A comparative analysis is performed by XPS, HAXPES and SEM of industrial functionalised graphene powder of different morphology. The chemical analysis carried out by XPS, which probing depth is around 10nm, and HAXPES, which can reach up to 30nm probing depth. By combining these two techniques is possible to get a rough, non-destructive depth profiling of the sample's surface. The results show a higher concentration of the functionlisation elements on the surface of the sample and the influence of the morphology on the functionalisation process and the C/O ratio.
Gold films coated with a graphene sheet are being widely used as sensors for the detection of label-free binding interactions using surface plasmon resonance (SPR). During the preparation of such sensors, it is often essential to subject the sensor chips to a high-temperature treatment in order to ensure a clean graphene surface. However, sensor chips used currently, which often use chromium as an adhesion promoter, cannot be subjected to temperatures above 250 °C, because under such conditions, chromium is found to reorganize and diffuse to the surface, where it is easily oxidized, impairing the quality of SPR spectra. Here we present an optimized preparation strategy involving a three-cycle tempering coupled with chromium (oxide) etching, which allows the graphene-coated SPR chips to be annealed up to 500 °C with little deterioration of the surface morphology. In addition, the treatment delivers a surface that shows a clear enhancement in spectral response together with a good refractive index sensitivity. We demonstrate the applicability of our sensors by studying the kinetics of avidin–biotin binding at different pH repeatedly on the same chip. The possibility to anneal can be exploited to recover the original surface after sensing trials, which allowed us to reuse the sensor for at least six cycles of biomolecule adsorption.
Since its discovery, graphene has got growing attention in the industrial and application research due to its unique properties . However, graphene has not been yet implemented into the industrial market, in particularly due to the difficulty of properly characterizing this challenging material. As most of other nanomaterials, graphene’s properties are closely linked to its chemical and structural properties, such as number of layers, flake thickness, degree of functionalisation and C/O ratio. For the commercialization, suitable procedures for the measurement and characterization of the ultrathin flakes, of lateral dimensions in the range from µm to tens of µm, are essential.Surface chemical methods, especially XPS, have an outstanding role of providing chemical information on the composition. Thereby, one well-known problem for surface analytical methods is the influence of contamination on the composition as in the case of adventitious carbon. The differentiation between carbon originated from the contamination or from the graphene sample itself is often not obvious, which can lead to altered results in the determination of the composition. To overcome this problem, Hard Energy X-ray Photoelectron Spectroscopy (HAXPES) offers new possibilities due to its higher information depth. Therefore, XPS measurement obtained with Al Kα radiation (E = 1486. 6 eV) were compared with analyses performed with a Cr Kα (E = 5414. 8 eV) excitation on functionalized graphene samples. Differences are discussed in terms of potential carbon contamination, but also of oxygen on the composition of the samples. Measurements are performed on O-, N- and F-functionalized graphene. Different preparation procedures (powder, pellet, drop cast from liquid suspension) will be also discussed, correlation of the results with the flakes morphology as well as their validation with other independent methods are in progress.