und Multiskalige Mikrostruktur. Einerseits können diese Mikrostrukturen zu einer Verbesserung der statischen mechanischen Eigenschaften führen (z. B. zu einer höheren Streckgrenze). Andererseits stehen diesen Verbesserungen der mechanischen Eigenschaften hohe Eigenspannungen gegenüber, die sich nachteilig auf das Ermüdungsverhalten auswirken können. Zur Reduzierung der Eigenspannungen und der daraus resultierenden negativen Auswirkungen auf die Ermüdungseigenschaften, werden Bauteile nach der Herstellung typischerweise wärmebehandelt. In dieser Studie wurde eine niedrige Wärmebehandlungstemperatur von 450°C höher temperierten Behandlungen bei 800 °C und 900 °C gegenübergestellt. Diese Wärmebehandlungstemperaturen bilden die oberen und die untere Grenze ein Spannungsarmglühendes Materials, ohne die prozessinduzierte Mikrostruktur signifikant zu verändern. Zusätzlich bieten diese Temperaturen den Vorteil, dass sie eine übermäßige intergranulare Ausscheidung von Karbiden und TCP-Phasen vermeiden, die zu einer Sensibilisierung des Werkstoffes gegen korrosive Umgebungen führen würden. Die Auswirkungen der Wärmebehandlung auf das Gefüge wurden mittels Rasterelektronenmikroskopie (BSE und EBSD) untersucht. Die Relaxation der Eigenspannungen wurde vor und nach den jeweiligen Wärmebehandlungen bei 800°C und 900°C mittels Neutronenbeugung charakterisiert. Die Ergebnisse zeigen, dass die Proben nach der Wärmebehandlung bei 900 °C nahezu spannungsfrei sind, was mit der Auflösung der zellularen Substruktur korreliert.
Al-Si alloys produced by Laser Powder Bed Fusion (PBF-LB/M) techniques allow the fabrication of lightweight free-shape components. Due to the extremely heterogeneous cooling and heating, PBF-LB/M induces high magnitude residual stress (RS) and a fine Si microstructure. As the RS can be deleterious to the fatigue resistance of engineering components, great efforts are focused on understanding their evolution before and after post-process heat treatments (HT).
The subsurface residual stress in laser powder bed fused 316L structures was analyzed using X-ray diffraction (XRD) and layer removal. The influence of varying structure thicknesses was investigated. In this study the importance of combining surface roughness measurements with XRD was shown. Moreover, a clear relation between the structure thickness and the subsurface residual stress profiles was observed.
In the present work, electron backscatter diffraction was used to determine the microscopic dislocation structures generated during creep (with tests interrupted at the steady state) in pure 99.8% aluminium. This material was investigated at two different stress levels, corresponding to the power-law and power-law breakdown regimes. The results show that the formation of subgrain cellular structures occurs independently of the crystallographic orientation. However, the density of these cellular structures strongly depends on the grain crystallographic orientation with respect to the tensile axis direction, with <111> grains exhibiting the highest densities at both stress levels. It is proposed that this behaviour is due to the influence of intergranular stresses, which is different in <111> and <001> grains.
The contribution discusses the processing and analysis of data generated on two different ways of investigations for impact damage in reinforced concrete structures. Damage investigations are essential to determine type and characteristics of damage and thus the residual capacity. Damage describing data is generated using two different types of investigation, a non-destructive tomographic as well as numerical examination. Subsequently, data of both sources was merged and analysed. Within the research project “Behaviour of structural components during impact load conditions caused by aircraft fuel tank collision” reinforces concrete plates were damaged by impact loading, see Hering (2020). Afterwards the damaged specimens were investigated tomographically as well as numerically using several methods and models. Aim of the presented research work was to specify an objective comparability of numerical data with experimentally determined damage patterns and based on this, to establish a quantitative damage evaluation.
The contribution discusses the processing and analysis of data generated on two different ways of investigations for impact damage in reinforced concrete structures. Damage investigations are essential to determine type and characteristics of damage and thus the residual capacity. Damage describing data is generated using two different types of investigation, a non-destructive tomographic as well as numerical examination. Subsequently, data of both sources was merged and analysed. Within the research project “Behaviour of structural components during impact load conditions caused by aircraft fuel tank collision” reinforces concrete plates were damaged by impact loading, see Hering (2020). Afterwards the damaged specimens were investigated tomographically as well as numerically using several methods and models. Aim of the presented research work was to specify an objective comparability of numerical data with experimentally determined damage patterns and based on this, to establish a quantitative damage evaluation.
Diffraction enhanced imaging (DEI) is an advanced digital radiographic imaging technique employing the refraction of X-rays to contrast internal interfaces. This study aims at qualitatively and quantitatively evaluating images acquired using this technique and to assess how different fitting functions to the typical rocking curves (RCs) influence the quality of images. RCs are obtained for every image pixel. This allows the separate determination of the absorption and the refraction properties of the material in a position-sensitive manner. Comparison of various types of fitting functions reveals that the Pseudo-Voigt (PsdV) function is best suited to fit typical RCs. A robust algorithm was developed in the Python programming language, which reliably extracts the physically meaningful information from each pixel of the image. We demonstrate the potential of the algorithm with two specimens: a silicone gel specimen that has well-defined interfaces, and an additively manufactured polycarbonate specimen.
Metal-based gas diffusion electrodes are utilized in chlor-alkali electrolysis or electrochemical reduction of carbon dioxide, allowing the reaction to proceed at high current densities. In contrast to planar electrodes and predominantly 2D designs, the industrially required high current densities can be achieved by intense contact between the gas and liquid phase with the catalytically active surfaces. An essential asset for the knowledge-based design of tailored electrodes is therefore in-depth information on electrolyte distribution and intrusion into the electrode’s porous structure. Lab-based and synchrotron radiography allow for monitoring this process operando. Herein, we describe the development of a cell design that can be modularly adapted and successfully used to monitor both the oxygen reduction reaction and the electrochemical reduction of CO2 as exemplary and currently very relevant examples of gas-liquid reactions by only minor modifications to the cell set-up. With the reported cell design, we were able to observe the electrolyte distribution within the gas diffusion electrode during cell operation in realistic
conditions.
Avoiding the formation of defects such as keyhole pores is a major challenge for the production of metal parts by Laser Powder Bed Fusion (LPBF). The use of in-situ monitoring by thermographic cameras is a promising approach to detect defects, however the data is hard to analyze by conventional algorithms. Therefore, we investigate the use of Machine Learning (ML) in this study, as it is a suitable tool to model complex processes with many influencing factors. A ML model for defect prediction is created based on features extracted from process thermograms. The porosity information calculated from an x-ray Micro Computed Tomography (µCT) scan is used as reference. Physical characteristics of the keyhole pore formation are incorporated into the model to increase the prediction accuracy. Based on the prediction result, the quality of the input data is inferred and future demands on in-situ monitoring of LPBF processes are derived.
The appearance of irregularities such as keyhole porosity is a major challenge for the production of metal parts by laser powder bed fusion (PBF-LB/M). The utilization of thermographic in-situ monitoring is a promising approach to extract the thermal history which is closely related to the formation of irregularities. In this study, we investigate the utilization of convolutional neural networks to predict keyhole porosity based on thermographic features. Here, the porosity information calculated from an x-ray micro computed tomography scan is used as reference. Feature engineering is performed to enable the model to learn the complex physical characteristics of the porosity formation. The model is examined with regard to the choice of hyperparameters, the significance of thermal features and characteristics of the data acquisition. Based on the results, future demands on irregularity prediction in PBF-LB/M are derived.
While there is a extensive literature on the micro-mechanical behavior of metal matrix composites (MMCs) under uniaxial applied stress, very little is available on multi-phase MMCs. In order to cast light on the reinforcement and damage processes in such multi-phase composites, an Al alloy with one and two ceramic reinforcements (planar-random oriented alumina fibers and SiC particles) were studied. In-situ compression tests during neutron diffraction experiments were used to track the load transfer among phases, while X-ray computed tomography was used to investigate pre-strained samples, in order to monitor and quantify damage. We found that damage progresses differently in composites with different orientations of the fiber mat. Because of the presence of the intermetallic network, it was observed that the second ceramic reinforcement changes the load transfer scenario only at very high applied load, when also intermetallic particles break. We rationalized the experimental results by means of a micromechanical model based on Maxwell’s homogenization scheme, and we could explain why no damage is observed in the ductile matrix under compression: the matrix finds itself in hydrostatic compression, and the Poisson’s tensile strain is totally carried by the reinforcement phases
Creep and creep damage behavior of stainless steel 316L manufactured by laser powder bed fusion
(2022)
This study presents a thorough characterization of the creep properties of austenitic stainless steel 316L produced by laser powder bed fusion (LPBF 316L) contributing to the sparse available data to date. Experimental results (mechanical tests, microscopy, X-ray computed tomography) concerning the creep deformation and damage mechanisms are presented and discussed. The tested LPBF material exhibits a low defect population, which allows for the isolation and improved understanding of the effect of other typical aspects of an LPBF microstructure on the creep behavior. As a benchmark to assess the material properties of the LPBF 316L, a conventionally manufactured variant of 316L was also tested. To characterize the creep properties, hot tensile tests and constant force creep tests at 600 °C and 650 °C are performed. The creep stress exponents of the LPBF material are smaller than that of the conventional variant. The primary and secondary creep stages and the times to rupture of the LPBF material are shorter than the hot rolled 316L. Overall the creep damage is more extensive in the LPBF material. The creep damage of the LPBF material is overall mainly intergranular. It is presumably caused and accelerated by both the appearance of precipitates at the grain boundaries and the unfavorable orientation of the grain boundaries. Neither the melt pool boundaries nor entrapped gas pores show a significant influence on the creep damage mechanism.
A large and increasing number of scientific domains pushes for high neutron imaging resolution achieved in reasonable times. Here we present the principle, design and performance of a detector based on infinity corrected optics combined with a crystalline Gd3Ga5O12 : Eu scintillator, which provides an isotropic sub-4 μm true resolution. The exposure times are only of a few minutes per image. This is made possible also by the uniquely intense cold neutron flux available at the imaging beamline NeXT-Grenoble. These comparatively rapid acquisitions are compatible with multiple high quality tomographic acquisitions, opening new venues for in-operando testing, as briefly exemplified here.
Clarifying the Electro-Chemo-Mechanical Coupling in Li10SnP2S12 based All-Solid-State Batteries
(2022)
A fundamental clarification of the electro-chemo-mechanical coupling at the solid–solid electrode|electrolyte interface in all-solid-state batteries (ASSBs) is of crucial significance but has proven challenging. Herein, (synchrotron) X-ray tomography, electrochemical impedance spectroscopy (EIS), time-of-flight secondary-ion mass spectrometry (TOF-SIMS), and finite element analysis (FEA) modeling are jointly used to decouple the electro-chemo-mechanical coupling in Li10SnP2S12-based ASSBs. Non-destructive (synchrotron) X-ray tomography results visually disclose unexpected mechanical deformation of the solid electrolyte and electrode as well as an unanticipated evolving behavior of the (electro)chemically generated interphase. The EIS and TOFSIMS probing results provide additional information that links the interphase/electrode properties to the overall battery performance. The modeling results complete the picture by providing the detailed distribution of the mechanical stress/strain and the potential/ionic flux within the electrolyte.
Collectively, these results suggest that 1) the interfacial volume changes induced by the (electro)chemical reactions can trigger the mechanical deformation of the solid electrode and electrolyte; 2) the overall electrochemical process can accelerate the interfacial chemical reactions; 3) the reconfigured interfaces in turn influence the electric potential distribution as well as charge transportation within the SE. These fundamental discoveries that remain unreported until now significantly improve the understanding of the complicated
electro-chemo-mechanical couplings in ASSBs.
Additive manufacturing (AM) technologies, generally called 3D printing, are widely used because their use provides a high added value in manufacturing complex-shaped components and objects. Defects may occur within the components at different time of manufacturing, and in this regard, non-destructive techniques (NDT) represent a key tool for the quality control of AM components in many industrial fields, such as aerospace, oil and gas, and power industries. In this work, the capability of active thermography and eddy current techniques to detect real imposed defects that are representative of the laser powder bed fusion process has been investigated. A 3D complex shape of defects was revealed by a μCT investigation used as reference results for the other NDT methods. The study was focused on two different types of defects: porosities generated in keyhole mode as well as in lack of fusion mode. Different thermographic and eddy current measurements were carried out on AM samples, providing the capability to detect volumetric irregularly shaped defects using non-destructive methods.
The printability of artificial defects inside the additively manufactured laser powder bed fusion (LPBF) 316L stainless steel is investigated. The printing parameters of the LPBF process are optimized to produce artificial defects with reproducible sizes at desired positions while minimizing redundant porosity. The smallest obtained artificial defect is 90 μm in diameter. The accuracy of the geometry of the printed defect depends on both the height and the diameter in the input model. The effect of artificial defects on the very-high-cycle fatigue (VHCF) behavior of LPBF 316L stainless steel is also studied. The specimens printed with artificial defects in the center are tested under VHCF using an ultrasonic machine. Crack initiation is accompanied by the formation of a fine granular area (FGA), typical of VHCF. Despite the presence of relatively large artificial defects, FGA formation is observed around accidental natural printing defects closer to the surface, which can still be considered as internal. The causes for this occurrence are discussed.
Additive manufacturing (AM) techniques have risen to prominence in many industrial sectors. This rapid success of AM is due to the freeform design, which offers enormous possibilities to the engineer, and to the reduction of waste material, which has both environmental and economic advantages. Even safety-critical parts are now being produced using AM. This enthusiastic penetration of AM in our daily life is not yet paralleled by a thorough characterization and understanding of the microstructure of materials and of the internal stresses of parts. The same holds for the understanding of the formation of defects during manufacturing. While simulation efforts are sprouting and some experimental techniques for on-line monitoring are available, still little is known about the propagation of defects throughout the life of a component (from powder to operando/service conditions). This Issue was aimed at collecting contributions about the advanced characterization of AM materials and components (especially at large-scale experimental facilities such as Synchrotron and Neutron sources), as well as efforts to liaise on-line process monitoring to the final product, and even to the component during operation. The goal was to give an overview of advances in the understanding of the impacts of microstructure and defects on component performance and life at several length scales of both defects and parts.
A paradigm shift in the description of creep in metals can only occur through multi-scale imaging
(2022)
The description of creep in metals has reached a high level of complexity; fine details are revealed by all sorts of characterization techniques and different theoretical models. However, to date virtually no fully microstructure-driven quantitative description of the phenomenon is available. This has brought to interesting inconsistencies; the classic description of (secondary) creep rests on the so-called power law, which however: a- has a pre-factor spanning over 10 orders of magnitude; b- has different reported exponents for the same material; c- has no explanation for the values of such exponents.
Recently, a novel description (the so-called Solid State Transformation Creep (SSTC) Model) has been proposed to tackle the problem under a different light. The model has two remarkable features: 1- it describes creep as the accumulation of elementary strains due to dislocation motion; 2- it predicates that creep is proceeding by the evolution of a fractal arrangement of dislocations. Such description, however, needs a great deal of corroborating evidence, and indeed, is still incomplete.
To date, we have been able to observe and somehow quantify the fractal arrangement of microstructures through Transmission Electron Microscopy (TEM), observe the accumulation of dislocations at grain boundaries by EBSD-KAM (Electron Back-Scattered Diffraction-Kernel Angular Misorientation) analysis, quantify the kinetic character (solid state transformation) of experimental creep curves, and estimate the sub-grain size of the fractal microstructure through X-ray refraction techniques. All pieces of the mosaic seem to yield a consistent picture: we seem being on the right path to reconstruct the whole elephant by probing single parts of it. What is still missing is the bond between the various scales of investigation.
The overview of the activity of group 8.5 Micro-NDT (BAM, Belin, Germany) in the field of additively manufacturing material characterization will be presented. The research of our group is focused on the 3D imaging of AM materials by means of X-ray Computed Tomography at the lab and at synchrotron, and the residual stress characterization by diffraction (nondestructive technique).