6 Materialchemie
Filtern
Dokumenttyp
- Zeitschriftenartikel (16)
- Vortrag (6)
- Posterpräsentation (5)
- Beitrag zu einem Tagungsband (2)
- Dissertation (1)
- Sonstiges (1)
- Forschungsdatensatz (1)
Schlagworte
- Hydrogen (6)
- Nanoparticles (5)
- ToF-SIMS (5)
- AISI 304L (4)
- Deuterium (4)
- Corrosion (3)
- High entropy alloy (3)
- Laser ablation in liquid (3)
- Oxidation (3)
- Round Robin (3)
- Titanium oxide (3)
- Austenitic stainless steel (2)
- Biofilm (2)
- Data analysis (2)
- Electron microscopy (2)
- High entropy alloys (2)
- High temperature corrosion (2)
- MOUSE (2)
- Mixed gas atmosphere (2)
- Nanostructure quantification (2)
- Particle morphology (2)
- SIMS (2)
- Silver nanoparticle (2)
- Starch (2)
- Starch nanoparticle (2)
- Sulfidation (2)
- Transmission electron microscopy (2)
- Wood protection (2)
- X-ray diffraction (2)
- XANES (2)
- Alkali zinc borate glass (1)
- Artefact (1)
- Atom probe tomography (1)
- Austenitic steel (1)
- Brown-rot fungi (1)
- Chemically complex alloys (1)
- Coniophora puteana (1)
- CrMnFeCoNi (1)
- Creep (1)
- Diffraction (1)
- EBSD (1)
- EXAFS (1)
- Eutectic (1)
- Femtosecond laser (1)
- Fluoride nanoparticles (1)
- Fluorolytic sol−gel (1)
- Friction (1)
- Fungi (1)
- Gitterfehlpassung (1)
- Hochentropie-Legierung (1)
- Homogenization (1)
- In situ (1)
- Infrared nano AFM (1)
- Interlaboratory comparability (1)
- Intermodulation AFM (1)
- Interphase (1)
- Iron (1)
- Kriechversuche (1)
- Lattice misfit (1)
- Martensite (1)
- Metal and alloys (1)
- Metallic silver precipitates (1)
- Methodology (1)
- Nano metal fluorides (1)
- Nanocomposites (1)
- Nanomaterials (1)
- Nanoparticle structure (1)
- Nanostructure (1)
- Phase separation (1)
- Rhodonia placenta (1)
- SAXS (1)
- SEM (1)
- SEM wood characterization (1)
- Sall-angle scattering (1)
- Scanning electron microscopy (1)
- Short range order (1)
- Silver diffusion (1)
- Size distribution (1)
- Small-angle Scattering (1)
- Small-angle scattering (1)
- Solubility (1)
- Steel (1)
- Sulphidation (1)
- Termites (1)
- Titanium (1)
- Transmissionselektronenmikroskopie (1)
- Vickers hardness (1)
- X-ray absorption spectroscopy (1)
- X-ray scattering (1)
- XRD (1)
- corrosion (1)
- high entropy alloys (1)
- oxidation (1)
- scanning electron microscopy (1)
- sulfidation (1)
Organisationseinheit der BAM
- 5.1 Mikrostruktur Design und Degradation (32) (entfernen)
Eingeladener Vortrag
- nein (6)
Spurenelemente spielen eine wichtige Rolle bei der Verfeinerung der Eigenschaften von komplexen Materialien. Diese Arbeit zeigt die Korrelation zwischen der Mikrostruktur, der Gitterfehlpassung und den Kriecheigenschaften. Die Legierung Al10Co25Cr8Fe15Ni36Ti6 (in at. %) mit komplexer Zusammensetzung wurde mit den Elementen Hf und W verstärkt. Die Zugabe von Hf bewirkt eine eckigere Form der würfelförmigen gamma'-Ausscheidungen und einen erhöhten Anteil der Heusler-Phase. Die Zugabe von W wiederum formt die Würfelchen rundlicher und löst die Heusler-Phase auf. Eine Mischung der beiden Spurenelemente zeigt einen Übergang zwischen den beiden Extremen, sowohl in Hinsicht auf die Form der Ausscheidungen als auch in Bezug auf die Gitterfehlpassung und die Kriecheigenschaften.
In this study, nanoscopic particles of magnesium Fluoride (MgF2) and calcium fluoride (CaF2) also known as nano metal fluorides (NMFs), were evaluated for their potential to improve wood durability. Even though these fluorides are sparingly soluble, their synthesis in the form of nano-sized particles turns them into promising candidates for wood preservation. Their distinct property of low-water solubility is proposed to maintain long-lasting protection of treated wood by reducing the leaching of fluoride. Analytical methods were used to characterize the synthesized NMFs and their distribution in treated wood specimens. Transmission electron microscopy images showed that these fluoride particles are smaller than 10 nm. In nano metal fluoride (NMF) treated specimens, aggregates of these particles are uniformly distributed in the wood matrix as confirmed with scanning electron microscopy images and their corresponding energy-dispersive X-ray spectroscopy maps. The fluoride aggregates form a protective layer around the tracheid walls and block the bordered pits, thus reducing the possible flow path for water absorption into wood. This is reflected in the reduced swelling and increased hydrophobicity of wood treated with NMFs. The biocidal efficacy of NMFs was tested against brown-rot fungi (Coniophora puteanaand Rhodonia placenta), white-rot fungus (Trametes versicolor), and termites (Coptotermes formosanus). The fungal and termite tests were performed in accordance with the EN 113 (1996) and EN 117 (2012) standards, respectively. Prior to fungal tests, the NMF treated wood specimens were leached according to the EN 84 (1997)standard. Compared to untreated specimens, the NMF treated wood specimens have a higher resistance to decay caused by brown-rot fungi, white-rot fungus, and termites. Although all NMF treatments in wood reduce the mass loss caused by fungal decay, only the combined treatment of MgF2 and CaF2 has efficacy against both brown-rot fungi and white-rot fungus. Similarly, wood treated with the combined NMF formulation is the least susceptible to attack by C. formosanus.It is proposed that combining MgF2 and CaF2changes their overall solubility to promote the release of fluoride ions at the optimal concentration needed for biocidal efficacy against fungi and termites. In this thesis, it was proven that even after leaching, sufficient fluoride was present to protect NMF treated wood from fungal decay. This shows that NMFs are robust enough for above ground contact outdoor applications of wood, where permanent wetness cannot be avoided according to Use Class 3.2, as per the EN 335 (2013) standard. Also, they pose a low risk to human health and the environment because they are sparingly soluble. Since NMFs significantly reduce the decay of wood, the CO2 fixed in it will be retained for longer than in unpreserved wood. Overall, the novel results of this study show the potential of NMFs to increase the service life of building materials made from non-durable wood.
During the energy transformation from fossil fuels to renewable energy sources, the use of hydrogen as fuel and energy storage can play a key role. This presents new challenges to industry and the scientific community alike. The storage and transport of hydrogen, which is nowadays mainly realized by austenitic stainless steels, remains problematic, which is due to the degradation of mechanical properties and the possibility of phase transformation by hydrogen diffusion and accumulation. The development of materials and technologies requires a fundamental understanding of these degradation processes. Therefore, studying the behavior of hydrogen in austenitic steel contributes to an understanding of the damage processes, which is crucial for both life assessment and safe use of components in industry and transportation. As one of the few tools that is capable of depicting the distribution of hydrogen in steels, time-of-flight secondary ion mass spectrometry was conducted after electrochemical charging. To obtain further information about the structural composition and cracking behavior, electron-backscattered diffraction and scanning electron microscopy were performed. Gathered data of chemical composition and topography were treated employing data fusion, thus creating a comprehensive portrait of hydrogen-induced effects in the austenite grade AISI 304L. Specimens were electrochemically charged with deuterium instead of hydrogen. This arises from the difficulties to distinguish between artificially charged hydrogen and traces existing in the material or the rest gas in the analysis chamber. Similar diffusion and permeation behavior, as well as solubility, allow nonetheless to draw conclusions from the experiments.
Commercial grade-1 titanium samples (Ti, 99.6%) were treated using three alternative methods, (i) femtosecond laser processing, (ii) thermal heat treatment, and (iii) electrochemical anodization, respectively, resulting in the formation of differently conditioned superficial titanium oxide layers. The laser processing (i) was carried out by a Ti:sapphire laser (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz) in a regime of generating laser-induced periodic surface structures (LIPSS). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning setup for the processing of several square-millimeters large surface areas covered homogeneously by these nanostructures. The differently oxidized titanium surfaces were characterized by optical microscopy, micro Raman spectroscopy, variable angle spectroscopic ellipsometry, and instrumented indentation testing. The tribological performance was characterized in the regime of mixed friction by reciprocating sliding tests against a sphere of hardened steel in fully formulated engine oil as lubricant. The specific tribological performance of the differently treated surfaces is discussed with respect to possible physical and chemical mechanisms.
The impact of the microstructure of Fe-16Cr-0.2C on high-temperature oxidation – sulphidation in SO2
(2021)
This study elucidates the impact of the microstructure of Fe-16Cr-0.2C on oxide layer formation at 650 ◦C in Ar-0.5 % SO2. A cold-rolled and two heat-treated states of the alloy were exposed for up to 1000 h. The samples were characterised in detail from microstructural and chemical perspectives using scanning electron microscopy (SEM), X-ray diffraction (XRD) and time-of-flight secondary ion mass spectrometry (ToF-SIMS). The microstructural modification of the alloy by heat-treatment was advantageous. It was found that Cr-carbides support chromia formation and reduce sulphidation when their area fraction is low and diameter is small.
A round-robin study has been carried out to estimate the impact of the human element in small-angle scattering data analysis. Four corrected datasets were provided to participants ready for analysis. All datasets were measured on samples containing spherical scatterers, with two datasets in dilute dispersions and two from powders. Most of the 46 participants correctly identified the number of populations in the dilute dispersions, with half of the population mean entries within 1.5% and half of the population width entries within 40%. Due to the added complexity of the structure factor, far fewer people submitted answers on the powder datasets. For those that did, half of the entries for the means and widths were within 44 and 86%, respectively. This round-robin experiment highlights several causes for the discrepancies, for which solutions are proposed.
A Round Robin study has been carried out to estimate the impact of the human element in small-angle scattering data analysis. Four corrected datasets were provided to participants ready for analysis. All datasets were measured on samples containing spherical scatterers, with two datasets in dilute dispersions, and two from powders.
Most of the 46 participants correctly identified the number of populations in the dilute dispersions, with half of the population mean entries within 1.5 % and half of the population width entries within 40 %, respectively. Due to the added complexity of the structure factor, much fewer people submitted answers on the powder datasets.
For those that did, half of the entries for the means and widths were within 44 % and 86 % respectively. This Round Robin experiment highlights several causes for the discrepancies, for which solutions are proposed.
Misfits of γ- γ’ based Al10Co25Cr8Fe15Ni36Ti6 and its Mo- and Hf-variations are studied up to a temperature of 980 °C and compared with Ni- and Co-based superalloys. The trace elements decrease (Hf) or increase (Mo) the edge radii of the γ’ cuboids without changing their sizes. Atom probe measurements revealed that the Hf alloy prefers the γ’ phase while Mo prefers the γ matrix, leading to a lattice parameters enhancement of both phases, as could be revealed by synchrotron X-ray diffraction. The misfit is influenced in opposite ways: Hf increases the positive misfit, while Mo reduces it at all investigated temperatures.
Among the very few techniques to localize hydrogen (H) at the microscale in steels, Time-of-flight secondary ion mass spectrometry (ToF-SIMS) was proven to be a reliable tool. The necessity to detect hydrogen stems from its deleterious effects in metals, that are often used as structural components and to obtain better understanding of the underlying metallurgical mechanisms of hydrogen embrittlement (HE) which are still unclear.
Austenitic stainless steels are nowadays commonly used in a wide variety of application, from hydrogen transport and storage facilities to petrochemical and offshore applications where they are exposed to aggressive environments and therefore prone to HE. One of the greater risks in the austenitic class is the embrittlement of the material due to the instability of the γ austenite and its transformation into a brittle α martensitic phase. This transformation takes place due to the local stresses that are induced by the uptake of hydrogen during service. Nonetheless, it was shown that this transformation can occur as an artefact during SIMS analysis itself where Cs-sputtering is necessary not only to remove surface contaminations but mainly to enhance H/D secondary ion yield.
In the following contribution we show the influence of different sputtering conditions on AISI 304L austenitic stainless steel in order to distinguish the artefact from the hydrogen induced transformation. The material was charged electrochemically in a deuterium based electrolyte. Deuterium (D) must be in these experiments as a replacement for hydrogen which cannot be used because adsorbed hydrogen superimposes hydrogen originating from charging the sample in the SIMS images. ToF-SIMS analyses were conducted by ToF SIMS IV (IONTOF GmbH, Münster, Germany). The experiments were carried out on deuterium charged and non-charged samples. The structural characterization was carried out by SEM and EBSD examinations before and after charging, both with a Leo Gemeni 1530VP field-emission scanning electron microscope and a Zeiss Supra 40 instrument (Carl Zeiss Microscopy GmbH, Oberkochen, Germany). The results showed that the use of 1keV Cs+ beam induces stacking faults while higher sputter beam energies results in γ→α transformation.
Small-angle Scattering Data Analysis Round Robin: anonymized results, figures and Jupyter notebook
(2023)
The intent of this round robin was to find out how comparable results from different researchers are, who analyse exactly the same processed, corrected dataset.
This zip file contains the anonymized results and the jupyter notebook used to do the data processing, analysis and visualisation. Additionally, TEM images of the samples are included