Metal-organic frameworks (MOFs) are suitable materials for gas storage of small molecules due to their nanoporous, crystalline structure. The extensively studied MOF HKUST-1 consist of Cu(II)-dimers in a paddlewheel structure, with 1,3,5-benzenetricarboxylic acid (BTC) as organic linker. Instability to humidity remains an issue for many types of MOFs, and for HKUST-1, it has been found that exposure to water vapor creates a surface barrier which reduces the gas uptake rate.
Near-ambient pressure XPS (NAP-XPS) is a promising method for investigations of the stability and interaction of HKUST-1 with various gas molecules. The oxidation state of copper can be monitored before, during and after exposure to various gases. This does not only provide information on the stability of the MOFs, but also on the interaction with the gas molecules.
NAP-XPS measurements of HKUST-1 exposed to methanol, pyridine and water vapor were performed with EnviroESCA, a laboratory NAP-XPS instrument developed by SPECS. Cu 2p, O 1s and C 1s core level spectra and Cu LMM Auger spectra were acquired at pressures ranging from high vacuum to 4 mbar to assess the oxidation state of copper and the stability of the organic linker. Reference measurements in argon atmosphere were conducted in order to have reference spectra with similar full width of half maxima (FHWM) as the spectra measured in reactive atmospheres. Peak fit analysis of the Cu 2p3/2 core level spectra shows that, as expected, the photoelectron signal mainly originates from Cu(II) species. The contribution from Cu(I) is negligible for samples exposed to argon and methanol, but approximately 4% for samples exposed to water vapor and 8% for samples exposed to pyridine. Within the error of the peak fit analysis, there are no changes in relative Cu(II) percentage with increasing water, methanol or pyridine exposure time pointing to saturation reached already at the lowest time of exposure.
Bacterial samples are typically freeze dried or cryo-prepared prior to XPS analysis to allow for measurements in ultra-high vacuum (UHV). The sample environment in the near-ambient pressure (NAP) XPS instrument EnviroESCA allows for measurements in up to 15 mbar water vapor, thus, sample preparation is no longer restricted to UHV-compatible techniques. For instance, biofilms grown in medium can be transferred directly from the medium to the measurements chamber, maintaining a humid environment throughout the measurements. Considering the complexity of bacterial samples, sample preparation must be carefully considered in order to obtain meaningful and reproducible results.
In this talk, various strategies for sample preparation of bacteria and biofilms for NAP-XPS measurements will be discussed. Model systems of planktonic bacteria, artificial biofilms resembling the exopolysaccharide matrix and biofilms have been characterised in various conditions. The stability and homogeneity of the samples was assessed by monitoring the C1s core level peak at different sample locations. The quality of the XPS-spectra is also influenced by the gas environment, which will be exemplified by core level spectra of P. Fluorescens acquired in air, water vapor and ultra-high vacuum.
Core-shell nanoparticles (CSNPs) have become indispensable in various industrial applications. However, their real internal structure usually deviates from an ideal core-shell structure. To control how the particles perform with regard to their specific applications, characterization techniques are required that can distinguish an ideal from a non-ideal morphology. In this work, we investigated PTFE-PMMA (four samples) and PTFE-PS (six samples) polymer CSNPs with constant core diameter (45 nm) but varying shell thickness (4-50 nm). As confirmed by transmission scanning electron microscopy (T-SEM), the shell completely covers the core for the PTFE-PMMA nanoparticles, while the encapsulation of the core by the shell material is incomplete for the PTFE-PS nanoparticles. X-ray photoelectron spectroscopy (XPS) was applied to determine the shell thickness of the nanoparticles. The software SESSA V2.0 was used to analyze the intensities of the elastic peaks and the QUASES software package to evaluate the shape of the inelastic background in the XPS Survey spectra.
For the first time, nanoparticle shell thicknesses are presented which are exclusively based on the analysis of the XPS inelastic background. Furthermore, principal component analysis (PCA) assisted time-of-flight secondary ion mass spectrometry (ToF-SIMS) of the PTFE-PS nanoparticle sample set revealed a systematic variation among the samples and, thus, confirmed the incomplete encapsulation of the core by the shell material. Opposed to that, no variation is observed in the PCA scores plots of the PTFE-PMMA nanoparticle sample set. Consequently, the complete coverage of the core by the shell material is proved by ToF-SIMS with a certainty that cannot be achieved by XPS and T-SEM.
Metal-organic frameworks (MOFs) are suitable materials for gas storage of small molecules due to their nanoporous, crystalline structure. The extensively studied MOF HKUST-1 consist of Cu(II)-dimers in a paddlewheel structure, with 1,3,5-benzenetricarboxylic acid (BTC) as organic linker. Instability to humidity remains an issue for many types of MOFs, and for HKUST-1, it has been found that exposure to water vapor creates a surface barrier which reduces the gas uptake rate.
Near-ambient pressure XPS (NAP-XPS) is a promising method for investigations of the stability and interaction of HKUST-1 with various gas molecules. The oxidation state of copper can be monitored before, during and after exposure to various gases. This does not only provide information on the stability of the MOFs, but also on the interaction with the gas molecules and the reversibility of the processes.
NAP-XPS measurements of HKUST-1 exposed to methanol, pyridine and water vapor were performed with EnviroESCA, a laboratory NAP-XPS instrument developed by SPECS. Cu 2p, O 1s and C 1s core level spectra were acquired in pressure ranging from 10-5 to 8 mbar to assess the oxidation state of copper and the stability of the organic linker. HKUST-1 does not show interaction with pyridine, but there are indications of copper-reduction upon exposure to methanol and water vapor. Radiation induced damage is considered and two different approaches for determining the ratio of Cu(I) to Cu(II) will be discussed.