- Additive manufacturing (42)
- Computed tomography (26)
- Residual stress (20)
- X-ray refraction (15)
- X-ray computed tomography (13)
- Laser powder bed fusion (11)
- Neutron diffraction (11)
- Additive Manufacturing (9)
- Creep (8)
- Neutron imaging (7)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (221)
- 8.5 Röntgenbildgebung (221)
- 9 Komponentensicherheit (34)
- 5 Werkstofftechnik (24)
- 9.4 Integrität von Schweißverbindungen (23)
- 5.1 Mikrostruktur Design und Degradation (14)
- 8.0 Abteilungsleitung und andere (13)
- 9.6 Additive Fertigung metallischer Komponenten (12)
- 5.2 Metallische Hochtemperaturwerkstoffe (9)
- 7 Bauwerkssicherheit (9)
Paper des Monats
- ja (3)
The stress-induced tetragonal to monoclinic (t-m) zirconia phase transformation can provide a certain degree of plasticity to Ceria-stabilized (Ce-TZP) zirconia-based composites. Characterizing and monitoring this phase transition on a millimeter-size range, within the bulk and in-situ remains a challenge. In this work, the mechanical behavior of Ce-TZP based composite was studied in tension, combining microscopy and synchrotron Xray refraction techniques. In contrast with microscopy methods, which only provide surface information, X-ray refraction radiography (SXRR) allowed the visualization of all the transformation bands, over the entire length and thickness of tested specimens, opening up new avenues for in-situ stress-induced t-m transformation studies.
Adhesively bonded composite joints can develop voids and porosity during fabrication, leading to stress concentration and a reduced load-carrying capacity. Hence, adhesive porosity analysis during the fabrication is crucial to ensure the required quality and reliability. Ultrasonic-guided wave (UGW)-based techniques without advanced signal processing often provide low-resolution imaging and can be ineffective for detecting small-size defects. This article proposes a damage imaging process for adhesive porosity analysis of bonded composite plates using UGWs measured by scanning laser Doppler vibrometer (LDV). To implement this approach, a piezoelectric transducer is mounted on the composite joint specimen to generate UGWs, which are measured over a densely sampled area. The signals obtained from the scan are processed using the proposed signal processing in different domains. Through the utilization of filter banks in frequency and wavenumber domains, along with the root-mean-square calculation of filtered signals, damage images of the adhesive region are obtained. It has been observed that different filters provide information related to different void sizes. Combining all the images reconstructed by filters, a final image is obtained which contains damages of various sizes. The images obtained by the proposed method are verified by radiography results and the porosity analysis is presented. The results indicate that the proposed methodology can detect the pores with the smallest detectable pore area of 2.41 mm^2, corresponding to a radius of 0.88 mm, with an overall tendency to overestimate the pore size by an average of 11%.
This study investigates the room‐ and high‐temperature (650 °C) tensile and low‐cycle‐fatigue behavior of Inconel 718 produced by laser powder bed fusion (PBF‐LB/M) with a four‐step heat treatment and compares the results to the conventional wrought material. The microstructure after heat treatment is characterized on different length scales. Compared to the wrought variant, the elastic and yield properties are comparable at both test temperatures while tensile strength, ductility, and strain hardening capacity are lower. The fatigue life of the PBF‐LB/M variant at room temperature is slightly lower than that of the wrought material, while at 650 °C, it is vice versa. The cyclic stress response for both material variants is characterized by cyclic softening, which is more pronounced at the higher test temperature. High strain amplitudes (≥0.7%) at room temperature and especially a high testing temperature result in the formation of multiple secondary cracks at the transitions of regions comprising predominantly elongated grain morphology and columns of stacked grains with ripple patterns in the PBF‐LB/M material. This observation and pronounced crack branching and deflection indicate that the cracks are controlled by sharp micromechanical gradients and local crystallite clusters.
Rechargeable alkali metal−CO2 batteries, which combine high theoretical energy density and environmentally friendly CO2 fixation ability, have attracted worldwide attention. Unfortunately, their electrochemical performances are usually inferior for practical applications. Aiming to reveal the underlying causes, a combinatorial usage of advanced nondestructive and postmortem characterization tools is used to intensively study the failure mechanisms of Li/Na−CO2 batteries. It is found that a porous interphase layer is formed between the separator and the Li/Na anode during the overvoltage rising and battery performance decaying process. A series of control experiments are designed to identify the underlying mechanisms dictating the observed morphological evolution of Li/Na anodes, and it is found that the CO2 synergist facilitates Li/Na chemical corrosion, the process of which is further promoted by the unwanted galvanic corrosion and the electrochemical cycling conditions. A detailed compositional analysis reveals that the as-formed interphase layers under different conditions are similar in species, with the main differences being their inconsistent quantity. Theoretical calculation results not only suggest an inherent intermolecular affinity between the CO2 and the electrolyte solvent but also provide the most thermodynamically favored CO2 reaction pathways. Based on these results, important implications for the further development of rechargeable alkali metal−CO2 batteries are discussed. The current discoveries not only fundamentally enrich our knowledge of the failure mechanisms of rechargeable alkali metal−CO2 batteries but also provide mechanistic directions for protecting metal anodes to build high-reversible alkali metal−CO2 batteries.
Rechargeable sodium–oxygen batteries (NaOBs) are receiving extensive research interests because of their advantages such as ultrahigh energy density and cost efficiency. However, the severe failure of Na metal anodes has impeded the commercial development of NaOBs. Herein, combining in situ synchrotron X-ray computed tomography (SXCT) and other complementary characterizations, a novel electro-chemo-mechanical failure mechanism of sodium metal anode in NaOBs is elucidated. It is visually showcased that the Na metal anodes involve a three-stage decay evolution of a porous Na reactive interphase layer (NRIL): from the initially dot-shaped voids evolved into the spindle-shaped voids and the eventually-developed ruptured cracks. The initiation of this three-stage evolution begins with chemical-resting and is exacerbated by further electrochemical cycling. From corrosion science and fracture mechanics, theoretical simulations suggest that the evolution of porous NRIL is driven by the concentrated stress at crack tips. The findings illustrate the importance of preventing electro-chemo-mechanical degradation of Na anodes in practically
rechargeable NaOBs.
Determination of short carbon fiber orientation in zirconium diboride ceramic matrix composites
(2024)
In fiber-reinforced components, the fiber alignment and orientation have paramount influence on the thermomechanical properties of the resulting composite, for both short and continuous fiber. Here we present the case of an ultra-refractory matrix intended for extreme environment applications, ZrB2, reinforced with 20 vol% and 50 vol% short carbon fibers. In both cases, fibers tend to align perpendicular to the uniaxial pressure applied during shaping and sintering of a pellet, although the fiber tilt across the pellet thickness is difficult to determine. Moreover, for high volume fractions of reinforcement, the spatial distribution of the fibers is heterogeneous and tends to have domains of preferential orientations. We compare the information on the fiber distribution as collected by scanning electron microscopy images, X-ray computed tomography and synchrotron X-ray refraction radiography (SXRR). The three techniques prove to be complementary. Importantly, we demonstrate that SXRR yields the most statistically significant information due to the largest field of view, yet with a sensitivity down to the nanometer, and that can be successfully applied also to heavy matrix materials, such as zirconium boride.
AbstractIn this study, we compare the residual stress state in a laser powder bed fusion (PBF‐LB/M) AlSi10Mg alloy in the as‐built (AB) condition with that after two different heat treatments (265 °C for 1 h, HT1; and 300 °C for 2 h, HT2). The bulk residual stress (RS) is determined using synchrotron X‐ray diffraction (SXRD), and near‐surface profiles are determined using laboratory energy‐dispersive X‐ray diffraction (EDXRD). The EDXRD results do not reveal any notable difference between the conditions at a depth of 350 μm, suggesting that the machining process yields a comparable residual stress state in the near‐surface regions. On the other hand, the SXRD results show that HT1 is more effective in relieving the bulk RS. It is observed that HT1 reduces the RS state in both the aluminium matrix and the silicon network. In addtion, HT2 does not have a significant impact on relaxing the RS as‐built state of the matrix, although it does induce a reduction in the RS magnitudes of the Si phase. It is concluded that the heat treatment stress relieving is effective as long as the Si‐network is not disaggregated.
Powder Bed Fusion – Laser Beam (PBF-LB) of high γ’ strengthened Ni-base superalloys, such as CM247LC, is of great interest for high temperature applications in gas turbines. However, PBF-LB of CM247LC is challenging due to the high cracking susceptibility during PBF-LB processing (solidification cracking) and heat treatment (strain age cracking, mostly caused by residual stresses). This study focuses on understanding the impact of process parameters on microstructure, residual stresses and solidification cracking. Laser power (P), speed (v) and hatch spacing (h) were varied while the layer thickness (t) was fixed. The melt pool size and shape were found to be key factors in minimizing solidification cracking. Narrower and shallower melt pools, achieved using a low line energy density (LED = P/v ≤ 0.1 J/mm), gave low crack densities (0.7 mm/mm2). A tight hatch spacing (h = 0.03 mm) resulted in reduced lack of fusion porosity. Electron backscatter diffraction investigations revealed that parameters giving finer microstructure with 〈100〉crystallographic texture had low crack densities provided they were processed with a low LED. Atom probe tomography elucidated early stages of spinodal decomposition in the as-built condition, where Cr and Al cluster separately. The extent of spinodal decomposition was found to be affected by the LED and the hatch spacing. Samples with low LED and small hatch spacing showed higher degrees of spinodal decomposition. X-ray diffraction residual stress investigations revealed that the residual stress is proportional to the volumetric energy density (VED = P/(v. h. t)). Although low residual stresses can be achieved by using low VED, there is a high risk of lack of fusion. Hence, other parameters such as modified scan strategy, build plate pre-heating and pulsed laser mode, must be further explored to minimize the residual stresses to reduce the strain age cracking susceptibility.
A systematic, nature-inspired chemical engineering approach is employed to solve the issue of flooding in electrochemical devices. The mechanism of passive water transport utilized by lizards living in arid environments is leveraged to design flow-fields with a microchannel structure on their surface, through which capillary pressure rapidly removes the water generated in the electrochemical device. This water management strategy is implemented in proton exchange membrane fuel cells (PEMFCs) with a lunginspired flow-field, which ensures uniform distribution of reactants across the catalyst layer. Jointly, this nature-inspired approach results in flood-free, stable operation at 100% RH and a B60% increase in current (B1.9 A cm-2) and peak power density (B650 mW cm−2) compared to current PEMFCs with a flood-prone, serpentine flow-field (B0.8 A cm-2 and 280 mW cm-2, respectively). This significant advance allows for PEMFC operation at fully humidified conditions.
Efficient density evolution during sintering of the as-printed component is vital to reach full densification and required properties of binder jet (BJT) components. However, due to the high porosity and brittle nature of the green compact, analysis of the microstructure development during sintering is very difficult, resulting in lack of understanding of the densification process. Density development from green state (57 ± 1.6 %) up to full density (99 ± 0.3 %) was characterized by high-resolution synchrotron X-Ray computed tomography (SXCT) on BJT 316L samples from ex-situ interrupted sintering tests. Periodicity of density fluctuations along the building direction was revealed for the first time and was related to the layer thickness of ~ 42 μm during printing that decreased down to ~ 33 μm during sintering. Sintering simulations, utilizing a continuum sintering model developed for BJT, allowed to replicate the density evolution during sintering with a mean error of 2 % and its fluctuation evolution from green (1.66 %) to sintered (0.56 %) state. Additionally, simulation of extreme particle size segregation (1 μm to 130 μm) suggested that non-optimized printing could lead to undesirable density fluctuation amplitude rapid increase (~10 %) during sintering. This might trigger the nucleation of defects (e.g., layer delamination, cracking, or excessive residual porosity) during the sintering process.