6.1 Oberflächen- und Dünnschichtanalyse
Filtern
Dokumenttyp
- Vortrag (221)
- Zeitschriftenartikel (196)
- Posterpräsentation (97)
- Forschungsdatensatz (27)
- Sonstiges (16)
- Beitrag zu einem Sammelband (10)
- Forschungsbericht (8)
- Beitrag zu einem Tagungsband (7)
- Handbuch (4)
- Sammelband (Herausgeberschaft für den kompletten Band) (2)
Sprache
- Englisch (593) (entfernen)
Schlagworte
- Nanoparticles (129)
- XPS (91)
- Electron microscopy (58)
- SEM (50)
- VAMAS (40)
- X-ray photoelectron spectroscopy (32)
- HAXPES (31)
- Particle size distribution (30)
- ToF-SIMS (29)
- NAP-XPS (23)
Organisationseinheit der BAM
- 6 Materialchemie (593)
- 6.1 Oberflächen- und Dünnschichtanalyse (593)
- 1 Analytische Chemie; Referenzmaterialien (52)
- 6.6 Physik und chemische Analytik der Polymere (46)
- 4 Material und Umwelt (32)
- 1.2 Biophotonik (27)
- 5 Werkstofftechnik (27)
- 6.3 Strukturanalytik (24)
- 6.7 Materialsynthese und Design (23)
- 6.2 Material- und Oberflächentechnologien (22)
Paper des Monats
- ja (7)
A new method for top‐down, one‐pot, gram‐scale production of high quality nanographene by incubating graphite in a dilute sodium hypochlorite solution at only 40 °C is reported here. The produced sheets have only 4 at% oxygen content, comparable with nanographene grown by chemical vapor deposition. The nanographene sheets are covalently functionalized using a nondestructive nitrene [2+1] cycloaddition reaction that preserves their π‐conjugated system. Statistical analyses of Raman spectroscopy and X‐ray photoelectron spectroscopy indicate a low number of sp3 carbon atoms on the order of 2% before and 4% after covalent functionalization. The nanographene sheets are significantly more conductive than conventionally prepared nanographene oxide, and conductivity further increases after covalent functionalization. The observed doping effects and theoretical studies suggest sp2 hybridization for the carbon atoms involved in the [2+1] cycloaddition reaction leading to preservation of the π‐conjugated system and enhancing conductivity via n‐type doping through the bridging N‐atom. These methods are easily scalable, which opens the door to a mild and efficient process to produce high quality nanographenes and covalently functionalize them while retaining or improving their physicochemical properties.
The uncertainty of measurement in quantitative XPS analysis can be reduced by using a calibrated spectrometer transmission function T (E), which is usually determined by taking spectra from Au, Ag, Cu and Ge elemental reference materials. However, this approach is quite time-consuming due to required sample preparation steps like sputter cleaning etc., and the relatively big number of samples to be measured. This contribution proposes the use of the ionic liquids [C2C1im][NTf2] and [C3C1im][NTf2] as reference materials for a determination of T(E). These multi-elemental samples deliver five intensive photoemission peaks, F 1s, O 1s, N 1s, C 1s and S 2p, in an energy window from 160 eV to 700 eV which is of specific interest for applications of quantitative XPS for surface chemical analysis of soft matter, one of the major applications of XPS.
The SAWG was established as an ad-hoc working group in 2003 before being established as a permanent working group. The first comparison was in 2007. Dr Unger recalled the terms of reference for the group, which paralleled those of the CCQM itself, with a focus on spatially resolved chemical surface analysis at the micro- and nano-scale. The group also had a remit to act as a forum for exchange of information on research and development of surface analysis, establish contact with relevant stakeholders and promote the development of SI traceable chemical surface measurements. The group currently had participants from 18 institutes, although five had not sent participants to recent meetings.
Reporting progress on studies, Dr Unger said that P-190CCQM-K-157 (measurement of HfO2 in thin film) had been completed, and the subsequent K-157 approved is ongoing and that for CCQM-K153 (Measurement of Specific Adsorption of N2 and Kr on nonporous SiO2 at liquid nitrogen temperature by BET) was at the draft B was completed stageand distributed to CCQM WG chairpersons for approval.
Dr Unger reported that CCQM-K-153 had covered measurement of specific absorption of nitrogen or krypton on nonporous silica at liquid nitrogen [ambient] temperature. This included an application of the BET method, a standard method for determination of surface area. This fitted into the ‘nonporous’ region of the SAWG measurement space, which included microporous, mesoporous and microporous regions. Of these regions, CCQM-K136 and CCQM-K153 demonstrated capability in meso- and microporous media respectively. CCQM-K153 involved two measurands; amount of absorbed gas at liquid nitrogen temperature, expressed as specific absorption, and the BET surface area. Specific absorption could in principle be traceable to the SI; BET was operationally defined. Five institutes participated. A detailed uncertainty budget was available for both measurands. Results had been excellent, with all laboratories agreeing well within their uncertainties and all in agreement with the reference value.
Reporting on CCQM P190, Dr Unger described the study objective measurand (amount of substance of HfO2 in a thin film), samples and methods. After showing transmission electron microscope images obtained in the study, he briefly reviewed the conclusions. The study identified a need to handle carbon contamination, harmonise the XPS measurement protocol, determine emission angle and identify a consensus value for attenuation length. These conclusions had informed the design of the proposed ongoing K157 study approved at the 24th Meeting of te CCQM.
The group planned a number of comparisons for the next three years:
2019: A pilot study on the amount of substance in a thin organic layer (previously approved).
2020: CCQMK-157, Measurement of the amount of substance of HfO2; A Key comparison on specific gas adsorption on microporous samples and a Pilot study on Homogeneous surface composition of an ionic liquid.
2021: A key comparison measuring the amount of substance in a thin organic layer.
Dr Unger additionally described a recently proposed pilot study to examine chemical composition in a deep nanoscale layer. This was important for the electronics industry. Four participants had expressed interest. The measurand will be the amount of Ir(ppy)2(acac) in a thin organic layer within an organic layer stack on a silicon substrate. He also reported that SAWG had started work on characterisation of graphene material grown by chemical vapour decomposition (CVD). The work would examine coverage on the substrate, number of layers, level of disorder, uncertainty budgets associated with the measurement, and data analysis. A link to VAMAS Technical Work Area 41 “Graphene and Related 2D Materials“ would also be established.
Looking forward, Dr Unger said the group had established a task group on application of Raman spectroscopy. This had important applications but was currently seen as qualitative. He presented the terms of reference for the task group for approval by the CCQM.
Dr Unger reviewed the SAWG activities that have progressed the state of the art in measurement science. He listed the past and ongoing comparisons that had addressed new and challenging measurement problems, and drew attention to a number of key publications in surface analysis. He additionally described stakeholder engagement activities, including collaboration with VAMAS, input to ISO TC 201, contributions to Euramet projects, and contributions to two recent stakeholder workshops.
The chemical composition of surfaces functionalized with self-assembled monolayers (SAMs) is an important parameter that determines their performance in a broad range of applications, from immobilizing molecular machines to initiation and growth control of MOFs (Metal-Organic Frameworks). In this article, a critical Survey of XPS (X-ray photoelectron spectroscopy) and NEXAFS (near edge X-ray absorption fine structure) spectroscopy data for pyridine-functionalized monolayers on gold surfaces is presented to compile correlations that have been indiscernible before. Monolayers with aromatic backbones are compared to monolayers with aliphatic backbones.
Monolayers with pyridine end-groups are compared to mixed monolayers formed terpyridine-functionalized by molecules end-groups and non-functionalized molecules. Thiol-oxidation during ageing of the SAMs in air is addressed. And finally, the addressability of the SAMs for the deposition of metal-ions and organic molecules is investigated and compared. This work consequently delivers a comprehensive set of spectroscopic data of (ter-)pyridine-terminated SAMs and their performance as template for the preparation of functional multilayers of macrocycles exhibiting a preferential orientation.
If the particle size decreases, the ratio of surface area to volume increases considerably. This provides benefits for all surface-driven processes that run faster or at lower temperatures than larger particles. However, handling and characterization of the nanopowders are much more difficult. Particularly polydisperse powders with irregular shape, as grinding products, represent a challenge. Granulometry in the submicron and nanoscale often leads to incorrect results without knowledge of particle morphology.
This presentation demonstrates potentials of using the volume-specific surface area (SV or VSSA) in the granulometric characterization of nanopowders, for instance, correlations between the volume-specific surface area and the median particle size are discussed considering the particle morphology and the model of the logarithmic normal distribution.
Moreover, the presentation deals with the optimal dispersion of nanopowders during sample preparation. Indirect ultrasound device with defined cooling was developed to prevent both contamination by sonotrode abrasion and sample changes by heat.
Successful granulometric characterization of nanopowders demands both improved dispersion technology and very often an effective combination of two or more measurement methods.
In this work, a novel boehmite (BA)-embedded organic/inorganic nanocomposite coating based on cycloaliphatic epoxy oligosiloxane (CEOS) resin was fabricated applying UV-induced cationic polymerization. The main changes of the material behavior caused by the nanofiller were investigated with regard to its photocuring kinetics, thermal stability, and glass transition. The role of the particle surface was of particular interest, thus, unmodified nanoparticles (HP14) and particles modified with p-toluenesulfonic acid (OS1) were incorporated into a CEOS matrix in the concentration range of 1–10 wt.%. Resulting nanocomposites exhibited improved thermal properties, with the glass transition temperature (Tg) being shifted from 30 °C for unfilled CEOS to 54 °C (2 wt.% HP14) and 73 °C (2 wt.% OS1) for filled CEOS. Additionally, TGA analysis showed increased thermal stability of samples filled with nanoparticles. An attractive interaction between boehmite and CEOS matrix influenced the curing. Real-time infrared spectroscopy (RT-IR) experiments demonstrated that the epoxide conversion rate of nanocomposites was slightly increased compared to neat resin. The beneficial role of the BA can be explained by the participation of hydroxyl groups at the particle surface in photopolymerization processes and by the complementary contribution of p-toluenesulfonic acid surface modifier and water molecules introduced into the system with nanoparticles.
Considerations for nanomaterial identification of powders using volume-specific surface area method
(2019)
The EC’s recommendation for a definition of nanomaterial (2011/696/EU) should allow the identification of a particulate nanomaterial based on the number-based metric criterion according to which at least 50% of the constituent particles have the smallest dimension between 1 and 100 nm. However, it has been recently demonstrated that the implementation of this definition for regulatory purposes is conditioned by the large deviations between the results obtained by different sizing methods or due to practical reasons such as high costs and time-consuming.
For most measurement methods for particle size determination it is necessary to initially disperse the particles in a suitable liquid. However, as the particle size decreases, the adhesion forces increase strongly, making it more difficult to deagglomerate the particles and to assess accurately the result of this process. Therefore, the success of the deagglomeration process substantially determines the measurement uncertainty and hence, the comparability between different methods.
Many common methods such as dynamic light scattering (DLS), centrifugal liquid sedimentation (CLS) or ultrasound attenuation spectroscopy (US) can give good comparable results for the size of nanoparticles, if they are properly separated and stabilized (e.g. in reference suspensions).
In order to avoid the use of hardly available and expensive methods such as SEM / TEM for all powders, an agglomeration-tolerant screening method is useful.
One of the measurement methods well suited to probe the size of particulate powder is the determination of the volume-specific surface area (VSSA) by means of gas adsorption as well as skeletal density. The value of 60 m2/cm3 corresponding to spherical, monodisperse particles with a diameter of 100 nm constitutes the threshold for decisioning if the material is a nano- or non-nanomaterial. The identification of a nanomaterial by VSSA method is accepted by the EU recommendation.
However, the application of the VSSA method was associated also with some limitations. The threshold of 60 m2/cm3 is dependent on the particle shape, so that it changes considerably with the number of nano-dimensions, but also with the degree of sphericity of the particles. For particles containing micro-pores or having a microporous coating, false positive results are induced. Furthermore, broad particle size distributions made necessary to additionally correct the threshold. Based on examples of commercially available ceramic powders, the applicability of the VSSA approach was tested in relation with SEM and TEM measurements. The introduction of a correction term for deviations from sphericity and further additions improved the applicability of VSSA as a screening method.
The stabilization of crystal phases and nanostructured morphologies is an essential topic in application-driven design of mesoporous materials. Many applications, e.g. catalysis, require high temperature and humidity. Typical metal oxides transform under such conditions from a metastable, low crystal-line material into a thermodynamically more favorable form, i.e. from ferrihy-drite into hematite in the case of iron oxide. The harsh conditions induce also
a growth of the crystallites constituting pore walls, which results in sintering and finally collapse of the porous network. Herein, a new method to stabi-lize mesoporous templated metal oxides against sintering and pore collapse is reported. The method employs atomic layer deposition (ALD) to coat the internal mesopore surface with thin layers of either alumina or silica. The authors demonstrate that silica exerts a very strong influence: It shifts hematite formation from 400 to 600 °C and sintering of hematite from 600 to 900 °C.
Differences between the stabilization via alumina and silica are rationalized by a different interaction strength between the ALD material and the ferrihydrite film.
The presented approach allows to stabilize mesoporous thin films that require a high crystallization temperature, with submonolayer quantity of an ALD material, and to apply mesoporous materials for high temperature applications.
The Scope of the Workshop was to provide a forum for discussion on progress in development, characterisation and application of reference nanomaterials. Results of recently finsihed national and international research projects have been presented. Moreover, the need for future developments have been addressed.
Attendees of teh Workshop were expected to be experts from academia, research institutes, regulatory bodies and industry working or interested in the area of reference nanomaterials.
The following structure of Workshop was planned: the main focus of the first day was on reference material needs and development, while teh second day was focussed on reference materials characterisation and standardisation.
Over 111 participants frm 13 countries and teh European Joint Research Centre have regsitered for the Workshop with 16 platform presentations and 42 poster contributions grouped in 2 sessions and 10 topical areas.
A summary of the observations, analysis and conclusions of the Workshop is made including an overview table of links to information on existing reference nanomaterials.
An overview of the activities in the field of surface and microbeam analysis at BAM-6.1 is given with focus on physico-chemical characterization at the nanoscale. Ideas of potential joint activities are presented: structural and chemical analysis of graphene, deposition techniques for nanoparticles, EBSD on steel for a broader range of methods, instruments and types of steel, soft X-ray Analysis of low-Z materials, analysis of mesoporous thin films, etc.
The damaging impact of hydrogen on the austenitic stainless steel AISI 304 L was analysed.
To this aim, samples were charged electrochemically with the hydrogen isotope deuterium (2H, D) and examined with time-of-flight secondary ion mass spectrometry (ToF-SIMS) and electron backscatter diffraction (EBSD). The fusion of the obtained chemical and structural information revealed local enrichment of deuterium in austenite, transformation into martensite, crack formation and severe roughening of the specimen surface. The results indicated that martensite was not only formed during charging but also during Desorption and ToF-SIMS examinations. Furthermore, cross-sections of deuterium-charged samples revealed that in preferred deformation bands a g/ε/a 0 evolution is taking place.
By means of microscopic analyses and carrier gas hot extraction (CGHE), it was found that the use of NaAsO2 as recombination poison decreased the uptake of hydrogen significantly and resulted in severe precipitation on the specimen surfaces. This is in contrast to the popular presumption that NaAsO2 enhances the uptake of hydrogen (and
deuterium) during electrochemical charging by hampering its recombination from Atoms to molecules.
UV-curing coatings are nowadays widely used due to their unique advantages. High-quality coatings can be obtained at short curing times and low temperatures so that thermal stress to the substrate is minimised. Photocured Cycloaliphatic-Epoxy Oligosiloxane (CEO) resin was reported to be used as encapsulation material for organic electronics. However, further reinforcement of CEO film properties is desired to achieve requested device lifetime.
In this work we introduced Boehmite nanoparticles (BA) into CEO matrix in order to modify the film properties and study the main changes of the material behaviour with regard to its photocuring kinetics, thermal stability and glass transition. Particular interest was focused on the role of particle surface in nanocomposite properties. Hence, BA particles without (HP14) and with organic surface modifier (OS1) at different loadings (up to 10 wt%) were applied in this study. Morphology investigation with SEM operated in transmission mode showed good BA dispersion forming network-like structure. At the same time, distribution of particles differed for HP14 and OS1 as a result of different interaction in CEO-solvent-particles system. CEO structure obtained via non-hydrolytic sol-gel reaction was verified by 13C and 29Si NMR. In situ monitoring of film curing was performed using RT-IR spectroscopy. No significant modification of final convention degree with particle incorporation was observed in contrast to considerable decrease of curing efficiency reported previously for similar system by Esposito et al.,2008. Further, cured hybrid nanocomposite films were analysed by TGA and DSC, which revealed impact of surface modifier on film thermal properties.
Organic-inorganic nanostructured materials have drawn much attention over the past decade, particularly due to their versatile and outstanding properties. Possessing the properties between those of polymers and those of glasses, siloxane-based resins are non-toxic, easy to synthesize and process hybrid materials, that hold a promising potential in the field of advanced coatings.
Photocurable resins are nowadays widely used as coatings due to their unique advantages. In particular, cationic ring-opening curing is not inhibited by oxygen, leads to low degree of shrinkage and superior adhesion. The most important, it enables production of high-quality coatings within short exposure times without applying temperature, thus, minimizing the presence of the thermal stress in the substrate. Photocured Cycloaliphatic-Epoxy Oligosiloxane (CEO) resin was reported to be used as encapsulation material for organic electronics. However, further reinforcement of CEO properties is desired to achieve requested device lifetime. One of the common approaches to improve material characteristics is by embedding inorganic nanoparticles into polymer matrix. It has been shown that the resulted nanocomposites exhibit enhanced functional properties included but not limited by optical, mechanical, thermal and barrier ones.
In this work we focused on the incorporation of Boehmite nanoparticles (BA) into CEO matrix as a tool to strengthen the film properties and to study the main changes occurred in the material behavior with regard to its photocuring kinetics, thermal stability and glass transition. Particular interest was focused on the role of particle surface in nanocomposite properties. Hence, BA particles without (HP14) and with organic surface modifier (OS1) at different loadings
(up to 10 wt%) were applied in this study. Morphology investigation with SEM operated in transmission mode showed good BA dispersion forming
network-like structure. At the same time, distribution of particles differed for HP14 and OS1 as a result of different interaction in CEO-solvent-particles system. CEO structure obtained via non-hydrolytic sol-gel reaction was verified by 13C and 29Si NMR. In situ monitoring of film curing was performed using
RT-IR spectroscopy. A slight increase of final convention degree with particle incorporation was observed in contrast to the considerable decrease of curing efficiency reported previously for similar system. Further, the cured hybrid nanocomposite films were analyzed by TGA and DSC, which revealed impact of surface modifier on thermal stability and glass transition temperature.
Coating materials are nowadays often required to deliver not only sufficient barrier performance and suited optical appearance but a broad range of other functional properties. The incorporation of inorganic nanoparticles (NPs) is known to improve many key characteristics and provide new functionalities in polymer materials. Presented work aims to prepare and characterize an organic-inorganic coating material designed to bring together advantageous properties of hybrid materials and reinforcement effect delivered from the inorganic NPs embedment.
Siloxane-based hybrid resins hold great advantages as coating materials as their properties can be tuned between those of polymers and those of glasses, thus, the compositions with superior thermal and mechanical properties can be achieved. We used Cycloaliphatic Epoxy Oligosiloxane (CEOS) resin as a polymeric matrix where the network formation was achieved by UV induced cationic polymerisation. Boehmite Alumina (BA) nanoparticles were added to CEOS resin as a reinforcing agent and resultant material was processed into films either by bar-coating or by spin-coating depending on further characterization procedure. Two different types of BA NPs, hydrophilic and organophilic, were used in order to assess the impact of particles surface on the resin characteristics. CEOS synthesis by condensation reaction was confirmed using 13C and 29Si NMR. Changes in CEOS photocuring process, resulting from particles incorporation, were monitored by real-time IR spectroscopy. At the same time, the thermal behaviour was evaluated by DSC and TGA methods. Morphology of the coatings was investigated by means of SEM operated in transmission mode.
It was observed that BA presence increased the epoxy conversion degree and glass transition temperature. Material formulations providing best film characteristics were determined with regard to the particle type and loading. Compared to the hydrophilic nanoparticles, organophilic BA NPs yield superior overall performance of the foils.
Thermosetting materials are gaining increasing attention in many structural composite applications. However, the incorporation of inorganic nanoparticles (NPs) into polymer matrix is a promising approach to enhance their functional characteristics, and thus, to enable the development of thermosets advanced application. It has been shown that Boehmite Alumina (BA) used as nanofillers can improve different parameters of polymers. This NPs can be easily tailored enabling desirable interactions with a big range of polymers. However, the overall effect of nanofiller depends on many factors, therefore, making it hard to predict the resulted performance of nanocomposites. In the current contribution we would like to discuss the impact of Boehmite NPs on two different epoxy resin nanocomposite systems with the focus on the possible influence mechanisms of this nanofiller.
As the first system, UV curable Cycloaliphatic-Epoxy Oligosiloxane (CEOS) resin/Boehmite nanocomposites were investigated by FTIR, TGA, DSC and T-SEM. It was observed that incorporation of BA leads to the reinforcement of glass transition (Tg) and overall thermal stability indicating the attractive interactions between BA and CEOS network. In addition, an increase in epoxy conversion of CEOS was concluded for nanocomposites assuming that particles are involved in UV polymerisation processes.
The second epoxy/Boehmite nanocomposite is based on the bisphenol-A-diglycidyl ether (DGEBA) cured with methyl tetrahydrophtalic acid anhydride (MTHPA). Thermomechanical as well as nanomechanical properties of this material were investigated by DMTA and IR spectroscopy and the advanced Intermodulation AFM, respectively. In contrast to the first system, it was found that BA leads to a decrease of Tg and crosslink density of the polymer while the young’s modulus of the composite and local stiffness of polymer matrix increase significantly.
As a result, the versatile role of Boehmite was detected depending on the investigated systems. Based on the obtained results, the parameters indicating property-efficient epoxy/Boehmite system are suggested.
We show that complex physical and chemical interactions between boehmite nanoparticles and epoxy drastically affect matrix properties, which in the future will provide tuning of material properties for further optimization in applications from automotive to aerospace. We utilize intermodulation atomic force microscopy (ImAFM) for probing local stiffness of both particles and polymer matrix. Stiff particles are expected to increase total stiffness of nanocomposites and the stiffness of polymer should remain unchanged. However, ImAFM revealed that stiffness of matrix in epoxy/boehmite nanocomposite is significantly higher than unfilled epoxy. The stiffening effect of the boehmite on epoxy also depends on the particle concentration. To understand the mechanism behind property alteration induced by boehmite nanoparticles, network architecture is investigated using dynamic mechanical thermal analysis (DMTA). It was revealed that although with 15 wt% boehmite nanoparticles the modulus at glassy state increases, crosslinking density of epoxy for this composition is drastically low.
The aim of this study was to evaluate cytotoxicity (WST-1 assay), LDH release (LDH assay) and genotoxicity (Comet assay) of three engineered TiO2-NPs with different shapes (bipyramids, rods, platelets) in comparison with two commercial TiO2-NPs (P25, food grade). After NPs characterization (SEM/T-SEM and DLS), biological effects of NPs were assessed on BEAS-2B cells in presence/absence of light. The cellular uptake of NPs was analyzed using Raman spectroscopy.
The cytotoxic effects were mostly slight. After light exposure, the largest cytotoxicity (WST-1 assay) was observed for rods; P25, bipyramids and platelets showed a similar effect; no effect was induced by food grade. No LDH release was detected, confirming the low effect on plasma membrane. Food grade and platelets induced direct genotoxicity while P25, food grade and platelets caused oxidative DNA damage. No genotoxic or oxidative damage was induced by bipyramids and rods. Biological effects were overall lower in darkness than after light exposure. Considering that only food grade, P25 and platelets (more agglomerated) were internalized by cells, the uptake resulted correlated with genotoxicity.
In conclusion, cytotoxicity of NPs was low and affected by shape and light exposure, while genotoxicity was influenced by cellular-uptake and aggregation tendency.
Combining X-ray Absorption Fine Spectroscopy (XAFS) with Anomalous Small-Angle X-ray Scattering (ASAXS) determines the location of Cu2+ ions in silicoaluminophosphate (SAPO-5) frameworks prepared by hydrothermal crystallization or impregnation. As expected, for the hydrothermally prepared sample, incorporation in the SAPO-5 framework was observed. For the first time preferential location of Cu2+ ions at the inner and outer surfaces of the framework is determined. Temperature-Programmed Reduction (TPR) and X-ray Photoelectron Spectroscopy (XPS) investigations demonstrated that such Cu2+ is stable in an argon (Ar) atmosphere up to 550 °C and can only be reduced under a hydrogen atmosphere. In contrast, Cu2+ deposited by impregnation on the pure SAPO-5 framework can be easily reduced to Cu+ in an Ar atmosphere. At lower Cu amounts, mononuclear tetrahedrally coordinated Cu species were formed which are relatively stable in the monovalent form. In contrast, at higher Cu amounts, CuO particles were found which change easily between the mono- and bivalent species.
Nanomaterials are a relatively new class of materials for which a regulatory framework still has to be established and regulators require comprehensive datasets of well characterized nanomaterials for the implementation. Especially information about the surface chemistry of nanoparticles is crucial, since it largely determines their biological and environmental fate. How the surface chemistry changes under relevant ageing conditions is of particular interest, because exposure will normally occur not to the pristine material but to a nanoform that underwent some kind of transformation.
In this talk, first a short overview about the contributions of division 6.1 to multiple European-funded projects will be presented, in which surface analytical techniques are used to improve the physical-chemical characterization of nanomaterials. Secondly, a study investigating the surface-chemical transformations of a representative set of titanium dioxide nanoparticles is discussed in more detail. The ageing has partly been performed at the BAM division 7.5, and the surface chemistry was analyzed using time-of-flight secondary ion mass spectrometry (ToF-SIMS) and X-ray photoelectron spectroscopy (XPS). By analyzing the complex mass spectra with principal component analysis (PCA), it was possible to identify even subtle changes that occur upon ageing.