A new concept for the ecotoxicological assessment of plastics under consideration of aging processes
(2023)
Microplastics are widely distributed in aquatic and terrestrial environments, but up to now less is known about (eco)toxicological impacts under realistic conditions. Research so far has focused mainly on impacts on organisms by fresh, single‐origin plastic fragments or beads. However, plastics found in the environment are complex in composition, this means different polymer types and sources, with and without additives and in all stages of age, and therefore, in a more or less advanced stage of degradation. For oxidized degradation products that might be released from plastic materials during aging, there is a lack of information on potentially adverse effects on aquatic biota. The latter is of particular interest as oxidized degradation products might become more water soluble due to higher polarity and are more bioavailable, therefore. The present study focused on plastic leachates of polystyrene (PS) and polylactic acid (PLA), which were derived from alternating stress by hydrolysis and ultraviolet (UV) radiation—representing a realistic scenario in the environment. Test specimens of PS, PLA, or a PLA/PS layer (each 50%) were alternately exposed to UV radiation for 5 days followed by hydrolysis for 2 days, for several weeks alternating. Ecotoxicological effects of the storage water (artificial freshwater) of the test specimens and additionally, in a second experimental setup, the effects of five potential polymer degradation products were detected by 72 h algae growth inhibition tests with Desmodesmus subspicatus. Results clearly indicate inhibitory effects on algae growth by contaminants in the storage water of stressed plastics with increasing growth inhibition of proceeding hydrolysis and UV stress times. Different polymers caused variable inhibitions of algae growth with stronger inhibitions by PS and less effects by PLA and the mixed layer of both. Moreover, not microplastic particles but the resulting dissolved degradation products after aging caused the ecotoxicological effects—with strong effects by the oxidized degradation products. The existing data highlight the relevance of plastic aging as a framework for microplastic ecotoxicity evaluation and allow a proof of concept.
A fast method for microplastic detection is thermal extraction desorption‐gas chromatography/mass spectrometry (TED‐GC/MS), which uses polymer‐specific thermal decomposition products as marker compounds to determine polymer mass contents in environmental samples. So far, matrix impacts of different environmental matrices on TED‐GC/MS performance had not yet been assessed systematically. Therefore, three solid freshwater matrices representing different aquatic bodies with varying organic matter contents were spiked with a total of eight polymers. Additionally, for the first time, the two biodegradable polymers polybutylene adipate terephthalate (PBAT) and polylactide (PLA) were analysed using TED‐GC/MS. The methodological focus of this work was on detectability, quality of signal formation as well as realisation of quantification procedures and determination of the limit of detection (LOD) values. Overall, TED‐GC/MS allowed the unambiguous detection of the environmentally most relevant polymers analysed, even at low mass contents: 0.02 wt% for polystyrene (PS), 0.04 wt% for the tyre component styrene butadiene rubber (SBR) and 0.2 wt% for polypropylene (PP), polyethylene (PE) and PBAT. Further, all obtained LOD values were increased in all matrices compared to the neat polymer without matrix. The LOD of the standard polymers were increased similarly (PS: 0.21–0.34 μg, SBR: 0.27–0.38 μg, PP: 0.32–0.36 μg, PMMA: 0.64–1.30 μg, PET: 0.90–1.37 μg, PE: 3.80–6.99 μg) and their decompositions by radical scission processes were not significantly influenced by the matrices. In contrast, matrixspecific LOD increases of both biodegradable polymers PBAT (LOD: 1.41–7.18 μg) and PLA (0.84–20.46 μg) were observed, probably due to their hetero‐functional character and interactions with the matrices. In conclusion, the TED‐GC/MS performance is not solely determined by the type of the polymers but also by the composition of the matrix.