7.4 Baustofftechnologie
Filtern
Erscheinungsjahr
- 2022 (29) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (14)
- Beitrag zu einem Tagungsband (7)
- Vortrag (5)
- Beitrag zu einem Sammelband (1)
- Dissertation (1)
- Posterpräsentation (1)
Schlagworte
- Structural build-up (5)
- Cement (3)
- Hydration (3)
- Non-destructive testing (3)
- Rheological properties (3)
- Superplasticizer (3)
- Accelerated testing (2)
- Additive manufacturing of concrete (2)
- Alkali-activated materials (2)
- Angle of repose (2)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (29)
- 7.4 Baustofftechnologie (29)
- 3 Gefahrgutumschließungen; Energiespeicher (2)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (2)
- 4 Material und Umwelt (2)
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (2)
- 7.1 Baustoffe (2)
- 7.7 Modellierung und Simulation (2)
- 8 Zerstörungsfreie Prüfung (2)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.1 Anorganische Spurenanalytik (1)
- 7.2 Ingenieurbau (1)
- 7.6 Korrosion und Korrosionsschutz (1)
Paper des Monats
- ja (2)
Eingeladener Vortrag
- nein (5)
The current understanding of the carbonation and the prediction of the carbonation rate of alkali-activated concretes is complicated inter alia by the wide range of binder chemistries used and testing conditions adopted. To overcome some of the limitations of individual studies and to identify general correlations between mix design parameters and carbonation resistance, the RILEM TC 281-CCC ‘Carbonation of Concrete with Supplementary Cementitious Materials’ Working Group 6 compiled and analysed carbonation data for alkali-activated concretes and mortars from the literature. For comparison purposes, data for blended Portland cement-based concretes with a high percentage of SCMs (≥ 66% of the binder) were also included in the database. The analysis indicates that water/CaO ratio and water/binder ratio exert an influence on the carbonation resistance of alkali-activated concretes; however, these parameters are not good indicators of the carbonation resistance when considered individually. A better indicator of the carbonation resistance of alkali-activated concretes under conditions approximating natural carbonation appears to be their water/(CaO + MgOeq + Na2Oeq + K2Oeq) ratio, where the subscript ‘eq’ indicates an equivalent amount based on molar masses. Nevertheless, this ratio can serve as approximate indicator at best, as other parameters also affect the carbonation resistance of alkali-activated concretes. In addition, the analysis of the database points to peculiarities of accelerated tests using elevated CO2 concentrations for low-Ca alkali-activated concretes, indicating that even at the relatively modest concentration of 1% CO2, accelerated testing may lead to inaccurate predictions of the carbonation resistance under natural exposure conditions.
Hydrous lithium aluminosilicate (L–A–S–H) and lithium aluminate (L–A–H) gels are candidate precursors for glass-ceramics and ceramics with potential advantages over conventional processing routes. However, their structure before calcination remained largely unknown, despite the importance of precursor structure on the properties of the resulting materials. In the present study, it is demonstrated that L–A–S–H and L–A–H gels with Li/Al ≤ 1 can be produced via an organic steric entrapment route, while higher Li/Al ratios lead to crystallization of gibbsite or nordstrandite. The composition and the structure of the gels was studied by thermogravimetric analysis, X-ray diffraction, 27Al and 29Si magic-angle spinning nuclear magnetic resonance, and Raman spectroscopy. Aluminium was found to be almost exclusively in six-fold coordination in both the L–A–H and the L–A–S–H gels. Silicon in the L–A–S–H gels was mainly in Q4 sites and to a lesser extent in Q3 sites (four-fold coordination with no Si–O–Al bonds). The results thus indicate that silica-rich and aluminium-rich domains formed in these gels.
Hybrid cements are composites made of Portland cement or Portland clinker and one or more supplementary cementitious materials like slag, fly ash or metakaolin, activated with an alkali salt. To date, their hydration mechanism and the phase formation at various temperatures is insufficiently understood, partly due to the large variability of the raw materials used. In the present study, three hybrid cements based on ground granulated blast furnace slag, fly ash, Portland clinker and sodium sulfate, and an alkali-activated slag/fly ash blend were cured at 10 and 21.5°C, and subsequently analyzed by XRD, 27Al MAS NMR, and TGA. The compressive strength of the hybrid cements was higher by up to 27% after 91-day curing at 10°C, compared to curing at 21.5°C. The experimental results as well as thermodynamic modeling indicate that the differences in compressive strength were related to a different phase assemblage, mainly differing amounts of strätlingite and C-N-A-S-H, and the associated differences of the volume of hydration products. While the strätlingite was amorphous to X-rays, it could be identified by 27Al MAS NMR spectroscopy, TGA and thermodynamic modeling. The microstructural properties of the hybrid cements and the alkali-activated slag/fly ash blend as well as the compatibility between thermodynamic modeling results and experimental data as a function of curing temperature and time are discussed.
Cementitious materials are frequently applied in environments in which they are exposed to acid attack, e.g., in sewer systems, biogas plants, and agricultural/food-related industries. Alkali-activated materials (AAMs) have repeatedly been shown to exhibit a remarkably high resistance against attack by organic and inorganic acids and, thus, are promising candidates for the construction and the repair of acid-exposed structures. However, the reaction mechanisms and processes affecting the acid resistance of AAMs have just recently begun to be understood in more detail. The present contribution synthesises these advances and outlines potentially fruitful avenues of research. The interaction between AAMs and acids proceeds in a multistep process wherein different aspects of deterioration extend to different depths, complicating the overall determination of acid resistance. Partly due to this indistinct definition of the ‘depth of corrosion’, the effects of the composition of AAMs on their acid resistance cannot be unambiguously identified to date. Important parallels exist between the deterioration of low-Ca AAMs and the weathering/corrosion of minerals and glasses (dissolution-reprecipitation mechanism). Additional research requirements relate to the deterioration mechanism of high-Ca AAMs; how the character of the corroded layer influences the rate of deterioration; the effects of shrinkage and the bond between AAMs and substrates.
The oxidation of sulfur in aqueous solutions is an important process in several geochemical and industrial contexts. In concrete technology, it is particularly relevant for the protection of steel reinforcement in slag cement-based concretes, as the presence of sulfides affects the passivation of the steel and corrosion initiation in the presence of chlorides. However, the knowledge about the kinetics of sulfide oxidation in alkaline solutions, such as concrete pore solutions, is incomplete. To address this issue, we prepared solutions with 0.80 M NaOH, and nominally 10, 100 and 350 mM HS−, respectively, and followed the evolution of the sulfur species during bubbling with oxygen-containing gas (concentration 100% or 22%) using X-ray absorption near-edge structure (XANES) spectroscopy at the sulfur K-edge. Polysulfide, thiosulfate, sulfite and sulfate were identified and quantified via linear combination fitting of the spectra, using previously measured standards. A preliminary analysis of the results shows that the initial rate constant of sulfide oxidation depends strongly on the HS− concentration, while it less strongly depending on the oxygen concentration, in line with previous results for lower pH values. Approaches to fit the data to obtain the rate constants of all relevant reactions will be discussed.
Introduction of a monitoring system for Bingham fluids in additive manufacturing with concrete
(2022)
Freeform additive manufacturing of concrete structures is a rising technology in civil engineering with several fascinating advantages. Nonetheless, to ensure reliability and structural integrity, standards and quality control are required in the future to bring this technology into the market. As the concrete is manufactured continuously, continuous quality control of the printing process is also required, i.e. comprehensive process monitoring. At BAM, a test rig will be installed, enabling the printing of concrete structures with a maximum size of 2 m x 1 m x 1 m (l x w x h). Here, process monitoring is the focus of the test rig. In this study, we show the results of the first pump tests, including the measurement of several parameters such as temperature and pressure along the supply system, i.e. from the concrete pump to the printer head.
Introduction of a monitoring system for Bingham fluids in additive manufacturing with concrete
(2022)
Freeform additive manufacturing of concrete structures is a rising technology in civil engineering with several fascinating advantages. Nonetheless, to ensure reliability and structural integrity, standards and quality control are required in the future to bring this technology into the market. As the concrete is manufactured continuously, continuous quality control of the printing process is also required, i.e. comprehensive process monitoring. At BAM, a test rig will be installed, enabling the printing of concrete structures with a maximum size of 2 m x 1 m x 1 m (l x w x h). Here, process monitoring is the focus of the test rig. In this study, we show the results of the first pump tests, including the measurement of several parameters such as temperature and pressure along the supply system, i.e. from the concrete pump to the printer head.
With increasing focus on industrialized processing, investigating, understanding, and modelling the structural build-up of cementitious materials becomes more important. The structural build-up governs the key property of fresh printable materials -- buildability -- and it influences the mechanical properties after the deposition. The structural build-up rate can be adjusted by optimization of the mixture composition and the use of concrete admixtures. Additionally, it is known, that the environmental conditions, i.e. humidity and temperature have a significant impact on the kinetic of cement hydration and the resulting hardened properties, such as shrinkage, cracking resistance etc. In this study, small amplitude oscillatory shear (SAOS) tests are applied to examine the structural build-up rate of cement paste subject to different temperatures under controlled humidity. The results indicate significant influences of the ambient temperature on the intensity of the re-flocculation (Rthix) rate, while the structuration rate (Athix) is almost not affected. A bi-linear thixotropy model extended by temperature dependent parameters coupled with a linear viscoelastic material model is proposed to simulate the mechanical behaviour considering the structural build-up during the SAOS test
With increasing focus on industrialized processing, investigating, understanding, and modelling the structural build-up of cementitious materials becomes more important. The structural build-up governs the key property of fresh printable materials -- buildability -- and it influences the mechanical properties after the deposition. The structural build-up rate can be adjusted by optimization of the mixture composition and the use of concrete admixtures. Additionally, it is known, that the environmental conditions, i.e. humidity and temperature have a significant impact on the kinetic of cement hydration and the resulting hardened properties, such as shrinkage, cracking resistance etc. In this study, small amplitude oscillatory shear (SAOS) tests are applied to examine the structural build-up rate of cement paste subject to different temperatures under controlled humidity. The results indicate significant influences of the ambient temperature on the intensity of the re-flocculation (Rthix) rate, while the structuration rate (Athix) is almost not affected. A bi-linear thixotropy model extended by temperature dependent parameters coupled with a linear viscoelastic material model is proposed to simulate the mechanical behaviour considering the structural build-up during the SAOS test.
Ziel des Projekts HYTEGRA ist die Herstellung leichter Gesteinskörnungen durch hydrothermale Behandlung quarz- und kalkreicher Reststoffe. Als Ausgangsstoffe dienen heterogener Mauerwerkbruch aus Bau- und Abbruchabfällen als SiO2-Träger und Papierasche aus dem Altpapierrecycling als CaO-Träger. Für beide Reststoffe besteht derzeit ein Verwertungsdefizit. Das Verfahren beruht auf der Idee des rohstofflichen Recyclings, d. h. die chemisch-mineralogischen Stoffeigenschaften werden für die hydrothermale Stoffumwandlung genutzt. Bei der Härtung der Hydrothermalgranulate bilden sich Calciumsilicathydrat-Phasen (CSH) aus der Reaktion zwischen Quarzpartikeln und Kalk im Autoklav bei 200 °C und 16 bar Sattdampf.