8.4 Akustische und elektromagnetische Verfahren
Filtern
Dokumenttyp
- Vortrag (2)
- Beitrag zu einem Tagungsband (1)
- Sonstiges (1)
Sprache
- Englisch (4) (entfernen)
Referierte Publikation
- nein (4) (entfernen)
Schlagworte
- Eddy current testing (2)
- NDT (2)
- CFRP (1)
- Communication (1)
- Composite preasure vessel (1)
- Composite pressure vessel (1)
- DICONDE (1)
- Data storage (1)
- Eddy currnet testing (1)
- Finite element analysis (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (2)
DICONDE (Digital Imaging and Communication in Non-Destructive Testing) is an open international standard for storing and exchanging industrial test data and process-related information. The DICONDE standard defines both the semantics for structured storage of data and the network-based communication between two endpoints. This allows many test processes to be mapped digitally and securely, while at the same time meeting normative requirements such as traceability to the tester and test object and reproducibility of test results.
Pressure vessels for the transport of hazardous gases are subjected to a hydraulic internal pressure test. Basis for the design of metallic pressure vessels is the fatigue strength according to Wöhler, whereby the number of load changes can be equated with the number of filling / emptying cycles of the pressure vessel. Metallic pressure vessels are increasingly replaced by composite pressure vessels due to the weight savings. However, at composite preasure vessels it is not possible to conclude from the number of load cycles on the fatigue strength, because composite pressure vessels are ageing even at constant internal pressure. Non-destructive conventional and high frequency eddy current testing of the metallic liner and load bearing CFRP layer are presented as an alternative to hydraulic internal pressure test.
Composite pressure vessels for transporting dangerous goods and for hydrogen and natural gas vehicles consist of a load-bearing composite and a gas-tight, metallic or polymeric barrier layer (liner). To investigate the aging behavior of such composite pressure vessels, BAM carried out the interdisciplinary project COD-AGE. The aim of the project was the development of methods and models for the description and determination of the aging behavior of carbon fiber composites using the example of pressure vessels in order to better predict aging and safe working life. One focus of this project was the provision of suitable NDT methods. These included both test-related tests and the possible development of test equipment for later practical use.
In the lecture, test results of the age-related eddy current test on composite pressure vessels are presented.
In aging tests, pressure vessels made of an approximately 4 mm thick aluminum liner and approx. 8 mm thick CFRP layer were examined. Typical application of such pressure vessels are respiratory protective devices of the fire department. The pressure vessels were tested using conventional eddy current technology from the outer and inner side as well as with high-frequency eddy current technology. Both damage to the metallic liner and structures of the CFRP could be detected. A particular mechanical challenge was the inspection of the inside of the liners, since a cylindrical surface with an inside diameter of 150 mm has to be tested with an access of only 15 mm diameter.
Non-destructive testing for surface crack detection and head check depth quantification at the gauge corner of railway tracks can be achieved using eddy current methods. With the extension of the tested zone to the running surface, rail defect signal types other than head checks can be measured. Due to their mostly irregular shape, a quantitation based on a calibration against regular test cracks of varying depth may not be linear. Estimates of the expected influence of more complex crack patterns may be obtained by a finite element simulation of sufficiently simple limiting cases, like two displaced or intersecting cracks or a simply branched or flexed crack. As a first step, a 3D finite element model of the HC10 eddy current probe distributed by Prüftechnik Linke und Rühe (PLR), Germany was built and verified against measured results from an (easily fabricated) reference block with isolated long cracks.