6 Materialchemie
Filtern
Erscheinungsjahr
- 2021 (15) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (15) (entfernen)
Sprache
- Englisch (15)
Schlagworte
- MALDI-TOF MS (13)
- Polylactide (12)
- Crystallization (5)
- Catalyst (3)
- Polycondensation (3)
- Polymerization (3)
- Ring-opening polymerization (3)
- Tin acetates (2)
- Alternating co-poly(ether pyridine)s (1)
- Annealing (1)
- Aromatic organic compounds, (1)
- Biosourced isosorbide (1)
- Catalysts (1)
- Conversion (1)
- Copolymerization (1)
- Glycolide (1)
- L-lactide (1)
- Polymers (1)
- Ring-expansion polymerization (1)
- SAXS (1)
- Sorption isotherm (1)
- Sorption mechanism (1)
- Transesterification (1)
Organisationseinheit der BAM
- 6 Materialchemie (15)
- 6.3 Strukturanalytik (15)
The catalytic potential of tin(II)acetate, tin(IV)acetate, dibutyltin-bis-acetate and dioctyl tin-bis-acetate was compared based on polymerizations of L-lactide conducted in bulk at 160 or 130°C. With SnAc2 low-Lac/Cat ratios (15/1–50/1) were studied and linear chains having one acetate and one carboxyl end group almost free of cyclics were obtained. Higher monomer/catalyst ratios and lower temperatures favored formation of cycles that reached weight average molecular weights (Mw's) between 100,000 and 2,500,000. SnAc4 yielded mixtures of cycles and linear species under all reaction conditions. Dibutyltin- and dioctyl tin bis-acetate yielded cyclic polylactides under most reaction conditions with Mw's in the range of 20,000–80,000. Ring-opening polymerizations performed with ε-caprolactone showed similar trends, but the formation of COOH-terminated linear chains was significantly more favored compared to analogous experiments with lactide. The reactivity of the acetate catalysts decreased in the following order: SnAc2> SnAc4>Bu2SnAc2~Oct2SnAc2
Cyclic polylactides were prepared in bulk at 170 °C, crystallized at 120 °C and then annealed at temperatures between 130 and 170 C with variation of catalyst, catalyst concentration and annealing time. The transformation of the initially formed low melting (LTm) crystallites, having melting temperatures (Tm) <180 °C into high melting (HTm) crystallites having Tm values > 189 °C was monitored by means of DSC measurements and characterized in selected cases by SAXS measurements. It was confirmed that the formation of HTm crystallites involves a significant growth of the thickness of the lamellar crystallites along with smoothing of their surface. Annealing at 170 °C for 1 d or longer causes thermal degradation with lowering of the molecular weights, a gradual transition of cyclic into linear chains and a moderate decrease of lamellar thickness. An unexpected result revealed by MALDI TOF mass spectrometry is a partial reorganization of the molecular weight distribution driven by a gain of crystallization enthalpy.
The catalytic potential of tin(II)acetate, tin(IV)acetate, dibutyltin-bis-acetate and dioctyl tin-bis-acetate was compared based on polymerizations of L-lactide conducted in bulk at 160 or 130C. With SnAc2 low-Lac/Cat ratios (15/1–50/1) were studied and linear chains having one acetate and one carboxyl end group almost free of cyclics were obtained. Higher monomer/catalyst ratios and lower temperatures favored formation of cycles that reached weight average molecular weights (Mw's) between 100,000 and 2,500,000. SnAc4 yielded mixtures of cycles and linear species under all reaction conditions. Dibutyltin- and dioctyl tin bis-acetate yielded cyclic polylactides under most reaction conditions with Mw's in the range of 20,000–80,000. Ring-opening polymerizations performed with ε-caprolactone showed similar trends, but the formation of COOH-terminated linear chains was significantly more favored compared to analogous experiments with lactide. The reactivity of the acetate catalysts decreased in the following order: SnAc2> SnAc4>Bu2SnAc2 Oct2SnAc2.
Polymerizations of L-lactide catalyzed either by neat SnCl2 or by SnCl2 + difunctional cocatalysts were conducted in bulk at 180, 160 and 140 °C with variation of the Lac/Cat ratio and time. With neat SnCl2 poly(L-lactide) having weight average molecular weights (uncorrected Mw’s) up to 190 000 g mol−1 were obtained mainly consisting of linear chains. Addition of salicylic acid or 1,1-bisphenol yielded a higher fraction of cyclic polylactides but lower molecular weights. Furthermore, SnCl2 was compared with Bu2SnCl2 and various other metal chlorides and the best results were obtained with SnCl2. With ethyl L-lactate as initiator SnCl2-catalyzed ROPs were performed at 120 °C and the lac/initiator ratio was varied. All these experiments were conducted under conditions allowing for comparison with ROPs catalyzed with neat Sn(II)-2-ethyhexanoate. Such a comparison was also performed with ε-caprolactone as monomer.
1:1 Copolymerizations of glycolide (GL) and L-lactide (LA) is performed in bulk at 100°C and at 160°C with four cyclic tin catalysts. The resulting copolyesters are characterized by SEC measurements, 1H and 13C NMR spectroscopy and by MALDI TOF mass spectrometry. At 160°C and longer reaction time (22 h) nearly complete conversion of both monomers is achieved, and cyclic copolymers with nearly random sequences are formed. At shorter times (0.5-3.0 h, depending on catalyst) the conversion of LA is incomplete, and only cyclics having even numbers of lactyl units are obtained. At 100°C at 22 h again cycles mainly consisting of even numbered lactyl units are formed, but with even and odd numbers of glycolyl units. Copolymerization of lactide at 160°C with small amounts of GL show that formation of high Tm crystallites (Tm > 190°C) is hindered even when only > 2% of GL is added. For polyglycolide containing a smaller amount of lactide complete solubility in hexafluoroisopropanol is only observed around and above 20 mol% of lactide.