The influence of zeolite support materials and their impact on CH4 oxidation activity was studied utilizing Pd supported on H-beta and H-SSZ-13. A correlation between CH4 oxidation activity, Si/Al ratio (SAR), the type of zeolite framework, reduction-oxidation behaviour, and Pd species present was found by combining catalytic activity measurements with a variety of characterization methods (operando XAS, NH3-TPD, SAXS, STEM and NaCl titration). Operando XAS analysis indicated that catalysts with high CH4 oxidation activity experienced rapid transitions between metallic- and oxidized-Pd states when switching between rich and lean conditions. This behaviour was exhibited by catalysts with dispersed Pd particles. By contrast, the formation of ion-exchanged Pd2+ and large Pd particles appeared to have a detrimental effect on the oxidation-reduction behaviour and the conversion of CH4. The formation of ion-exchanged Pd2+ and large Pd particles was limited by using a highly siliceous beta zeolite support with a low capacity for cation exchange. The same effect was also found using a small-pore SSZ-13 zeolite due to the lower mobility of Pd species. It was found that the zeolite support material should be carefully selected so that the well-dispersed Pd particles remain, and the formation of ion-exchanged Pd2+ is minimized.
Li-rich nanoparticles of Li1+xMn2–xO4 doped with Al, Co, or Ni are successfully synthesized using a facile, fast, and efficient microwave-assisted hydrothermal route. Synchrotron X-ray diffraction confirms the formation of the crystalline cubic spinel phase type. X-ray absorption spectroscopy analysis at the Co and Ni K- and L-edges verifies that the dopants are within the Li1+xMn2–xO4 spinel structure and are inactive during cycling in the bulk and at the surface. Moreover, we demonstrate that nanocrystallinity and cationic doping play an important role in improving the electrochemical performance with respect to LiMn2O4 microparticles. They significantly reduce the charge-transfer resistance, lower the first cycle irreversible capacity loss to 6%, and achieve a capacity retention between 85 and 90% after 380 cycles, with excellent Coulombic efficiency close to 99% without compromising the specific charge at a 5C cycling rate. Furthermore, the Mn K- and L-edges attest that after long cycling, the Mn oxidation state in the bulk differs from that at the surface caused by the Mn disproportion reaction; however, the cationic doping helps mitigate the Mn dissolution with respect to the undoped Li1+xMn2–xO4 nanoparticles, as indicated by inductively coupled plasma atomic emission spectrometry.