6 Materialchemie
Filtern
Dokumenttyp
- Vortrag (21)
- Zeitschriftenartikel (8)
- Posterpräsentation (5)
- Beitrag zu einem Tagungsband (1)
Schlagworte
- Corrosion (35) (entfernen)
Organisationseinheit der BAM
- 6 Materialchemie (35)
- 6.2 Material- und Oberflächentechnologien (27)
- 4 Material und Umwelt (6)
- 4.1 Biologische Materialschädigung und Referenzorganismen (6)
- 6.3 Strukturanalytik (6)
- 5 Werkstofftechnik (3)
- 5.1 Mikrostruktur Design und Degradation (3)
- 6.1 Oberflächen- und Dünnschichtanalyse (3)
- 1 Analytische Chemie; Referenzmaterialien (2)
- 7 Bauwerkssicherheit (2)
Eingeladener Vortrag
- nein (21)
The performance of functional coatings and adhesively joined hybrid components relies strongly on the stability of the polymer-metal interface. With the increasing utilization of multi-material structures in the automotive and aerospace industry, it is of great scientific and technical interest to understand the processes leading to interface degradation and to develop novel strategies to increase corrosion and delamination resistance.
The aim of this project is to develop thin epoxy-based films and their carbon nanofiller loaded composites on aluminium alloy AA2024-T3 as a model system and to investigate their interfacial stability under corrosive and coupled corrosive-mechanical load. Spin coating was used for the layer-by-layer deposition of poly[(o-cresyl glycidyl ether)-co-formaldehyde] and poly-(ethylenimine) bi-layers. Atomic force microscopy (AFM) results indicate a very homogeneous and dense film with low surface roughness. Carbon nanofillers were introduced either by mixing into the coating components or in between individual layers to control the separation between the carbon nanofillers and alloy surface. The film chemistry and barrier properties were characterized by means of spectroscopic and electrochemical methods, respectively. The degradation and delamination behavior of the epoxy-based films was characterized by means of in situ AFM corrosion experiments. The quantitative imaging (QI) mode allowed the observation of hydrogen-generation induced blister formation during exposure to corrosive electrolyte and how the local corrosion processes evolved with exposure time. Complementary energy dispersive X-ray spectroscopy (EDX) analysis was performed to correlate the corrosion behavior with the different intermetallic particle chemistries and distributions. The presentation will summarize our results on the effect of interface chemistry and carbon nanofiller – alloy separation on the initiation of local corrosion processes on thin film covered AA2024-T3 aluminium alloys.
With increasing demand and environmental concerns, researchers are exploring new materials that can perform as well or better than traditional materials while reducing environmental impact. The BAMline, a real-life sample materials research beamline, provides unique insights into materials’ electronic and chemical structure at different time and length scales. The beamline specializes in x-ray absorption spectroscopy, x-ray fluorescence spectroscopy, and tomography experiments. This enables real-time optimization of material properties and performance for various applications, such as energy transfer, energy storage, catalysis, and corrosion resistance. This paper gives an overview of the analytical methods and sample environments of the BAMline, which cover non-destructive testing experiments in materials science, chemistry, biology, medicine, and cultural heritage. We also present our own synthesis methods, processes, and equipment developed specifically for the BAMline, and we give examples of synthesized materials and their potential applications. Finally, this article discusses the future perspectives of the BAMline and its potential for further advances in sustainable materials research.
The efficient exploration of novel alloy compositions is crucial for advancing the development of new materials. One widely utilized approach for creating phase diagrams is the use of diffusion-controlled synthesis for gradient alloys. This method is also an effective means for rapidly identifying potential material combinations.
The present study focusses on the exploration of quaternary multi-principle-element alloys (MPEAs) using diffusion multiples. We established a diffusion system by combining an equimolar ternary alloy (FeNiCr) with single diffusing elements Mn and Mo. Using ThermoCalc simulations, we determined suitable temperature ranges where we can expect the formation of single-phase alloys. Depending on the diffusion constants of the selected metals, diffusion times were adjusted to obtain diffusion zones with a depth of greater than 50 μm. Microstructural and compositional information was gathered via scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX) and correlated to local mechanical properties evaluated by means of nanoindentation. Local corrosion properties were examined using Atomic Force Microscopy (AFM) and Scanning Electrochemical Microscopy (SECM).
Our results indicate that the ThermoCalc simulations have a good predictive power for crystallographic phases. However, especially with the Mn-FeNiCr system, formation of Cr-rich secondary phases were observed, which led to Cr-depletion and thus to localized corrosion processes in the matrix at the vicinity of the secondary phases. Based on the results of the local electrochemical tests, we have selected single-phase compositions along the diffusion zone and synthesized these alloys in bulk for corrosion studies by means of potentiodynamic polarization and SECM.
The presentation will summarize our methodology using diffusion couples as an
efficient tool for exploring compositional spaces of MPEAs in the search for novel single-phase alloys and the results of our correlative study on the mechanical and corrosion properties of these materials.
The efficient exploration of novel alloy chemistries is crucial for advancing the development of new materials. Diffusion-controlled synthesis of gradient alloys is an intelligent approach for creating phase diagrams and to effectively identify potential material combinations with tailored properties.
This project focusses on the design of quaternary multi-principle-element alloys (MPEAs) using diffusion couples. Our diffusion system contains an equimolar ternary alloy (FeNiCr) and additional single diffusing elements e.g. Mn and Mo. We determined the optimal temperature ranges for the diffusion thermal treatment by means of ThermoCalc simulations with the aim to form single-phase MPEAs. Microstructure and chemical characterization of the diffusion couples were performed by means of scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX). For most alloy couples, the diffusion zone contained a single-phase alloy matrix with diffusion-induced compositional gradient as well as precipitation phases. This heterogeneity makes the diffusion couples interesting materials to investigate local mechanical and corrosion properties. Thus, local corrosion properties were examined using Atomic Force Microscopy (AFM) and Scanning Electrochemical Microscopy (SECM). Nanoindentation was used for the analysis of local mechanical properties.
Based on the results of the local corrosion analysis, we have selected single-phase alloy chemistries along the diffusion zone and reproducibly synthesized these alloys in bulk for detailed corrosion studies by means of potentiodynamic polarization and SECM.
The presentation will briefly summarize our methodology and motivation for using diffusion couples as an efficient tool for exploring phase diagrams of MPEAs in the search for new alloy chemistries and the results of our correlative study on the mechanical and corrosion properties of these materials.
While a lage amount of research on high entropy alloys is oriented towards mechanical properties and the microstructural improvement it is also necessary to keep an eye on the environment that potential application materials will be submitted to. The Co-Cr-Fe-Ni based high entropy family has shown great potential over the years of high entropy research and some candidate alloys are chosen for an insight into their corrosion behaviour. Several atmospheres are studied, i.e. O2, H2O, SO2 and a mix thereof in argon as well as synthetic air. Just as for classic alloys, the chromium is the most important element in terms of protection agains further corrosion. The addition of manganese, as in case of the “Cantor alloy” CrMnFeCoNi, overpasses Cr when it comes to oxygen affinity and thus counteracts the layer formation of Cr2O3. Even without Mn, a temperature chosen too high will also affect the formation of the chromium oxide layer and spall it off, annulling its protective potential. We can also observe how trace elements influence the layer formation. These effects and their mechanisms will be discussed for the alloys CrFeNi, CoCrNi, CrMnFeCoNi and variations of Al10Co25Cr8Fe15Ni36Ti6 using a combination of electron microscopy, thermodynamic calculations and x-ray diffraction.
Civilization and modern societies would not be possible without manmade materials. Considering their production volumes, their supporting role in nearly all industrial processes, and the impact of their sourcing and production on the environment, metals and alloys are and will be of prominent importance for the clean energy transition. The focus of materials discovery must move to more specialized, application-tailored green alloys that outperform the legacy materials not only in performance but also in sustainability and resource efficiency. This white paper summarizes a joint Canadian-German initiative aimed at developing a materials acceleration platform (MAP) focusing on the discovery of new alloy families that will address this challenge. We call our initiative the “Build to Last Materials Acceleration Platform” (B2L-MAP) and present in this perspective our concept of a three-tiered self-driving laboratory that is composed of a simulation-aided pre-selection module (B2L-select), an artificial intelligence (AI)-driven experimental lead generator (B2L-explore), and an upscaling module for durability assessment (B2L-assess). The resulting tool will be used to identify and subsequently demonstrate novel corrosion-resistant alloys at scale for three key applications of critical importance to an offshore, wind-driven hydrogen plant (reusable electrical contacts, offshore infrastructure, and oxygen evolution reaction catalysts).
Ferritic high temperature alloys are widely used as boiler tube and heat exchanger materials in coal, biomass and co-fired power plants. All technologies have in common that the applied materials are exposed to different temperatures, process pressures and reactive atmospheres that lead to a change of the material properties and a further degradation of the material. Material changes caused by aging in highly corrosive and toxic gases such as SO2 are mainly studied ex situ after the reaction is finished. The solid material is deposited in the atmosphere for a certain period of time, and material changes are then examined by various microscopic techniques such as optical microscopy (OM), electron microprobe analysis (EMPA), scanning electron microscopy (SEM and TEM) and X-ray diffraction (XRD). Nevertheless, extensive efforts were made to study material changes of high temperature alloys under oxidizing and reducing atmospheres by environmental scanning electron microscopy or in situ TEM techniques However, the possibilities of microscopic in situ techniques are very limited for the use of highly corrosive and toxic gases such as SO2. Since Sulfur induced corrosion at temperatures relevant for coal and biomass fired power plants, which is causing breakaway oxidation and sulfide precipitation at grain boundaries, is still of scientific interest, the current work focuses on the effect of SO2 in an initial stage of corrosion of ferritic alloys. For the analysis of early stages of combined oxidation and sulphidation processes of Fe-Cr model alloys the usage of a light furnace to conduct a rapid reactive annealing experiment is feasible. Previous studies presented distinct results of the influence of chromium on early high temperature corrosion by SO2 by this technique and subsequent classical metallographic analyses. However, it is still not possible to trace the corrosion mechanism in real time by conducting single aging experiments. The current work introduces two different approaches to study the initial stages of high temperature oxidation processes by applying above state of the art X-ray diffraction and spectroscopy methods. One part focuses on the real time observation of the formation of corrosion products such as oxides and sulfides by energy dispersive X-ray diffraction (EDXRD). The potential of this technique to study crystallization and growth processes of thin films in a reactive environment in real time was previously shown for different compound semiconductors. This approach was now applied to follow oxidation and sulphidation processes of ferritic model alloys in SO2 and SO2/H2O environments. The diffraction signals of the X-rays were detected during the corrosion process and the peak area and positions were analyzed as a function of time. This procedure enables monitoring external oxide growth and material loss in real time in an early stage of corrosion.
The other part of the current work presents the possibilities of X-ray absorption near edge structure spectroscopy (XANES) to characterize oxide scales and their growth mechanisms. Precise phase identification and quantification of corrosion products in a multi-phase oxide/sulfide scale is a pre-requisite to understand diffusion paths of metal ions and gas components. It is a challenging task to distinguish structurally similar reaction products such as Fe3O4 and FeCr2O4 especially in thin films with texture effects by diffraction. To illustrate for example Cr-out diffusion of an alloy throughout an inner and external oxide scale the differentiation of Fe3O4 and FeCr2O4 is indispensable. XANES uses the photoionization effect at the metal absorption edge in an aging product and accesses by this structural and chemical information. The current work uses XANES at the Fe-K and Cr-K absorption edge to identify various aging products grown as thin layers on alloys after short time aging experiments. A reaction chamber for combining high temperature oxidation experiments with surface sensitive X-ray absorption near edge structure spectroscopy will be introduced and first results of XANES on scales at high temperatures will be presented.
The high-temperature corrosion behaviors of the equimolar CrCoNi medium- and CrMnFeCoNi high-entropy alloy were studied in a gas atmosphere consisting of a volumetric mixture of 10% H2O, 2% O2, 0.5% SO2, and 87.5% Ar at 800 °C for up to 96 h. Both alloys were initially single-phase fcc structured and showed a mean grain size of ~50 µm and a homogeneous chemical composition. The oxide layer thickness of the Cantor alloy CrMnFeCoNi increased linearly with exposure time while it remained constant at ~1 µm for CrCoNi. A Cr2O3 layer and minor amounts of (Co,Ni)Cr2O4 developed on CrCoNi while three layers were detected on the Cantor alloy. These layers were a thin and continuous chromium rich oxide layer at the oxide/alloy interface, a dense (Mn,Cr)3O4 layer in the center and a thick and porous layer of Mn3O4 and MnSO4 at the gas/oxide interface. Additionally, a few metal sulfides were observed in the CrMnFeCoNi matrix. These results were found to be in reasonable agreement with thermodynamic calculations.
Biocide mitigation strategies of microbiologically influenced corrosion (MIC) in the oil and gas industry have been primarily used to eliminate the growths of sulfate-reducing microorganisms (SRM). However, methanogenic Archaea (MA) can also be highly corrosive by using iron as an electron source for methanogenesis. Because of the fundamental physiological differences between archaea and bacteria, responses of MA towards SRM-specific biocides cannot be deduced using SRM. Due to the lack of information available on the effect of biocides on corrosive MA, we selected THPS, glutaraldehyde, nitrate and perchlorate to compare against corrosive SRM.
Preliminary results showed that at low concentrations of THPS (0-10 ppm), growth of MA was not affected, methane production and corrosion rates (0.1 mm/yr) were comparable between the different THPS concentrations. On the contrary, the SRM strain showed decreased corrosion rates (0.18 mm/yr to 0.03 mm/yr) with increasing THPS concentrations. Further corrosion tests including electrochemical measurements of different biocides on the growth of MA and SRM will be conducted. Such knowledge not only provide important insights on the physiological response of MA to biocides but also contribute to more effective mitigation strategies that can be both economic and environmentally beneficial.
Microbiologically induced corrosion due to bacterial biofilms causes several problems in industrial systems, technical applications and in medicine. Prior to the formation of a biofilm on a substrate, planktonic cells attach on the surface. Hence, the properties of the surface play a key role in biofilm formation and are of great importance for the development of strategies to prevent bacterial attachment and biofilm formation.
This project aims at clarifying to which extent surface micro-/nanostructuring and chemical functionalization affects bacterial attachment and whether a synergistic combination of the two can be used to control bacterial adhesion. To answer these questions, model surfaces with regular patterns of 5-10 micrometers in size have been prepared, which provide distinct zones differing in terms of their chemistry or nano-roughness. This was achieved by micro contact printing of self-assembled monolayers with different functional groups and deposition of patterned ZnO nanorod arrays for studying the effect of surface chemistry and morphology, respectively. Typical contrasts studied were combinations of positively/negatively charged, hydrophobic/hydrophilic or flat/rough.
The attachment behavior of bacteria on tailored surfaces were studied in a flow chamber as a function of time. The strain Pseudomonas fluorescens SBW25 was chosen as a model organism. DNA-intercalating dyes such as Syto9 have a high affinity to adsorb on ZnO nanorods. To overcome this limitation a genetic modification was performed by introducing a gene which expresses a green fluorescent protein in P. fluorescens SBW25 enabling the quantitative evaluation of the flow chamber studies by means of fluorescence microscopy. Further analysis of the attachment behavior was performed by means of scanning electron microscopy.
The presentation will summarize the results of our systematic study on the role of individual parameters on bacterial attachment and highlight synergistic combinations, showing an inhibition or enhancing effect. As the investigations with model substrates enable a precise control of the surface parameters, this approach can be applied to different microorganisms and material systems to achieve a correlative description of bacterial adhesion on solid surfaces.
Novel agar-based test electrolytes are used to perform electrochemical corrosion investigations on ZnFe and ZnNi binary as well as ZnFeMo ternary zinc coatings. The objectives of the electrochemical investigations include the characterization of the corrosion behavior, the description of the protective effect of the coatings as well as the investigation of the layer formation and degradation under artificial aging. ZnFe and ZnFeMo coatings are applied with varying iron content as well as an additional passivation layer, respectively, to study the effect on corrosion resistance. The results show that the protective effect of the coatings is not negatively influenced by different iron contents or the addition of molybdenum. Additional passivation of the ZnFe-containing coatings by means of a passivating agent leads to a significant improvement in the protective effect. Artificial aging leads to slight degradation of the additional passivation layer whereas coatings without post-treatment enhance their protective effect by the formation of corrosion product layers.
In this study, we propose the use of nondestructive, depth-resolved, element-specific characterization using grazing exit X-ray absorption near-edge structure spectroscopy (GE-XANES) to investigate the corrosion process in compositionally complex alloys (CCAs). By combining grazing exit X-ray fluorescence spectroscopy (GE-XRF) geometry and a pnCCD detector, we provide a scanning-free, nondestructive, depth-resolved analysis in a sub-micrometer depth range, which is especially relevant for layered materials, such as corroded CCAs. Our setup allows for spatial and energy-resolved measurements and directly extracts the desired fluorescence line, free from scattering events and other overlapping lines. We demonstrate the potential of our approach on a compositionally complex CrCoNi alloy and a layered reference sample with known composition and specific layer thickness. Our findings indicate that this new GE-XANES approach has exciting opportunities for studying surface catalysis and corrosion processes in real-world materials.
High-entropy alloys (HEAs) are characterized by a solid solution of minimum five and medium-entropy alloys (MEAs) of minimum three principal alloying elements in equiatomic proportions. They show exceptional application properties, such as high-strength and ductility or corrosion resistance. Future HEA/MEA-components could be exposed to hydrogen containing environments like vessels for cryogenic or high-pressure storage where the hydrogen absorption and diffusion in these materials is of interest. In our study, we investigated the HEA Co20Cr20Fe20Mn20Ni20 and the MEA Co33.3Cr33.3Ni33.3. For hydrogen ingress, cathodic charging was applied and diffusion kinetic was measured by high-resolution thermal desorption spectros-copy using different heating rates up to 0.250 K/s. Peak deconvolution resulted in high-temperature desorption peaks and hydrogen trapping above 280 °C. A total hydrogen concentration > 40 ppm was identified for the MEA and > 100 ppm for HEA. This indicates two important effects: (1) delayed hydrogen diffusion and (2) considerable amount of trapped hydrogen that must be anticipated for hydrogen assisted cracking phenomenon. Local electrochemical Volta potential maps had been measured for the hydrogen free condition by means of high-resolution Scanning Kelvin Probe Force Microscopy (SKPFM).
The performance of functional coatings and adhesively joined hybrid components relies strongly on the stability of the polymer-metal interface. With the increasing utilization of multi-material structures in the automotive and aerospace industry, it is of great scientific and technical interest to understand the processes leading to interface degradation and to develop novel strategies to increase corrosion and delamination resistance.
The aim of this project is to develop thin epoxy-based films on aluminium alloy AA2024-T3 as a model system and to investigate their interfacial stability under corrosive and coupled corrosive-mechanical load. Electrochemical and spectroscopic methods were used for the characterisation of the film properties and in situ corrosion experiments were performed by means of AFM. The deformation properties of the aluminium alloy and the model coatings were investigated by means of scanning Kelvin probe force microscopy (SKPFM) utilizing the integrated tensile stage.
The presentation will give a brief overview of the capabilities of the new AFM setup to foster future collaborations and summarize our work on the interface stability of model coatings.
In service, most materials are operated under simultaneous corrosive and mechanical load and there are very few methods capable for testing material degradation under these conditions, especially when it comes to high resolution analysis. For this purpose, in this work, a tensile module capable of uniaxial stretching and compression with up to 5 kN force was integrated into an AFM stage. The elimination of the need for sample unmounting and remounting and the resulting possibility of keeping the sample under constant mechanical load during AFM measurements not only enables a precise positioning of the area of interest but also allows for the analysis of processes in the elastic deformation regime.
This methodology was demonstrated for two case studies. Scanning Kelvin Probe Force Microscopy (SKPFM) was used as the main tool to characterize the deformation behavior. Moreover, a flexible electrochemical measurement cell was used to enable electrochemical analysis by means of electrochemical impedance spectroscopy (EIS) and Linear Sweep Voltammetry (LSV) during AFM measurements at different levels of strain. The in situ AFM results are complemented by microstructure analysis by means of electron backscatter diffraction (EBSD).
In the first case study, the deformation induced delamination of a thin organic coating on AA2024 T3 aluminium alloy was investigated as a function of alloy surface treatment. The formation of cracks in the insulating passive film enabled an early detection of deformation processes by means of SKPFM. The second case study focused on the comparison of corrosion and deformation behavior of conventional and additively manufactured 316 stainless steels. In comparison to the conventional 316 stainless steel, the effect of processing was clearly detectable on the additively manufactured material as zones of inhomogeneous potential, which also affected the initiation of local corrosion processes. The contribution will provide detailed information on the new AFM setup and summarize our results from both case studies.
The performance of functional coatings relies strongly on the stability of the polymer-metal interface. The increasing utilization of multi-material structures in the automotive and aerospace industry necessitates a fundamental understanding of the processes leading to interface degradation for the development of novel strategies to increase corrosion and delamination resistance.
The aim of this project is to investigate the corrosion processes at the buried interface of thin film coated aluminium alloy AA2024-T3 under corrosive and coupled corrosive-mechanical load. A spin coating procedure was developed to synthesize epoxy-like coatings and their nanofiller loaded composites with controlled thickness by layer-by-layer deposition of poly[(o-cresyl glycidyl ether)-co-formaldehyde] and poly-(ethylenimine) bi-layers. Our results indicate that the incorporation of graphene into the epoxy-based coatings leads to the improvement of mechanical and barrier properties. Furthermore, the functional groups play important roles in the interfacial bonding between polymer matrix and the nanofillers. Atomic force microscopy (AFM) results indicate very homogeneous and dense films with a thickness of ~25 nm per bi-layer and the successful integration of the nanofillers into the composite coatings. Ellipsometry measurements of film thickness verified a proportional film growth with the number of deposited layers.
The degradation and delamination behavior of the coating systems was characterized by means of in situ AFM corrosion experiments. Complementary energy dispersive X-ray spectroscopy (EDX) analysis was used to correlate the corrosion and delamination behavior with the different intermetallic particle chemistries and distributions. The presentation will summarize our results on the effect of coating composition and build-up on the local corrosion processes on thin film covered AA2024-T3 aluminium alloys.
The presentation summarizes our recent results on the coupled electrochemical methods for high resolution corrosion studies. The combination of Scanning Electrochemical Microscopy (SECM) and multielectrode (MMA) based real-time corrosion monitoring was presented as a new method for achieving high time resolution in local electrochemical analysis. Correlative imaging by means of Atomic Force Microscopy (AFM) and Scanning Electron Microscopy (SEM) was demonstrated as a tool for the investigation of local corrosion processes initiated by the intermetallic particles (IMPs) on AA2024-T3 aluminium alloy.