5.2 Metallische Hochtemperaturwerkstoffe
Filtern
Dokumenttyp
- Zeitschriftenartikel (3) (entfernen)
Sprache
- Englisch (3)
Referierte Publikation
- ja (3)
Schlagworte
- Fatigue (3) (entfernen)
Organisationseinheit der BAM
- 5 Werkstofftechnik (3)
- 5.2 Metallische Hochtemperaturwerkstoffe (3)
- 5.1 Mikrostruktur Design und Degradation (2)
- 9 Komponentensicherheit (2)
- 9.4 Integrität von Schweißverbindungen (2)
- 4 Material und Umwelt (1)
- 4.2 Material-Mikrobiom Wechselwirkungen (1)
- 5.4 Multimateriale Fertigungsprozesse (1)
- 5.5 Materialmodellierung (1)
- 8 Zerstörungsfreie Prüfung (1)
Fatigue tests were performed on the forged aluminum alloy EN AW-2618A in the T61 state. Different stress ratios (R = -1, R = 0.1) were selected to study the influence of mean stress on fatigue life. Two overaged states (10 h/230 ◦C, 1000 h/230 ◦C) were also tested to investigate the influence of overaging on fatigue life. Transmission electron microscopy (TEM) was used to characterize the precipitates (S-phase), which are mainly responsible for the strength of the alloy. A fractographic analysis was also performed to determine the failure mode. Overaging reduces the fatigue life compared to the T61 state. The longer the aging time, the lower the fatigue resistance. The reason is the decrease in (yield) strength, which correlates with the radius of the S-phase: the precipitate radius increases by a factor of approximately two for the overaged states compared to the initial state. The analysis of the fracture surfaces showed crack initiation occurs predominantly on the outer surface and is
associated with the primary phases.
Computational methods for lifetime prediction of metallic components under high-temperature fatigue
(2019)
The issue of service life prediction of hot metallic components subjected to cyclic loadings is addressed. Two classes of lifetime models are considered, namely, the incremental lifetime rules and the parametric models governed by the fracture mechanics concept. Examples of application to an austenitic cast iron are presented. In addition, computational techniques to accelerate the time integration of the incremental models throughout the fatigue loading history are discussed. They efficiently solve problems where a stabilized response of a component is not observed, for example due to the plastic strain which is no longer completely reversed and accumulates throughout the fatigue history. The performance of such an accelerated Integration technique is demonstrated for a finite element simulation of a viscoplastic solid under repeating loading–unloading cycles.