The small-pore framework sodium stannosilicate AV-10, chemical composition Na2SnSi3O9⋅2H2O and known crystallographic structure, was synthesized by hydrothermal crystallization. This stannosilicate is built up of a three-dimensional network of corner-shared SiO4 tetrahedra and SnO6 octahedra. The SnO6 sites are linked to six SiO4 tetrahedra (Sn(6Si)) while each of the two crystallographically different SiO4 units are connected to two SnO6 and SiO4 units (Si(2Si,2Sn)). This material was used as model compound for developing a solid-state MAS NMR strategy aimed on the challenges and possibilities for structural studies, particularly considering the short and medium range order to verify the connectivity of SiO4 and SnO6 of such compounds despite the low natural abundances of 4.68% for 29Si and 8.59% for 119Sn nuclei as a real challenge. 29Si{119Sn} and 119Sn{29Si} REDOR (Rotational-Echo Double-Resonance) NMR measurements after 1H cross-polarization (CP) were carried out. The REDOR curves show a significant change after the “normal” quadratic short time evolution from which both (i) the shortest internuclear 29Si – 119Sn distances (and vice versa) and (ii) the number of corner-sharing SiO4 tetrahedra around the SnO6 octahedra (and vice versa) can be obtained. Based on these data, optimized 29Si {119Sn} and 119Sn{29Si} REPT-HMQC (Recoupled Polarization Transfer-Heteronuclear Multiple-Quantum Correlation, again after 1H CP) experiments were implemented, which directly show those heterogroup connectivity as correlation peaks in a 2D spectrum. This information was also obtained using 2D29Si{119Sn}-J-Coupling NMR experiments. Furthermore, 2D29Si INADEQUATE NMR experiments are also feasible, showing the connectivity of SiO4 tetrahedra. The combination of REDOR, REPT-HMQC, J-Coupling and INADEQUATE experiments yielded a complete analysis of the short and medium range structure of this microporous stannosilicate, in agreement with the previously published structure obtained Ab Initio from powder X-Ray diffraction data (XRD).
Einkomponentige alkaliaktivierte Bindemittel (AAB), d. h. AAB, bei denen der Aktivator als Feststoff im Bindemittel vorliegt, weisen Vorteile hinsichtlich der praktischen Anwendung im Bauwesen gegenüber konventionellen AAB auf. Einkomponentige AAB lassen sich als Gemische aus reaktiver Silica und Natriumaluminat herstellen, wobei die Reaktionsprodukte von der eingesetzten Silica und den Verhältnissen Na2O/Al2O3/SiO2/H2O abhängen: Während Mikrosilica und ähnliche Reststoffe zu zeolithreichen Produkten führen, erhält man aus Reisschalenasche vollständig amorphe Gele (sog. «Geopolymere »). Mörtel auf Basis solcher Bindemittel entsprechen den Anforderungen von DIN 19573:2016-03 hinsichtlich des Widerstands gegen Schwefelsäureangriff (Prüfung bei pH = 1 für 70 d) und sind damit potentiell als Reparatursysteme für Abwasserinfrastruktur geeignet. Untersuchungen mittels 29Si-MAS-NMR und 1H-29Si-Kreuzpolarisations(CP)-MAS-NMR sowie REM-Aufnahmen von erhärteten und dem Schwefelsäureangriff ausgesetzten AAB zeigen, dass der hohe Säurewiderstand v. a. auf die Fällung von Silicagel an der Grenzfläche Mörtel/Säure zurückzuführen ist, wodurch der Korrosionsfortschritt in darunterliegenden Schichten verlangsamt wird.
Mixing and curing of geopolymers and related alkali-activated materials without storage and handling of highly alkaline solutions possesses advantages regarding safety and economic viability. One possible approach is to produce these materials from solid silica feedstocks and solid sodium aluminate, and subsequent mixing with water. We present a comparison between geopolymers and aluminosilicate gel-zeolite composites synthesized by this route from different silica feedstocks (by-product silica from chlorosilane production, microsilica, rice husk ash) and with different SiO2/Al2O3 ratios, using results from XRD, NMR, SEM, thermal analysis, mechanical and acid resistance testing. The use of rice husk ash favors formation of a fully amorphous geopolymer with high strength. Utilization of the other silica feedstocks leads to formation of aluminosilicate gel-zeolite composites, the amount and kind of zeolites depending on the feedstock and the SiO2/Al2O3 ratio. These composites show beneficial dehydration behavior, viz. no distinct dehydration step of thermal strain, with the phase assemblage after heating to 1000°C controlled by the starting composition. Mortars produced from both, the geopolymers as well as the composites, exhibit high resistance to sulfuric acid attack, making them promising materials for the construction and the repair of industrial and sewer structures.
The influence of starting materials and synthesis route on the properties and the structure of cementitious sodium aluminosilicate gels is not fully understood, partly due their amorphous nature and the fact that they often contain residual reactants, which can make the results of single-pulse NMR spectroscopy applied to these materials difficult to interpret or ambiguous. To overcome some of these limitations, 29Si{27Al} TRAPDOR NMR as well as 27Al{29Si} and 27Al{1H} REDOR NMR spectroscopy were applied to materials synthesized by the one-part alkali-activation route from three different amorphous silica starting materials, including rice husk ash. The latter led to formation of a fully amorphous sodium aluminosilicate gel (geopolymer), while the materials produced from the other silicas contained amorphous phase and crystalline zeolites. Application of the double-resonance NMR methods allowed to identify hydrous alumina gel domains in the rice husk ash-based material as well as significantly differing amounts of residual silica in the three cured materials. Four-coordinated Al existed not only in the aluminosilicate gel framework but also in a water-rich chemical environment with only a small amount of Si in proximity, likely in the alumina gel or possibly present as extra-framework Al in the aluminosilicate gel. The results demonstrate how the employment of different silica starting materials determines the phase assemblage of one-part alkali-activated materials, which in turn influences their engineering properties such as the resistance against chemically/biologically aggressive media.