7.5 Technische Eigenschaften von Polymerwerkstoffen
Filtern
Dokumenttyp
- Zeitschriftenartikel (5)
- Beitrag zu einem Tagungsband (3)
- Vortrag (3)
- Monografie (1)
Schlagworte
- Weathering (12) (entfernen)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (3)
We report the selective ring opening copolymerisation (ROCOP) of
oxetane and phthalic thioanhydride by a heterobimetallic Cr(III)K
catalyst precisely yielding semi-crystalline alternating poly(esteralt-
thioesters) which show improved degradability due to the
thioester links in the polymer backbone.
Die Forderung, dass der Flammschutz von Kunststoffen nicht nur zum bei der Herstellung der jeweiligen Produkte, sondern auch über die gesamte Einsatzdauer im geforderten Maß wirksam ist, stellt eine große Aufgabe dar. Ferner ist die Anforderung für viele Produkte in der Praxis neu, da bisher vor allem der Einfluss der Flammschutzmittel auf die Stabilität der Polymerwerkstoffe, nicht aber die Stabilität des Flammschutzes untersucht wurde. Das Langzeitverhalten halogenfreier Systeme ist bis heute wenig untersucht, insbesondere weil Phosphor- und Stickstoff-basierte Systeme die oxidative Beständigkeit von Polymeren weniger zu beeinflussen scheinen als halogenhaltige FSM. Die Frage, wie zuverlässig der Flammschutz wirkt, wenn Kunststoffe einige Jahre im Innen- und Außenbereich im Einsatz sind und dabei wechselnden Beanspruchungen ausgesetzt waren, wurde bislang nur vereinzelt untersucht. Mögliche Auswirkungen von Witterungseinflüssen auf flammgeschützte Polymerwerkstoffe sind, dass die Flammschutzmittel selbst abbauen, ausgewaschen werden, oder auch durch Wechselwirkung mit den eingesetzten Additiven oder mit den Alterungsprodukten der Polymermatrix in ihrer Wirkung nachlassen. Hier bestand großer Forschungsbedarf, um an den Punkt zu gelangen, die Beständigkeit der Flammschutzeigenschaften eines Produktes über seine gesamte Lebensdauer zuverlässig garantieren zu können. Diese Fragestellung greift das durchgeführte Forschungsvorhaben auf.
Ziel war die Untersuchung der Langzeitstabilität der Flammschutzwirkung von halogenfrei flammgeschützten Polymerwerkstoffen unter diversen Witterungseinflüssen. Dazu wurden die Schädigungsmechanismen der Polymerwerkstoffe und der Flammschutzmittel sowie die auftretenden Wechselwirkungen analysiert, um ein Verständnis für die ablaufenden Prozesse zu entwickeln und Empfehlung für die Reduzierung der Alterung zu erarbeiten. Gegenstand der Untersuchungen waren anwendungsrelevante Flammschutz-Konzepte, die miteinander verglichen wurden. Die Erarbeitung von Struktur-Eigenschafts-Beziehungen ermöglichte die Beschreibung der Empfindlichkeiten und den Vergleich zwischen den Systemen. Darauf basierend wurden für die FSM spezifische Leitlinien für die Optimierung der Langzeitstabilität des Flammschutzes erstellt.
A systematic approach was used to investigate the weathering-induced degradation of a common water–based intumescent coating. In this study, the coatings are intended for humid indoor applications on steel substrates. The coating contains ammonium polyphosphate, pentaerythritol, melamine, and polyvinyl acetate. By replacing each ingredient with a less water-soluble substance, the most vulnerable substances, polyvinyl acetate and pentaerythritol, were identified. Furthermore, the weathering resistance of the system was improved by exchanging the ingredients. The coatings were stressed by artificial weathering tests and evaluated by fire tests. Thermogravimetry and Fourier-transform infrared spectroscopy were used to study the thermal decomposition. This study lays the foundation for the development of a new generation of water-based intumescent coatings.
The durability of flame retardancy is a challenge for cables over long lifetimes. The degradation of flame retardance is investigated in two kinds of exposures, artificial weathering and humidity. In this basic study, typical mineral flame retardants in two polymers frequently used in cable jackets are investigated to get the fundamental picture. Aluminum hydroxide (ATH) and magnesium hydroxide (MDH) are compared in ethylene‐vinyl acetate (EVA), and further in EVA and linear low‐density polyethylene (LLDPE) cables containing the same ATH. The changes in chemical structure at the surface are studied through attenuated total reflectance Fourier transform infrared spectroscopy (ATR‐FTIR), the formation of cracks, and changes in color are investigated. The cone calorimeter and a bench scale fire testing cable module are utilized to evaluate the fire behavior of the cables. Although the flame retardancy deteriorated slightly, it survived harsh exposure conditions for 2000 h. Compared to EVA/MDH and LLDPE/ATH, the fire behavior of EVA/ATH is the least sensitive. Taken together, all of the results converge to estimate that there will be no problem with flame retardancy performance, for materials subjected to natural exposure for several years; the durability of fire retardancy is questionable for longer periods, and thus requires further investigation.
Scientific publications addressing the durability of the flame retardance of cables during their long-term application are rare and our understanding lacks. Three commercial flame retardants, aluminum hydroxide, aluminum diethyl phosphinate (AlPi-Et), and intumescent flame retardant based on ammonium polyphosphate, applied in ethylene-vinyl acetate copolymer (EVA) model cables, are investigated. Different artificial aging scenarios were applied: accelerated weathering (UV-irradiation/temperature/rain phases), humidity exposure (elevated temperature/humidity), and salt spray exposure. The deterioration of cables’ surface and flame retardancy were monitored through imaging, color measurements, attenuated total reflectance Fourier transform infrared spectroscopy, and cone calorimeter investigations. Significant degradation of the materials’ surface occurred. The flame retardant EVA cables are most sensitive to humidity exposure; the cable with AlPi-Et is the most sensitive to the artificial aging scenarios. Nevertheless, substantial flame retardance persisted after being subjected for 2000 h, which indicates that the equivalent influence of natural exposure is limited for several years, but less so for long-term use.
Bare steel constructions are often integrated in modern buildings. Intumescent coatings are widely used to protect the steel from heating up too quickly in a case of fire. As the functionality of intumescent coatings decreases with the impact of weathering processes, it is important to understand the mechanisms of material degradation to maintain long durability. The weathering-induced degradation behavior of a water-borne intumescent coating was examined, and the weakest points of the formulation were identified by a systematic approach. Resulting from this investigation, adjustments to the formula were made, leading to improved weathering resistance.
On the basis of a lot of investigation on the spectral sensitivity of photo degradation of plastics and on the underestimated influence of temperature and relative humidity on degradation processes a new type of weathering device was presented at the end of the seventies:
It was a combination of a radiation source with fluorescent UV lamps and a precise climatic cabinet.
The radiation emission from a combination of four different types of fluorescent UV lamps was superimposed on the specimen surfaces in the climatic cabinet to match the UV part of solar radiation as closely as possible. Air temperature was controlled to within ± 1 °C, and relative humidity to within ± 5 %RH.
As the lamps’ emission is focussed on the UV range almost no radiation heating of the sample occurs. Therefore, the temperature of the sample, which is the quantity of consideration for the degradation, is nearly identical with the chamber’s air temperature, which is the quantity to be controlled. Also, therefore, high humidity can be obtained on the sample surface. The limitation of the emission to the UV range is sufficient for the study of the polymer matrix.
This type of weathering device offers an exactness of microclimatic control of the sample’s surface, which should be a standard for weathering devices. Even now it is the only weathering device which generates pure relative humidity (without aerosol).
Weathering reference materials (WRMs) are used to characterize the harshness of an exposure, aiming on either reproducibility of a specific exposure or on the comparability between various kinds of natural or artificial weathering exposure.
The materials that are used as weathering reference materials differ in their sensitivities (as well as in interactions and interferences of the latter), conditioned by the different processes which lead to the respective property change. It is also essential to take into account the necessary measurement equipment for the respective property change, in order to allow timely intervention.
What are the key issues on choosing a weathering reference material?
What can be learned from the weathering reference materials, investigated so far?
Possibilities and limitations are discussed on the basis of existing weathering reference materials. Conclusions are drawn, for establishing new weathering reference materials.
Exposure response function for a quantitative prediction of weathering caused aging of polyethylene
(2019)
The exposure response function of the carbonyl formation over the bulk has been determined for a high-density polyethylene of a thickness of 200 μm, which was used as a weathering reference material according to ISO TR 19032. To this end, spectral sensitivity was studied by local measurement of the effect of spectrally dispersed irradiation. Both the exposure device and the methodology of determination are described.
The temperature dependency of photooxidation was determined by UV exposure at various temperatures between 23 and 80 °C. Deviations from linearity and thus reciprocity below 40 °C are discussed and assumed to be related to diffusion limitations. An Arrhenius approach –based on data of linear carbonyl formation – has been incorporated into the exposure response function. Using this exposure response function, aging in terms of the distribution of a quantitative property change over a plastic component can be predicted for a specific outdoor location with real chronologic weather data as input for the exposure. Thus, artificial and natural weathering can be linked and compared. The established exposure response function has been validated by outdoor exposure results from the literature. If an estimated diffusion limitation is taken into consideration, calculations and published data are in good agreement.
High-throughput fire tests and weathering-induced degradation behaviour of intumescent coatings
(2018)
In this work, the weathering-induced degradation of intumescent coatings was investigated by a systematic and comprehensive approach. A mechanism is revealed that is proposed to be responsible for the loss of function of intumescent coatings induced by weathering.
First, the thermal decomposition of artificially weathered intumescent coatings was examined. To get a better understanding of the weathering and ageing phenomena, the degradation behaviour of the single ingredients during the weathering process was investigated, as well as their chemical and physical interactions. For the systematic approach, the materials that are essential for intumescence (ammonium polyphosphate, pentaerythritol, titanium dioxide, melamine and the binder) are treated with moisture, elevated temperature and UV radiation.
Thermogravimetry (TG) and IR spectroscopy were used to compare the initial samples with their different grades of weathering. We demonstrate that ammonium polyphosphate, melamine and the binder are mainly responsible for the ageing process. Further, it was demonstrated that TG and IR spectroscopy are suitable measuring methods to detect the effects of weathering on intumescent coatings.
Finally, a small-scale fire test procedure is introduced. Based on the reduction of the sample size, up to 50 samples can be tested in a single fire test. The results of this fire test have the same quality as the results from standard intermediate fire tests corresponding to DIN 4102-8.