5.1 Mikrostruktur Design und Degradation
Filtern
Erscheinungsjahr
- 2022 (4) (entfernen)
Dokumenttyp
- Posterpräsentation (4) (entfernen)
Sprache
- Englisch (4)
Referierte Publikation
- nein (4)
Schlagworte
- Additive Manufacturing (1)
- Corrosion (1)
- EDX (1)
- Electron Backscatter Diffraction (1)
- Electron beam induced modification (1)
- Electron microscopy (1)
- FIB (1)
- GD-OES (1)
- Gold nanoparticles (1)
- Heat Treatment (1)
Organisationseinheit der BAM
- 5 Werkstofftechnik (4)
- 5.1 Mikrostruktur Design und Degradation (4)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.6 Anorganische Referenzmaterialien (1)
- 3 Gefahrgutumschließungen; Energiespeicher (1)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (1)
- 8 Zerstörungsfreie Prüfung (1)
- 8.5 Röntgenbildgebung (1)
Damage induced by electric field (DIEF) that happens in the transmission electron microscope (TEM) when converging the electron beam (e-beam) on microparticles (MPs) can be used to synthesis new nanomaterial and nanomaterial compositions. The research questions are to clarify the limits and possibilities of the method regarding materials that can be produced, systems to which it is applicable and working beam parameters. Synthesis of nano-objects from microparticles using DIEF in TEM could be shown for different materials. Additionally, DIEF using the e-beam in a scanning electron microscope (SEM) can also be used to synthesis nano-objects. A deeper material analysis of this nano-objects was done using TEM and shows that the material of the nanoparticles (NPs) can be gold or/and silicon. Furthermore, the size of the NPs depends on the distance to the center of DIEF whereby the larger NPs are closer to the center. The areas of gold NPs are promising candidates for plasmonic or photonic devices for energy storage or transport.
Lithium-ion batteries (LIBs) are one technology to overcome the challenges of climate and energy crisis. They are widely used in electric vehicles, consumer electronics, or as storage for renewable energy sources. However, despite innovations in batteries' components like cathode and anode materials, separators, and electrolytes, the aging mechanism related to metallic aluminum current collector degradation causes a significant drop in their performance and prevents the durable use of LIBs. Glow-discharge optical emission spectroscopy (GD-OES) is a powerful method for depth-profiling of batteries' electrode materials. This work investigates aging-induced aluminum deposition on commercial lithium cobalt oxide (LCO) batteries' cathodes. The results illustrate the depth-resolved elemental distribution from the cathode surface to the current collector. An accumulation of aluminum is found on the cathode surface by GD-OES, consistent with results from energy-dispersive X-ray spectroscopy (EDX) combined with focused ion beam (FIB) cutting. In comparison to FIB-EDX, GD-OES allows a fast and manageable depth-profiling. Results from different positions on an aged cathode indicate an inhomogeneous aluminum film growth on the surface. The conclusions from these experiments can lead to a better understanding of the degradation of the aluminum current collector, thus leading to higher lifetimes of LIBs.
The interest to additively manufacture Nickel-based superalloys has substantially grown within the past decade both academically and industrially. More specifically, additive manufacturing processes such as laser powder bed fusion (LPBF) offer the ability to produce dense parts within a single manufacturing step. In fact, the exceptional freedom in design associated with the layer-based nature of the processes is of particular interest for the complex shapes typically required in turbine applications. In certain cases, the overall part performance can be achieved by tailoring the microstructure and the crystallographic texture to the specific application. However, these advantages must be paid at a price: the large local temperature gradients associated with the rapid melting and solidification produce parts that inherently contain large residual stress in the as-manufactured state. In addition, the presence of pores in the final part may further affect the in-service part failure. As among Nickel-based alloys Inconel 718 exhibits excellent weldability, this alloy has been widely studied in open research in the domain of LPBF. However, significant microsegregation of the heavier alloying elements such as Niobium and Molybdenum accompanied by dislocation entanglements may preclude the application of conventional heat treatment schedules. Therefore, different post processing heat treatments are required for laser powder bed fused Inconel 718 as compared to conventional variants of the same alloy.
In this study, we investigated two different heat treatment routes for LPBF Inconel 718. In a first routine, the samples were stress relieved and subsequently subjected to hot isostatic pressing (HIP) followed by a solution heat treatment and a two-step age (referred to as FHT). In a second routine, the samples were subjected to a single-step direct age post stress relieving heat treatment (referred to DA). We investigated the consequences of such heat treatment schedules on the microstructure, texture, and mechanical behavior. We show that by applying a DA heat treatment the typical columnar microstructure possessing a crystallographic texture is retained, while an equiaxed untextured microstructure prevails in case of an FHT heat treatment. We further evaluate how these heat treatments affect the mechanical behaviour on the macroscopic and microscopic scale.
Early Material Damage in Equimolar CrMnFeCoNi in Mixed Oxidizing/Sulfiding Hot Gas Atmosphere
(2022)
The use of more and more varied fuels implies an increased list of criteria that need to be addressed when choosing a material for a combustion chamber and its supply pipes. The materials must be very resistant against corrosion, especially when the process takes place at temperatures above 500°C. In this work the influence of SO2 on the surface of the “Cantor alloy” is investigated.