Adhesively bonded composite joints can develop voids and porosity during fabrication, leading to stress concentration and a reduced load-carrying capacity. Hence, adhesive porosity analysis during the fabrication is crucial to ensure the required quality and reliability. Ultrasonic-guided wave (UGW)-based techniques without advanced signal processing often provide low-resolution imaging and can be ineffective for detecting small-size defects. This article proposes a damage imaging process for adhesive porosity analysis of bonded composite plates using UGWs measured by scanning laser Doppler vibrometer (LDV). To implement this approach, a piezoelectric transducer is mounted on the composite joint specimen to generate UGWs, which are measured over a densely sampled area. The signals obtained from the scan are processed using the proposed signal processing in different domains. Through the utilization of filter banks in frequency and wavenumber domains, along with the root-mean-square calculation of filtered signals, damage images of the adhesive region are obtained. It has been observed that different filters provide information related to different void sizes. Combining all the images reconstructed by filters, a final image is obtained which contains damages of various sizes. The images obtained by the proposed method are verified by radiography results and the porosity analysis is presented. The results indicate that the proposed methodology can detect the pores with the smallest detectable pore area of 2.41 mm^2, corresponding to a radius of 0.88 mm, with an overall tendency to overestimate the pore size by an average of 11%.
Background Due to physical coupling between mechanical stress and magnetization in ferromagnetic materials, it is assumed in the literature that the distribution of the magnetic stray field corresponds to the internal (residual) stress of the specimen.
The correlation is, however, not trivial, since the magnetic stray field is also influenced by the microstructure and the geometry of component. The understanding of the correlation between residual stress and magnetic stray field could help to evaluate the integrity of welded components.
Objective This study aims at understanding the possible correlation of subsurface and bulk residual stress with magnetic stray field in a low carbon steel weld. Methods The residual stress was determined by synchrotron X-ray diffraction (SXRD, subsurface region) and by neutron diffraction (ND, bulk region). SXRD possesses a higher spatial resolution than ND. Magnetic stray fields were mapped by utilizing high-spatial-resolution giant magneto resistance (GMR) sensors.
Results The subsurface residual stress overall correlates better with the magnetic stray field distribution than the bulk stress.
This correlation is especially visible in the regions outside the heat affected zone, where the influence of the microstructural features is less pronounced but steep residual stress gradients are present.
Conclusions It was demonstrated that the localized stray field sources without any obvious microstructural variations are associated with steep stress gradients. The good correlation between subsurface residual stress and magnetic signal indicates that the source of the magnetic stray fields is to be found in the range of the penetration depth of the SXRD measurements.
Additive manufacturing (AM) technologies, generally called 3D printing, are widely used because their use provides a high added value in manufacturing complex-shaped components and objects. Defects may occur within the components at different time of manufacturing, and in this regard, non-destructive techniques (NDT) represent a key tool for the quality control of AM components in many industrial fields, such as aerospace, oil and gas, and power industries. In this work, the capability of active thermography and eddy current techniques to detect real imposed defects that are representative of the laser powder bed fusion process has been investigated. A 3D complex shape of defects was revealed by a μCT investigation used as reference results for the other NDT methods. The study was focused on two different types of defects: porosities generated in keyhole mode as well as in lack of fusion mode. Different thermographic and eddy current measurements were carried out on AM samples, providing the capability to detect volumetric irregularly shaped defects using non-destructive methods.
This study examines the relationship between the magnetic mesostructure with the microstructure of low carbon steel tungsten inert gas welds. Optical microscopy revealed variation in the microstructure of the parent material, in the heat affected and fusion zones, correlating with distinctive changes in the local magnetic stray fields measured with high spatial resolution giant magneto resistance sensors. In the vicinity of the heat affected zone high residual stresses were found using neutron diffraction.
Notably, the gradients of von Mises stress and triaxial magnetic stray field modulus follow the same tendency transverse to the weld. In contrast, micro-X-ray fluorescence characterization indicated that local changes in element composition had no independent effect on magnetic stray fields.