A look inside nanoparticles
(2019)
Small-angle scattering is the method of choice when it comes to obtaining information about the interior of nanoparticles. The aim is to make nanotechnology safer. While the use of small-angle neutron scattering (SANS) is limited to a few instruments in the world, small-angle X-ray scattering (SAXS) is widely accessible, with an upward trend. The example of core-shell particles shows how simple their analysis is with data from an Anton Paar laboratory system. Here, SAXS is a central tool for the development of new reference materials based on poly(methyl) acrylate-PVDF core-shell particles. The dimensions of the cores and shells can be precisely determined. A detailed analysis makes it possible to show that the cores contain fluorinated and nonfluorinated polymers, whereas the shell consist only of PVDF. This core-shell particles with a diameter around 40 nm show a significantly higher PVDF beta phase content than the PVDF homopolymer when using an emulsion polymerization technique. This finding is of importance with respect to applications in electroactive devices.
Mesoporous phosphates are a group of nanostructured materials with promising applications, particularly in biomedicine and catalysis. However, their controlled synthesis via conventional template-based routes presents a number of challenges and limitations. Here, we show how to synthesize a mesoporous Magnesium phosphate with a high surface area and a well-defined pore structure through thermal decomposition of a crystalline struvite (MgNH4PO4·6H2O) precursor. In a first step, struvite crystals with various morphologies and sizes, ranging from a few micrometers to several millimeters, had been synthesized from supersaturated aqueous solutions (saturation index (SI) between 0.5 and 4) at ambient pressure and temperature conditions. Afterwards, the crystals were thermally treated at 70–250 °C leading to the release of structurally bound water (H2O) and ammonia (NH3). By combining thermogravimetric analyses (TGA), scanning and transmission electron microscopy (SEM, TEM), N2 sorption analyses and small- and wide-angle X-ray scattering (SAXS/WAXS) we show that this decomposition process results in a pseudomorphic transformation of the original struvite into an amorphous Mg-phosphate. Of particular importance is the fact that the final material is characterized by a very uniform mesoporous structure with 2–5 nm wide pore channels, a large specific surface area of up to 300 m2 g−1 and a total pore volume of up to 0.28 cm3 g−1. Our struvite decomposition method is well controllable and reproducible and can be easily extended to the synthesis of other mesoporous phosphates. In addition, the so produced mesoporous material is a prime candidate for use in biomedical applications considering that Magnesium phosphate is a widely used, non-toxic substance that has already shown excellent biocompatibility and biodegradability.
Experimenting on MAUS
(2019)
Polymeric core-shell particles were synthesized in a semi-batch emulsion polymerization process. The shell of the particles consist of PVDF with a high amount of beta-phase. Small-angle X-ray scattering (SAXS) was used to quantify the size of the cores of the particles and the thickness of the shell.
Ordered mesoporous silica materials such as COK-12, analogous to the well-known SBA-15, are characterized by high surface areas and unique features such as defined pore sizes in the meso-size range and high pore ordering.
The aim of this work was to prove the washing step and choice of calcination and aging temperature during the COK-12 synthesis as effective tools in tailoring, markedly improving the specific surface area, pore size, and pore volume. By controlling the aging temperature, the pore size was linearly adjusted between 5.7 and 8.1 nm, while preserving the hexagonal ordering of the pores. The synthesized COK-12 powders possess pore volumes and specific surface areas up to 1.23 cm3 g−1 and 860m2 g−1, respectively, which is markedly higher than what has previously been reported about COK-12. The presented results and the environmentally friendly character of the synthesis will make COK-12 more interesting for future adaption to the industrial processes, for example in catalysis, adsorption, or drug delivery.
Zinc oxide nanostructures possess optical properties that are dependent on particle shape and size. Here, we report on the synthesis of elongated zinc oxide tubes via the in-situ aggregation of spherical particles. Using a custom-built, lab-based instrument, x-ray scattering can be investigated over more than three decades in scattering vector q, allowing for a complete investigation from atomic distances up to larger-than-nano structures.
For this study, the hydrolytic synthesis of stearate stabilized zinc oxide nanostructures in tetrahydrofuran was performed and the reaction mixture was continuously fed through the SAXS/WAXS apparatus by means of a peristaltic pump. For comparison to nanospheres, oleate-functionalized zinc oxide particles were synthesized in a microwave-assisted fashion, and depending on reaction temperature, sphere radii could be adjusted between 2.6 and 3.8 nm, changing the optical and crystal lattice properties.
The evaluation of the in-situ measurements showed that at the beginning of the synthesis of the stearate-stabilized zinc oxide, similar, spherical particles are formed as in the oleate-based synthesis. In contrast, as the reaction progresses, the stearate-capped particles aggregate into elongated rods with radii of a few nanometres, which eventually form the nanotubes. These have radii of 30-50 nm and lengths of several hundred nanometres. Nevertheless, these structures still possess optical properties like the ultra-small zinc oxide spheres, i.e. a bright, yellow fluorescence. Therefore, we assume that the originally formed, ultra-small spheres, are still present within the tube structure, but separated by stearate, and thus determine their fluorescence properties.
Zinc is an essential trace element and is ingested daily by humans, partly in dissolved form. The first contact is with saliva, in which many ions are dissolved whose solubility product with zinc can be low. This could result in compounds forming, possibly in nanoparticular form, which could have different effects on the organism than pure zinc ions. Available biopolymers, e.g. α-amylase, can in turn stabilise as-formed nanostructures.
In this study, we report on the saliva stage of the artificial digestion of zinc chloride as a model substance for zinc ions. To facilitate in situ measurements, the sample is continuously passed through a small-angle x-ray scattering (SAXS) system. This custom-made machine is capable of measuring over a wide q-range and thereby able to resolve structures from around 250 nm down to the crystal structure. It is thus an excellent tool for investigating both the particle size distribution and the atomic structure of the sample.
By curve fitting (see Figure 1), we found that shortly after addition of zinc chloride to saliva, small particles with a mean radius of 1.9 ± 0.1 nm and a distribution width of 0.6 ± 0.1 nm formed. These particles are aggregated to compact mass fractals with a fractal aggregate size of 14.7 ± 0.1 nm and a fractal dimension of 2.96 ± 0.02. Approximately 7200 single particles stick together by protein and form mass fractals, whose radii of gyration were found to be 36 ± 1 nm. To determine the compound that was formed, infrared spectroscopy was used in addition to the SAXS measurements, and zinc phosphate was identified as the product.
We report on ultrasmall zinc oxide single-crystalline nanoparticles of narrow size distribution and long-term colloidal stability. These oleate-stabilized nanoparticles were synthesized using microwave-assisted synthesis for 5 min, corresponding to a 99% decrease in synthesis time, when compared to the conventional synthesis method. It was observed that the average particle radius increases from 2.6 ± 0.1 to 3.8 ± 0.1 nm upon increasing synthesis temperature from 125 to 200 °C. This change also corresponded to observed changes in the optical band gap and the fluorescence energy of the particles, from 3.44 ± 0.01 to 3.36 ± 0.01 eV and from 2.20 ± 0.01 to 2.04 ± 0.01 eV, respectively. Small-angle X-ray scattering, dynamic light scattering, and UV–vis and fluorescence spectroscopy were employed for particle characterization. Debye–Scherrer analysis of the X-ray diffraction (XRD) pattern reveals a linear increase of the crystallite size with synthesis temperature. The consideration of the convolution of a Lorentz function with a Gaussian function for data correction of the instrumental peak broadening has a considerable influence on the values for the crystallite size. Williamson–Hall XRD analyses in the form of the uniform deformation model, uniform stress deformation model, and uniform deformation energy density model revealed a substantial increase of strain, stress, and deformation energy density of the crystallites with decreasing size. Exponential and power law models were utilized for quantification of strain, stress, and deformation energy density.
Small-angle scattering (SAS) offers a reliable route to characterize the nanostructure of large amounts of material with a minimum of tedium, for example, easily extracting size distributions and volume fractions. There are a variety of analysis programs available while the evaluation of SAS measurements has been dominated by the classical curve fitting approach. SASfit represents such a classical curve fitting toolbox: it is one of the mature programs for SAS data analysis and has been available and used for many years. The latest developments will be presented and a scattering function of a mass fractal model of branched polymers in solution is provided as an example for implementing a plug-in.
Alternatively to classical curve fitting, part two presents the latest developments of the user-friendly open-source Monte Carlo regression package McSAS. The form-free Monte Carlo nature of McSAS means, it is not necessary to provide further restrictions on the mathematical form of the parameter distribution: without prior knowledge, McSAS is able to extract complex multimodal or odd- shaped parameter distributions from SAS data. The headless mode is presented by an example of operation within interactive programming environments such as a Jupyter notebook.