In order to obtain a statement on the corrosion resistance of stainless steel against pitting corrosion, a well-tested measuring arrangement is required. For this purpose, the so-called ECISS test can be used to determine the critical chloride content. This makes it possible to assess the corrosion resistance of various stainless steels that have different chromium contents.
Due to the large number of stainless steels with different chemical composition and different microstructure the selection of the suitable material represents a huge challenge. In order to facilitate the appropriate grade selection, in the current European standard EN 1993-1-4 a procedure is defined based on the use of a look-up table considering the key variables that influence the selection of stainless steels. The table uses descriptions that competent designers should be able to readily understand or define without prior knowledge. The output from the look-up table is used to select alloys based on a Corrosion Resistance Class (CRC) from I to V. The advantage of this approach is that the designer simply specifies the relevant CRC and does not need to consider in detail which of the many (very similar) alloys to specify.
Susceptibility of 304 Stainless Steel to Crevice Corrosion in Electrochemically Active Fluids
(2020)
The susceptibility of Type 304 stainless steel (SS) to crevice corrosion upon contacting with electrochemically active fluids was investigated using exposure tests and stepwise potentiostatic polarization. Crevice materials made of 304 SS and polyether ether ketone (PEEK) were focused on in this study. The combined influence of oxidant and chloride concentration on crevice corrosion was examined in detail in the two types of crevice combinations (304 SS-to-PEEK and 304 SS-to-304 SS). The 304 SS specimens were strongly susceptible to crevice corrosion when coupled with 304 SS. Even at a low concentration of 5 mg/L free chlorine and 150 mg/L chloride, which is below nominal dilutions in beverage industries, the examined specimens underwent crevice corrosion in both crevices. The effect of water composition on crevice corrosion was also studied, indicating high susceptibility of 304 SS to crevice corrosion in low pH (pH ≤ 5) solutions. The corroded surface morphology was analyzed using scanning electron microscope, energy dispersive x-ray, and confocal.
Geothermal energy is an interesting alternative to polluting fossil energy sources. Therefore, in Belgium, two wells have been drilled for a deep geothermal power plant. However, the environment to which the installations are exposed is challenging. The geothermal brine has 165 g/l total dissolved solids (of which 90% are sodium and chlorine) and the production temperature can be up to 130 °C. To assess their suitability to be used in a geothermal power plant, the corrosivity of the artificial brine to three common construction materials was investigated with exposure and electrochemical tests. The metals under consideration are a low-alloyed carbon steel (S235JR), an austenitic stainless steel (UNS S31603) and a duplex stainless steel (UNS S31803). The carbon steel, that was found to corrode uniformly, could be considered as a constructional material if a sufficient wall thickness is chosen. The austenitic stainless steel and the duplex stainless steel demonstrate very low uniform
corrosion rates. They are however susceptible to pitting and crevice corrosion. To guarantee safe operation of the geothermal power plant, the susceptibility of the alloys to stress corrosion cracking should be tested and in situ experiments should be performed.