6 Materialchemie
Filtern
Erscheinungsjahr
- 2018 (36) (entfernen)
Dokumenttyp
- Vortrag (22)
- Posterpräsentation (6)
- Zeitschriftenartikel (5)
- Beitrag zu einem Tagungsband (2)
- Forschungsbericht (1)
Schlagworte
Organisationseinheit der BAM
- 6.7 Materialsynthese und Design (36) (entfernen)
Eingeladener Vortrag
- nein (22)
Der Vortrag widmet sich der „ELLIPSOMETRISCHE KLASSIFIZIERUNG VON KOHLENSTOFFSCHICHTEN“ und beschreibt die Punkte: 1. Anwendungen Kohlenstoffschichten–Carbon–based films (DLC) aus dem Vortrag N. Ohtakeet. al. (ISO TC 107, Tokyo 2017),2. Präparation der Kohlenstoffschichten für ISO TC 107 Ringversuch aus Vortrag M. Hiratsuka et. al. (ISO TC 107, Tokyo 2017), 3. Ellipsometrische Charakterisierung von Kohlenstoffschichten, Ergebnisse des Ringversuchs (ISO TC 107, Tokyo 2017) Vortrag Beck et. al. und 4.Deutsche Normungsaktivitäten national/international zur Ellipsometrie DIN NA 062-01-061 (DIN 50989-1)/TC 107 (PWI DE)“ im Einzelnen.
The paper addresses “WHITE LIGHT INTERFERENCE MICROSCOPY, ELLIPSOMETRY, AND INSTRUMENTED INDENTATION TESTING AS REFERENCE PROCEDURES“ and is subdivided in the following sections: 1. Measurement vs. testing vs. reference procedures, 2. White light interference microscopy (WLIM) for determination of step height h, 3. Spectroscopic ellipsometry (SE) for determination of layer thickness d and 4. Instrumented indentation testing (IIT) for determination of indentation hardness HIT. The following points are discussed in more detail: methodology of measurement and testing, uncertainty budgets for direct (WLIM), model-based (SE) and formula-based (IIT) reference procedures by means of specific examples. It is shown that standardization efforts are connected to reference procedures.
In Glasfasern eingeschriebene Bragg-Gitter (FBG: fibre-based Bragg gratings) sind über die Verschiebung der Bragg-Wellenlänge in der Lage, Stauchungen und Dehnungen von Glasfasern hochgenau zu erfassen. In Kompositwerkstoffe eingebettete faseroptische Sensoren können Bauteile bezüglich ihrer mechanischen Integrität überwachen und früh-zeitig Informationen über Materialveränderungen gewinnen.
Um die Zuverlässigkeit eines solchen Sensors zu gewährleisten, ist es wichtig, die korrekte Funktion des Sensors im Verbund mit der Werkstoff-Matrix on-line und in-situ sicherzu-stellen. Im Rahmen des DFG-Projekts FAMOS² (FAser-basierter Magneto-Optischer SchichtSensor) wurde ein selbstdiagnosefähiger Schichtsensor entwickelt, der mit Hilfe von magnetostriktiven Aktorschichten aus Nickel bzw. Eisen-Nickel validiert werden kann.
Der FAMOS²-Schichtsensor wird durch ein PVD (physical vapour deposition)/ECD (electro-chemical deposition) Hybridschichtsystem realisiert, das auf dem Fasermantel im Bereich des FBG haftfest, homogen und langzeitfunktional abzuscheiden ist. Dabei wird in einem ersten Schritt ein etwa 100 Nanometer dünnes PVD-Schichtsystem aus Chrom und Kupfer als Haftvermittler auf der Glasfaser bzw. als leitfähige Startschicht für den nachfolgenden ECD-Prozess abgeschieden. Um eine rotationssymmetrische Schich-tabscheidung zu gewährleisten, erfolgt während der PVD-Beschichtung eine Rotation der Glasfasern. In einem zweiten Schritt wird dann unter Verwendung eines klassischen Watts-Elektrolyten in einer speziell entwickelten ebenfalls rotationssymmetrisch aufgebau-ten ECD-Durchströmungszelle dann die etwa 30 Mikrometer dicke, magnetostriktive Ak-torschicht auf dem PVD-Schichtsystem abgeschieden, im Vergleich sowohl reine Nickel-Schichten als auch Nickel-Eisen-Schichten.
Ein äußeres Magnetfeld dehnt die magnetostriktive Aktorschicht und damit auch die Faser reversibel. Diese Dehnung führt zu einer Verschiebung der Bragg-Wellenlänge, welche direkt mit der Stärke eines zu messenden oder zu Validierungszwecken vorgegebenen Magnetfeldes korreliert. Die Anpassung der Beschichtungsverfahren an die Fasergeome-trie und die mechanischen Eigenschaften der Hybridschichten werden hinsichtlich der me-chanischen Integrität des faseroptischen Sensors diskutiert und der Nachweis der Selbst-diagnosefähigkeit erbracht.
In Glasfasern eingeschriebene Bragg-Gitter (FBG: fibre-based Bragg gratings) sind über die Verschiebung der Bragg-Wellenlänge in der Lage, Stauchungen und Dehnungen von Glasfasern hochgenau zu erfassen. In Kompositwerkstoffe eingebettete faseroptische Sensoren können Bauteile bezüglich ihrer mechanischen Integrität überwachen und früh-zeitig Informationen über Materialveränderungen gewinnen.
Um die Zuverlässigkeit eines solchen Sensors zu gewährleisten, ist es wichtig, die korrekte Funktion des Sensors im Verbund mit der Werkstoff-Matrix on-line und in-situ sicherzu-stellen. Im Rahmen des DFG-Projekts FAMOS² (FAser-basierter Magneto-Optischer SchichtSensor) wurde ein selbstdiagnosefähiger Schichtsensor entwickelt, der mit Hilfe von magnetostriktiven Aktorschichten aus Nickel bzw. Eisen-Nickel validiert werden kann.
Der FAMOS²-Schichtsensor wird durch ein PVD (physical vapour deposition)/ECD (electro-chemical deposition) Hybridschichtsystem realisiert, das auf dem Fasermantel im Bereich des FBG haftfest, homogen und langzeitfunktional abzuscheiden ist. Dabei wird in einem ersten Schritt ein etwa 100 Nanometer dünnes PVD-Schichtsystem aus Chrom und Kupfer als Haftvermittler auf der Glasfaser bzw. als leitfähige Startschicht für den nachfolgenden ECD-Prozess abgeschieden. Um eine rotationssymmetrische Schich-tabscheidung zu gewährleisten, erfolgt während der PVD-Beschichtung eine Rotation der Glasfasern. In einem zweiten Schritt wird dann unter Verwendung eines klassischen Watts-Elektrolyten in einer speziell entwickelten ebenfalls rotationssymmetrisch aufgebau-ten ECD-Durchströmungszelle dann die etwa 30 Mikrometer dicke, magnetostriktive Ak-torschicht auf dem PVD-Schichtsystem abgeschieden, im Vergleich sowohl reine Nickel-Schichten als auch Nickel-Eisen-Schichten.
Ein äußeres Magnetfeld dehnt die magnetostriktive Aktorschicht und damit auch die Faser reversibel. Diese Dehnung führt zu einer Verschiebung der Bragg-Wellenlänge, welche direkt mit der Stärke eines zu messenden oder zu Validierungszwecken vorgegebenen Magnetfeldes korreliert. Die Anpassung der Beschichtungsverfahren an die Fasergeome-trie und die mechanischen Eigenschaften der Hybridschichten werden hinsichtlich der me-chanischen Integrität des faseroptischen Sensors diskutiert und der Nachweis der Selbst-diagnosefähigkeit erbracht.
Mit der Zentrifugentechnologie ist seit einigen Jahren ein neuartiges Mehr-Proben-Prüf-verfahren auf dem Markt etabliert, welches die klassische Zugprüfung in den Trommelrotor einer Tischzentrifuge überträgt. In der Beanspruchung auf Zug ist die Prüfung der Verbundfestigkeit mittels CAT-Technologie (centrifugal adhesion testing) an der BAM seit 2017 nach DIN EN ISO/IEC 17025 akkreditiert, wobei die Verbundfestigkeit von Klebungen direkt bestimmt wird und in Abhängigkeit von den Versagensformen Rückschlüsse auf die Klebfestigkeit von Klebstoffen/Klebebändern oder die Haftfestigkeit von Beschichtungen gezogen werden können.
Mit der Zentrifugentechnologie ist seit einigen Jahren ein neuartiges Mehr-Proben-Prüf-verfahren auf dem Markt etabliert, welches die klassische Zugprüfung in den Trommelrotor einer Tischzentrifuge überträgt. In der Beanspruchung auf Zug ist die Prüfung der Verbundfestigkeit seit 2017 nach DIN EN ISO/IEC 17025 akkreditiert, wobei die Verbundfestigkeit von Klebungen direkt bestimmt wird und in Abhängigkeit von den Versagensformen Rückschlüsse auf die Klebfestigkeit von Klebstoffen/Klebebändern oder die Haftfestigkeit von Beschichtungen gezogen werden können.
Bei der zerstörenden Beanspruchung auf Zug ist zu beachten, dass es sich bei der Verbundfestigkeit um eine Systemeigenschaft handelt, d.h. nicht nur die chemischen und topografischen Oberflächeneigenschaften, sondern auch die plasto-elastischen Volumeneigenschaften des Klebstoffes und der Fügeteile haben Einfluss auf die ermittelten Kennwerte. Dabei ist eine qualitative Bestimmung der Versagensformen und Bruchbilder nach DIN EN ISO 10365 zwingend erforderlich, um eine Aussage über die Art des Versagens treffen zu können.
Mit der Erweiterung der Zentrifugentechnologie um Beanspruchungen auf Druck wurde dann der Nachweis erbracht, dass auch die klassische Härteprüfung in einer Zentrifuge als Mehr-Proben-Prüfung durchgeführt werden kann. Im Verbundvorhaben QUO VADIS PLUS werden derzeit invasive Beanspruchungen auf Druck zur Bestimmung der Härte von Materialien, der Kompressibilität von Metallschäumen sowie der Kompaktierbarkeit von Pulvern untersucht, was das Anwendungspotential der Zentrifugentechnologie nochmals erweitert. Dazu gehören auch kombinierte Beanspruchungen wie Zug-Scher- und Druck-Scher-Prüfungen.
Die Verbundfestigkeit von CFK-Platten in Abhängigkeit der Beanspruchungsart (Zug vs. Zug-Scher) bzw. der Faserorientierung (0°, 45°, 90°), die Klebfestigkeit von Klebstoffen bzw. Klebebändern auf unterschiedlichen Fügeteilwerkstoffen in Abhängigkeit von der Vorbehandlung, die Haftfestigkeit optischer Schichten auf Kunststoffen, die Bestimmung der Vickers-, Brinell- bzw. Kugeldruck-Härte sowie die Kompressibilität von metallischen Schäumen und Federn werden als ausgewählte Beispiele diskutiert.
Imaging of surfaces regarding topographical, morphological, micro-structural, and chemical features is a key requirement for quality control for the identification of contaminated, degraded, damaged or deliberately modified surface areas vs. clean, virgin, undamaged or unmodified regions. As optical functions may represent any of these changes on the micro- and nano-scale, imaging ellipsometry (IE) is the technique of choice using either intensity, phase, or/and amplitude contrast for visualization of low-contrast surface modifications [1, 2]. Defects or surface and film features whether native or artificial, intended or unintended, avoidable or unavoidable as well as surface pattern are of interest for quality control. In contrast to microscopic techniques operated at normal incidence, ellipsometry as oblique-incidence technique provides improved contrast for vertically nano-scaled add-on or sub-off features such as ultra-thin transparent films, metallic island films, carbon-based thin films, laser modification or laser induced damage, dried stain, cleaning agent or polymeric residue. Two-sample reference techniques, i.e. referenced spectroscopic ellipsometry (RSE) may further increase sensitivity and decrease measurement time. In case of particulate accumulations depolarization contrast imaging (DCI) may improve the lateral resolution beyond the Abbe limit. This has been proven for silica spheres as reference in terms of single particles, particulate accumulations or particulate monolayers and layer stacks. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) were used for reference measurements of particle diameter, particle height, or particulate layer/accumulation thickness. It has been shown that single silica particles of 250 nm in diameter, i.e. at least a factor of 4 better than the lateral resolution limit as of now, can be visualized on even substrates. However, the ellipsometric measurement of particle diameters of this size needs further efforts interpretation.
The application of PVD-coatings ranges from mechanical engineering, i.e. thicker tribological coatings, to precision optics, i.e. thinner optical coatings. For physical vapor deposition (PVD) technologies such as evaporation, sputtering, ion beam assisted/driven deposition, vacuum is a prerequisite for two reasons: at first process-related ones (evaporation source, plasma discharge, and mean free path) and at second coating-related ones (pure, perfect, and dense films). Usually, the goal is a homogenous coating of defined stoichiometry and micro-structure without any imperfection.
However, the implementation of micro- or nano-particles may occur accidentally or delibe-rately. Independent of the particle origin, there are two fundamental rules regarding coating functionality: at first, the larger the particle diameter to coating thickness ratio the more affected the functionality of the coating, and at second, the larger the material contrast in terms of the functional feature of interest the more affected the coating performance. Hence, embedded particles have to be avoided for the majority of thin films by all means. The unintended implementation of particles usually results in a malfunction of the coating from the beginning or is at least considered as a weak point of the coating creating a time-dependent defect under service conditions. The intended implementation of particles on surfaces and in coatings may create add-on features, topographic ones and functional ones, however, the facts mentioned hold true.
Examples of particle-initiated coating defects are demonstrated in dependence on the origin and the field of application. Strategies for deliberate attachment/embedding of particles on surfaces/in coatings are discussed regarding process compatibility and coating integrity. For industrial applications, both the validation of process compatibility of particle injection and the plasma resistance of particles under vacuum and plasma conditions have to be confirmed. Further points of interest are the homogeneity of particle distribution and the avoidance of particle agglomeration which is still a crucial point for dry dispersed particles. So far, technical applications are limited to PVD hybrid coatings, plasma dispersion coatings are still a challenge except for applications where homogeneity is not required as in case of product authentication.
Multi-functional coatings are a key requirement for surface engineering. General demands are adhesion and long-term stability under service conditions. The modification of surfaces by means of PVD-, ECD- or hybrid processes allows an add-on functionalization of surfaces by a huge diversity of materials with both lateral and vertical micro-/nano-designs. This fact is a prerequisite for micro- and sensor-systems in lab-on-chip and sensor-on-chip technology. Two layer-based sensor principles are presented, i.e. surface plasmon resonance enhanced spectroscopic ellipsometry (SPREE) for detection of hazardous gases and magneto-optical sensors on smart-coated fiber Bragg gratings (FBG) for structural health monitoring (SHM).
The interdependence of substrate features, coating properties, and layer design is discussed firstly for gas sensitivity and selectivity of SPREE-sensors and secondly for sensitivity and selectivity of magneto-strictive coatings to mechanical strain or external magnetic fields resulting in an optical displacement of the Bragg wavelength of FBG-sensors. Moreover, generic features such long-term stability, crucial process-related fabrication conditions, and effects of operational and environmental parameters are discussed with respect to the sensor performance. It has been shown that appropriate layer design and adapted selection of layer materials (SnOx/Au, Fe/Ni:SnOx/Au; Ni/NiFe-Cu-Cr) result in improved sensor parameters and may enable new sensor applications.
In well-annealed thin polymer films, with non-repulsive polymer/substrate interactions, an irreversibly adsorbed layer is expected to form. These adsorbed layers have shown great potential for technological applications. However, their growth kinetics and molecular dynamics are still not fully understood. This is partially due to the hard accessibility of these layers in thin films. Here, the irreversibly adsorbed layers of homopolymer thin films are revealed by solvent-leaching experiments. First, the growth kinetics of these layers is investigated as a function of annealing times and original film thickness. The thickness, topography and quality of the adsorbed layer is controlled with Atomic Force Microscopy (AFM). Secondly, the molecular mobility of the adsorbed layer is investigated with Broadband Dielectric Spectroscopy (BDS). A recently developed nanostructured capacitor is employed to measure the adsorbed layers with a free surface layer. The results are quantitatively compared and discussed with respect to recently published work.
In well-annealed thin polymer films, with non-repulsive polymer/substrate interactions, an irreversibly adsorbed layer is expected to form. These adsorbed layers have shown great potential for technological applications. However, their growth kinetics and molecular dynamics are still not fully understood. This is partially due to the hard accessibility of these layers in thin films. Here, the irreversibly adsorbed layers of homopolymer thin films are revealed by solvent-leaching experiments. First, the growth kinetics of these layers is investigated as a function of annealing times and original film thickness. The thickness, topography and quality of the adsorbed layer is controlled with Atomic Force Microscopy (AFM). Secondly, the molecular mobility of the adsorbed layer is investigated with Broadband Dielectric Spectroscopy (BDS). A recently developed nanostructured capacitor is employed to measure the adsorbed layers with a free surface layer. The results are quantitatively compared and discussed with respect to recently published work.
In this presentation, we report on the Determination of the glass transition temperature of thin layers of Polyvinylmethylether (PVME) depending on the thickness of the polymer layer. The glass Transition of thin polymer layers is currently under much investigation due to the nano-confinement effects proposed to appear in dependence on the layer thicknesses in the nm range. The properties of the polymer, the temperature range, as well as the thicknesses range of the polymer layers pose a serious challenge to the investigation by means of
spectroscopic ellipsometry. By careful choice of experimental parameters, we were able to investigate the thickness change by temperature of PVME layers in the range between 2 and 300 nm and in the temperature range between 200 K and 340 K. By optimizing the analysis process, we were able to determine Tg values within this parameter range with sufficient accuracy to investigate the Tg change due to confinement effects.
Alongside the change of position of the glass transition with thickness, we discuss the details of the ellipsometric analysis and its implications for the resulting thermal properties of the thin polymer layers as well as the accuracy of the Tg value with respect to the method used in the analysis process.
Ellipsometry is well known as a highly sensitive and reproducible surface analysis technique. However, in a context of metrological applications, the most important property of a measurement process is accuracy, relying on statistical precision, (reproducibility) and trueness (in an absolute sense versus a given standard). The latter is much more difficult to achieve. In this presentation, we discuss the possibility of establishing ellipsometry in a diverse metrological landscape by means of defining standard procedures and best practice methodologies for the measurement and for calibration purposes. The most important task of this approach is to determine the model-inherent uncertainty, originating from parameter coupling. We achieve this by means of sensitivity analysis of the parameters resulting from the fit process. We discuss the definition of reference materials by which accuracy can be made available for ellipsometry, passed along between ellipsometry laboratories and for other measurement techniques. The determination of uncertainty is presented in this work for a number of examples involving difficult analysis models employed for samples from different production environments. We present a standardization initiative with the goal to disseminate this work into an international standard alongside an inter-laboratory study comparing the results for complex samples gained by laboratories with different instrumentation. We also present the results gained within EURAMET projects focused on the metrology of materials with strong non-idealities used in photovoltaics and other energy technology.
Laser texturing is an emerging technology for generating surface functionalities on basis of optical, mechanical, or chemical properties. Taking benefit of laser sources with ultrashort (fs) pulse durations features outstanding precision of machining and negligible rims or burrs surrounding the laser-irradiation zone. Consequently, additional mechanical or chemical post-processing steps are usually not required for fs-laser surface texturing (fs-LST). This work aimed to provide a bridge between research in the field of tribology and laser materials processing. The paper reviews the current state-of-the-art in fs-LST, with a focus on the tribological performance (friction and wear) of specific self-organized surface structures (so-called ripples, grooves, and spikes) on steel and titanium alloys. On the titanium alloy, specific sickle-shaped hybrid micro-nanostructures were also observed and tribologically tested. Care is taken to identify accompanying effects affecting the materials hardness, superficial oxidation, nano- and microscale topographies, and the role of additives contained in lubricants, such as commercial engine oil.
The talk addresses the STANDARDIZATION OF ELLIPSOMETRY and the following points are discussed in more detail: historical background of ellipsometry, history of International Conferences on Ellipsometry, Workshops Ellipsometry in Germany and Europe, information on German/European Working Group Ellipsometry, technical/industrial importance of ellipsometry, applications on non-ideal material systems and standardization activities on ellipsometry.
Thin mesoporous metal oxide films are versatile and attractive candidates for several energy applications like photovoltaics, electrolysis or batteries. Due to their high surface area and ordered pore structure, mesoporous metal oxides demonstrate higher activities. The performance of the porous films is affected by properties like size and shape of the mesopores as well as the crystallinity of the framework. The exact determination and metrological evaluation of the complex morphology of thin mesoporous films requires a new analytical approach employing to combined data of different analytical methods. In this contribution we present a novel evaluation procedure for spectroscopic ellipsometry (SE) to analyse thin mesoporous iridium oxide films.
Mesoporous iridium oxide films were prepared via dip-coating of a solution containing a triblock-copolymer as structure directing agent and an iridium precursor in ethanol. Deposited films were calcined in air at temperatures between 300 and 600 °C. Their morphology was studied with SEM and an electron probe microanalysis (EPMA) and correlated via SE with a Bruggeman effective medium approximation (BEMA). The developed SE model described the film thickness as well as the porosity.
...
The contribution will assess in detail the novel approach to analyse the morphology and porosity of thin metal oxide films with spectroscopic ellipsometry. Moreover, the advantages of the new developed approach will be discussed as well as combination of datasets from multiple measurements to development new methods for innovative energy technologies.
Thin mesoporous metal oxide films are versatile and attractive candidates for several energy applications like photovoltaics, electrolysis or batteries. Due to their high surface area and ordered pore structure, mesoporous metal oxides demonstrate higher activities. The performance of the porous films is affected by properties like size and shape of the mesopores as well as the crystallinity of the framework. The exact determination and metrological evaluation of the complex morphology of thin mesoporous films requires a new analytical approach employing to combined data of different analytical methods. In this contribution we present a novel evaluation procedure for spectroscopic ellipsometry (SE) to analyse thin mesoporous iridium oxide films. Mesoporous iridium oxide films were prepared via dip-coating of a solution containing a triblock-copolymer as structure directing agent and an Iridium precursor in ethanol. Deposited films were calcined in air at temperatures between 300 and 600 °C. Their morphology was studied with SEM and an electron probe microanalysis (EPMA) and correlated via SE with a Bruggeman effective medium approximation (BEMA). The developed SE model described the film thickness as well as the porosity.
... The contribution will assess in detail the novel approach to analyse the morphology and porosity of thin metal oxide films with spectroscopic ellipsometry. Moreover, the advantages of the new developed approach will be discussed as well as combination of datasets from multiple measurements to development new methods for innovative energy technologies.
Thin mesoporous metal oxide films are versatile and attractive candidates for several energy applications like photovoltaics, electrolysis or batteries. Due to their high surface area and ordered pore structure, mesoporous metal oxides demonstrate higher activities. The performance of the porous films is affected by properties like size and shape of the mesopores as well as the crystallinity of the framework. The exact determination and metrological evaluation of the complex morphology of thin mesoporous films requires a new analytical approach employing to combined data of different analytical methods. In this contribution we present a novel evaluation procedure for spectroscopic ellipsometry (SE) to analyse thin mesoporous iridium oxide films.
Mesoporous iridium oxide films were prepared via dip-coating of a solution containing a triblock-copolymer as structure directing agent and an iridium precursor in ethanol. Deposited films were calcined in air at temperatures between 300 and 600 °C. Their morphology was studied with SEM and an electron probe microanalysis (EPMA)and correlated via SE with a Bruggeman effective medium approximation (BEMA). The developed SE model described the film thickness as well as the porosity.
Figure 1a shows a top-view SEM image of mesoporous IrO2 film calcined at 375 °C. The image reveals that the films exhibit a well-ordered mesopore structure with an average pore diameter of 16 nm and a periodic distance between pore centres of 24 nm (FFT inset). Figure 1b is a parity plot of film thicknesses determined by cross-section SEM versus SE of IrO2 film samples prepared at different calcination temperatures. The porosity from the SE model is in good agreement to the porosity values obtained by EPMA.
The contribution will assess in detail the novel approach to analyse the morphology and porosity of thin metal oxide films with spectroscopic ellipsometry. Moreover, the advantages of the new developed approach will be discussed as well as combination of datasets from multiple measurements to development new methods for innovative energy technologies.
Der Mangel an Anwendungsrichtlinien und Validierungsverfahren für struktur-eingebettete faseroptische Dehnungssensoren, insbesondere auf Faser-Bragg-Gitter (FBG)-Basis, führte bislang dazu, dass diese Sensoren trotz ihrer hervorragenden Eigenschaften im Bereich der kommerziellen Material- und Strukturüberwachung nur in geringem Umfange eingesetzt wurden. Fragen zur Degradation der Sensoren unter Beanspruchung, Alterung durch klimatische Einflüsse und Enthaftung infolge Belastung der Struktur konnten bisher nur theoretisch simuliert oder anhand exemplarischer Proben für einzelne einflussnehmende Parameter im Labor untersucht werden. Die Erfassung des Sensorverhaltens im Bauteil unter komplexen Umwelteinflüssen während des Bauteilbetriebes, um damit eine Aussage zur Zuverlässigkeit der Sensormessdaten zu gewinnen, war bisher nicht möglich.
Im Forschungsprojekt FAMOS² wurde deshalb von 2014 bis 2018 die Realisierung eines Autodiagnoseverfahrens für faseroptische Dehnungssensoren erarbeitet, um die Funktionszuverlässigkeit und Langzeitstabilität der Sensoren während des Bauteilbetriebes innerhalb einer Bauteilstruktur bewerten zu können. Im Rahmen des Forschungsprojektes wurde gezeigt, dass ein FBG-Sensor mit einer speziell angepassten magnetostriktiven Schicht magnetisch so angeregt werden kann, dass mit einer zugeschnittenen Messmethodik zu jedem Zeitpunkt eine Bewertung der Sensorzuverlässigkeit unter Betriebsbedingungen möglich ist. Die auf den Sensor aufgebrachte magnetostriktive Schicht erzeugt bei Anregung mit einem passenden Magnetfeld eine gepulste, synthetische Dehnung. Diese Dehnung steht in einem definierten Verhältnis zum anregenden Magnetfeld und wird optisch über die Verschiebung der Bragg-Wellenlänge ausgelesen. Die Konstanz dieses Verhältnisses stellt dann ein Maß für die korrekte Funktionsfähigkeit des Sensors dar. Das Beschichtungs-verfahren, das magnetische Anregungs- und optische Ausleseverfahren, wie auch die Validierung des Sensors unter Berücksichtigung faseroptischer Effekte wurden während des Projekts konzeptionell entwickelt, aufgebaut und charakterisiert. Qualitativ kann mit diesem Verfahren zunächst eine Gut-/Schlecht-Beurteilung des Sensors vorgenommen werden. Perspektivisch bietet das Verfahren jedoch auch die Möglichkeit, verschiedene Versagensmechanismen bestimmen und klassifizieren zu können. Es zeichnete sich schon während des Projektverlaufs ab, dass sich aus den erzielten Ergebnissen über das Autodiagnoseverfahren hinaus weitere Anwendungsmöglichkeiten für den Einsatz des kombinierten magnetostriktiv-faseroptischen Sensorprinzips, beispielsweise als reiner Magnetfeldsensor, ergeben.
Nach Abschluss dieses Forschungsprojekts besteht nun die Möglichkeit, den Funktionszustand faseroptischer Dehnungssensoren jederzeit unabhängig von Alter, Belastung oder Kenntnis eines Referenzzustands zu einem bestimmten Zeitpunkt bestimmen zu können. Aufbauend auf diesen Ergebnissen können weiterführende Forschungen die Messmethodik vertiefend charakterisieren und weitere Anwendungsfälle erschließen.
Der Vortrag gibt den aktuellen Stand der Normung im Bereich der Oberflächen-technik insbesondere der Oberflächenanalytik und der Oberflächenmess- und -prüftechnik wider. Vorgestellt wird der Status technischer Berichte, Normenentwürfe und Normen u.a. zur Charakterisierung von funktionellen Glasoberflächen für bioanalytische Anwendungen, zur Messung der Schichtdicke von Nanomaterialien mittels Ellipsometrie, zur Kalibrierung von Interferometern und Interferenzmikroskopen für die Formmessung, zur Rockwelleindringprüfung zur Bewertung der Schicht-haftung, zu den Grundlagen der Ellipsometrie, zur Messung der Schichtdicke mittels Wirbelstromverfahren, zur Schichtpotentialmessung von Mehrfach-Nickelschichten, zu Filtern und Augenschutzgeräten gegen Laserstrahlung sowie zur Bestimmung der Schichthaftung mittels Zugversuch.
Nowadays the Instrumented Indentation Testing (IIT) is one of the most commonly used methods to determine the mechanical properties of materials in the nano range. This method is already extensive standardized in EN ISO 14577 part 1-4. Because of the great interest of researchers and industries in investigations of time depending material behavior mostly all suppliers of IIT equipment are offering the possibility of dynamic testing. Realizing this development ISO/TC 164/SC3 Hardness Testing has proposed to start the new standardization project “Linear elastic dynamic instrumented indentation testing DIIT”. The development of this standard is accompanied by the first international intercomparing exercise comparing results of dynamic instrumented indentation testing from testing machines using different hardware solutions and different models for data evaluation.
The draft of part 5 of ISO 14577 “Linear elastic dynamic instrumented indentation testing DIIT” specifies verification and calibration of testing machines for carrying out the measurement of the dynamic material response when an oscillatory force or displacement, with amplitudes small in comparison to the prescribed target values, is imparted to the indenter while the indenter is continuously loaded to a prescribed target load or target depth or while the load or displacement is held constant at a prescribed target value. In case of a material showing plastic-elastic behavior, the measured dynamic response is used for continuous evaluation of the dynamic stiffness of the contact as a function of depth and frequency. Using the dynamic stiffness of the contact a reduced dynamic modulus will be calculated. In case of a material showing visco-elastic behavior from the measured dynamic response also the dynamic contact damping coefficient as function of depth and frequency is evaluated continuously. Using dynamic contact stiffness and dynamic contact damping coefficient reduced lost and storage modulus for visco-elastic materials will be calculated.
The main normative requirements of the draft will be presented and discussed in the light of the first results of the intercomparing excise.
For the determination of porosity of Ir oxide thin films, electron probe microanalysis (EPMA) can be used as part of a combined SEM/EDS/STRATAGem analysis. The mass deposition (in μg cm-2) of films was calculated with the analysis software STRATAGem via k-values measured with EDS. The average density of coated films was obtained from the mass deposition and the film thickness as measured by the cross-section SEM. The porosity was calculated by dividing the average film density by the bulk (theoretical) density of the film material.
Film porosities were counterchecked by spectroscopic ellipsometry (SE) using the Bruggeman effective medium approximation (BEMA).
The results obtained by both analytical approaches/methods used, SEM/EDS/STRATAGem and SE were in good agreement.
For the determination of porosity of Ir oxide thin films, electron probe microanalysis (EPMA) can be used as part of a combined SEM/EDS/STRATAGem analysis. The mass deposition (in μg cm-2) of films was calculated with the analysis software STRATAGem via k-values measured with EDS. The average density of coated films was obtained from the mass deposition and the film thickness as measured by the cross-section SEM. The porosity was calculated by dividing the average film density by the bulk (theoretical) density of the film material.
Film porosities were counterchecked by spectroscopic ellipsometry (SE) using the Bruggeman effective medium approximation (BEMA).
The results obtained by both analytical approaches/methods used, SEM/EDS/STRATAGem and SE were in good agreement.
In well-annealed thin polymer films, with non-repulsive polymer/substrate interactions, an irreversibly adsorbed layer is expected to from. These adsorbed layers have shown greate potential for technological applications. However, their growth kinetics and molecular dynamics are still not fully understood. This is partly due to the hard accessibility of these layers in thin films. Here, the irreversibly adsorbed layers of homopolymer thin films are revealed by solvent-leaching experiments. First, the growth kinetics of these layers is investigated as a function of annealing time, annealing temperature, leaching time and the original filme thickness. The film thickness, topography and the quality of the adsorbed layer is controlled by Atomic Force Microscopy (AFM). Secondly, the molecular mobility of the adsorbed layer is investigated by Broadband Dielectric Spectroscopy (BDS). A recently developed nanostructured capacitor arrangement is employed to measure the layer with a free surface. The results are quantitatively compared and discussed with respect to recently published work.
The majority of all products have coated surfaces designed to fulfil different requirements. Building constructions are exposed to external influences like a wide temperature and humidity range, rain and UV radiation to name a few. The extension of machine life for metal cutting tools, like drills or milling cutters is another field of application for coated surfaces. The surfaces have to be modified in a way to maintain their specific functionality. Although adhesion testing of coatings is of great interest, it is still a challenge to obtain reliable quantitative results and to meet economic requirements.
In this talk we deal with the curing behaviour of different 2-component epoxy paint systems for corrosion protection of metal constructions. After preparation of specimens the strength was determined in specified time intervals during curing. It could be shown that epoxy paints differ significantly on curing time as well as final strength. The second experimental study deals with coating systems on glass fibre reinforced plastics which are used for wind power turbines to reduce abrasive wear and ice adhesion for aerodynamic and safety reasons.
All measurements have been carried out by CAT-TechnologyTM (Centrifugal Adhesion Testing), which uses the radially directed centrifugal force as test-load. The multi-sample test instrument analyses up to eight test specimen under identical testing conditions. By varying the rotational speed (100 rpm up to 13,000 rpm), forces from 0.1 N to 6.5 kN are applied. Upon reaching the critical rupture force, the stamp separates from the substrate and a sample related IR-signal is sent from the spinning rotor. For each test specimen breaking force is calculated and displayed in real-time. The innovative measurement principle meets the requirements of DIN EN 15870 and ISO 4624.
Bonding strength is crucial on polymers of low surface energy, for clean surfaces limited to 0.5, 1, and 2 MPa for PTFE, PP, and PE. Plasma treatment may improve bonding strength by a factor of 2 (PTFE) or 5 (PP and PE). The efficiency of treatment is usually 10% as both low pressure and atmospheric pressure processes show low topographic conformity.
Besides, lifetime of activation/modification is rather short. Hence, bonding has to be carried out immediately after plasma treatment.
The concept of plasma-assisted ALD (atomic layer deposition) interlayers was introduced in the project HARFE of SENTECH (modification/deposition/in-situ monitoring) and BAM (bonding, characterization, testing). ALD deposition has a high surface conformity and for dielectric films of Al2O3 also a good long-term stability given that the films are dense enough.
Based on TMA and O2/O3 precursors, ALD layer stacks from 60 to 375 monolayers were prepared under different conditions. For a transfer time of 24 hours from deposition to measurement, bonding strength could be increased up to 5 MPa (PTFE) respectively 10 MPa (PP, PE). The huge potential of ALD layers as adhesive interlayers was demonstrated for Al2O3 on stainless steel with bonding strength beyond 15 MPa, i.e. interface
strength within the ALD stack is also in this range.
This is a prerequisite for subsequent PVD/CVD-deposition in hybrid systems. By means of the SI ALD LL system of SENTECH thermal and plasma-supported ALD processes can be alternatively realized.
Ellipsometric in-situ monitoring provides monolayer sensitivity and reveals that the efficient bonding of the lower ALD layers on the polymer has to be further improved. Testing of bonding strength was realized by CAT (centrifugal adhesion testing) technology. It was shown that ALD modification correlates with the increase of surface energy and bonding strength.
Transparent conductive oxide (TCO) films are a vital part of a large part of modern technology. The production of TCO materials has sparked much development in plasma coating technology. Quality control measurements of these layers are therefore important in many fields of optics and electronics such as high efficiency thin film photovoltaics. In this presentation, we report on optical measurements of ZnSnOx layers generated by DC/RF magnetron plasma co-sputtering. By changing the respective power on two different targets, the overall power, the gas composition and post-treatment, the properties of this type of layers can be varied in a number of parameters. The optical, electrical, and chemical properties of TCO layers are the technically most important properties together with the layer thickness. The dielectric function of layers is accessible by means of spectroscopic ellipsometry, which also yields the very important value for the layer thickness at the same time. It would be a significant step forward in quality control to use this non-destructive method also as a fast test for electrical properties. Therefore, we report on the optical properties connected to the production parameters, and also on our preliminary results connecting the optical dielectric function (in the visible and near infrared) to the electrical conductivity of the layers. We discuss the effect of deposition parameters on the optical properties of the layers and present an approach for correlating optical and electrical properties. Further, we discuss the question of accuracy of optical properties gained from model-fit-based optical methods and the use of different parameterised models for the dielectric function to achieve this.
The paper addresses the “State-of-the-Art in Multiple-Sample Evaluation of Adhesive and Bonding Strength” and the following points are discussed in more detail:
1. Motivation (coatings, varnishes, tapes, laminates, CFRP, adhesive-bonded joints)
2. Conventional single-sample testing (evaluation of adhesive and bonding strength; failure pattern)
3. Multiple-sample handling (MSH), bonding (MSB), and testing: centrifugal adhesion testing (CAT) (multiple-sample approach, tensile test within a centrifuge)
4. Application examples of CAT-Technology™ (laminates, optical coatings, CFRP joints)
Finally, a summary is given regarding status quo and benefits of CAT-technology under tensile stress conditions whereas examples of testing in a centrifuge under compressive stress conditions are mentioned in the outlook.
ZnSnOx coatings were deposited from two 2in magnetron targets made of
ZnO and SnO2 connected to DC pulsed and RF power supplies, respectively.
The pure Ar and reactive gas mixture Ar/O2 were used. DC pulsed power applied on ZnO target was kept constant 50W 50kHz, 20% d.c. and the RF power applied on SnO2 target was set to values from 0W (pure ZnO deposited) up to 150W (up to 8 at.% of Sn in films). The deposited films were investigated by multiple techniques as deposited at RT as well as after annealing at temperatures 200o C and 450o C. The lower annealing temperature is still compatible with many of common polymeric substrates.
The amount of Sn in the films is proportional to applied RF power on SnO2 target. But there is also significant influence of the post Deposition annealing on the film compositions. The ratio Zn/Sn is reduced by the annealing process. Therefore the annealing is promoting the migration of Sn toward the surface and Zn to inside. Moreover the films deposited in oxygen rich reactive gas mixture does not reduces the resistivity with added Sn in contrary to films deposited in Ar where the resistivity was reduced by 5 orders of magnitudes. The plasma parameters were investigated and mean energies of dominant species were in DC pulsed only about 3eV and DC + RF powered plasma up to 15eV. The expected higher energetic particles in the RF influenced plasma deliver an additional energy to the growing film. Therefore, we observed systematic differences between refractive indexes in the films deposited with low RF powered SnO2 magnetron at RT and post-annealed at 200 ° and practically no difference between RT and post-annealed film at higher RF power above 50 W. The XRD results proved the transitions from an amorphous to more crystalline structure by post-annealing of the films.
Surface analysis is still gaining importance, as most modern technology is in essence surface and thin film technology. In microelectronics and optics but also in many fields of energy storage and conversion, thin surface layers or structured surfaces are key components. Optical surface measurements are useful because of their reliability, robustness, and scalability – properties, which are especially desirable in a production environment. However, many of these methods take require considerable effort in data analysis. Spectroscopic ellipsometry (SE) is maybe the prime example of this class of methods. To combine the advantages of SE with metrological trueness and traceability, we combine it in a group of other methods, such as electron microscopy, instrumental surface analysis, X-ray diffraction.
This presentation will give an overview on the principles of SE, its available quantities and the general properties of this measurement technique. Several examples from current and past projects of BAM-6.7 will show how a measurement community involving ellipsometry can benefit many fields of interest, from polymer science to energy applications. In the context of creating a “measurement landscape”, standardisation and standard compliance play an important role. The efforts of BAM in standardisation and accrediting of ellipsometry will be shown demonstrating the possible impact on quality assurance in different fields of technology.
Morphology and structure of TixOy nanoparticles generated by femtosecond laser ablation in water
(2018)
In this work femto-second pulsed laser ablation in liquid (PLAL) procedure for the generation of titanium oxide nanoparticles (NP) is reported with the purpose of understanding morphology and structure of the newly generated NPs. Ablation duration was varied for optimization of NP generation processes between 10 and 90 min. Surface morphology of NPs as well as their size and shape (distribution) were analysed by various complementary electron microscopy techniques, i.e. SEM, TSEM and TEM. The crystalline structure of titanium oxide particles was investigated byXRD(two instruments operated in different geometries) and HR-TEM. Concentration of generated titanium oxide NPs in liquid was analysed by ICP-MS. A mix of crystalline (mainly anatase), partly crystalline and amorphous spherical titanium oxide NPs can be reported having a mean size between 10 and 20 nm, which is rather independent of the laser ablation (LA) duration. A second component consisting of irregularly shaped, but crystalline titanium oxide nanostructures is co-generated in the LA water, with more pronounced occurrence at longer LA times. The provenance of this component is assigned to those spherical particles generated in suspension and passing through the converging laser beam, being hence subject to secondary irradiation effects, e. g. fragmentation.
Commercial grade-1 titanium samples (Ti, 99.6%) were treated using three alternative methods, (i) femtosecond laser processing, (ii) thermal heat treatment, and (iii) electrochemical anodization, respectively, resulting in the formation of differently conditioned superficial titanium oxide layers. The laser processing (i) was carried out by a Ti:sapphire laser (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz) in a regime of generating laser-induced periodic surface structures (LIPSS). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning setup for the processing of several square-millimeters large surface areas covered homogeneously by these nanostructures. The differently oxidized titanium surfaces were characterized by optical microscopy, micro Raman spectroscopy, variable angle spectroscopic ellipsometry, and instrumented indentation testing. The tribological performance was characterized in the regime of mixed friction by reciprocating sliding tests against a sphere of hardened steel in fully formulated engine oil as lubricant. The specific tribological performance of the differently treated surfaces is discussed with respect to possible physical and chemical mechanisms.
A femto-second pulsed laser ablation in liquid (PLAL) procedure for the generation of titanium oxide nanoparticles (NP) is reported with the purpose of understanding morphology and structure of the newly generated NPs. Ablation duration was varied for optimization of NP generation processes between 10 and 90 min. Surface morphology of NPs as well as their size and shape (distribution) were analysed by various complementary electron microscopy techniques, i.e. SEM, TSEM and TEM. The crystalline structure of titanium oxide particles was investigated by XRD(two instruments operated in different geometries) and HR-TEM. Concentration of generated titanium oxide NPs in liquid was analysed by ICP-MS. A mix of crystalline (mainly anatase), partly crystalline and amorphous spherical titanium oxide NPs can be reported having a mean size between 10 and 20 nm, which is rather independent of the laser ablation (LA) duration. A second component consisting of irregularly shaped, but crystalline titanium oxide nanostructures is co-generated in the LA water, with more pronounced occurrence at longer LA times. The provenance of this component is assigned to those spherical particles generated in suspension and passing through the converging laser beam, being hence subject to secondary irradiation effects, e. g. fragmentation.
A femto-second pulsed laser ablation in liquid (PLAL) procedure for the generation of titanium oxide nanoparticles (NP) is reported with the purpose of understanding morphology and structure of the newly generated NPs. Ablation duration was varied for optimization of NP generation processes between 10 and 90 min. Surface morphology of NPs as well as their size and shape (distribution) were analysed by various complementary electron microscopy techniques, i.e. SEM, TSEM and TEM. The crystalline structure of titanium oxide particles was investigated by XRD and HR-TEM. Concentration of generated titanium oxide NPs in liquid was analysed by ICP-MS. A mix of crystalline (mainly anatase), partly crystalline and amorphous spherical titanium oxide NPs can be reported having a mean size between 10 and 20 nm, which is rather independent of the laser ablation (LA) duration. A second component consisting of irregularly shaped, but crystalline titanium oxide nanostructures is co-generated in the LA water, with more pronounced occurrence at longer LA times. The provenance of this component is assigned to those spherical particles generated in suspension and passing through the converging laser beam, being hence subject to secondary irradiation effects, e. g. fragmentation.