Benefits of hyperbranched structure:
Molecular weight, miscibility, number of FR groups, end-group functionalization, glass transition temperature, decreased PBT.
Examples of hyperbranched FRs:
Charring agent, silicone, triazine, etc.
Systematic study of effect of chemical surrounding and impact of Complex shape of phosphorus-based hyperbranched polymers on flame retardant efficacy in epoxy resins.
Flexible polyurethane foams with densities of 40 ± 2 kg m−3 were prepared by combining different ecofriendly fillers such as layered double hydroxides (LDH) and kraft lignin (a byproduct of the pulp and paper industry) with a phosphorous polyol (E560) in order to study their effect on the mechanical performance and fire behavior of the foams. Two series of foams were prepared, some containing lignin or LDH separately, and some with a combination of both: one of the series was prepared without E560 (0E foam series) and the other with 5 parts per hundred of E560 polyol (5E series). The use of fillers resulted in increased viscosity of the reactive mixture, requiring higher blowing agent content in order to hold the density of the foams constant. It was observed that urea phase segregation was favored in the series of 0E foams due to their lower viscosity than the 5E series. This had consequent effects on the resilience, compression force deflection and compression set of these foams. In terms of fire behavior it was observed that while the limiting oxygen index decreased, cone calorimeter results showed that the combination of lignin, LDH and E560 decreased the heat release of the foams. In addition, the combination of fillers and E560 contributed to increase the viscosity of the pyrolysis products, preventing the dripping of the molten polymer, which is a key factor in flame propagation towards adjacent objects in fire scenarios.
Elastomers are used in a wide range of automotive and railway applications. However, a severe drawback of most rubbers are their high flammability. Therefore, flame retardants (FRs) are added to improve the performance in fire. Generally, rubber composites are filled with high amounts of mineral fillers such as aluminium trihydroxide (ATH) to fulfil fire safety regulations. These high loadings may cause deterioration of the physical properties of the material. This work shows the implementation of two new strategies to achieve the modern demands on non-toxic FRs and the reduction of fillers.
The first approach was the implementation of multilayer graphene (MLG), acting as a multifunctional filler, reinforcing agent and FR. The study presents filler combinations with a systematic variation of the fillers carbon black (CB), MLG and ATH. The nanocomposites were prepared via master batch by an ultrasonically assisted solution mixing. Afterwards the master batch was compounded into the rubber in a two-roll milling. MLG substituted high amounts of the conventional filler CB, leading to reduced filler loadings and a consistent improvement in curing, mechanical and FR properties.
The second strategy was the combination of phosphorous-containing FRs with a potential new polymeric char promoting agent polyaniline (PANI). Char promoting additives such as pentaerythritol (PER) improve the effectiveness of the FR system. The combination of ammonium polyphosphate (APP) with PER was successfully investigated for natural and styrene-butadiene rubber composites. This work investigates the flame retardancy of the combination of FRs with PANI and its capability to act as a char/barrier promoter in EPDM.
The morphology of the rubbers and homogenously dispersion of MLG was investigated via scanning/transmission electron microscope (SEM/TEM) micrographs. Rheological and mechanical measurements assessed the influence of the fillers on the physical properties of the rubber composites. Characterization via thermogravimetric analysis (TGA) led to a broader understanding of the decomposition. In order to determine the flame retardancy effect of these materials, a multi-methodical approach was selected. Limiting oxygen index (LOI) and UL-94 were used to quantify the flammability of the rubber composites. The cone calorimeter provided information about the fire behaviour in forced flaming conditions. Residues were investigated via elementary analysis and XPS to clarify the composition of the remaining material. Glow-Wire and FMVSS 302 tests revealed significant results in terms of flame retardancy. The flame retardancy investigation of rubber composites, combinations of ATH with MLG and ATH with phosphorous-containing FRs, broaden the horizons of rubber flame retardancy solutions. By examining alternate FR formulations and their effect on mechanical and physical properties of the rubber, new insight into the range of applicable additives for rubber composites may be won.
The need to develop effective flame retardants that retain polymer properties and are safe for consumers and the environment is a continuous challenge for material scientists. While halogenated flame retardants were once commonplace, the shift to non-halogenated materials has steadily progressed due to concerns over impact on health and the environment. One prominent group of flame retardants has become a viable alternative for halogenated materials, namely phosphorus-based flame retardants. The chemical versatility of phosphorus-based flame retardants and the ability to work as reactive or additive compounds makes them ideally suited for modern materials. There exists a trend toward complex, polymeric, and multifunction flame retardants, as these materials show greater flame retardancy performance than low molecular weight counterparts and affect material properties to a much lesser extent.
One group of organophosphorus flame retardants that shows great potential for high-performance polymers like epoxy resins are hyperbranched phosphorus-based polymers. These additives exhibit great miscibility with the polymer matrix and a significantly decreased diffusion through the material, which greatly reduce leaching or blooming out of the matrix. Moreover, the material’s thermal stability remains intact at elevated temperatures due to its low impact on the glass transition temperature. Finally, following market trends and legislation such as the guidelines for the Restriction of Hazardous Substances Directive implemented by REACH (Registration, Evaluation, Authorization and Restriction of Chemicals) in the EU, these macromolecules are non-accumulating, non-toxic and have a lower risk of leeching or blooming from the matrix, further reducing environmental impact.
The work presented herein focusses on two distinct parts studying hyperbranched polymeric flame retardants and their corresponding monomeric compounds.
The first part, involving the low molecular weight components, investigated the role of the chemical surrounding of phosphorus in terms of flame retardant efficacy. Here, a systematic variance of the surrounding of phosphorus was investigated: by changing the ratio of oxygen to nitrogen (4:0 until 1:3), four materials, namely phosphoester (4:0), phosphoramidate (3:1), phosphorodiamidate (2:2), and phosphoramide (1:3), were synthesized, characterized, and finally added to Bisphenol A based epoxy resins (10 wt.-% loading). Pyrolysis investigations showed that low molecular weight components volatize at lower temperatures than the polymer matrix. Additionally, cone calorimeter measurements and TGA-FTIR investigations show trends in respect to FR efficacy in pyrolysis and full flaming conditions.
The second part involves the hyperbranched variants of the monomeric counterparts and investigates the role of complex shape on flame retardant efficacy. By comparing the low to the high molecular weight compounds, the influence of the complex shape becomes apparent and can be quantified. Cone calorimeter measurements show an increase in flame retardancy for some materials, while for others, the mode of action is altered.
By implementing a multi-methodical approach, various flame retardancy aspects, from pyrolysis behavior in the gas and condensed phase, to ignitability / reaction-to-small-flame performance, to action in forced flammability experiments, are identified and quantified, allowing for a clearer understanding of the behavior in fire of these novel flame retardants. By comprehending the roles of chemical composition and complex shape, it opens the path for new and effective multifunctional, polymeric flame retardants with decreased PBT, higher miscibility, and low impact on Tg.
This work is funded by the Deutsche Forschungsgemeinschaft (DFG: SCHA 730/15-1; WU 750/8-1).
The ubiquity of polymeric materials in daily life Comes with an increased fire risk, and sustained research into efficient flame retardants is key to ensuring the safety of the populace and material goods from accidental fires. Phosphorus, a versatile and effective element for use in flame retardants, has the potential to supersede the halogenated variants that are still widely used today: current formulations employ a variety of modes of action and methods of implementation, as additives or as reactants, to solve the task of developing flameretarding polymeric materials. Phosphorus-based flame retardants can act in both the gas and condensed phase during a fire. This Review investigates how current phosphorus chemistry helps in reducing the flammability of polymers, and addresses the future of sustainable, efficient, and safe phosphorus-based flame-retardants from renewable sources.
Polyesters with 9,10-dihydro-9-oxy-10-phosphaphenanthrene-10-oxide-containing comonomers are synthesized aiming to improve the flame retardancy of aliphatic polyesters such as poly(butylene succinate) and poly(butylene sebacate). The influence of the chemical structure on the thermal decomposition and pyrolysis is examined using a combination of thermogravimetric analysis (TGA), TGA-Fourier transform infrared (FTIR) spectroscopy, pyrolysis-gas chromatography/mass spectrometry, and microscale combustion flow calorimetry. Thermal decomposition pathways are derived and used to select suitable candidates as flame retardants for PBS. The fire behavior of the selected polymers is evaluated by forced-flaming combustion in a cone calorimeter. The materials show two modes of action for flame retardancy: strong flame inhibition due to the release of a variety of molecules combined with charring in the solid state.